    There is disclosed a semiconductor light emitting element formed by selective growth and being high in light emitting efficiency, in which at least one GaN-based layer grown by ELO is stacked/formed on a sapphire substrate, and a fluorescent substance for converting an ultraviolet light to a visible light is contained in a selective growth mask material layer for use in this case. Since this fluorescent substance converts the ultraviolet light to the visible light, a binding efficiency of the ultraviolet light to the fluorescent substance is enhanced in either one of a center light emitting type and UV light emitting type of light emitting elements. By further containing the fluorescent substance into a passivation film, the efficiency is further enhanced.
    公开号:US20010004112A1
    申请号:US09/745,250
    申请日:2000-12-20
    公开日:2001-06-21
    发明作者:Chisato Furukawa；Hideto Sugawara；Nobuhiro Suzuki
    申请人:Toshiba Corp；
    IPC主号:H01L33-32
    专利说明:
    [0001] This application claims benefit of priority under 35 U.S.C. §119 to Japanese Patent Application No. Hei11-362839 (1999), filed on Dec. 21, 1999, the entire contents of which are incorporated by reference herein. [0001] BACKGROUND OF THE INVENTION
    [0002] The present invention relates to a semiconductor light emitting element and a manufacturing method thereof, and more specifically, to a semiconductor light emitting element which is suitable for a semiconductor light emitting apparatus with a high light emitting efficiency. [0002]
    [0003] A storage apparatus utilizing an optical recording has a large storage capacity and is characterized by a long life and a high reliability due to non-contact, so that this type of apparatus is broadly utilized. As the light for use herein has a shorter wavelength, a recording density can be raised, and hence, blue to green light emitting elements are to be used. Moreover, some novel light emitting elements have been realized such as white LED's which obtain a white light by combining a blue LED with a YAG fluorescent substance. [0003]
    [0004] As the blue to green light emitting elements, a light emitting diode (LED) and a laser diode (LD) having a high luminance have been now obtained with a GaN-based material. [0004]
    [0005] As a crystal growth technique of this GaN-based light emitting element, much attention has been paid to epitaxially laterally overgrown (ELO) in recent years. [0005]
    [0006] FIG. 11A is a sectional view showing an outline of a growth state in ELO. First, a selective growth mask [0006] 2 is formed on a sapphire substrate 1 (FIG. 11A), and the growth of a GaN-based film is then performed with ELO, so that for a crystal defect, the GaN-based film grows so as to embed the selective growth mask owing to a difference of a growth speed in ELO between lateral and vertical directions (FIGS. 11B and 11D). Moreover, in this case, since the crystal defect is generated along with the fast lateral direction growth, there is very little transition in the GaN film by ELO on the selective growth mask. When an epitaxial layer is stacked onto this film to obtain an element structure (FIG. 11D), a defect density of a substrate is very low, and therefore a semiconductor light emitting element having excellent light emitting properties can be obtained.
    [0007] In a light emitting center (D/A) type blue LED structure of the light emitting diodes (LED) with the high luminance in which such a GaN-based material is used, InGaN which is an active layer is doped with Si as a donor and Zn, Mg or the like as an acceptor, a desired light emitting wavelength is to be obtained in a light emitting center, not in a band end, and therefore in addition to a visible light, numerous ultraviolet (UV) lights are generated. That is to say, in the case of In 13% in the composition of this active layer, the light emitting wavelength in the band end of a center wavelength 400 nm is about 365 nm, but besides the ultraviolet light from the light emitting center, the ultraviolet light from this band end is also present, and as injection current is increased, a proportion of the light emitted from the band end increases. However, this ultraviolet light is not effectively utilized, so that a light extraction efficiency remains at a low level. [0007]
    [0008] Moreover, in a UV light emitting LED which decreases In composition and generates only the ultraviolet light from the active layer, the generated ultraviolet light is not effectively extracted, and an external quantum efficiency remains to be low. Furthermore, the aforementioned ELO technique is utilized only for transition reduction. [0008]
    [0009] Additionally, in order to enhance the light emitting efficiency, in the GaN-based semiconductor light emitting element, it has been proposed to contain the fluorescent substance at least one of p-type and n-type semiconductor layers (Japanese Patent Application Laid-Open No. 82849/2000). [0009]
    [0010] However, it is difficult in manufacture to contain a particulate fluorescent substance in the semiconductor layer generally formed by vapor phase growth. [0010] SUMMARY OF THE INVENTION
    [0011] The present invention has been developed to solve the problem, and an object thereof is to provide a semiconductor light emitting apparatus high in light extraction efficiency. [0011]
    [0012] According to the present invention, there is provided a semiconductor light emitting element comprising, as a lamination structure: [0012]
    [0013] an insulating substrate; [0013]
    [0014] GaN-based stacked films stacked/formed on said insulating substrate, one of these films being a GaN-based film grown by using a selective growth mask material layer containing a fluorescent substance for converting an ultraviolet light to a visible light; and [0014]
    [0015] an active layer, formed on the GaN-based stacked films, for emitting at least an ultraviolet light component. [0015]
    [0016] According to the semiconductor light emitting element, since a fluorescent substance is mixed beforehand into a selective growth mask layer for ELO, it is possible to convert an ultraviolet light which has heretofore failed to be effectively utilized to a visible light in the vicinity of an active layer, and a bonding efficiency with the fluorescent substance can remarkably be enhanced. [0016]
    [0017] A topmost layer may further preferably be provided with a protective layer containing the fluorescent substance, and a light emitting efficiency can further be enhanced by raising a conversion efficiency to the visible light from the ultraviolet light. [0017]
    [0018] A lens may be formed on an insulating substrate back surface side, thereby it is possible to extract the light from the back-surface side, and the present invention can also be applied to flip chip mounting or the like. [0018]
    [0019] A thickness of the selective growth mask layer containing the fluorescent substance may be 50 nm or more, 20 μm or less. [0019] BRIEF DESCRIPTION OF DRAWINGS
    [0020] FIG. 1 is an element sectional view showing a constitution of a semiconductor light emitting element according to the present invention. [0020]
    [0021] FIG. 2 is a sectional view showing a structure of a semiconductor light emitting apparatus using the semiconductor light emitting element shown in FIG. 1. [0021]
    [0022] FIG. 3 is a schematic view showing a light emitting operation in the semiconductor light emitting element according to the present invention. [0022]
    [0023] FIG. 4 is a graph showing a light emitting intensity distribution of the semiconductor light emitting element shown in FIG. 3. [0023]
    [0024] FIG. 5 is an element sectional view showing a modification example of the semiconductor light emitting element. [0024]
    [0025] FIG. 6 is a schematic diagram showing a light emitting operation in the semiconductor light emitting element of a UV light emitting type. [0025]
    [0026] FIG. 7 is a plan view showing a pattern shape of a selective growth mask. [0026]
    [0027] FIG. 8 is a plan view showing another pattern shape of the selective growth mask. [0027]
    [0028] FIG. 9 is a plan view showing still another pattern shape of the selective growth mask. [0028]
    [0029] FIGS. 10A to [0029] 10D are step sectional views showing a manufacture process of the semiconductor light emitting element according to the present invention.
    [0030] FIGS. 11A to [0030] 11D are step sectional views showing a growth state by an ELO mask and ELO. DESCRIPTION OF THE PREFERRED EMBODIMENTS
    [0031] An embodiment of the present invention will be described hereinafter in detail with reference to the drawings. [0031]
    [0032] FIG. 1 is a sectional view showing a structure of a semiconductor light emitting element [0032] 10 according to the present invention.
    [0033] A GaN buffer layer [0033] 12 and n-GaN layer 13 are stacked on a sapphire substrate 11, on the layers an ELO mask layer 15 formed of SiO2 uniformly mixed with a fluorescent substance is stacked, on the layer an n-GaN layer 16 formed using the mask with ELO, further an InGaN active layer 17, p-AlGaN gap layer 18, p-GaN clad layer 19 and p+-GaN contact layer 20 are stacked, a transparent electrode 22 is formed on a light extraction surface of the p+-GaN contact layer 20, a p-electrode 24 to contact the transparent electrode and an n-electrode 25 on the exposed n-GaN layer 16 are formed, respectively, and the entire surface is covered with passivation films 21 and 23. This passivation film is also mixed with the fluorescent material.
    [0034] Additionally, the active layer is here an Al[0034] xInyGa1-x-yN (0≦x≦0.1≦y≦1) film, but various films such as a BzGa1-zN (0≦z≦1) film can be used.
    [0035] FIG. 2 is a sectional view showing a constitution of a semiconductor light emitting apparatus [0035] 30 using the semiconductor light emitting element 10 of the present invention.
    [0036] The semiconductor light emitting element [0036] 10 is mounted on a stem 31, and the p-electrode 24 of the semiconductor light emitting element 10 is connected to the stem 31 and the n-electrode 25 is connected to a lead 32 via wires 33, respectively. Moreover, the entire apparatus is covered with a cap 35.
    [0037] FIG. 3 is a schematic view showing a light emitting operation of the semiconductor light emitting element shown in FIG. 1. Here, a light emitting center type will be described. [0037]
    [0038] A light emitted from the InGaN active layer [0038] 17 as a light emitting layer is discharged in all directions (spherical shape), and an ultraviolet light component hits the fluorescent substance contained in the passivation film 23 and is converted to a visible light. Specifically, the fluorescent substance also serves as a light emitting source.
    [0039] Additionally, a light [0039] 43 turning directly to a substrate side from the active layer 17 is reflected by an insulating substrate bottom surface, that is, a lead frame reflective surface, and is extracted from above.
    [0040] As a result, since a part of the ultraviolet light component in a light [0040] 44 finally discharged from the light emitting element serves as a visible light component, a light emitting amount as the visible light increases.
    [0041] FIG. 4 is a graph showing this state. In the light emitting apparatus of a usual center light emitting type shown by a solid line, a light emitted from the active layer has peaks in a visible light band and ultraviolet light band, while in the light emitting apparatus of the present invention shown by a broken line, the peaks are reduced to one by using the fluorescent substance in the ELO mask to perform conversion, and it is seen that the light emitting amount in the visible light band increases. [0041]
    [0042] Moreover, to contain the fluorescent substance in the ELO mask material in this manner is easier in manufacture than to contain the fluorescent substance in the semiconductor layer, as proposed conventionally. [0042]
    [0043] Additionally, since a GaN-based material and sapphire substrate [0043] 11 are both transparent to the visible light, the converted light can effectively be extracted from a sapphire substrate side, that is, an element lower surface side.
    [0044] FIG. 5 shows a modification example of the semiconductor light emitting element shown in FIG. 1, and a light turning downward from the active layer [0044] 17 is positively utilized. Here, in order to enhance an extraction efficiency, a lens 50 is formed on the undersurface of the sapphire substrate 11.
    [0045] Moreover, since it is unnecessary to extract the light from the surface, the transparent electrode necessary in the constitution of FIG. 1 is omitted, and the p-electrode [0045] 24 is directly connected to the contact layer 20. Therefore, contact resistance can be reduced.
    [0046] By employing this constitution, it is possible to effectively extract the light from a back surface side which could not be extracted. Therefore, it is possible to manufacture a so-called flip chip mount type back surface emitting LED which performs light extraction from the back surface. Additionally, for flip chip mount, an assembly process is simplified, and a cost down effect is large. [0046]
    [0047] FIG. 6 shows a light emitting operation in an example in which the present invention is applied to a UV light emitting LED. An ultraviolet ray is radiated in all directions from the active layer [0047] 18, but when the fluorescent substance in the ELO mask 15 is irradiated with the ultraviolet ray, the fluorescent substance serves as a light emitting substance to emit the visible light. In other words, the fluorescent substance acts as a visible light source.
    [0048] FIGS. [0048] 7 to 9 show embodiments of a mask layer pattern, and patterns such as a striped pattern 51 shown in FIG. 7, a grid pattern 52 shown in FIG. 8, and a polka-dot pattern 53 shown in FIG. 9 can be selected.
    [0049] Additionally, by appropriately selecting the fluorescent substance, blue light emission is performed in the active layer, and mixed color conversion to yellow can be performed by the fluorescent substance in the ELO mask. [0049]
    [0050] FIGS. 10A to [0050] 10D are step sectional views showing a manufacture process of the semiconductor light emitting element according to the present invention.
    [0051] First, the sapphire substrate [0051] 11 is prepared, and the GaN buffer layer 12 and n-GaN layer 13 are successively grown on the surface of the substrate (FIG. 10A).
    [0052] Subsequently, liquidized SiO[0052] 2, for example, a material obtained by uniformly mixing the fluorescent substance with a tradename OCD (manufactured by Tokyo Ohka Kogyo Co., Ltd.) is uniformly applied with a spinner or the like, and a mask layer 14 with a film thickness of 50 nm or more, 20 nm or less is formed (FIG. 10B). A material of this mask layer will be described later.
    [0053] Subsequently, the mask layer [0053] 14 is patterned by photolithography, and the mask pattern 15 for ELO is formed (FIG. 10C).
    [0054] Moreover, this mask is used to perform ELO and grow the n-GaN layer [0054] 16, and further on the layer the InGaN active layer 17, p-AlGaN cap layer 18, p-GaN clad layer 19, and p+-GaN contact layer 20 are successively grown (FIG. 10D).
    [0055] Subsequently, a part of the element is etched as shown in FIG. 1 to expose an n-contact surface, the passivation film [0055] 21 is formed over the entire surface, a most part of the passivation film 21 on the p+-GaN contact layer 20 is removed, the transparent electrode 22 is selectively formed in the part, and the passivation film 23 is formed to cover the transparent electrode 22. These passivation films 21 and 23 are mixed with the fluorescent substance.
    [0056] Subsequently, by selectively removing the passivation films [0056] 21 and 23 to expose a part of the end of the transparent electrode and a part of the n-contact surface, and forming the p-electrode 24 and n-electrode 25 in respective places, the light emitting element 30 is obtained.
    [0057] In this embodiment, the passivation films [0057] 21 and 23 are mixed with the fluorescent substance, but the mixing of the fluorescent substance only with the passivation film 23 on the transparent electrode is functionally sufficient, and the passivation film may contain no fluorescent substance.
    [0058] Furthermore, instead of the passivation film [0058] 23 formed on the transparent electrode, a fluorescent layer may be formed.
    [0059] To use the semiconductor light emitting element formed in this manner and manufacture the semiconductor light emitting apparatus, the semiconductor light emitting element is mounted on the mount member [0059] 31 such as a lead frame, the p-electrode 24 is connected to the frame 31 via the metal wire 33, the n-electrode 25 is connected to the lead 32 via the metal wire, and the semiconductor light emitting element 10 is filled with resin 34 or the like on the lead frame. The resin 34 can contain the fluorescent substance. By containing the entire element into the cap 35 at least a top surface of which is transparent, the semiconductor light emitting apparatus is completed.
    [0060] Here, as the fluorescent substance mixed in the ELO mask pattern or the passivation film, for example, (Ba, Ca)B[0060] 4O7 (tradename CMZ-152 manufactured by Asahi Chemical Industry Co., Ltd.) and (CaSr)2P2O7 (tradename CMZ-165 manufactured by Asahi Chemical Industry Co., Ltd.) are used.
    [0061] A fluorescent slurry for applying the fluorescent substance is prepared as follows. [0061]
    [0062] By first preparing 1.5% of NC binder obtained by mixing 1.5 wt. % of nitrocellulose (e.g., H12000 by Asahi Chemical Industry Co., Ltd.) with 98.5% of butyl acetate, mixing 100 g in total of a mixture of the aforementioned fluorescent substance (Ba, Ca)B[0062] 4O7 (tradename CMZ-152 manufactured by Asahi Chemical Industry Co., Ltd.) and (CaSr)2P2O7 (tradename CMZ-165 manufactured by Asahi Chemical Industry Co., Ltd.), 100 CC of the NC binder, and 5 CC of a binding agent mixture containing glass beads finely pulverized by milling, adding butyl acetate as a viscosity modifier to perform mixing/agitating for 24 hours or more, and passing the mixture through a 200 or 250 mesh filter, the fluorescent slurry is obtained.
    [0063] This fluorescent slurry is applied. However, in a case in which a binding force is weak although sufficient milling is performed, an addition amount of NC binder is increased. When the binding force is excessively strong, a blend ratio of the fluorescent substance may be changed to solve the problem. [0063]
    [0064] The applied fluorescent slurry is baked at a temperature of around 550°C. to solidify. [0064]
    [0065] Additionally, without using such inorganic binder, an organic solvent or the like is used to apply the fluorescent substance, and the fluorescent substance can be left by performing heating to evaporate the solvent. [0065]
    [0066] As described above, according to the semiconductor light emitting apparatus of the present invention, since the fluorescent substance is mixed beforehand in the selective growth mask material, it is possible to convert a part of the ultraviolet light emitted from the light emitting layer to the visible light in the vicinity of the active layer, and the light emitting efficiency of the entire light emitting apparatus can remarkably be enhanced. [0066]
    [0067] Moreover, by further disposing a protective film containing the fluorescent substance on its topmost layer, the conversion efficiency to the visible light from the ultraviolet light is further enhanced, and the light emitting efficiency is further enhanced. [0067]
    [0068] Furthermore, according to the manufacturing method of the semiconductor light emitting apparatus of the present invention, the selective growth mask containing the fluorescent substance is securely formed by evaporation of the inorganic binder and organic solvent, and the semiconductor light emitting element with a high light emitting efficiency can steadily be manufactured. [0068]
    权利要求:
    Claims (12)
    [1" id="US-20010004112-A1-CLM-00001] 1. A semiconductor light emitting element comprising, as a lamination structure:
    an insulating substrate;
    GaN-based stacked films stacked/formed on said insulating substrate, one of these films being a GaN-based film grown by using a selective growth mask material layer containing a fluorescent substance for converting an ultraviolet light to a visible light; and
    an active layer, formed on the GaN-based stacked films, for emitting at least an ultraviolet light component.
    [2" id="US-20010004112-A1-CLM-00002] 2. The semiconductor light emitting element according to
    claim 1 , further comprising a protective film containing the fluorescent substance on a topmost layer.
    [3" id="US-20010004112-A1-CLM-00003] 3. The semiconductor light emitting element according to
    claim 1 wherein said light emitting layer includes an AlxInyGa1-x-yN (0≦x≦0.1≦y≦1) film, or a BzGa1-zN (0≦z≦1) film.
    [4" id="US-20010004112-A1-CLM-00004] 4. The semiconductor light emitting element according to
    claim 1 wherein the selective growth mask material layer containing said fluorescent substance is formed in a stripe shape.
    [5" id="US-20010004112-A1-CLM-00005] 5. The semiconductor light emitting element according to
    claim 1 wherein the selective growth mask material layer containing said fluorescent substance is formed in a grid shape.
    [6" id="US-20010004112-A1-CLM-00006] 6. The semiconductor light emitting element according to
    claim 1 wherein the selective growth mask material layer containing said fluorescent substance is formed in a polka-dot pattern.
    [7" id="US-20010004112-A1-CLM-00007] 7. The semiconductor light emitting element according to
    claim 1 , further comprising a lens formed on a back surface side of said insulating substrate.
    [8" id="US-20010004112-A1-CLM-00008] 8. The semiconductor light emitting element according to
    claim 1 wherein a thickness of the mask layer containing said fluorescent substance is in a range of 50 nm to 20 μm.
    [9" id="US-20010004112-A1-CLM-00009] 9. A manufacturing method of a semiconductor light emitting element, comprising:
    a step of forming a stack of a GaN-based semiconductor layer on an insulating substrate, said step comprising steps of using a fluorescent substance for converting an ultraviolet light to a visible light or a coat material containing the fluorescent substance as a base material to partially stack a mask material for selective growth and using the mask material layer to grow a GaN-based film; and
    a step of stacking an active layer for emitting at least the ultraviolet light on this GaN-based semiconductor layer stack.
    [10" id="US-20010004112-A1-CLM-00010] 10. The manufacturing method of the semiconductor light emitting element according to
    claim 9 wherein the step of stacking said mask material comprises a step of supplying the mask material containing said fluorescent substance together with a solvent, and evaporating a solvent component in the vicinity of 500° C. to obtain the mask material.
    [11" id="US-20010004112-A1-CLM-00011] 11. The manufacturing method of the semiconductor light emitting element according to
    claim 9 wherein the mask material containing said fluorescent substance is supplied together with an inorganic binder, heated/sealed and obtained.
    [12" id="US-20010004112-A1-CLM-00012] 12. The manufacturing method of the semiconductor light emitting element according to
    claim 11 wherein the inorganic binder is silicon oxide.
    类似技术:
    公开号 | 公开日 | 专利标题
    US6627521B2|2003-09-30|Semiconductor light emitting element and manufacturing method thereof
    US8633503B2|2014-01-21|Wafer level light emitting diode package and method of fabricating the same
    US7569989B2|2009-08-04|Light emitting device
    US8742438B2|2014-06-03|Semiconductor light-emitting device, method for manufacturing the same, and light-emitting apparatus including the same
    CN102544267B|2015-01-28|Wafer level phosphor coating method and devices fabricated utilizing method
    TWI420688B|2013-12-21|Method of removing the growth substrate of a semiconductor light-emitting device
    US8796115B2|2014-08-05|Light-emitting diode arrangement and method for producing the same
    US7141445B2|2006-11-28|Semiconductor light emitting device and method for manufacturing same
    TWI520371B|2016-02-01|Iii-nitride light emitting device with reduced strain light emitting layer
    CN101443923B|2010-12-08|Optoelectronic semiconductor component
    US20110049555A1|2011-03-03|Optoelectronic Semiconductor Chip and Method for Producing Same
    US20040124428A1|2004-07-01|Light emitting diode and method of making the same
    US20070023763A1|2007-02-01|Semiconductor light-emitting device and method for fabricating the same
    US20040090179A1|2004-05-13|Light emitting diode and method of making the same
    CN101675534A|2010-03-17|Semiconductor light emitting device configured to emit multiple wavelengths of light
    JP6419077B2|2018-11-07|Wavelength conversion light emitting device
    CN108321272A|2018-07-24|Light-emitting device and preparation method thereof
    JP2003234504A|2003-08-22|Light-emitting device
    WO2011016201A1|2011-02-10|Light-emitting element and light-emitting device
    US10361351B2|2019-07-23|Semiconductor light emitting element package including solder bump
    KR20170043312A|2017-04-21|Light emitting device package
    KR20110073114A|2011-06-29|Light emitting device and method for manufacturing thereof
    JP3503551B2|2004-03-08|Light emitting diode
    同族专利:
    公开号 | 公开日
    EP1111689A2|2001-06-27|
    JP2001177145A|2001-06-29|
    US6627521B2|2003-09-30|
    EP1111689B1|2008-03-05|
    US20030062531A1|2003-04-03|
    US20040079955A1|2004-04-29|
    US6504181B2|2003-01-07|
    DE60038216T2|2009-03-19|
    US6791118B2|2004-09-14|
    TW466787B|2001-12-01|
    DE60038216D1|2008-04-17|
    EP1111689A3|2006-06-07|
    引用文献:
    公开号 | 申请日 | 公开日 | 申请人 | 专利标题
    US20050093004A1|2002-06-26|2005-05-05|Yoo Myung C.|Thin film light emitting diode|
    US20050263776A1|2002-07-15|2005-12-01|Min-Hsun Hsieh|Semiconductor light-emitting device and method for forming the same|
    US20060006793A1|2004-07-12|2006-01-12|Baroky Tajul A|Deep ultraviolet used to produce white light|
    US20060145165A1|2002-05-15|2006-07-06|Matsushita Electric Industrial Co., Ltd.|Semiconductor light emitting device and fabrication method thereof|
    US20070148332A1|2005-12-27|2007-06-28|Samsung Electro-Mechanics Co., Ltd.|Method of forming phosphor film and method of manufacturing light emitting diode package incorporating the same|
    US20070166861A1|2006-01-02|2007-07-19|Samsung Electro-Mechanics Co., Ltd.|Gallium nitride based light emitting diode and method of manufacturing the same|
    US20070187696A1|2004-03-29|2007-08-16|Shigeya Naritsuka|Semiconductor light emitting device|
    US20080108160A1|2000-12-28|2008-05-08|Sony Corporation|Semiconductor Light Emitting Device, Its Manufacturing Method, Semiconductor Device and Its Manufacturing Method|
    US20100105156A1|2008-10-27|2010-04-29|Po-Shen Chen|Method of manufacturing light-emitting diode package|
    US20100283062A1|2003-07-04|2010-11-11|Min-Hsun Hsieh|Optoelectronic system|
    US20110095325A1|2005-01-18|2011-04-28|Epistar Corporation|Optoelectronic semiconductor device and manufacturing method thereof|
    US20150349214A1|2013-01-15|2015-12-03|Osram Opto Semiconductors|Optoelectronic Semiconductor Chip|
    US9627584B2|2013-07-15|2017-04-18|Lg Innotek Co., Ltd.|Light emitting device and light emitting device package|DE4206668A1|1991-03-05|1992-09-10|Bkl Inc|IMPROVED ELECTROLUMINESCENCE DEVICE|
    JPH05152609A|1991-11-25|1993-06-18|Nichia Chem Ind Ltd|Light emitting diode|
    JPH09153645A|1995-11-30|1997-06-10|Toyoda Gosei Co Ltd|Group-iii nitride semiconductor light-emitting device|
    JP3240926B2|1996-06-25|2001-12-25|日立電線株式会社|Light emitting element|
    TW383508B|1996-07-29|2000-03-01|Nichia Kagaku Kogyo Kk|Light emitting device and display|
    DE19638667C2|1996-09-20|2001-05-17|Osram Opto Semiconductors Gmbh|Mixed-color light-emitting semiconductor component with luminescence conversion element|
    US5813752A|1997-05-27|1998-09-29|Philips Electronics North America Corporation|UV/blue LED-phosphor device with short wave pass, long wave pass band pass and peroit filters|
    US6340824B1|1997-09-01|2002-01-22|Kabushiki Kaisha Toshiba|Semiconductor light emitting device including a fluorescent material|
    JPH1187778A|1997-09-02|1999-03-30|Toshiba Corp|Semiconductor light emitting element, semiconductor light emitting device and manufacture thereof|
    JP3036495B2|1997-11-07|2000-04-24|豊田合成株式会社|Method for manufacturing gallium nitride-based compound semiconductor|
    JP3620269B2|1998-02-27|2005-02-16|豊田合成株式会社|GaN-based semiconductor device manufacturing method|
    JPH11307813A|1998-04-03|1999-11-05|Hewlett Packard Co <Hp>|Light emitting device, its manufacture, and display|
    JP3584748B2|1998-09-10|2004-11-04|富士電機ホールディングス株式会社|Fluorescence conversion filter and color display device having the filter|
    US6404125B1|1998-10-21|2002-06-11|Sarnoff Corporation|Method and apparatus for performing wavelength-conversion using phosphors with light emitting diodes|
    JP2000082849A|1999-09-27|2000-03-21|Toshiba Corp|Semiconductor light emitting element, semiconductor light emitting device and manufacture thereof|
    JP2001111109A|1999-10-07|2001-04-20|Sharp Corp|Gallium nitride compound semiconductor light emitting device|DE10010638A1|2000-03-03|2001-09-13|Osram Opto Semiconductors Gmbh|Making light emitting semiconducting body with luminescence conversion element involves applying suspension with solvent, adhesive, luminescent material|
    JP2002170989A|2000-12-04|2002-06-14|Sharp Corp|Nitride based compound semiconductor light emitting element|
    JP3812827B2|2001-08-23|2006-08-23|ソニー株式会社|Mounting method of light emitting element|
    US20030189215A1|2002-04-09|2003-10-09|Jong-Lam Lee|Method of fabricating vertical structure leds|
    KR100499129B1|2002-09-02|2005-07-04|삼성전기주식회사|Light emitting laser diode and fabricatin method thereof|
    CN100508221C|2002-10-30|2009-07-01|奥斯兰姆奥普托半导体有限责任公司|Method for producing a light source provided with electroluminescent diodes and comprising a luminescence conversion element|
    EP1556904B1|2002-10-30|2018-12-05|OSRAM Opto Semiconductors GmbH|Method for producing a light source provided with electroluminescent diodes and comprising a luminescence conversion element|
    US6855571B1|2003-02-14|2005-02-15|Matsushita Electric Industrial Co., Ltd.|Method of producing GaN-based semiconductor laser device and semiconductor substrate used therefor|
    CN100509994C|2003-03-13|2009-07-08|日亚化学工业株式会社|Light emitting film, luminescent device, method for manufacturing light emitting film and method for manufacturing luminescent device|
    US7923918B2|2003-03-13|2011-04-12|Nichia Corporation|Light emitting film, luminescent device, method for manufacturing light emitting film and method for manufacturing luminescent device|
    US7521854B2|2003-04-15|2009-04-21|Luminus Devices, Inc.|Patterned light emitting devices and extraction efficiencies related to the same|
    US7667238B2|2003-04-15|2010-02-23|Luminus Devices, Inc.|Light emitting devices for liquid crystal displays|
    US7274043B2|2003-04-15|2007-09-25|Luminus Devices, Inc.|Light emitting diode systems|
    US6831302B2|2003-04-15|2004-12-14|Luminus Devices, Inc.|Light emitting devices with improved extraction efficiency|
    US7450311B2|2003-12-12|2008-11-11|Luminus Devices, Inc.|Optical display systems and methods|
    US7084434B2|2003-04-15|2006-08-01|Luminus Devices, Inc.|Uniform color phosphor-coated light-emitting diode|
    US7074631B2|2003-04-15|2006-07-11|Luminus Devices, Inc.|Light emitting device methods|
    US7211831B2|2003-04-15|2007-05-01|Luminus Devices, Inc.|Light emitting device with patterned surfaces|
    US7098589B2|2003-04-15|2006-08-29|Luminus Devices, Inc.|Light emitting devices with high light collimation|
    US7262550B2|2003-04-15|2007-08-28|Luminus Devices, Inc.|Light emitting diode utilizing a physical pattern|
    US20040259279A1|2003-04-15|2004-12-23|Erchak Alexei A.|Light emitting device methods|
    US7083993B2|2003-04-15|2006-08-01|Luminus Devices, Inc.|Methods of making multi-layer light emitting devices|
    US7105861B2|2003-04-15|2006-09-12|Luminus Devices, Inc.|Electronic device contact structures|
    KR101034055B1|2003-07-18|2011-05-12|엘지이노텍 주식회사|Light emitting diode and method for manufacturing light emitting diode|
    US7341880B2|2003-09-17|2008-03-11|Luminus Devices, Inc.|Light emitting device processes|
    US7344903B2|2003-09-17|2008-03-18|Luminus Devices, Inc.|Light emitting device processes|
    JP2005167138A|2003-12-05|2005-06-23|Nec Lighting Ltd|White light emitting element|
    KR100581831B1|2004-02-05|2006-05-23|엘지전자 주식회사|Light emitting diode|
    DE202005002110U1|2004-02-19|2005-05-04|Hong-Yuan Technology Co., Ltd., Yonghe|Light-emitting device|
    CN100359705C|2004-03-30|2008-01-02|深圳市蓝科电子有限公司|Method of mfg. white light LED|
    US20050224812A1|2004-03-31|2005-10-13|Yu-Chuan Liu|Light-emitting device and manufacturing process of the light-emitting device|
    US7227192B2|2004-03-31|2007-06-05|Tekcove Co., Ltd|Light-emitting device and manufacturing process of the light-emitting device|
    US7553683B2|2004-06-09|2009-06-30|Philips Lumiled Lighting Co., Llc|Method of forming pre-fabricated wavelength converting elements for semiconductor light emitting devices|
    US20060038188A1|2004-08-20|2006-02-23|Erchak Alexei A|Light emitting diode systems|
    US20060043400A1|2004-08-31|2006-03-02|Erchak Alexei A|Polarized light emitting device|
    KR100616631B1|2004-11-15|2006-08-28|삼성전기주식회사|Nitride based semiconductor light emitting device and method for manufacturing the same|
    KR100624449B1|2004-12-08|2006-09-18|삼성전기주식회사|Semiconductor emitting device with approved and manufacturing method for the same|
    US20070145386A1|2004-12-08|2007-06-28|Samsung Electro-Mechanics Co., Ltd.|Semiconductor light emitting device and method of manufacturing the same|
    US8680534B2|2005-01-11|2014-03-25|Semileds Corporation|Vertical light emitting diodeshaving metal substrate and spin coated phosphor layer for producing white light|
    US8012774B2|2005-01-11|2011-09-06|SemiLEDs Optoelectronics Co., Ltd.|Coating process for a light-emitting diode |
    KR100665116B1|2005-01-27|2007-01-09|삼성전기주식회사|Galium Nitride-Based Light Emitting Device Having LED for ESD Protection|
    US7291864B2|2005-02-28|2007-11-06|The Regents Of The University Of California|Single or multi-color high efficiency light emitting diodeby growth over a patterned substrate|
    DE102005023134A1|2005-05-19|2006-11-23|Patent-Treuhand-Gesellschaft für elektrische Glühlampen mbH|Luminescence conversion LED|
    KR100655162B1|2005-06-24|2006-12-08|더리즈|Fabrication method of passivation layer for light emitting devices|
    US20070045640A1|2005-08-23|2007-03-01|Erchak Alexei A|Light emitting devices for liquid crystal displays|
    US7196354B1|2005-09-29|2007-03-27|Luminus Devices, Inc.|Wavelength-converting light-emitting devices|
    JP2007109792A|2005-10-12|2007-04-26|Sony Corp|Semiconductor light-emitting element and wavelength conversion substrate|
    JP2007165409A|2005-12-09|2007-06-28|Rohm Co Ltd|Semiconductor light emitting element and method of manufacturing same|
    KR100723233B1|2006-03-31|2007-05-29|삼성전기주식회사|White light emitting device|
    US20070295951A1|2006-06-26|2007-12-27|Jen-Inn Chyi|Light-emitting diode incorporating an array of light extracting spots|
    JP2008041739A|2006-08-02|2008-02-21|Tokai Kogaku Kk|Fluorescent device|
    US7847306B2|2006-10-23|2010-12-07|Hong Kong Applied Science and Technology Research Insitute Company, Ltd.|Light emitting diode device, method of fabrication and use thereof|
    US20080101062A1|2006-10-27|2008-05-01|Hong Kong Applied Science and Technology Research Institute Company Limited|Lighting device for projecting a beam of light|
    US8110425B2|2007-03-20|2012-02-07|Luminus Devices, Inc.|Laser liftoff structure and related methods|
    US8916890B2|2008-03-19|2014-12-23|Cree, Inc.|Light emitting diodes with light filters|
    JP5279006B2|2008-03-26|2013-09-04|パナソニック株式会社|Nitride semiconductor light emitting device|
    WO2010100942A1|2009-03-05|2010-09-10|株式会社小糸製作所|Light-emitting module, method of producing light-emitting module, and lighting unit|
    KR101662010B1|2010-05-20|2016-10-05|엘지이노텍 주식회사|Light Emitting Device|
    DE102010051287A1|2010-11-12|2012-05-16|Osram Opto Semiconductors Gmbh|Optoelectronic semiconductor chip and method for its production|
    US8492746B2|2011-09-12|2013-07-23|SemiLEDs Optoelectronics Co., Ltd.|Light emitting diodedice having wavelength conversion layers|
    US8912021B2|2011-09-12|2014-12-16|SemiLEDs Optoelectronics Co., Ltd.|System and method for fabricating light emitting diodedice with wavelength conversion layers|
    US8410508B1|2011-09-12|2013-04-02|SemiLEDs Optoelectronics Co., Ltd.|Light emitting diodepackage having wavelength conversion member and wafer level fabrication method|
    US8841146B2|2011-09-12|2014-09-23|SemiLEDs Optoelectronics Co., Ltd.|Method and system for fabricating light emitting diodedice with wavelength conversion layers having controlled color characteristics|
    CN102723418A|2012-01-18|2012-10-10|许并社|Conformal coating white light LED chip structure possessing fluorescent characteristic passivation layer|
    DE102012217640B4|2012-09-27|2020-02-20|Osram Opto Semiconductors Gmbh|Optoelectronic component and method for its production|
    CN102867901B|2012-09-29|2015-10-07|晶科电子（广州）有限公司|A kind of white light LED part with phosphor powder layer and preparation method thereof|
    JP2015173142A|2014-03-11|2015-10-01|株式会社東芝|semiconductor light-emitting device|
    TWI550902B|2014-04-02|2016-09-21|國立交通大學|Light emitting diode device|
    CN104681721B|2015-03-15|2017-10-24|西安电子科技大学|GaN Gunn diodes and preparation method based on notch structures|
    KR101761856B1|2016-03-02|2017-07-26|서울반도체 주식회사|Light emitting diode having plurality of light emitting cells and method of fabricating the same|
    法律状态:
    2000-12-20| AS| Assignment|Owner name: KABUSHIKI KAISHA TOSHIBA, JAPAN Free format text: ASSIGNMENT OF ASSIGNORS INTEREST;ASSIGNORS:FURUKAWA, CHISATO;SUGAWARA, HIDETO;SUZUKI, NOBUHIRO;REEL/FRAME:011419/0247 Effective date: 20001218 |
    2006-06-09| FPAY| Fee payment|Year of fee payment: 4 |
    2010-06-09| FPAY| Fee payment|Year of fee payment: 8 |
    2014-08-15| REMI| Maintenance fee reminder mailed|
    2015-01-07| LAPS| Lapse for failure to pay maintenance fees|
    2015-02-02| STCH| Information on status: patent discontinuation|Free format text: PATENT EXPIRED DUE TO NONPAYMENT OF MAINTENANCE FEES UNDER 37 CFR 1.362 |
    2015-02-24| FP| Expired due to failure to pay maintenance fee|Effective date: 20150107 |
    优先权:
    申请号 | 申请日 | 专利标题
    JP1999-362839||1999-12-21||
    JP36283999A|JP2001177145A|1999-12-21|1999-12-21|Semiconductor light emitting device and method of manufacturing the same|
    JP11-362839||1999-12-21||US10/281,852| US6627521B2|1999-12-21|2002-10-28|Semiconductor light emitting element and manufacturing method thereof|
    US10/602,099| US6791118B2|1999-12-21|2003-06-23|Semiconductor light emitting element and manufacturing method thereof|
    [返回顶部]