    • 专利摘要:
    The present invention relates a high-temperature Ni-MH battery and the method for making the same. By adding a titanium additive in the anode materials at an amount of 0.1-15.0 % (weight), based on the weight of the active spherical nickel hydroxide, the high-temperature charging efficiency of the Ni-MH battery can be greatly improved. The charging efficiency of the Ni-MH battery of the present invention can reach 95% at a temperature higher than 50° C. The Ni-MH battery of the present Invention can be used at a temperature of 50° C. or higher.
    公开号:US20010000484A1
    申请号:US09/726,645
    申请日:2000-11-29
    公开日:2001-04-26
    发明作者:Haigang Lv
    申请人:Shenzhen BYD Industrial Co Ltd；
    IPC主号:H01M10-345
    专利说明:
    [1] 1. This is a continuation application of patent application No. PCT/CN00/00074 which claims priority from Chinese patent application No. 991161130 filed on Apr. 5, 1999. FIELD OF THE INVENTION
    [2] 2. The present invention relates to a high-temperature Ni-MH battery and a method for making the same. BACKGROUND OF THE INVENTION
    [3] 3. The present Ni-MH battery usually comprises a pair of electrodes composed of a Ni anode of nickel hydroxide, a cathode of hydrogen-storing alloy, and a separator, and KOH solution is used as electrolyte. The anode is made by mixing an active material of Ni (OH)2, an electroconductive agent, an adhesive agent and water to make a syrup, and filling the syrup into an alkali-resistance basic plate.
    [4] 4. In the Ni-MH battery adopting the anode mentioned above, two reactions will take place on the anode during charge, namely the following reaction (1) and reaction (2). The reaction (1) is the charging reaction of Ni (OH)2 on the anode; the reaction (2) is the oxygen-formation reaction. When the temperature arises, the electric potential of reaction (2) will decrease, which will decrease the electric potential difference between reaction (2) and reaction (1).
    [5] 5. The competition between the two reactions mentioned above results in low charging efficiency of the anode mentioned above. At the temperature of 50°C., the charging efficiency can only reach 50-60%, which severely influences the performance of battery at high temperatures.
    [6] 6. Japanese patent 8 - 31448 disclosed a high-temperature battery and a method for making the same. According to this patent, CeO2, Ce(OH)3, Ce(OH)4 H2O, Nd2O3, and Nd(OH)3 were added into the Ni anode material as additives to improve the charging efficiency of the anode. For instance, at 45°C., the charging efficiency of the battery can reach 80-90%. However, this improvement is not enough. Nowadays, the Ni-MH battery has been used at high temperatures more and more common, and the Ni-MH battery with higher high-temperature performance is required. The present invention is based on this. OBJECTS OF THE INVENTION
    [7] 7. One object of the present invention is to provide a Ni-MH battery for using at high temperatures.
    [8] 8. Another object of the present invention is to provide a method for making the Ni-MH battery for using at high temperatures. SUMMARY OF THE INVENTION
    [9] 9. The present invention provides a high-temperature Ni-MH battery, comprising an anode plate made up of a base plate and anode substances adhering on the base plate, a cathode plate made up of a base plate and cathode substances adhering on the base plate, a separator, a steel housing, built-up covers, characterized in that: the said anode base plate is selected from the base plates of foamed nickel, fiber nickel, and porous steel strip; the said anode substances comprise an active material of spherical nickel hydroxide, an electroconductive agent, an adhesive and an additive; in which, the said electroconductive agent is at least one selected from the group consisting of nickel powder, carbon powder, acetylene black, graphite powder, cadmium powder, zinc powder, Co—Zn alloy powder, cobalt powder, CoO, Co2O3, Co(OH)2 and Co(OH)3; the said adhesive is at least one selected from the group consisting of PTFE, CMC,MC and PVA; the said additive is selected from the titanium additives which can restrain the electric potential descent in the oxygen-formation reaction at the Ni anode during the charging at a temperature over 40° C.
    [10] 10. The present invention also provides a method for making the high-temperature Ni-MH battery as mentioned above, comprising the following steps:
    [11] 11. (1) making an anode plate: mixing nickel hydroxide, an electroconductive agent, a titanium additive, an adhesive and water together, stirring the resulting mixture homogeneously, filling the homogeneous mixture into an anode base plate which has been welded with electrode terminals, baking to dry, roller-compacting it to a desired thickness to obtain an anode plate;
    [12] 12. (2) making a cathode plate: mixing a hydrogen-storing alloy powder, an electroconductive agent, an adhesive and water together, stirring the resulting mixture homogeneously, filling the homogeneous mixture into a cathode base plate which has been welded with electrode terminals, baking to dry, roller-compacting it to a desired thickness to obtain a cathode plate;
    [13] 13. (3) Selecting a proper separator, putting it between the anode and the cathode made above, pressing them together tightly, or convoluting into a cylinder, and then putting it into a quadrate or cylindrical steel housing;
    [14] 14. (4) Welding electrodes, injecting an electrolyte solution and then sealing;
    [15] 15. (5) Battery activating;
    [16] 16. (6) Battery assembling. BRIEF DESCRIPTION OF THE DRAWINGS
    [17] 17.FIG. 1 is the sectional view of the high-temperature Ni-MH battery of the present invention.
    [18] 18.FIG. 2 is the flow sheet for making the high-temperature Ni-MH battery of the present invention.
    [19] 19.FIG. 3 is a graph showing the relationship between the amount of the titanium additives and the charging efficiency of the battery. DETAILED DESCRIPTION OF THE INVENTION
    [20] 20. According to one aspect of the present invention, the present invention provides a high-temperature Ni-MH battery. As is shown by FIG. 1, the said battery comprises an anode plate 1 made up of a base plate and anode substances adhering on the base plate, a cathode plate 3 made up of a base plate and cathode substances adhering on the base plate, a separator 2, a steel housing 4, built-up covers 5, characterized in that: the said anode base plate is selected from the base plates of foamed nickel, fiber nickel, and porous steel strip; the said anode substances comprise an active material of spherical nickel hydroxide, an electroconductive agent, an adhesive and an additive; in which, the said electroconductive agent is at least one selected from the group consisting of nickel powder, carbon powder, acetylene black, graphite powder, cadmium powder, zinc powder, Co—Zn alloy powder, cobalt powder, CoO, Co2O3, Co(OH)2 and Co(OH)3; the said adhesive is at least one selected from the group consisting of PTFE, CMC,MC and PVA; the said additive is selected from the titanium additives which can restrain the electric potential descent in the oxygen-formation reaction at the Ni anode during the charging at a temperature over 40°C.
    [21] 21. According to the high-temperature Ni-MH battery of the present invention, in which, the said titanium additive is at least one selected from the group consisting metal titanium, Ti(OH)2, Ti(OH)3, TiO, Ti2O3, TiO2,Ti 3O5, titanates and titanium salts.
    [22] 22. According to the high-temperature Ni-MH battery of the present invention, in which, the amount of the said titanium additive is in the range of 0.1-15.0% (weight), based on the spherical nickel hydroxide in the anode substances.
    [23] 23. According to the high-temperature Ni-MH battery of the present invention, in which, the amount of the said titanium additive is preferably in the range of 1.0-5.0% (weight), based on the spherical nickel hydroxide in the anode substances.
    [24] 24. According to the high-temperature Ni-MH battery of the present invention, in which, the said cathode base plate is selected from foamed nickel base plate, fiber nickel base plate, and porous steel strip base plate. The said cathode substances comprise an AB5 or AB2 type hydrogen-storing alloys, an electroconductive agent, an adhesive; in which, the electroconductive agent is at least selected from the group consisting nickel powder, carbon powder, acetylene black, graphite power, cadmium powder, zinc powder, Co—Zn alloy powder, cobalt powder, CoO, Co2O3, Co(OH)2 and Co(OH)3; the said adhesive is at least one selected from the group consisting PTFE, CMC, MC and PVA.
    [25] 25. According to another aspect of the present invention, the present invention provides a method for making the high-temperature Ni-MH battery, the flow sheet is shown in FIG. 2. The method comprises the following steps:
    [26] 26. (1) making an anode plate; mixing nickel hydroxide, an electroconductive agent, a titanium additive, an adhesive and water together, stirring the resulting mixture homogeneously, filling the homogeneous mixture into an anode base plate which has been welded with electrode terminals, baking to dry, roller-compacting it to a desired thickness to obtain an anode plate;
    [27] 27. (2) making a cathode plate: mixing a hydrogen-storing alloy powder, an electroconductive agent, an adhesive and water together, stirring the resulting mixture homogeneously, filling the homogeneous mixture into a cathode base plate which has been welded with electrode terminals, baking to dry, roller-compacting it to a desired thickness to obtain a cathode plate;
    [28] 28. (3) Selecting a proper separator, putting it between the anode and the cathode made above, pressing them together tightly, or convoluting into cylinder, and then putting it into a quadrate or cylindrical steel housing;
    [29] 29. (4) Welding electrodes, injecting an electrolyte solution and then sealing;
    [30] 30. (5) Battery activating;
    [31] 31. (6) Battery assembling.
    [32] 32. According to the method of the present invention, in which, the said titanium additive is at least one selected from the group consisting metal titanium, Ti(OH)2, Ti(OH)3, TiO, Ti2O3, TiO2, Ti 3O5, titanates and titanium salts.
    [33] 33. According to the method of the present invention, in which, the amount of the said titanium additive is in the range of 0.1-15.0% (weight), based on the spherical nickel hydroxide in the anode substances.
    [34] 34. According to the method of the present invention, in which, the amount of the said titanium additive is preferably in the range of 1.0-5.0% (weight), based on the spherical nickel hydroxide in the anode substances.
    [35] 35. According to the method of the present invention, in which, the said cathode base plate is selected from foamed nickel base plate, fiber nickel base plate, and porous steel strip base plate. The said cathode substances comprise an AB5 or AB2 type hydrogen-storing alloys, an electroconductive agent, an adhesive; in which, the electroconductive agent is at least one selected from the group consisting nickel powder, carbon powder, acetylene black, graphite power, cadmium powder, zinc powder, Co—Zn alloy powder, cobalt powder, CoO, Co2O3, Co(OH)2 and Co(OH)3; the said adhesive is at least one selected from the group consisting of PTFE, CMC, MC and PVA.
    [36] 36. According to the high-temperature Ni-MH battery of the present invention, in which, the electrolyte is those usually used in the Ni-MH battery.
    [37] 37. According to the method of the present invention, in which, the battery activating and battery assembling methods are those well-known by the skilled person in the art.
    [38] 38. According to the present invention, in which, the separator 2 are those well known by the skilled person in the art, such as the modified polypropylene separator.
    [39] 39. In the high-temperature Ni-MH battery of the present invention, a titanium additive is added in the anode, particularly the amount of the said titanium additive is more than 1.0% (weight) based on the weight of the active spherical nickel hydroxide in the anode substances. Therefore, when the high-temperature Ni-MH battery of the present invention is used at high temperatures, the electric potential of the following oxygen formation reaction (2) carried out on the nickel hydroxide anode rises greatly:
    [40] 40. and the following reaction (1) can be carried out thoroughly:
    [41] 41. The amount of formed NiOOH increases, so that the charging efficiency of the anode has been enhanced greatly. At a temperature of 50°C. or higher temperatures, the charging efficiency of the battery of the present invention can reach 95%, which can satisfy the requirements on the battery performance at high temperatures.
    [42] 42.FIG. 3 shows the relationship between the amount of the titanium additive and the charging efficiency of the battery. As it can be seen from FIG. 3, the addition of titanium additive, such as titanium dioxide, metal titanium powder and/or sodium titanates, in the anode can greatly increase the charging efficiency of the high-temperature Ni-MH battery of the present invention. When the amount of the said titanium additive is more than 1.0% (weight), based on the weight of spherical nickel hydroxide in the anode substances, the charging efficiency of the battery can reach 95% or higher. According to the present invention, the amount of the titanium additive is in the range of 0.1-15.0% (weight), based on the weight of the active spherical nickel hydroxide in the anode substances. It can be seen further from FIG. 3, when the amount of the said titanium additive is less than 1.0% (weight), based on the weight of the active spherical nickel hydroxide in the anode substances, the charging efficiency of the battery cannot reach 95%. When the amount is more than 5% (weight), the increase of the charging efficiency of the battery is not proportional to the increase of the amount of the said titanium additive. Therefore, the amount of the said titanium additive is preferably in the range of 1.0-5.0% (weight), based on the weight of the active spherical nickel hydroxide in the anode substances. THE BEST MODES FOR CARRYING OUT THE INVENTION
    [43] 43. The high-temperature Ni-MH battery of present invention will be described in detail in combination with the drawings and the following Examples. EXAMPLE 1
    [44] 44. 90 parts by weight of spherical Ni(OH)2 powder, 10 parts by weight of CoO powder, 1.0 part by weight of TiO2 powder, 0.3 part by weight of CMC, 1.0 part by weight of PTFE, and 45 parts by weight of water were mixed together. The mixture was stirred homogeneously, then the obtained homogeneous mixture was filled into a foamed nickel base plate. The obtained base plate was baked to dry, then it was roller-compacted and cut to desired size to obtain an anode 1.
    [45] 45. 95 parts by weight of a AB5 type hydrogen-storing alloy powder MmNi3.7Co0.7Mn0.3Al0.3 (in which, Mm is a mixed rare earth metal), 4 parts by weight of carbon powder, 1 part by weight of CMC powder and 50 parts by weight of water were mixed together. The mixture was stirred homogeneously, then the obtained homogeneous mixture was filled into a foamed nickel base plate. The obtained base plate was baked to dry, then it was roller-compacted and cut to desired size to obtain a cathode 3.
    [46] 46. Subsequently, the above made cathode 3 and anode 1 were put together, and a modified polypropylene separator 2 was inserted between the cathode 3 and the anode 1. The obtained structure was rolled and was put into a cylindrical steel housing 4. An alkaline electrolyte solution containing KOH, NaOH and LiOH was injected into the housing. After welding built-up covers 5, the housing was sealed. Thus, an AA type Ni-MH battery as shown by FIG. 1 was obtained.
    [47] 47. The obtained battery was activated at room temperature, and was circled thoroughly to make the battery having a stable capacity. It was charged at room temperature under 0.06 C. for 24 hours, and discharged under 1.0 C. to 1.0V to obtain a capacity of C0. By adopting the same procedure, it was charged and discharged at 55°C. to obtain a capacity of C1. The charge efficiency of the battery was calculated with the formula F=C1/C0, and the result were shown in FIG. 3. EXAMPLES 2-6
    [48] 48. The Ni-MH batteries of the present invention were prepared in the same manner and materials as explained in Example 1, instead of 1 part by weight of TiO2 was replaced by 0.1, 3, 5, 15, and 0 part by weight of TiO2. The charge efficiency of the obtained batteries was calculated in the same manner as explained in Example 1. The results were shown in FIG. 3. EXAMPLES 7-11
    [49] 49. The Ni-MH batteries of the present invention were prepared in the same manner and materials as explained in Example 1, instead of 1 part by weight of TiO2 was replaced by 0.1, 1, 3, 5, and 15 parts by weight of metal titanium powder. The charge efficiency of the obtained batteries was calculated in the same manner as explained in Example 1. The results were shown in FIG. 3. EXAMPLES 12-16
    [50] 50. The Ni-MH batteries of the present invention were prepared in the same manner and materials as explained in Example 1, instead of 1 part by weight of TiO2 was replaced by 0.1, 1, 3, 5, and 15 parts by weight of Na2TiO3. The charge efficiency of the obtained batteries was calculated in the same manner as explained in Example 1. The results were shown in FIG. 3.
    [51] 51. As is shown by the results, the addition of titanium additive in the nickel hydroxide anode can greatly improve the charge efficiency of Ni-MH batteries at high temperatures.
    权利要求:
    Claims (10)
    [1" id="US-20010000484-A1-CLM-00001] 1. A high-temperature Ni-MH battery, comprising an anode plate (1) made up of a base plate and anode substances adhering on the base plate, a cathode plate (3) made up of a base plate and cathode substances adhering on the base plate, a separator (2), a steel housing (4), built-up covers (5), characterized in that: the said anode base plate is selected from the base plates of foamed nickel, fiber nickel, and porous steel strip; the said anode substances comprise an active material of spherical nickel hydroxide, an electroconductive agent, an adhesive and an additive; in which, the said electroconductive agent is at least one selected from the group consisting of nickel powder, carbon powder, acetylene black, graphite powder, cadmium powder, zinc powder, Co—Zn alloy powder, cobalt powder, CoO, Co2O3, Co(OH)2 and Co(OH)3; the said adhesive is at least one selected from the group consisting of PTFE, CMC,MC and PVA; the said additive is selected from the titanium additives which can restrain the electric potential descent in the oxygen-formation reaction at the Ni anode during charging at temperatures higher than 40°C.
    [2" id="US-20010000484-A1-CLM-00002] 2. The high-temperature Ni-MH battery as claimed in
    claim 1 , characterized in that, the said titanium additive is at least one selected from the group consisting metal titanium, Ti(OH)2, Ti(OH)3, TiO, Ti2O3, TiO2,Ti3O5, titanates and titanium salts.
    [3" id="US-20010000484-A1-CLM-00003] 3. The high-temperature Ni-MH battery as claimed in
    claim 1 or
    2 , characterized in that, the amount of the said titanium additive is in the range of 0.1-15.0% (weight), based on the spherical nickel hydroxide in the anode substances.
    [4" id="US-20010000484-A1-CLM-00004] 4. The high-temperature Ni-MH battery as claimed in
    claim 3 , characterized in that, the amount of the said titanium additive is in the range of 1.0-5.0% (weight), based on the spherical nickel hydroxide in the anode substances.
    [5" id="US-20010000484-A1-CLM-00005] 5. The high-temperature Ni-MH battery as claimed in
    claim 1 or
    2 , characterized in that, the said cathode base plate is selected from foamed nickel base plate, fiber nickel base plate, and porous steel base plate. The said cathode substances comprise an AB5 or AB2 type hydrogen-storing alloys, an electroconductive agent, an adhesive; in which, the electroconductive agent is at least one selected from the group consisting nickel powder, carbon powder, acetylene black, graphite power, cadmium powder, zinc powder, Co—Zn alloy powder, cobalt powder, CoO, Co2O3, Co(OH)2 and Co(OH)3; the said adhesive is at least one selected from the group consisting PTFE, CMC, MC and PVA.
    [6" id="US-20010000484-A1-CLM-00006] 6. A method for making the high-temperature Ni-MH battery as claimed in
    claim 1 , comprising:
    (1) making an anode plate; mixing nickel hydroxide, an electroconductive agent, a titanium additive, an adhesive and water together, stirring the resulting mixture homogeneously, filling the homogeneous mixture into an anode base plate which has been welded with electrode terminals, baking to dry, roller-compacting it to a desired thickness to obtain an anode plate;
    (2) making an anode plate: mixing a hydrogen-storing alloy powder, an electroconductive agent, an adhesive and water together, stirring the resulting mixture homogeneously, filling the homogeneous mixture into a cathode base plate which has been welded with electrode terminals, baking to dry, roller-compacting it to a desired thickness to obtain a cathode plate;
    (3) Selecting a proper separator, putting it between the anode and the cathode made above, pressing them together tightly, or convoluting into cylindrical model, and then putting it into a quadrate or cylindrical steel housing;
    (4) Welding electrodes, injecting an electrolyte solution and then sealing;
    (5) Battery activating;
    (6) Battery assembling.
    [7" id="US-20010000484-A1-CLM-00007] 7. The method as claimed in
    claim 6 , characterized in that, the said titanium additive is at least one selected from the group consisting metal titanium, Ti(OH)2, Ti(OH)3, TiO, Ti2O3, TiO2, Ti3O5, titanates and titanium salts.
    [8" id="US-20010000484-A1-CLM-00008] 8. The method as claimed in
    claim 6 or
    7 , characterized in that, the amount of the said titanium additive is in the range of 0.1 15.0% (weight), based on the spherical nickel hydroxide in the anode substances.
    [9" id="US-20010000484-A1-CLM-00009] 9. The method as claimed in
    claim 8 , characterized in that, the amount of the said titanium additive is preferably in the range of 1.0-5.0% (weight), based on the spherical nickel hydroxide in the anode substances.
    [10" id="US-20010000484-A1-CLM-00010] 10. The method as claimed in
    claim 6 or
    7 , characterized in that, the said cathode base plate is selected from foamed nickel base plate, fiber nickel base plate, and porous steel strip base plate, the said cathode substances comprise an AB5 or AB2 type hydrogen-storing alloy, an electroconductive agent, an adhesive; in which, the electroconductive agent is at least one selected from the group consisting nickel powder, carbon powder, acetylene black, graphite power, cadmium powder, zinc powder, Co—Zn alloy powder, cobalt powder, CoO, Co2O3, Co(OH)2 and Co(OH)3; the said adhesive is at least one selected from the group consisting of PTFE, CMC, MC and PVA.
    类似技术:
    公开号 | 公开日 | 专利标题
    US6689514B2|2004-02-10|High-temperature Ni-MH battery and a method for making the same
    EP1519434A1|2005-03-30|Sealed nickel-zinc primary cell
    JPH11176436A|1999-07-02|Alkaline storage battery
    EP0170519B1|1992-06-17|A method of producing a sealed metal oxide-hydrogen storage cell
    US6818348B1|2004-11-16|Nickel hydroxide paste with molasses binder
    JP4475840B2|2010-06-09|Nickel metal hydride storage battery and assembly thereof
    US6218047B1|2001-04-17|Active electrode compositions comprising Raney based catalysts and materials
    JP2944152B2|1999-08-30|Method for manufacturing nickel-hydrogen storage battery
    JP2001357872A|2001-12-26|Nickel-hydrogen secondary battery
    JP3429684B2|2003-07-22|Hydrogen storage electrode
    JPH08264174A|1996-10-11|Hydrogen storage alloy cathode and its preparation
    EP0567132B1|1997-08-13|Sealed type nickel/hydrogen alkaline storage battery
    JP3330088B2|2002-09-30|Negative electrode for secondary battery
    JP2004164863A|2004-06-10|Sealed type nickel zinc primary cell
    JP4767515B2|2011-09-07|Pocket hydrogen storage alloy electrode and nickel / hydrogen storage battery
    JP3482478B2|2003-12-22|Nickel-metal hydride storage battery
    JP2000251883A|2000-09-14|Sealed alkaline zinc storage battery
    JP2005100732A|2005-04-14|Alkaline zinc primary cell
    JP2595664B2|1997-04-02|Cadmium negative electrode plate and alkaline secondary battery using the negative electrode plate
    JP2003317798A|2003-11-07|Nickel - hydrogen battery and its manufacturing method
    JPH08213003A|1996-08-20|Nickel-metal hydride battery
    JP2000200612A|2000-07-18|Rectangular alkaline secondary battery
    JP2940952B2|1999-08-25|Method for manufacturing nickel-hydrogen alkaline storage battery
    JP2000106184A|2000-04-11|Nickel hydroxide electrode for alkaline storage battery, and the alkaline storage battery using this electrode
    JPH10255788A|1998-09-25|Positive electrode for alkaline secondary battery and alkaline secondary battery
    同族专利:
    公开号 | 公开日
    EP1195832A4|2003-07-09|
    HK1042381A1|2002-08-09|
    US6689514B2|2004-02-10|
    JP2002541636A|2002-12-03|
    CN1269615A|2000-10-11|
    WO2000060688A1|2000-10-12|
    DE60044780D1|2010-09-16|
    EP1195832A1|2002-04-10|
    AU3653800A|2000-10-23|
    CN1127163C|2003-11-05|
    HK1028678A1|2001-02-23|
    EP1195832B1|2010-08-04|
    引用文献:
    公开号 | 申请日 | 公开日 | 申请人 | 专利标题
    US20030054247A1|2001-04-17|2003-03-20|Sanyo Electric Co., Ltd.|Nickel electrode for alkaline storage battery and alkaline storage battery|
    US20030104277A1|2001-09-18|2003-06-05|Mitsunori Tokuda|Nickel hydroxide electrode for alkaline storage battery and akaline storage battery|
    US20090253036A1|2004-04-13|2009-10-08|Nanotecture Ltd.|Electrochemical Cell|
    US20160293934A1|2014-07-11|2016-10-06|Lg Chem, Ltd.|Positive electrode material of secondary battery and preparation method thereof|FR2567326B1|1984-07-04|1987-04-10|Wonder|IMPROVEMENTS IN NICKEL HYDROXIDE POSITIVE ELECTRODES FOR ALKALINE ACCUMULATORS|
    US5523182A|1992-11-12|1996-06-04|Ovonic Battery Company, Inc.|Enhanced nickel hydroxide positive electrode materials for alkaline rechargeable electrochemical cells|
    JPH07262990A|1994-03-18|1995-10-13|Hitachi Maxell Ltd|Manufacture of nickel electrode for alkaline storage battery|
    JP3527594B2|1995-11-16|2004-05-17|松下電器産業株式会社|Alkaline storage battery and method of manufacturing the same|
    JPH09237630A|1996-02-29|1997-09-09|Matsushita Electric Ind Co Ltd|Active material and positive electrode for alkali storage battery|
    EP0833397B1|1996-09-20|2002-05-15|Matsushita Electric Industrial Co., Ltd.|Positive electrode active material for alkaline storage batteries|
    US6042753A|1996-10-06|2000-03-28|Matsushita Electric Industrial Co., Ltd.|Active materials for the positive electrode in alkaline storage batteries|
    JP3387381B2|1997-09-04|2003-03-17|松下電器産業株式会社|Alkaline storage battery|
    US6287724B2|1997-11-03|2001-09-11|Eveready Battery Company, Inc.|Nickel metal hydride cells designed for high rate/low temperature performance|
    JP3923157B2|1997-12-11|2007-05-30|松下電器産業株式会社|Alkaline storage battery|
    US6177213B1|1998-08-17|2001-01-23|Energy Conversion Devices, Inc.|Composite positive electrode material and method for making same|
    US6017655A|1998-08-18|2000-01-25|Ovonic Battery Company|Nickel hydroxide positive electrode material exhibiting improved conductivity and engineered activation energy|
    CN1085419C|1998-12-15|2002-05-22|冶金工业部钢铁研究总院|Manufacture of alkaline secondary nickel-hydrogen cell and its positive and negative pole material|JP2001222853A|2000-02-08|2001-08-17|Matsushita Electric Ind Co Ltd|Method for changing rotation speed of disk device, input device and disk device|
    CN100397683C|2002-06-28|2008-06-25|三洋电机株式会社|Alkali cell|
    CN100389514C|2004-08-03|2008-05-21|比亚迪股份有限公司|Preparation method for nickel positive electrode sheet of alkaline storage battery|
    JP2006107966A|2004-10-07|2006-04-20|Sanyo Electric Co Ltd|Nickel-hydrogen storage battery|
    CN100424923C|2004-12-09|2008-10-08|广州市鹏辉电池有限公司|Nickle-hydrogen alkaline battery and preparation method thereof|
    CN1824724B|2005-02-23|2011-05-18|深圳市比克电池有限公司|Water binder, its application in manufacturing lithium ion battery positive plate and battery|
    CN100557867C|2006-07-27|2009-11-04|深圳市力可兴电池有限公司|High temperature composite additive agent for nickel base charging battery|
    CN101207196B|2006-12-22|2011-01-12|比亚迪股份有限公司|Method for preparation of nickel-metal hydride storage cell nickel anode|
    CN101267047B|2007-03-16|2010-10-06|深圳市力可兴电池有限公司|Nickel hydrogen charging battery|
    CN101459241B|2007-12-10|2012-03-07|比亚迪股份有限公司|Composite nickel powder, preparation thereof, nickel anode and alkaline accumulator|
    EP2534717B1|2010-02-09|2017-04-19|BAE Systems PLC|Rechargeable batteries|
    CN103078116B|2011-10-26|2016-10-05|比亚迪股份有限公司|The anode additive of a kind of Ni-MH battery and positive electrode|
    CN109119635B|2013-12-20|2021-10-15|苏州宝时得电动工具有限公司|Battery with a battery cell|
    JP5648772B1|2014-02-10|2015-01-07|エクセルギー・パワー・システムズ株式会社|Alkaline secondary battery|
    CN108054370A|2017-12-15|2018-05-18|淄博君行电源技术有限公司|The positive electrode and preparation method of a kind of Ni-MH battery|
    法律状态:
    2000-11-29| AS| Assignment|Owner name: BYD BATTERY CO., LTD., CHINA Free format text: ASSIGNMENT OF ASSIGNORS INTEREST;ASSIGNOR:LV, HAIGANG;REEL/FRAME:011336/0278 Effective date: 20001122 |
    2001-06-25| AS| Assignment|Owner name: BYD BATTERY CO., LTD., CHINA Free format text: ASSIGNMENT OF ASSIGNORS INTEREST;ASSIGNOR:HAIGANG LV;REEL/FRAME:011935/0223 Effective date: 20001122 |
    2004-01-22| STCF| Information on status: patent grant|Free format text: PATENTED CASE |
    2007-08-10| FPAY| Fee payment|Year of fee payment: 4 |
    2011-07-13| FPAY| Fee payment|Year of fee payment: 8 |
    2015-07-17| FPAY| Fee payment|Year of fee payment: 12 |
    优先权:
    申请号 | 申请日 | 专利标题
    CN99116113A|CN1127163C|1999-04-05|1999-04-05|High-temperature Ni/H2 battery and its manufacture|
    CN99116113.0||1999-04-05||
    CN99116113A||1999-04-05||
    PCT/CN2000/000074|WO2000060688A1|1999-04-05|2000-04-05|A high-temperature nickel-hydrogen battery and producing method thereof|
    [返回顶部]