    • 专利摘要:
    A coating composition for fabrics includes wetted microspheres containing a phase change material dispersed throughout a polymer binder, a surfactant, a dispersant, an antifoam agent and a thickener. Preferred phase change materials include paraffinic hydrocarbons. The microspheres may be microencapsulated. To prepare the coating composition, microspheres containing phase change material are wetted and dispersed in a dispersion in a water solution containing a surfactant, a dispersant, an antifoam agent and a polymer mixture. The coating is then applied to a fabric.
    公开号:US20010000517A1
    申请号:US09/735,380
    申请日:2000-12-11
    公开日:2001-04-26
    发明作者:Joseph Zuckerman；Robert Pushaw；Bernard Perry；Daniel Wyner
    申请人:Gateway Technologies Inc；
    IPC主号:D06N3-0061
    专利说明:
    [1] 1. This invention relates to substrate coatings containing energy absorbing, temperature stabilizing phase change materials and methods of manufacturing same. More particularly, this invention relates to fabric coatings containing microspheres of phase change material dispersed in a polymer binder and methods of manufacturing same. BACKGROUND OF THE INVENTION
    [2] 2. Coatings are typically applied to fabrics to increase water resistance, water transport, insulative ability or heat storage properties of the fabrics. Recently, microencapsulated phase change materials have been described as a suitable component for fabric coatings when exceptional heat transfer and storage capabilities are desired. In particular, International Patent Application No. PCT/US93/05119 for “Fabric with Reversible Enhanced Thermal Properties” to Colvin, et al., which is incorporated herein by reference, discloses that fabrics coated with a binder containing microcapsules filled with energy absorbing phase change material enables the fabric to exhibit extended or enhanced heat retention or storage properties.
    [3] 3. Research has demonstrated that applying a binder containing microspheres of phase change materials with commercial coating equipment can be problematic. For example, use of solvent based gravure printing techniques in which a solvent system was employed to achieve uniform dispersion of the microspheres in a binder proved unsuccessful because the solvent systems damaged the microspheres.
    [4] 4. Thermoplastic gravure printing techniques also proved unsatisfactory for use with microspheres of phase change material. When using higher temperature thermoplastic gravure printing techniques, sustained temperature of 325° F. caused severe damage to the microspheres. Although lower temperature thermoplastic gravure printing techniques avoided significant damage to the microspheres, the resulting coating was found lacking in washability and durability. Moreover, lower temperature thermoplastic gravure printing techniques precluded addition of the desired amounts of the microspheres, allowing addition of microspheres of up to only about 20% by dry weight of the microsphere/binder material. This low percentage of phase change material in the coating makes the coating susceptible to undesirable heat transfer across the coating, especially in locations where phase change material is sparsely applied.
    [5] 5. Attempts to encapsulate microspheres of phase change materials in a thermoplastic spray have also proved unsatisfactory. In particular, scattering microspheres into a stream of sprayed, fibrous thermoplastic material resulted in a binder matrix that did not fully encase the microspheres. The resulting binder/microsphere material was susceptible to loss of microspheres, which worked loose and were continually shedded from the fabric. In addition, the coating lacked uniformity of thickness and microsphere distribution.
    [6] 6. Attempts were also made to utilize thermoplastic extrusion techniques to create a film of continuous web in which microspheres of phase change material were uniformly distributed. However, thermal breakdown of the microspheres resulted from the higher temperatures utilized. The extrusion screw employed with these techniques also physically damaged the microspheres.
    [7] 7. Phase change materials in microencapsulated form are commonly supplied as a dry powder. This powder is difficult to wet and uniformly disperse in aqueous systems. Moreover, some microencapsulated phase change materials have an internal layer of modified gelatin which is hydrophilic and capable of absorbing its own weight in water. Not only does the hydrophilic quality of such microcapsules make more standard component proportions inapplicable, microcapsules which have absorbed water tend to swell and associate, increasing the viscosity of the coating system above acceptable limits. Although the precise behavior of microcapsules in the coating system which have absorbed water is uncertain, it is believed that such microcapsules agglomerate, reducing their dispersion throughout the binder of the coating system, which de-stabilizes the binder. This de-stabilization can increase over time. When latex binders are used with microencapsulated phase change material, de-stabilization of the latex binder can continue until the latex binder coagulates.
    [8] 8. U.S. Pat. Nos. 5,254,380, 5,211,949, 5,282,994 and 5,106,520 for “Dry Powder Mixes Comprising Phase Change Materials” describe free flowing, conformable powder-like mixes of silica particles and a phase change material which the silica particles of between 7×10−3 to 7×10−2 microns are mixed with phase change material in a ratio of up to 80% by weight of phase change material. While these patents describe a matrix in which microspheres of phase change materials need not be separately encapsulated, they do not describe the use of dry powder mixes containing phase change materials in binder matrices for coating fabrics.
    [9] 9. It is against this background that the significant improvements and advancement of the present invention have taken place in the field of fabric coatings containing energy absorbing, temperature stabilizing phase change materials and methods of manufacturing same. OBJECTS OF THE INVENTION
    [10] 10. It is the principal object of the present invention to provide an improved fabric coating composition containing phase change material of a density sufficient to effect or control heat and energy transfer across the coating and/or store heat in the coating.
    [11] 11. It is another object of the present invention to provide a coating composition of the foregoing character which will maintain substantially all of the breathability, flexibility or other principal qualities of the fabric to which it is applied.
    [12] 12. It is a further object of the present invention to provide coated fabrics having the aforementioned properties which are resistant to heat, pressure and chemicals encountered during the coating process.
    [13] 13. It is a still further object of the present invention to provide coated fabrics having the aforementioned qualities which are durable, resistant to heat, moisture, solvents, laundering, and/or drycleaning, without degradation to or loss of the phase change material.
    [14] 14. It is still another object of the present invention to provide an improved method of applying coating compositions containing phase change materials and having the aforementioned qualities as coatings on fabrics by utilizing commercially available equipment.
    [15] 15. It is yet another object of the present invention to provide an improved method of applying coatings containing phase change materials to fabrics without damage or degradation to the phase change materials.
    [16] 16. It is still another object of the present invention to provide an improved method for evenly dispersing phase change material throughout a binder and maintaining an even distribution of the phase change material while coating a fabric with the binder and phase change material dispersion. SUMMARY OF THE INVENTION
    [17] 17. The present invention comprises coatings for fabrics and methods for manufacturing the same. A preferred coating includes wetted microspheres containing a phase change material dispersed throughout a polymer latex binder, and including a surfactant, a dispersant, an antifoam agent and a thickener. Preferred phase change materials include paraffinic hydrocarbons. To prepare a preferred coating composition of the present invention, microspheres containing phase change material are dispersed in an aqueous solution of a surfactant, a dispersant, and an antifoam agent mixture, followed by dispersion in a polymer mixture to form a coating composition. An alternative method of preparing the coating composition of the present invention includes dispersing microspheres containing phase change material in wet cake form in an aqueous solution of a surfactant, a dispersant, antifoam agent and polymer to form a coating composition. The coating composition of the present invention are then applied as a coating on a fabric. DETAILED DESCRIPTION OF THE INVENTION
    [18] 18. In accordance with the present application, it has been discovered that wetting microspheres of phase change materials with water and maintaining a uniform dispersion of the microcapsules in a wet coating minimizes or eliminates the tendency of such microspheres to destabilize the binder polymer in which the microspheres are dispersed.
    [19] 19. A coating composition which includes microspheres containing a phase change material is prepared by mixing dry microspheres with an excess of water to induce the microspheres to swell with water until swelling is complete. Preferably, a surfactant and a dispersant are added to the water prior to mixing with the microspheres. The surfactant decreases surface tension of the layers of the microspheres and thereby promotes wetting of the microspheres. An antifoam agent is added to and mixed slowly with the microsphere/water mixture to remove air trapped as dispersed bubbles in the mixture. A thickener is added to adjust the viscosity of the mixture to prevent the microspheres from floating or sinking in the mixture. A viscosity of at least 500 cps is preferred. Adjusting the pH of the mixture to 8.5 or greater promotes swelling of the microspheres. Swelling is typically complete in from 6 to 24 hours, at which time the microspheres will have reached an equilibrium with the aqueous phase in which they are dispersed. Thereafter, the microsphere dispersion is added to a mixture of a polymer dispersion, surfactant and dispersant having a pH approximately the same as the pH of the microsphere dispersion. The viscosity and rheology of the resulting coating compound is adjusted to meet the requirements of the coating method employed.
    [20] 20. The polymeric binder may be in the form of a solution, dispersion or emulsion in water or in organic solvent. The polymeric binder may initially be polymeric, or in the form of monomers and/or oligomers, or low molecular weight polymers which upon drying and/or curing are converted to their final molecular weight and structure. These binders are preferably film-forming, elastomeric, and have a glass transition temperature in the range of about −45° C. to +45° C., depending upon the desired application. For most garment applications, an elastomeric polymer with a glass transition temperature of about −30° C. to about +12° C. is preferred.
    [21] 21. The polymers may be linear or branched. Copolymers may be random, block or radial. The polymers may have pendant reactive groups, reactive ends or other crosslinking mechanisms, or be capable of entanglement and/or hydrogen bonding in order to increase the toughness of the finished coating and/or its resistance to heat, moisture, solvents, laundering, dry-cleaning or other chemicals.
    [22] 22. Suitable monomers include, but are not limited to, acrylic eaters (preferably alkyl-acrylates and methacrylates containing 4 to 17 carbon atoms); styrene; isoprene; acrylonitrile; butadiene; vinyl acetate; vinyl chloride; vinyldiene chloride; ethylene; butylene; propylene; chloroprene; etc. Polymers and copolymers based upon the above mentioned monomers and/or upon silicone; epoxy; polyurethane; fluorocarbons; chlorosulfonated polyethylene; chlorinated polyethylene; and other halogenated polyolefins are also useful.
    [23] 23. The surfactant described above has a preferred wetting time of not greater than 50 seconds at a concentration of 0.10% by the Draves Wetting Test. Nonionic and anionic surfactants are acceptable. Dioctyl sodium sulfosuccinamate (sometimes referred to herein as “DOS”) is a preferred surfactant.
    [24] 24. The dispersing agent employed as described above is preferably a nonionic or anionic dispersant, such as dispersants based upon phosphate esters. A 90% solution of the potassium salt of a phosphated coester of an alcohol and an aliphatic ethoxylate such as Strodex PK90™ available from Dexter Chemical company of New York City, N.Y. is a preferred dispersant.
    [25] 25. From 0.1% to 0.8% by weight of dry DOS to dry microspheres and from 0.1% to 0.8% by weight of dry PK90™ to dry microspheres is effective. The total amount of DOS and PK90™ is preferably apportioned equally between the dry microsphere dispersion and the polymer dispersion to which the microspheres will be added after swelling is complete.
    [26] 26. Suitable thickeners include polyacrylic acid, cellulose esters and their derivative, polyvinyl alcohols, and others known in the art. A preferred thickener is Acrysol ASE60™ available from Rohm and Haas Company of Philadelphia, Pa. ASE60™ is preferably obtained as a 28% solution of an alkali-swellable polyacrylic acid which increases in viscosity upon neutralization. As described above, thickener is added first to achieve the desired viscosity of the microsphere dispersion, which will vary depending on the particular phase change material selected, and then to adjust the wet coating to meat the requirements of the coating method employed.
    [27] 27. Preferred antifoam agents include aqueous dispersions of silicone oil, such as polydimethylsiloxane, containing dispersed fine particle silica, and mixtures of mineral oil, surfactant and fine particle silica, such as AF 9020™ available from General Electric Company of Waterford, N.Y., and Advantage 831™ available from Hercules Chemical Company of Wilmington, Del.
    [28] 28. A preferred polymer binder is made with a dispersed polymer latex is an anionic, heat reactive, acrylic latex containing 59% non-volatiles in water, such as the acrylic polymer latex marketed under the tradename Hycar XT9202™ and available from B. F. Goodrich Chemical Company of Cleveland, Ohio. The polymer latex has a glass transition temperature of −25° C. When properly dried and cured, fabric coatings made from polymer latex such as Hycar XT9202™ are washable and dry-cleanable.
    [29] 29. The coating compositions of the present invention preferably include from 30 to 500 parts by dry weight of microspheres for each 100 parts by dry weight of acrylic polymer latex. The coating compositions preferably include from 0.005% to 6% dry weight each of surfactant and dispersant to dry weight of microspheres. Water is added to total 25% to 80% of the final wet coating composition. An antifoam agent of from 0% to 1% dry weight to total weight of the final wet coating composition is preferred. The most preferred ratios of components of the coating composition of the present invention are: 70 to 300 parts by dry weight of microspheres for each 100 parts by dry weight of acrylic polymer latex, 0.1% to 1% dry weight each of surfactant and dispersant to dry weight of microspheres, water totaling 40% to 60% of the final wet coating composition and antifoam agent of from 0.1% to 0.5% dry weight to total weight of the final wet coating composition.
    [30] 30. An alternative method utilizes microspheres of phase change material which are not completely dried during the manufacturing process. Wet microspheres containing from about 25% to about 65% by weight water are preferred and can be readily handled. When using such microspheres, a surfactant and a dispersant are added to a polymer binder dispersion before the wetted microspheres are dispersed therein. DOS and Strodex PK90™ are preferably mixed with the polymer binder dispersion before the wet microspheres are mixed with and dispersed therein.
    [31] 31. Generally speaking, phase change materials have the capability of absorbing or releasing thermal energy to reduce or eliminate heat transfer at the temperature stabilizing range of the particular temperature stabilizing material. The phase change material inhibits or stop the flow of thermal energy through the coating during the time the phase change material is absorbing or releasing heat, typically during the material's change of phase. This action is transient, i.e., it will be effective as a barrier to thermal energy until the total latent heat of the temperature stabilizing material is absorbed or released during the heating or cooling process. Thermal energy may be stored or removed from the phase change material, and can effectively be recharged by a source of heat or cold. By selecting an appropriate phase change material, a fabric can be coated for use in a particular application where the stabilization of temperatures is desired. Two or more different phase change materials can be used to address particular temperature ranges and such materials can be mixed.
    [32] 32. Paraffinic hydrocarbon phase change materials suitable for incorporation into fabric coatings are shown below in Table I. The number of carbon atoms contained in such materials and is directly related to the melting point of such materials. TABLE I COMPOUND NO. CARBON ATOMS MELTING POINT ° C.n-Octacosane 28 61.4 n-Heptacosane 27 59.0 n-Hexacosane 26 56.4 n-Pentacosane 25 53.7 n-Tetracosane 24 50.9 n-Tricosane 23 47.6 n-Docosane 22 44.4 n-Henelcosane 21 40.5 n-Eicosane 20 36.8 n-Nonadecane 19 32.1 n-Octadecane 18 28.2 n-Heptadecane 17 22.0 n-Hexadecane 16 18.2 n-Pentadecane 15 10.0 n-Tetradecane 14 5.9 n-Tridecane 13 −5.5
    [33] 33. Phase change materials such as the listed paraffinic hydrocarbons are preferably formed into microspheres and encapsulated in a single or multi-layer shell of gelatin or other materials. Encapsulated microsphere diameters of from 1 to 100 microns are preferred, most preferably in the range 10 to 60 microns. Encapsulated microspheres containing phase change materials are sometimes referred to herein as “microPCMs.” Microspheres may also be bound in a silica matrix of sub-micron diameters. Microspheres containing n-octadecane or n-eicosane are suitable for fabric coatings for clothing. Such microspheres are available from MacGill Enterprises, Inc. of West Milton, Ohio and Microtek Laboratories, Inc. of Dayton, Ohio. EXAMPLE I
    [34] 34. A preferred coating formulation where high phase change material content and limited extensibility is required, for example with non- or low-stretch fabrics such as non-woven or woven fabrics, is prepared as shown in Table II. TABLE II COMPONENT WT % DIRECTIONSMICROSPHERE DISPERSION: Water 35.00 75% DOS 0.40 Strodex PK90 (90% NV) 0.20 n-Eicosane microspheres (dry) 36.50 Acrysol ASE60 (28% NV) 1.00 Mix, dispersing ingredients well. AF9020 (20% NV) 0.05 Mix slowly with dispersed ingredients until foam dissipates. Ammonium hydroxide (28%) 0.50 Add slowly to the defoamed dispersion, with good mixing. Let stand 6 hours. Remix immediately before use. POLYMER BINDER DISPERSION: Hycar XT9202 latex polymer 21.35 75% DOS 0.20 Strodex PK90 0.10 Acrysol ASE60 (28% NV) 3.40 Hercules Advantage 831 0.30 Mix ingredients slowly until foam dissipates. COATING: Ammonium Hydroxide 1.00 Slowly add Microsphere Dispersion to Polymer Binder Dispersion; add ammonium hydroxide slowly with good mixing thereto. EXAMPLE II
    [35] 35. An alternative coating formulation where high phase change material content and limited extensibility is required, for example with non- or low-stretch fabrics such as non-woven or woven fabrics, is prepared as shown in Table III. TABLE III COMPONENT WT % DIRECTIONSHycar XT9202 21.00 75% DOS 0.40 Strodex PK90 (90% NV) 0.33 Mix. 50% wet n-Octadecane 72.00 Add slowly to latex polymer microspheres mixture, with good mixing, dispersing microspheres well. Acrysol ASE60 (28% NV) 4.40 AF9020 (20% NV) 0.05 Hercules Advantage 831 0.30 Mix Ingredients slowly until foam dissipates. Ammonium Hydroxide (28%) 1.52 Add slowly, with good mixing.
    [36] 36. Addition of microspheres as described above in the preferred weight ratios eliminates tack and prevents blocking of the coated fabrics typically experienced with coatings having low glass transition temperature polymers such as those based on acrylic latex polymers. Tack, the tendency of material to stick to itself, can make rolls of coated fabric difficult to unroll. This can occur when rolls of coated fabric are stored in warm places or are stored under pressure of rolls stacked on top of one another. Antiblocking additives are typically added to coating formulations to prevent tack. The presence of microspheres in the coatings of the present invention eliminates the need for antiblocking additives.
    [37] 37. Non-foam coating compositions like those described in Examples I and II above are suitable for application to substantially non-extensible fabrics of both woven and non-woven construction. A preferred coated fabric is produced using the non-foam coating like that of Example I and a 100% polyester, non-woven fabric having a weight of 0.8 oz/sq yd. A preferred fabric selected is HEF™ (a hydro-entangled fiber) obtained from Veretec™ of Bethune, S.C. Similar fabrics are available from du Pont de Nemours Company. Using a wet coating composition containing 50% by dry weight of microspheres, a knife-over-roll coating head configuration is employed. A desired weight of 2.5 oz dry weight of microspheres/sq yd is obtained with a knive-over roll gap of 0.022 inches off the fabric. The coating line speed is 8 linear yards per minute. The coating is cured at a temperature of approximately 260° F. EXAMPLE III
    [38] 38. A preferred foam coating formulation of the present invention may be used with breathable fabric to maintain the heat and moisture dissipation capability of the fabric. In this example, the materials are subject to mechanical frothing. Foam stabilizers are added to maintain the foam after application to the fabric. Foam stabilizers may be inorganic salts of fatty acids or their sulfate partial esters, anionic surfactants, among other compounds. Preferred foam stabilizers for use with phase change material microspheres are sodium lauryl sulfate, ammonium stearate, di-sodium-n-octadecyl sulfosuccinamate and mixtures thereof. Ammonium stearate concentrations (dry as a percent of wet coating) of 0.5% to 6% plus 0.2% to 4% sulfosuccinamate are most preferred. The coatings are prepared as shown in Table IV. TABLE IV COMPONENT WT % DIRECTIONSWater 4.69 75% DOS 0.20 Strodex PK90 (90% NV) 0.17 Hycar XT9202 33.74 35% wet n-Octadecane 54.53 Add slowly to above ingredients, microspheres dispersing microspheres well. AF9020 (20% NV) 0.05 Mix slowly, until foam dissipates. Acrysol ASE60 (20% NV) 1.55 Hercules Advantage 831 0.23 Mix ingredients slowly until foam (28% NV) dissipates. Ammonium Hydroxide 0.60 Add slowly while mixing. Do (28%) not mix in air. Ammonium Stearate (33%) 2.96 Di-sodium-n-octadecyl- 1.28 Add slowly, with good mixing. sulfosuccinamate (35%)
    [39] 39. Preferred foam coatings contain ammonium stearate in an amount by dry weight of from 0.25% to 10% of the total weight of the final wet coating composition foam is preferred and from 0.1 to 8% dry weight of sulfosuccinamate to total weight of the final wet coating composition foam. Most preferably, ammonium stearate by dry weight 1% to 3% of the total weight of the final wet coating composition foam and the sulfosuccinamate by dry weight comprises from 0.3 to 2% dry weight to total weight of the final wet coating composition foam.
    [40] 40. The liquid coating is mechanically foamed by pumping through an Oakes mixer or similar mechanical foamer. The mixer injects air into the liquid and finely disperse the air. The foamed liquid is pumped to a coating head, usually a knife coater, where it is spread onto the fabric. The fabric/foam coating is then passed through a heated oven to dry and cure the foam.
    [41] 41. Foam coating compositions like those described in Example III are also suitable for application to substantially non-extensible fabrics of both woven and non-woven construction when maintaining breathability of the fabric is desired. A preferred methodology includes applying the foam coating of Example III to HEF™ having a weight of 1¼oz/sq yd. The wet coating composition of Example III is foamed to a preferred blow ratio of air to wet compound of 2:1, with acceptable blow ratios ranging from ½:1 to 10:1. A knife-over-roll coating head configuration is employed. The desired weight of 0.5 oz dry weight of microspheres/sq yd is obtained with a knive-over roll gap of 0.018 inches off the fabric. The fabric is drawn through the coating line at a rate of 10 linear yards per minute. The coating is cured at a temperature of approximately 260° F., with the fabric carried on a tenter frame to prevent shrinkage of the fabric. EXAMPLE IV
    [42] 42. Tests were conducted on acrylic fleeces in which the fibers containing microPCMs, and on non-woven materials (sometimes referred to herein as “substrate”) having a coating containing microPCMs. Acrylic fleeces without microPCMs having approximately the same weight per unit area as the fleeces with microPCMs, and substrates without microPCMs having the same thickness as the non-woven substrates having a coating containing microPCMs, served as comparison materials. Specific data regarding the sample materials tested are included in Table V. TABLE V Acrylic Substrate Acrylic without Substrate without Materials Tested with PCM PCM with PCM PCMWt/unit area (g/m2) 270 250 227 207 Stand thickness (mm) 5.40 5.63 0.63 0.61 Compressibility (lbs) 12 16 13 20 Raw density (kg/m3) 49 44 360 339
    [43] 43. The content of microPCM in the acrylic fleeces was approximately 10 per cent. About 7 g/m2 microPCM was included in the coating of the non-woven substrate. This is equal to a content of microPCM of about 3%. The phase change temperature of the microPCM material ranged from about 22° C. to about 25° C.
    [44] 44. Tests of water-vapor permeability and water-vapor absorption of the materials were based upon the test methods of the standards DIN 53 332 and DIN 53 333. The tests of the water-vapor permeability were carried out under constant climatic conditions of 23° C. temperature and 40% relative humidity. The water-vapor absorption of the materials was tested at a constant environmental temperature of 23° C. at varying relative humidities. The following thermophysical parameters of the materials were measured: thermal conductivity (A); thermal resistance (R); temperature conductivity (a); and specific thermal capacity (c).
    [45] 45. Test results indicated that the water-vapor permeability is not influenced by the incorporation of microPCMs. The acrylic fleeces tested possess a water-vapor permeability of about 5 mg/cm2/h as a result of the material structure. The non-woven substrate to which the microPCM layer is applied is with about 0.75 mg/cm2/h, nearly impermeable for water-vapor.
    [46] 46. The water-vapor absorption of the samples is primarily determined by the absorption ability of the basic material. The incorporated microPCM causes a slight increase of the water-vapor absorption under the same climatic conditions. The water-vapor absorption of the acrylic fleece without microPCM was about 1.5% at a temperature of 23° C. and a relative humidity of 80%. The acrylic fleece with microPCM absorbs about 0.3% more water-vapor under the same conditions.
    [47] 47. Tests of heat insulation and the heat storage were carried out under varying temperature, humidity and static pressure. Test conditions with a material temperature in the phase change range of 24° C., a material humidity that results from 30% air humidity and a pressure of 1 kPa were selected as a starting point for the measurements. Table VI is a summary of the test results. TABLE VI thermophysical Acrylic Acrylic Substrate Substrate parameters with PCM without PCM with PCM without PCMA (w/m K) 0.0398 0.0342 0.1012 0.1782 R (m2 K/W) 0.1281 0.1491 0.0057 0.0029 c (kJ/kg K) 3.022 2.391 2.468 1.840
    [48] 48. As shown above in Table VI, materials with incorporated microPCM possess an essentially higher heat storage than the comparison material. The heat insulation of the compact non-woven substrate is enhanced by the microPCM coating. The heat insulation of the acrylic fleece is mainly determined by the air enclosed in the material as a result of the dispersed structure of the fabric.
    [49] 49. It has been determined that the heat insulation properties of the materials containing microPCM remain nearly constant in the temperature range of the specific phase change, in contrast to the behavior of materials which do not contain microPCM. The variation of the heat insulation of the materials with microPCM is essentially lower contrary to the comparison material in changes of material humidity. The materials with microPCM possess when raising the pressure on the textile a lower decrease in the heat insulation than the comparison material due to a lower compressibility of the materials with microPCM.
    [50] 50. To determine the protection effect of the samples, the samples were brought in contract with a 70° C. tempered plate after cooling under the phase change temperature. The time required to reach a temperature equivalent to the pain threshold of the human skin on back of the sample was determined. The higher protection effect for the materials with microPCM was confirmed.
    [51] 51. Presently preferred embodiments of the present invention and many of its improvements have been described with a degree of particularity. It should be understood that this description has been made by way of preferred examples, and that the invention is defined by the scope of the following claims.
    权利要求:
    Claims (20)
    [1" id="US-20010000517-A1-CLM-00001] 1. A wet coating composition for fabrics, comprising:
    100 parts dry weight of a polymer binder;
    30 to 500 parts by dry weight of microspheres containing a phase change material for each 100 parts dry weight of said polymer binder;
    0.001% to 6% dry weight of a surfactant to dry weight of said microspheres;
    0.001% to 6% dry weight of a dispersant to dry weight of said microspheres;
    25% to 80% by weight water of the total weight of the wet coating composition; and
    0% to 1% by weight of dry antifoam agent to the total weight of the wet coating composition.
    [2" id="US-20010000517-A1-CLM-00002] 2. The coating of
    claim 1 wherein said phase change material is a paraffinic hydrocarbon.
    [3" id="US-20010000517-A1-CLM-00003] 3. The coating of
    claim 2 wherein said binder polymer is an anionic acrylic latex polymer, said microspheres are from 70 to 300 parts by dry weight of said polymer latex and said water is from 40% to 60% of the total weight of the wet coating composition.
    [4" id="US-20010000517-A1-CLM-00004] 4. The coating of
    claim 2 wherein said binder polymer is film-forming, elastomeric and has a glass transition temperature in the range of about −45° C. to +45° C.
    [5" id="US-20010000517-A1-CLM-00005] 5. The coating of
    claim 2 wherein said binder polymer is film-forming, elastomeric and has a glass transition temperature in the range of about −30° C. to about +12° C.
    [6" id="US-20010000517-A1-CLM-00006] 6. The coating of
    claim 2 wherein said binder polymer is comprised of monomers selected from the group consisting of acrylic eaters, styrene, isoprene, acrylonitrile, butadiene, vinyl acetate, vinyl chloride, vinyldiene chloride, ethylene, butylene, propylene and chloroprene.
    [7" id="US-20010000517-A1-CLM-00007] 7. The coating of
    claim 2 wherein said binder polymer is selected from the group consisting of silicone, epoxy, polyurethane, fluorocarbons, chlorosulfonated polyethylene and chlorinated polyethylene.
    [8" id="US-20010000517-A1-CLM-00008] 8. The coating of
    claim 5 wherein the dry weight ratio of said dispersant to dry weight of said microspheres is from 0.1 to 1%.
    [9" id="US-20010000517-A1-CLM-00009] 9. The coating of
    claim 5 wherein the dry weight ratio of said surfactant to dry weight of said microspheres is from 0.1 to 1%.
    [10" id="US-20010000517-A1-CLM-00010] 10. The coating of
    claim 1 wherein the phase change material is a paraffinic hydrocarbon.
    [11" id="US-20010000517-A1-CLM-00011] 11. The coating of
    claim 10 wherein the polymer is an anionic acrylic latex polymer, the microspheres are from 70 to 300 parts by dry weight of the polymer latex and the water is from 40% to 60% of the total weight of the wet coating composition.
    [12" id="US-20010000517-A1-CLM-00012] 12. The coating of
    claim 11 further comprising:
    0.3% to 18% by dry weight of a foam stabilizing agent selected from the group consisting of inorganic salts of fatty acids, sulfate partial esters of inorganic salts of fatty acids, anionic surfactants, and mixtures thereof, to the total weight of the wet coating composition.
    [13" id="US-20010000517-A1-CLM-00013] 13. The coating of
    claim 11 further comprising:
    0.3% to 18% by dry weight of a foam stabilizing agent selected form the group consisting of sodium lauryl sulfate, ammonium stearate, di-sodium-n-octadecyl sulfosuccinamate and mixtures thereof, to the total weight of the wet coating composition.
    [14" id="US-20010000517-A1-CLM-00014] 14. The coating of
    claim 11 further comprising:
    0.2% to 10% by weight of dry ammonium stearate to the total weight of the wet coating composition; and
    0.1% to 8% by weight of dry di-sodium-n-octadecyl-sulfosuccinamate.
    [15" id="US-20010000517-A1-CLM-00015] 15. The coating of
    claim 11 further comprising:
    1% to 3% by weight of dry ammonium stearate to the total weight of the wet coating composition; and
    0.3% to 2% by weight of dry di-sodium-n-octadecyl-sulfosuccinamate.
    [16" id="US-20010000517-A1-CLM-00016] 16. A method of manufacturing a coated composition for a substantially non-extensible fabric comprising the steps of:
    mixing water, a surfactant, a dispersant, microspheres containing a phase change material, and a thickener to produce a microsphere mixture;
    dispersing said microspheres throughout said microsphere mixture to produce a microsphere dispersion;
    adding an antifoam agent to said microsphere dispersion to dissipate foam from said microsphere dispersion;
    mixing a latex polymer, a surfactant, a dispersant, a thickener and an antifoam agent to form a polymer binder dispersion; and
    mixing said polymer binder dispersion with said microsphere dispersion to produce the coating composition.
    [17" id="US-20010000517-A1-CLM-00017] 17. The method of
    claim 16 further comprising the steps of:
    adjusting the pH of said microsphere dispersion by addition of a base prior to mixing said microsphere dispersion with said polymer binder dispersion; and
    adjusting the pH of said coating composition by addition of a base after mixing said microsphere dispersion with said poly binder dispersion.
    [18" id="US-20010000517-A1-CLM-00018] 18. The method of
    claim 16 further comprising the step of:
    maintaining said microspheres in said microsphere dispersion for from 1 to 48 hours prior to mixing said polymer binder dispersion with said microsphere dispersion to produce the coating composition.
    [19" id="US-20010000517-A1-CLM-00019] 19. The method of
    claim 16 further comprising the step of:
    maintaining said microspheres in said microsphere dispersion for from 6 to 24 hours prior to mixing said polymer binder dispersion with said microsphere dispersion to produce the coating composition.
    [20" id="US-20010000517-A1-CLM-00020] 20. A method of manufacturing a coating composition comprising the steps of:
    mixing a latex polymer, a surfactant and a dispersant;
    adding microspheres containing a phase change material and at least 25% by weight of water to the latex polymer mixture to obtain a microsphere/latex mixture;
    dispersing the microspheres throughout the microsphere/latex mixture to obtain a microsphere/latex dispersion;
    mixing the microsphere/latex dispersion with an antifoam agent and a thickener to defoam and thicken the microsphere/latex dispersion; and
    adjusting the pH of the defoam and thickened microsphere/latex dispersion to create the coating composition.
    类似技术:
    公开号 | 公开日 | 专利标题
    US6503976B2|2003-01-07|Fabric coating containing energy absorbing phase change material and method of manufacturing same
    US6514362B1|2003-02-04|Fabric coating containing energy absorbing phase change material and method of manufacturing same
    US5677048A|1997-10-14|Coated skived foam and fabric article containing energy absorbing phase change material
    US5955188A|1999-09-21|Skived foam article containing energy absorbing phase change material
    JP6208793B2|2017-10-04|Polymer composite having highly reversible thermal properties and method for forming the same
    US3713868A|1973-01-30|Acrylic-nitrile foam-backed fabric and method of preparation
    US8449947B2|2013-05-28|Thermal control nonwoven material
    EP2262863B1|2013-09-04|Microcapsules, production and use thereof
    US20080233368A1|2008-09-25|Articles having enhanced reversible thermal properties and enhanced moisture wicking propertiesto control hot flashes
    US20060030227A1|2006-02-09|Intumescent flame retardent compositions
    US6309746B1|2001-10-30|Halogen-free fire-retarding composition, yarn fire-retarded with the latter and fire-resistant textile structure comprising such yarns
    WO2002059414A9|2004-02-19|Coated articles having enhanced reversible thermal properties and exhibiting improved flexibility, softness, air permeability, or water vapor transport properties
    CN102471512A|2012-05-23|Foam composition
    KR20090025348A|2009-03-10|Stable suspensions containing microcapsules and methods for the preparation thereof
    US3791849A|1974-02-12|Process for the manufacture of a chemically bondedtextile sheet material based on synthetic fibers and having a high water vapor absorption capacity
    JP4832821B2|2011-12-07|Moisture permeable waterproof windproof film having heat retention and breathability, and composite material obtained by laminating this on fabric
    DE69737569T2|2007-12-13|STUFFED ARTICLE WITH MATERIAL FOR ENERGY ABSORPTION THROUGH PHASE TRANSFORMATION
    WO2020206318A1|2020-10-08|Compositions and methods for thermal management of textiles and foams
    PL63439B1|1971-06-30|
    同族专利:
    公开号 | 公开日
    US6207738B1|2001-03-27|
    US6503976B2|2003-01-07|
    引用文献:
    公开号 | 申请日 | 公开日 | 申请人 | 专利标题
    US20040026659A1|2002-07-08|2004-02-12|China Textile Institute|Composition for fabricating phase-change-material microcapsules and a method for fabricating the microcapsules|
    US20070248824A1|2004-08-10|2007-10-25|Basf Aktiengesellschaft|Coarse-Particle Microcapsule Preparation|
    US20080157415A1|2003-07-07|2008-07-03|Taiwan Textile Research Institute|Composition and Method for Fabricating Microcapsules Encapsulating Phase-Change Material|
    GB2474578A|2009-10-15|2011-04-20|Michael Trevor Berry|Latent heat storage material formulations|
    TWI411002B|2005-11-09|2013-10-01|Gen Electric|High intensity discharge lamp with improved crack control and method of manufacture|
    DE102012218378A1|2012-10-09|2014-04-10|Wacker Chemie Ag|Sheet or molding containing latent heat storage|
    US20180271184A1|2015-09-28|2018-09-27|Delta Galil Industries Ltd.|Fabric for articles of clothing, and method and system of producing same|
    WO2021045849A1|2019-09-04|2021-03-11|Wilsey Mark E|Building method|US3615972A|1967-04-28|1971-10-26|Dow Chemical Co|Expansible thermoplastic polymer particles containing volatile fluid foaming agent and method of foaming the same|
    US3769126A|1970-01-30|1973-10-30|Westinghouse Electric Corp|Resinous-microsphere-glass fiber composite|
    JPS5022613B1|1971-06-29|1975-08-01|||
    US4006273A|1975-02-03|1977-02-01|Pratt & Lambert, Inc.|Washable and dry-cleanable raised printing on fabrics|
    US4003426A|1975-05-08|1977-01-18|The Dow Chemical Company|Heat or thermal energy storage structure|
    US4094685A|1976-07-23|1978-06-13|Polymerics, Inc.|Expandable polymeric coating compositions|
    US4208485A|1978-04-18|1980-06-17|Gaf Corporation|Foaming composition for textile finishing and coatings|
    US4446917A|1978-10-04|1984-05-08|Todd John C|Method and apparatus for producing viscous or waxy crude oils|
    JPS5630473A|1979-08-22|1981-03-27|Matsumoto Yushi Seiyaku Kk|Coating composition|
    US4357428A|1981-03-12|1982-11-02|Union Carbide Corporation|Foamable composition|
    US4747240A|1981-08-06|1988-05-31|National Gypsum Company|Encapsulated PCM aggregate|
    US4612239A|1983-02-15|1986-09-16|Felix Dimanshteyn|Articles for providing fire protection|
    US4504402A|1983-06-13|1985-03-12|Pennwalt Corporation|Encapsulated phase change thermal energy _storage materials|
    US4581285A|1983-06-07|1986-04-08|The United States Of America As Represented By The Secretary Of The Air Force|High thermal capacitance multilayer thermal insulation|
    US4531511A|1983-07-14|1985-07-30|Hochberg Nelson D|Means for controlling heat flux|
    US4617332A|1984-08-31|1986-10-14|University Of Dayton|Phase change compositions|
    US4797160A|1984-08-31|1989-01-10|University Of Dayton|Phase change compositions|
    US4587279A|1984-08-31|1986-05-06|University Of Dayton|Cementitious building material incorporating end-capped polyethylene glycol as a phase change material|
    US4825939A|1984-08-31|1989-05-02|The University Of Dayton|Polymeric compositions incorporating polyethylene glycol as a phase change material|
    US4572864A|1985-01-04|1986-02-25|The United States Of America As Represented By The United States Department Of Energy|Composite materials for thermal energy storage|
    US4774133A|1985-02-08|1988-09-27|Minnesota Mining And Manufacturing Company|Article containing microencapsulated materials|
    US4645613A|1985-07-15|1987-02-24|John D. Brush & Co., Inc.|Heat storage composition|
    US5211949A|1990-01-09|1993-05-18|University Of Dayton|Dry powder mixes comprising phase change materials|
    US5053446A|1985-11-22|1991-10-01|University Of Dayton|Polyolefin composites containing a phase change material|
    US5254380A|1985-11-22|1993-10-19|University Of Dayton|Dry powder mixes comprising phase change materials|
    US4711813A|1985-11-22|1987-12-08|University Of Dayton|Polyethylene composites containing a phase change material having a C14 straight chain hydrocarbon|
    US5106520A|1985-11-22|1992-04-21|The University Of Dayton|Dry powder mixes comprising phase change materials|
    JP2631841B2|1987-03-05|1997-07-16|株式会社日本カプセルプロダクツ|Latent heat storage material microcapsules|
    GB8709043D0|1987-04-15|1987-05-20|Sericol Group Ltd|Masking compositions|
    JPH0356894B2|1987-06-24|1991-08-29|||
    US4756958A|1987-08-31|1988-07-12|Triangle Research And Development Corporation|Fiber with reversible enhanced thermal storage properties and fabrics made therefrom|
    US4856294B1|1988-02-04|1997-05-13|Mainstream Engineering Corp|Micro-climate control vest|
    US4853270A|1988-06-27|1989-08-01|Essex Specialty Products, Inc.|Knee blocker for automotive application|
    US4935294A|1988-11-17|1990-06-19|Colgate-Palmolive Company|Composite sheet material|
    EP1314575B1|1990-09-07|2005-12-07|Dai Nippon Printing Co., Ltd.|Thermal transfer image receiving sheet and thermal transfer sheet|
    SE9003600L|1990-11-12|1992-05-13|Casco Nobel Ab|EXPANDABLE THERMOPLASTIC MICROSPHERES AND PROCEDURES FOR PRODUCING THEREOF|
    US5069358A|1991-01-03|1991-12-03|John D. Brush & Co., Inc.|Media case|
    US5290904A|1991-07-31|1994-03-01|Triangle Research And Development Corporation|Heat shield|
    JP2970963B2|1991-08-14|1999-11-02|日東電工株式会社|Peelable pressure-sensitive adhesive and adhesive member thereof|
    US5224356A|1991-09-30|1993-07-06|Triangle Research & Development Corp.|Method of using thermal energy absorbing and conducting potting materials|
    JPH05156570A|1991-12-10|1993-06-22|Kanebo Ltd|Fibrous structure having heat storage ability and its production|
    US5499460A|1992-02-18|1996-03-19|Bryant; Yvonne G.|Moldable foam insole with reversible enhanced thermal storage properties|
    JP3133131B2|1992-02-27|2001-02-05|旭化成工業株式会社|Composite sheet|
    US5366801A|1992-05-29|1994-11-22|Triangle Research And Development Corporation|Fabric with reversible enhanced thermal properties|
    US6004662A|1992-07-14|1999-12-21|Buckley; Theresa M.|Flexible composite material with phase change thermal storage|
    CA2170512A1|1993-09-21|1995-03-30|Gordon L. Mcgregor|Puffed insulative material and methods for making such material|
    US5356683A|1993-10-28|1994-10-18|Rohm And Haas Company|Expandable coating composition|
    US5415222A|1993-11-19|1995-05-16|Triangle Research & Development Corporation|Micro-climate cooling garment|
    US6207738B1|1994-06-14|2001-03-27|Outlast Technologies, Inc.|Fabric coating composition containing energy absorbing phase change material|
    US5677049A|1994-12-27|1997-10-14|Dai Nippon Printing Co., Ltd.|Heat transfer printing sheet for producting raised images|US6319599B1|1992-07-14|2001-11-20|Theresa M. Buckley|Phase change thermal control materials, method and apparatus|
    US6207738B1|1994-06-14|2001-03-27|Outlast Technologies, Inc.|Fabric coating composition containing energy absorbing phase change material|
    EP0766720B1|1994-06-14|2004-04-14|Outlast Technologies, Inc.|Energy absorbing fabric coating and manufacturing method|
    FR2767541B1|1997-08-21|1999-10-08|Hutchinson|SPONGIOUS MATERIAL, MANUFACTURING METHOD THEREOF AND APPLICATIONS THEREOF|
    GB2331717B|1997-11-26|1999-12-22|Ranier Ltd|Reticulated coatings|
    EP1242239B1|1999-07-14|2011-04-06|Claude Q.C. Hayes|Thermal control composite|
    US6759476B1|1999-07-14|2004-07-06|Claude Q. C. Hayes|Flexible thermal control composite|
    US20030224679A1|1999-11-30|2003-12-04|Younger Ahluwalia|Fire resistant structural material and fabrics made therefrom|
    US8030229B2|2002-01-29|2011-10-04|Elkcorp.|Composite material|
    US20040229052A1|2003-01-29|2004-11-18|Elkcorp|Composite material|
    US8017531B2|2001-09-18|2011-09-13|Elkcorp|Composite material|
    US7563733B2|2002-01-29|2009-07-21|Elkcorp|Composite material|
    US7521385B2|1999-11-30|2009-04-21|Building Materials Invest Corp|Fire resistant structural material, fabrics made therefrom|
    US6615906B1|2000-03-31|2003-09-09|Schümann Sasol Gmbh & Co. Kg|Latent heat body|
    AU8539301A|2000-08-05|2002-02-18|Freudengerg Viesstoffe Kg|Thermal control nonwoven material|
    US20040043212A1|2000-08-05|2004-03-04|Peter Grynaeus|Thermal control nonwoven material|
    US9434869B2|2001-09-21|2016-09-06|Outlast Technologies, LLC|Cellulosic fibers having enhanced reversible thermal properties and methods of forming thereof|
    US7160612B2|2000-09-21|2007-01-09|Outlast Technologies, Inc.|Multi-component fibers having enhanced reversible thermal properties and methods of manufacturing thereof|
    US20050208286A1|2000-09-21|2005-09-22|Hartmann Mark H|Polymeric composites having enhanced reversible thermal properties and methods of forming thereof|
    US6855422B2|2000-09-21|2005-02-15|Monte C. Magill|Multi-component fibers having enhanced reversible thermal properties and methods of manufacturing thereof|
    AU9464201A|2000-09-21|2002-04-02|Outlast Technologies Inc|Stable phase change materials for use in temperature regulating synthetic fibers, fabrics and textiles|
    US6793856B2|2000-09-21|2004-09-21|Outlast Technologies, Inc.|Melt spinable concentrate pellets having enhanced reversible thermal properties|
    US20030054141A1|2001-01-25|2003-03-20|Worley James Brice|Coated articles having enhanced reversible thermal properties and exhibiting improved flexibility, softness, air permeability, or water vapor transport properties|
    US6598251B2|2001-06-15|2003-07-29|Hon Technology Inc.|Body support system|
    FR2827316B1|2001-07-13|2004-07-30|Inter Unec Interaction Univers|TEXTILE FIBER SURFACE TREATMENT PROCESS|
    CA2455405A1|2001-07-31|2003-02-13|Giat Industries|Method for making a tank containing compressed gas and resulting tank|
    WO2003014460A1|2001-08-08|2003-02-20|The Procter & Gamble Company|A climate control composition|
    US6517648B1|2001-11-02|2003-02-11|Appleton Papers Inc.|Process for preparing a non-woven fibrous web|
    US6814882B2|2002-07-08|2004-11-09|China Textile Institute|Fabric coating composition with latent heat effect and a method for fabricating the same|
    JP2004083765A|2002-08-27|2004-03-18|China Textile Inst|Method for producing microcapsule-combined aqueous polyurethane|
    US6953129B2|2002-08-27|2005-10-11|The United States Of America As Represented By The Administrator Of The National Aeronautics And Space Administration|Pressure vessel with impact and fire resistant coating and method of making same|
    JP3723554B2|2003-03-19|2005-12-07|正隆股▲ふん▼有限公司|Waterproof and moisture-permeable thin film having a heat retaining function and method for manufacturing the same|
    US7056335B2|2003-03-21|2006-06-06|Kimberly-Clark Worldwide, Inc.|Thermal therapy sleeve|
    FR2858637A1|2003-08-05|2005-02-11|Inst Rech Appliquee A La Formu|Textile article comprising non-woven support and microcapsules containing active agent, e.g. perfume or deodorant, having optimized thickness and capsule size to inhibit premature release|
    DE10342416A1|2003-09-13|2005-04-07|Outlast Technologies, Inc., Boulder|filter material|
    US7052563B2|2003-12-10|2006-05-30|Owens Corning Fiberglas Technology, Inc.|Apparatus and method for fiber batt encapsulation|
    US7041897B2|2004-02-10|2006-05-09|Adc Telecommunications, Inc.|Hinge for cable trough cover|
    US20050215149A1|2004-03-23|2005-09-29|Elkcorp|Fire resistant composite material and fabrics therefrom|
    US20050215150A1|2004-03-23|2005-09-29|Elkcorp|Fire resistant composite material and fabrics therefrom|
    US20050215152A1|2004-03-23|2005-09-29|Elkcorp|Fire resistant composite material and fabrics therefrom|
    US8822355B2|2004-03-23|2014-09-02|Elkcorp|Fire resistant composite material and fabrics made therefrom|
    US7361617B2|2004-03-23|2008-04-22|Elkcorp|Fire resistant composite material and fabrics therefrom|
    JP5280051B2|2004-07-02|2013-09-04|ディスカスデンタル，エルエルシー|Dental light device with improved heat sink|
    US7301465B2|2005-03-24|2007-11-27|Tengshe Vishwas V|Drowsy driving alarm system|
    DE102005030484B4|2005-06-28|2007-11-15|Carl Freudenberg Kg|Elastic nonwoven fabric, process for its preparation and its use|
    US20080101073A1|2006-11-01|2008-05-01|Discus Dental, Llc|Dental Light Devices Having an Improved Heat Sink|
    US20070148446A1|2005-12-28|2007-06-28|Kimberly-Clark Worldwide, Inc.|Wipes including microencapsulated delivery vehicles and processes of producing the same|
    US20070145617A1|2005-12-28|2007-06-28|Kimberly-Clark Worldwide, Inc.|Processes for producing microencapsulated heat delivery vehicles|
    US20070148448A1|2005-12-28|2007-06-28|Kimberly-Clark Worldwide, Inc.|Microencapsulated delivery vehicles including cooling agents|
    US20070145618A1|2005-12-28|2007-06-28|Kimberly-Clark Worldwide, Inc.|Methods of making microencapsulated delivery vehicles|
    US20070202185A1|2005-12-28|2007-08-30|Kimberly-Clark Worldwide, Inc.|Microencapsulated Delivery Vehicles Having Fugitive Layers|
    US7442439B2|2005-12-28|2008-10-28|Kimberly-Clark Worldwide, Inc.|Microencapsulated heat delivery vehicles|
    US20070149435A1|2005-12-28|2007-06-28|Kimberly-Clark Worldwide, Inc.|Cleansing composition including microencapsulated delivery vehicles|
    US7914891B2|2005-12-28|2011-03-29|Kimberly-Clark Worldwide, Inc.|Wipes including microencapsulated delivery vehicles and phase change materials|
    US20070148459A1|2005-12-28|2007-06-28|Kimberly-Clark Worldwide, Inc.|Microencapsulated delivery vehicles|
    US20070145619A1|2005-12-28|2007-06-28|Kimberly-Clark Worldwide, Inc.|Processes for producing microencapsulated delivery vehicles|
    US20100015430A1|2008-07-16|2010-01-21|Outlast Technologies, Inc.|Heat Regulating Article With Moisture Enhanced Temperature Control|
    US20070173154A1|2006-01-26|2007-07-26|Outlast Technologies, Inc.|Coated articles formed of microcapsules with reactive functional groups|
    US8404341B2|2006-01-26|2013-03-26|Outlast Technologies, LLC|Microcapsules and other containment structures for articles incorporating functional polymeric phase change materials|
    US7654412B2|2006-05-30|2010-02-02|Kimberly-Clark Worldwide, Inc.|Wet wipe dispensing system for dispensing warm wet wipes|
    US7648046B2|2006-05-30|2010-01-19|Kimberly-Clark Worldwide, Inc.|Dispensing system for dispensing warm wet wipes|
    US7497351B2|2006-05-30|2009-03-03|Kimberly-Clark Worldwide, Inc.|Wet wipe dispensing system|
    IL176693D0|2006-07-04|2006-10-31|Aharon Eyal|Stable suspensions containing microcapsules and methods for the preparation thereof|
    US20080120761A1|2006-08-31|2008-05-29|Kaiyuan Yang|Thermal Moderating Donnable Elastic Articles|
    US8039011B2|2006-10-10|2011-10-18|Kimberly-Clark Worldwide, Inc.|Skin cooling compositions|
    US7799394B2|2006-11-14|2010-09-21|Millercoors, Llc|Container with insulative label|
    GB0623005D0|2006-11-17|2006-12-27|Unilever Plc|Fabric treatment method and composition|
    GB0623004D0|2006-11-17|2006-12-27|Unilever Plc|Fabric treatment method and composition to impart differential hydrophobocity|
    US8192841B2|2006-12-14|2012-06-05|Kimberly-Clark Worldwide, Inc.|Microencapsulated delivery vehicle having an aqueous core|
    US20090239429A1|2007-03-21|2009-09-24|Kipp Michael D|Sound Attenuation Building Material And System|
    US8445101B2|2007-03-21|2013-05-21|Ashtech Industries, Llc|Sound attenuation building material and system|
    MX367591B|2007-03-21|2019-08-27|Ash Tech Ind L L C|Utility materials incorporating a microparticle matrix.|
    US7721804B2|2007-07-06|2010-05-25|Carbo Ceramics Inc.|Proppants for gel clean-up|
    US20090110656A1|2007-10-31|2009-04-30|Lemke Sarah A|Skin cooling composition|
    US20090157153A1|2007-12-13|2009-06-18|Sarah Anne Lemke|Skin cooling system|
    US7924142B2|2008-06-30|2011-04-12|Kimberly-Clark Worldwide, Inc.|Patterned self-warming wipe substrates|
    US8221910B2|2008-07-16|2012-07-17|Outlast Technologies, LLC|Thermal regulating building materials and other construction components containing polymeric phase change materials|
    US20100016513A1|2008-07-16|2010-01-21|Outlast Technologies, Inc.|Functional Polymeric Phase Change Materials and Methods of Manufacturing the Same|
    US20100012883A1|2008-07-16|2010-01-21|Outlast Technologies, Inc.|Functional Polymeric Phase Change Materials|
    US9234059B2|2008-07-16|2016-01-12|Outlast Technologies, LLC|Articles containing functional polymeric phase change materials and methods of manufacturing the same|
    WO2010042566A1|2008-10-08|2010-04-15|Microtek Laboratories, Inc.|Microencapsulation of a phase change meterial with enhanced flame resistance|
    WO2010054029A2|2008-11-04|2010-05-14|Ashtech Industries, L.L.C.|Utility materials incorporating a microparticle matrix formed with a setting system|
    MX2011007579A|2009-01-15|2011-08-04|Procter & Gamble|Reusable outer cover for an absorbent article having zones of varying properties.|
    MX2011007576A|2009-01-15|2011-08-04|Procter & Gamble|Reusable wearable absorbent articles with anchoring subsystems.|
    BRPI1006800A2|2009-01-15|2016-04-12|Procter & Gamble|two-piece absorbent wear articles|
    US8998870B2|2009-01-15|2015-04-07|The Procter & Gamble Company|Reusable wearable absorbent articles with anchoring systems|
    EP2391324A4|2009-01-15|2014-12-17|Procter & Gamble|Reusable outer cover for an absorbent article|
    US9387138B2|2009-01-15|2016-07-12|The Procter & Gamble Company|Reusable outer covers for wearable absorbent articles|
    JP2013511628A|2009-11-17|2013-04-04|アウトラストテクノロジーズ，リミテッドライアビリティカンパニー|Fibers and articles having a combination of fire resistance and enhanced reversible thermal properties|
    CN102711689A|2010-01-14|2012-10-03|宝洁公司|Article of commerce including two-piece wearable absorbent article|
    WO2011087502A1|2010-01-14|2011-07-21|The Procter & Gamble Company|Leg and waist band structures for an absorbent article|
    US8808263B2|2010-01-14|2014-08-19|The Procter & Gamble Company|Article of commerce including two-piece wearable absorbent article|
    US20110172628A1|2010-01-14|2011-07-14|Donald Carroll Roe|Leg And Waist Band Structures For An Absorbent Article|
    US8652115B2|2010-05-21|2014-02-18|The Procter & Gamble Company|Insert with advantageous fastener configurations and end stiffness characteristics for two-piece wearable absorbent article|
    US8652114B2|2010-05-21|2014-02-18|The Procter & Gamble Company|Insert with advantageous fastener configurations and end stiffness characteristics for two-piece wearable absorbent article|
    US8585667B2|2010-05-21|2013-11-19|The Procter & Gamble Company|Insert with advantageous fastener configurations and end stiffness characteristics for two-piece wearable absorbent article|
    US20120022491A1|2010-07-22|2012-01-26|Donald Carroll Roe|Flexible Reusable Outer Covers For Disposable Absorbent Inserts|
    US8821470B2|2010-07-22|2014-09-02|The Procter & Gamble Company|Two-piece wearable absorbent article with advantageous fastener performance configurations|
    US8546641B2|2010-07-22|2013-10-01|The Procter & Gamble Company|High-capacity disposable absorbent inserts for reusable outer covers|
    US8673448B2|2011-03-04|2014-03-18|Outlast Technologies Llc|Articles containing precisely branched functional polymeric phase change materials|
    US9078792B2|2011-06-30|2015-07-14|The Procter & Gamble Company|Two-piece wearable absorbent article having advantageous front waist region and landing zone configuration|
    CN103889383A|2011-10-19|2014-06-25|宝洁公司|Wearable absorbent articles with reusable chassis having extensible body zones|
    US8932273B2|2012-06-29|2015-01-13|The Procter & Gamble Company|Disposable absorbent insert for two-piece wearable absorbent article|
    PT2877064T|2012-07-27|2019-07-04|Tempur World Llc|Body support cushion having multiple layers of phase change material|
    KR101379427B1|2013-02-13|2014-03-28|경북대학교병원|Composition for preventing or treating renal fibrosis comprising dimethylfumarate|
    US8936586B2|2013-03-08|2015-01-20|The Procter & Gamble Company|Ergonomic grasping aids for reusable pull-on outer covers|
    US20140257228A1|2013-03-08|2014-09-11|The Procter & Gamble Company|Outer covers and disposable absorbent inserts for pants|
    US9078789B2|2013-03-08|2015-07-14|The Procter & Gamble Company|Outer covers and disposable absorbent inserts for pants|
    US9060905B2|2013-03-08|2015-06-23|The Procter & Gamble Company|Wearable absorbent articles|
    US8926579B2|2013-03-08|2015-01-06|The Procter & Gamble Company|Fastening zone configurations for outer covers of absorbent articles|
    US20140257231A1|2013-03-08|2014-09-11|The Procter & Gamble Company|Outer covers and disposable absorbent inserts for pants|
    EP3051968B1|2013-10-04|2020-11-25|Under Armour, Inc.|Article of apparel|
    US10106717B2|2014-01-13|2018-10-23|Honeywell International Inc.|Composite phase change material , method for manufacturing a composite PCM, and article of clothing including a composite PCM|
    USD769628S1|2014-10-07|2016-10-25|Under Armour, Inc.|Textile sheet|
    USD779216S1|2015-01-30|2017-02-21|Under Armour, Inc.|Woven, knitted or non-woven textile for apparel|
    US10431858B2|2015-02-04|2019-10-01|Global Web Horizons, Llc|Systems, structures and materials for electrochemical device thermal management|
    US10003053B2|2015-02-04|2018-06-19|Global Web Horizons, Llc|Systems, structures and materials for electrochemical device thermal management|
    US10687632B1|2016-04-03|2020-06-23|Soothsoft Innovations Worldwide, Inc.|PCM containing liquid saturated foam device|
    FR3050457B1|2016-04-21|2020-04-17|Protec Industries|MULTILAYER SYSTEM OF THERMO-REGULATING PAINTS|
    EP3481545B1|2016-07-11|2021-02-24|Microtek Laboratories, Inc.|Capsules having surfactant tethered outer shells and methods for making same|
    US11130895B2|2016-09-20|2021-09-28|Aspen Aerogels, Inc.|Aerogel composites having thermal storage capacity|
    JP1609254S|2017-04-03|2018-07-17|||
    BR112020023591A2|2018-06-15|2021-02-09|Essity Hygiene And Health Aktiebolag|absorbent article and method for applying phase change material|
    RU2750447C1|2018-06-15|2021-06-28|Эссити Хайджин Энд Хелт Актиеболаг|Absorbing item containing microcapsulated material with variable phase state, and method for applying material with variable phase state on absorbing item|
    法律状态:
    2002-12-19| STCF| Information on status: patent grant|Free format text: PATENTED CASE |
    2004-02-03| CC| Certificate of correction|
    2005-12-13| AS| Assignment|Owner name: SILICON VALLEY BANK, CALIFORNIA Free format text: SECURITY INTEREST;ASSIGNOR:OUTLAST TECHNOLOGIES, INC.;REEL/FRAME:017336/0455 Effective date: 20051031 |
    2006-06-30| FPAY| Fee payment|Year of fee payment: 4 |
    2007-12-11| AS| Assignment|Owner name: OUTLAST TECHNOLOGIES, INC., COLORADO Free format text: RELEASE BY SECURED PARTY;ASSIGNOR:SILICON VALLEY BANK;REEL/FRAME:020227/0608 Effective date: 20071205 |
    2010-06-09| FPAY| Fee payment|Year of fee payment: 8 |
    2012-03-30| AS| Assignment|Owner name: SILICON VALLEY BANK, COLORADO Free format text: SECURITY AGREEMENT;ASSIGNOR:OUTLAST TECHNOLOGIES LLC;REEL/FRAME:027956/0939 Effective date: 20120330 |
    2012-08-14| AS| Assignment|Owner name: OUTLAST TECHNOLOGIES LLC, COLORADO Free format text: ASSIGNMENT OF ASSIGNORS INTEREST;ASSIGNOR:OUTLAST TECHNOLOGIES, INC.;REEL/FRAME:028786/0402 Effective date: 20120327 |
    2014-06-11| FPAY| Fee payment|Year of fee payment: 12 |
    优先权:
    申请号 | 申请日 | 专利标题
    US25996494A| true| 1994-06-14|1994-06-14||
    US08/850,944|US6207738B1|1994-06-14|1997-05-05|Fabric coating composition containing energy absorbing phase change material|
    US09/735,380|US6503976B2|1994-06-14|2000-12-11|Fabric coating containing energy absorbing phase change material and method of manufacturing same|US09/735,380| US6503976B2|1994-06-14|2000-12-11|Fabric coating containing energy absorbing phase change material and method of manufacturing same|
    [返回顶部]