    • 专利摘要:
    The invention provides an alternative liquid crystal and light emitting display which include at least one Transparent Conductive Oxide layers which comprises a zinc oxide doped with a group III, IV, V, or transition metal dopant, and sputtered from a sputtering target. In a further embodiment, this Transparent Conductive Oxide layer can optionally include a layer of a patternable TCO, such as ITO.
    公开号:SE1750267A1
    申请号:SE1750267
    申请日:2015-08-11
    公开日:2017-03-10
    发明作者:Mcginnis Robert；Yang Jing；Lin Tzu-Chieh
    申请人:Sci Eng Mat Inc；
    IPC主号:
    专利说明:

    [1] [0001] The present invention relates generally to a novel display, such as an LCD orOLED display, having at least one 10-2000 nm (and preferably from 50-400 nm) layer ofTransparent Conducting Oxide (“TCO”) which is one or more of Metal doped ZincOxide (“Metal-ZnO”), deposited by AC or DC magnetron sputtering, or by pulsed laserdeposition, and using a target that is doped with metal such as aluminum, gallium andsilicon (generally at a level of from 0.05% to 5%, and preferably at 1%, 2%, or 3% each+/- 0.25%) and optionally having an additional layer of TCO, specifically Indium Tinoxide (“ITO”), in the display.BACKGROUND OF THE INVENTION
    [2] [0002] A LCD display is not a light generator, but rather a light controller. That lightcan come from the front of the device and be reflected by a mirror at the back; this is thecommon application for calculators and watches. They can also get the light from a lightsource at the back (in place of the mirror and frequently LED”s) and then control the lightthat shines out thru the front. This is the method used for computer monitors and TV”s.The basic principle is to have two polarizing filters at some specific angle, such as 45° tol25°, and more preferably 60° to ll0°, and most preferably from 80° to l00°. The heartof the device is the liquid crystal layer working as a waveguide to change the polarizationof the light. If this remains the case, no light will get thru and the display will be dark,and preferably black (indicating that light in the visible wave range is not transmittedthrough the display). There are a number of types of liquid crystal and which include, forexample, nematic, cholesteric, dichroic, discotic and blue phase liquid crystals, all ofwhich may have advantageous application in the present invention. When a voltage isapplied to the liquid crystal layer the organic molecules adjacent to the electrode twist thelight polarization allowing it to pass thru to the second polarizing filter for thetransmissive LCDs or be reflected back by the mirror and allow the light to pass thru forthe reflective LCDs. The invention is also useful in OLED displays. In these orgaiiiclight-emitting diode (OLED) the display includes a light-emitting diode (LED) in which the emissive electroluminescent layer is a film of organic compound (rather than theliquid crystal types mentioned above) which emits light in response to an electric current.This layer of organic semiconductor is situated between two electrodes; typically, at leastone of these electrodes is transparent, and is advantageously the TCO in accordance withthe present invention.
    [3] [0003] The Voltage that is applied to the liquid crystal layer is applied thru a TCO.(i.e., a positive electrode) The criteria of good TCO layer are light transmittance--i.e.above 80%, and preferably above 85%, and more preferably above 87% in the visiblewavelength--and low sheet resistance i.e. < 100, and preferable less than 80 and mostpreferably less than <50 Q/U. In most applications, voltage is applied on one side thru apattern that will determine which portion of the liquid crystal will change polarization.The TCO on the other side (called the negative electrode in the picture) completes thecircuit. This is not necessarily patterned. For TV”s and monitors the pattern becomes amatrix of pixels, and for color LCD”s there are red, green and blue sub-pixels with a colormask for each.
    [4] [0004] In accordance with the present invention, Metal-ZnO is used alone or incombination with ITO as the negative electrode, while a patternable layer is used for thefront. In addition for applications that use seven segment displays such as watches andcalculators, the patterning complexity is much reduced from that required for highdensity pixels, and the ability to pattern the Metal-ZnO would be suff1cient to eliminatethe need for any additional ITO patterned layer so that this optional layer may be left offof this layer of TCO. An edge seal with the LCD display is used in order to inhibit dampheat degradation of Metal-ZnO.
    [5] [0005] The primary critical characteristics of a TCO are resistivity, and transmittance.These are controlled by film composition, carrier concentration, film thickness, and thedeposition process. The etch-ability and ability to withstand damp heat, are alsoimportant parameters. The wide band gap (over 3 eV) n-type conductive oxides such asindium tin oxide (ITO), Metal doped Zinc Oxide (Metal-ZnO), and are two importantpotential materials for use as a TCO. Applications in which the Metal-ZnO TCO layer ofthe present invention could be used include rigid LCD and other flat panel displays, touchscreens, flexible displays (such as might be used for Wearable electronicsmoVement), organic light emitting diodes (OLED), electronic paper displays and plasmadisplay panels. An additional application area Where Metal-ZnO is the primary or astrong candidate for use as a TCO is thin film smart Windows or architectural glass.[0006] In accordance With the present inVention, the Metal-ZnO is preferablydeposited by sputtering, both DC and RF, With Variations of the configurations and thedeposition parameters depending on the end-use application. Sputtering has theadVantage of being able to deposit films With loW substrate temperature (<200°C). This isVery important for flexible applications Where the conductiVe film is deposited on plasticfilms of Various types. Another process that could be used With good results With Metal-ZnO is pulsed laser deposition (PLD). While other methods could be used to deposit theTCO layer, in general, the results obtained from these processes are not as good as thoseobtained from sputtering and PLD.BRIEF DESCRIPTION OF THE DRAWINGS
    [7] [0007] FIG. l is a cross section of a liquid crystal display in accordance With theinVention; and
    [8] [0008] FIG.2 is a cross section of an organic light emitting display in accordance Withthe inVention.
    [9] [0009] As in many things in nature the increase in carrier concentration With itsresulting decrease in resistiVity, causes a reduction in transmittance. In addition, as theconcentration becomes fairly high, oxides of the impurity donors start to form reducingthe electrical performance. So there is a sweet spot for all of these films.
    [10] [0010] The resistiVity determines the Voltage drop across the film as current floWsinto (or out depending on the application) the deVice. If the Voltage drop is too high, forinstance, a display screen might be darker in the center as the current must floW from theedges. This is both a static and dynamic characteristic of the film. Mobility is related tothe speed With Which the carriers moVe thru the film. In fact the drift Velocity of thecarriers is equal to the mobility times the applied Voltage field. The implications here areassociated With the rate of change of the applied Voltage. The practical result is that therefresh rate of displays can be limited by the film mobility.
    [11] [0011] Transmittance is a key characteristic of the films for use as a TCO. The largeband-gap conductive oxides are transparent in the visible light spectrum because theincoming photons do not have enough energy to create hole-electron pairs and cause lossof transparency by absorption. ZnO has a band-gap of 3.37 eV, the addition of impuritieschanges that number, generally making it a bit higher. At the upper (blue) edge of thevisible spectrum the photons have energy around 3.5 eV so light is not absorbed by thefilm. On the longer wave length (infrared) side the light is reflected due to free electrons.This makes these films ideal for window coatings as they let in the light, and keep out theheat. Metal-ZnO is not as reflective in the shorter wavelength infrared region as ITO.Properly fabricated ITO has transmittance in the visible spectrum of around 80-85%,while Metal-ZnO is a little better in the 85-90% range or higher depending on the filmthickness.
    [12] [0012] Thickness is also a major factor especially for Metal-ZnO as these films areknown to have significantly lower performance when they are thinner than 100 nm. Thisis caused by boundary effects with the deposition surface due to the initial islandsformation. Changes in these conditions can have profound effects on the filmperformance. Such changes result from crystalline structure, oxygen vacancies, andothers and are influenced by deposition methods and post processes such as annealing.ITO is successfully deposited with thickness down to 50 nm. ITO mobility is drivenprimarily by ionized impurity scattering and seems to be somewhat less sensitive to theboundary conditions. Interestingly the Metal-ZnO films deposited on thin film solar cells(CIGS) have thickness ranging from 500-2000 nm. It seems that the higher thickness maybe the way to avoid serious degradation of the film in damp heat. Each application hasdifferent thickness requirements. Growth Temperature has an impact on the electricalperformance of the films. In general the higher temperatures give better results. However,there is a major effort to obtain good results at lower temperatures for deposition onvarious plastic films, such as polyimide, or polycarbonate such as at temperatures belowl00°C, and preferably below 80°C. Deposition rate is an important manufacturing costfactor. The typical rate appears to be about 30 nm/min.
    [13] [0013] The following chart compares some of the key Characteristics of ITO and ZnO based alternatives.
    [14] [0014] There are a number of interesting things that can be gleaned from thisinformation and the prior art: Both AZO and ITO are n-type degenerate (means highlydoped) semiconductors. Although AZO f1lms have been made that match the resistivityof ITO f1lms, the ITO f1lms generally have better mobility. However, AZO f1lms havebetter stability at high temperatures and AZO has slightly better transmittance. PLDdeposition may provide improved results, however, there is a question how reasonable aprocess it is for high volume manufacturing, Most of the higher performing AZO f1lmshave some differences in technology specifically may be influenced by process changessuch as varying the kind of deposition, including, for example: PLD deposition; Co-doping the n-type dopant with a smaller amount of p-type dopant; AZO and Zn put downin sequential layers; use of a Homo-Buffer layer; and post annealing in and reactive orinert atmosphere, such as H2, Nz, or Oz, For both AZO and ITO the mobility isproportional to the thickness, only ITO seems to be less effected. At least part of thiseffect is believed to be due to AZO adsorbing Oz at the surface and reducing the numberof oxygen vacancies and therefore the number of available free carriers. This is probablyalso the driver in the damp heat degradation issue. The electrical and optical results are dependent on the deposition process and parameters and specif1cally things as Oz concentration, Ar concentration, addition of H2, gas pressure, DC or RF magnetronsputtering, substrate type and temperature, and many others. The resistivity of AZOf1lms has been improved over the past 30 years going from over 6 to about 1X10'4 Q-cmwith relatively thick film, while the best ITO f1lms have remained about the same in therange of lXl0_4 Q-cm. The required mobility, although it tends to track with theresistivity.
    [15] [0015] Solid panel LCD
    [16] [0016] This technology serves the LCD TVs, computer monitors, and other non- touch screen applications. The property requirements for this application are: Location Substrate Deposition Film Resistivity Sheetmaterial temp. °C thickness nm Q-cm resistanceQ/squareTFT side Glass Approx.200 35-140 4-8 X10'4 30-120CF side Glass <200 120-160 1.6-4 X10'4 16-30
    [17] [0017] The Metal-ZnO thin f1lms suitable for the present invention meet theresistivity requirements and appear to be in the desired range for thickness and resistivity.[0018] Plasma Display Panels
    [19] [0019] Plasma display panels have used in flat screen TVs and other similarapplications. They have the advantage of better picture quality and viewing at large offnormal angles than LCD TVs, and the disadvantage of high power dissipation.
    [20] [0020] The TCO properties requirements for this application are: Substrate Deposition temp. Film thickness Resistivity Q-cm Sheet resistancematerial °C nm Q/ squareGlass Approx. 200 150-200 2-3 X10'4 <20
    [21] [0021] Touch screen Panels
    [22] [0022] There are two principal technologies for touch screens; resistive (whichusually requires some sort of a stylus) and capacitive. Metal-ZnO is suitable for bothtechnologies
    [23] [0023] Resistive
    [24] [0024] Resistive touch screens are favored because of low cost; however they canwear out due to continuous flexing of the top layer. Metal-ZnO is potentially useful inthis type of device. This uses the piezoelectric properties of the ZnO to generate a voltage at the touch point.
    [25] [0025] The table below is for the high sheet resistance TCO film Where the pressurefrom the stylus generates the contact signal. There may also be applications that can use a thicker film.
    [26] [0026] Capacitive
    [27] [0027] The requirements for ITO films in these applications are currently in the rangeof 100-250 nm.
    [28] [0028] Other potential applications include OLED, and Flexible Displays andElectronic Paper Displays (EPD).
    [29] [0029] FIG. 1 is a cross-section of a liquid crystal display 10 as a representation of afirst embodiment of the inVention. The layers are as follows going from top to bottom inthe figure: front polarizer 12 (Which is usually included), the substrate 14 Which can berigid such as glass - can be soda lime or borosilicate, or can be flexible, such astransparent polymers including, for example, polycarbonate polyimide or PET, a barrierlayer 16, such as an SiOz undercoat - to block Na from the glass; a TCO layer 20, Whichin this case is Metal-ZnO alone or in combination With Indium Tin Oxide - a secondbarrier layer 22 - this is usually SiOz, an LC alignment layer 24 - typically rubbedpolyimide for LC alignment Which is not necessary When the light emissiVe layer is anorganic light emitting diode (OLED), the light emissiVe layer, in this instance a LiquidCrystal material and spacers 30, a second LC alignment layer 32 Which is again notnecessary for the OLED , a third barrier layer 34, a second transparent conductiVe oxidelayer 36, Which is either the same Metal ZnO alone or With ITO or just ITO, a fourthbarrier layer 38, an optional second substrate layer 40 and an optional rear polarizer andreflector 42. On one side, the cell includes a conductiVe cross-over 44, and on the otherside a seal 46. A Hybrid Liquid Crystal Display (HLCD) in accordance With theinVention Would be one With the top layer of ITO partially or totally replaced With a metaldoped zinc oxide With one or more elements from group III, IV, V or transition metal dopants such as boron, aluminum, gallium, silicon, titanium, niobium and indium at dopant levels of less than 5%, and preferably less than 3%, and optionally including co-dopants, such as less than 1% silicon, aluminum, or gallium.
    [30] [0030] FIG.2 is an illustration of an OLED display 105 in accordance with thepresent invention. Starting from the top and working downward through the layers, thetop layer is a cathode 110, which is over the light emitting layer 120, which is over theconductive layer 130, and the next layer is the anode layer that is the transparentconductive oxide layer (TCO) which is a metal oxide layer in accordance with the presentinvention, and the bottom layer is the substrate, which is glass or an appropriatetransparent plastic material. The display also includes posts 150.
    [31] [0031] In accordance with the present invention, ZnO based sputtering targets werefabricated using the following method. A pressing powder was prepared by mixingoXides of the dopant metal with ZnO in water containing an organic binder, then spraydrying the resultant slurry to obtain a free flowing powder. The powder was loaded intoa die and was formed using cold isostatic pressing (CIP). The pre-formed green bodywas sintered at temperatures above 1000°C for more than 1 hour to obtain a denseceramic, preferably higher than 95%. The ceramic was diamond ground to obtain thefinal dimensions.
    [32] [0032] For the resulting target, the density and the microstructure were measured.The density was in the desired range of 75-100%, and preferably above 90%. Thedensity achieved was above 95% theoretical density (“TD”). The microstructure was alsoin the desired range of from 25-100 um, preferably less than 50um grain size, and morepreferably less than 20 um. The resistivity of the thin f1lm by DC sputtering using thetarget is lower or in the range of 1E10-3 Q-cm with the thickness less than 300 nm, andpreferably less than 200 nm.
    [33] [0033] In accordance with the patent statutes, the best mode and preferredembodiment have been set forth; the scope of the invention is not limited thereto, but rather by the scope of the attached claims.
    权利要求:
    Claims (27)
    [1] 1. A liquid crystal display having at least the following layers: a front polarizer, a transparent substrate of glass or plastic, a first transparent conductive oxide having a transrnittance in the visibleWavelength of at least 80% and cornprising a layer of rnetal doped zinc oxide applied bysputtering, a liquid crystal alignrnent layer, a liquid crystal layer, and a second transparent conductive oxide layer including a pattern in the layer.
    [2] 2. A liquid crystal display as set forth in clairn 1 Wherein the second transparent conductive oxide layer includes a pattern in the layer.
    [3] 3. A liquid crystal display as set forth in clairn 1 Wherein the second transparent conductive coinprises indiuin tin oxide.
    [4] 4. A liquid crystal display as set forth in claiin 1 Wherein the first transparent conductive layer is froin about 10 to about 2000 nin in thickness.
    [5] 5. A liquid crystal display as set forth in claiin 4 Wherein the first transparent conductive layer is froin about 50 to about 400 nrn in thickness.
    [6] 6. A liquid crystal display as set forth in claiin 1 Wherein the first transparent conductivelayer is deposited using a sputtering target by rnagnetron sputtering or by pulsed laser deposition.
    [7] 7. A liquid crystal display as set forth in claiin 1 Wherein the target cornprises zinc oxide doped With a inetal at a level of level of frorn 0.05% to 5%.
    [8] 8. A liquid crystal display as set forth in claim 1 Wherein the metal used for the dopingcomprises one or more of aluminum or gallium alone, or in combination With each other, and one or more of indium or silicon.
    [9] 9. A device having at least the following layers: a transparent substrate of glass or plastic; a transparent conductiVe oxide comprising a layer of zinc oxide doped With agroup III, IV, V, or transition metal dopant, and applied by sputtering; and a liquid crystal layer and a liquid crystal alignment layer or a light emitting layer.
    [10] 10. A deVice as set forth in claim 9 Wherein the transparent conductiVe oxide is zincoxide doped With less than 5% of the dopant.
    [11] 11. A deVice as set forth in claim 10 Wherein the transparent conductiVe oxide is zinc oxide doped With one or more from group III, IV, V, or transition metal dopant.
    [12] 12. A deVice as set forth in claim 11 Wherein the zinc oxide is doped With aluminum or gallium alone, or in combination With each other, and optionally including indium.
    [13] 13. A deVice as set forth in claim 12 Wherein the transparent conductiVe oxide layer also includes less than 1% of a co-dopant.
    [14] 14. A deVice as set forth in claim 13 Wherein the co-dopant is from group III, IV, V, or transition metal dopant such as boron, silicon, titanium, niobium and indium.
    [15] 15. A deVice as set forth in claim 9, Which is one of a liquid crystal display or an organic light emitting diode display.
    [16] 16. A method of making a deVice comprising the steps of forming a compositecomprising, a transparent substrate of glass or plastic, a transparent conductiVe oxidecomprising a layer of zinc oxide doped With a group III, IV, V, or transition metal dopant, a liquid crystal layer and a liquid crystal alignment layer or a light emitting layer, and 11 including the step of applying the transparent conductiVe oxide layer to the transparentsubstrate layer by sputtering unto the substrate from a sputtering target haVing amicrostructure haVing an aVerage grain size of less than100 pm and density of more than 75% TD.
    [17] 17. A method of making a deVice as set forth in claim 16 Wherein the deVice is a liquid crystal display.
    [18] 18. A method of making a deVice as set forth in claim 17 Wherein the sputtering target has an aVerage grain size of 20 rim and density of 95% TD and aboVe.
    [19] 19. A display haVing at least the following layers: a transparent substrate of glass or plastic; a first transparent conductiVe oxide comprising a layer of metal doped zinc oxideapplied by sputtering from a sputtering target haVing a microstructure haVing an aVeragegrain size of 25-100 pm and density of more than 75% TD; a light emissiVe layer; and a second transparent conductiVe oxide layer.
    [20] 20. A display as set forth in claim 19 Wherein the atensity ofthe sputtering target is in title range of 75-1 0094» 'TER
    [21] 21. A display as set forth in claim 19 Wherein the density' of the sputtering target is alëove 9094:-.
    [22] 22. A display as set forth in claim 19 in the microstructure is less than 50nm grain size.
    [23] 23. A display as set forth in claim 22 in the microstructure is less than 20nm grain size.
    [24] 24. A display as set forth in claim 19 xfvherein a first transparent conductiVe oxide is applied by DC sputtering. 12
    [25] 25. A display as set forth in claim 19 in Which the resistiVity of the first transparent conductiVe oxide is in the range of 1E10-3 Q-cm at a thickness of less than 300 nm.
    [26] 26. A display as set forth in claim 25 in Which the resistiVity of the first transparentconductiVe oxide is in the range or loWer than lEl0-ß Q-cm at a thickness of less than 200 nm.
    [27] 27. A display haVing at least the following layers: a transparent substrate of glass or plastic; a first transparent conductiVe oxide comprising a layer of metal doped zinc oxideincluding a dopant of aluminum or gallium alone, or in combination With each other, andoptionally including indium and applied by sputtering from a sputtering target haVing amicrostructure haVing an aVerage grain size of 25-100 iim and density of more than 75%TD, and the first transparent conductiVe oxide haVing a resistiVity of from lEl0 to 3Q-cm at a thickness of less than 300 nm; a light emissiVe layer; and a second transparent conductiVe oxide layer.
    类似技术:
    公开号 | 公开日 | 专利标题
    JP6987952B2|2022-01-05|Transistor
    CN101036200B|2010-12-29|Transparent conductor, transparent electrode, solar cell, luminescent device and display panel
    TW201610961A|2016-03-16|Display panel, display device, and driving method of display device
    TW202026727A|2020-07-16|Display device, manufacturing method of display device, and electronic device
    CN100363531C|2008-01-23|Preparation method of gallium adulterated zinc oxide transparent conductive film
    US10366803B2|2019-07-30|Metal oxide thin film, method for depositing metal oxide thin film and device comprising metal oxide thin film
    CN203658697U|2014-06-18|Conducting support for vitrage with variable scattering characteristic of liquid crystal medium and vitrage
    Yamamoto et al.2008|Ga‐doped zinc oxide: An attractive potential substitute for ITO, large‐area coating, and control of electrical and optical properties on glass and polymer substrates
    US10613397B2|2020-04-07|Display having a transparent conductive oxide layer comprising metal doped zinc oxide applied by sputtering
    CN103617831B|2016-02-03|Preparing aluminum-doped zinc oxide transparent conducting films of a kind of high mobility and preparation method thereof
    US20180247726A1|2018-08-30|Sputtered transparent conductive aluminum doped zinc oxide films
    CN105390178B|2017-11-03|A kind of zinc-oxide-base transparent conducting film and preparation method and application
    Kim et al.2014|Transparent conductive ZnInSnO–Ag–ZnInSnO multilayer films for polymer dispersed liquid-crystal based smart windows
    KR20150135977A|2015-12-04|Transparent electode and electronic device comprising the same
    CN101834009B|2013-05-01|Low-indium doping amount zinc oxide transparent conducting film and preparation method thereof
    US20170306470A1|2017-10-26|Indium Tin Oxide Thin Films With Both Near-Infrared Transparency and Excellent Resistivity
    Heo et al.2014|Characteristics of ion beam assisted ITO thin films deposited by RF magnetron sputtering
    CN109346625A|2019-02-15|Display panel and preparation method thereof, display module
    WO2018029886A1|2018-02-15|Substrate with transparent conductive layer, liquid crystal panel and method for producing substrate with transparent conductive layer
    KR101719037B1|2017-03-22|Blind
    CN209417491U|2019-09-20|A kind of full-inorganic solid-state electrochromic device transparent conductive film structure
    CN102945694B|2015-05-20|ITO | base plate and preparation method of ITO base plate
    CN104078531B|2016-04-13|A kind of preparation method with the ZnO:Li transparent conductive film of wide range territory light transmission characteristic and crater matte direct growth
    TW201618951A|2016-06-01|Layer system for use in a touch screen panel, method for manufacturing a layer system for use in a touch screen panel, and touch screen panel
    TWI420542B|2013-12-21|A surface treatment method and structure of a transparent conductive film
    同族专利:
    公开号 | 公开日
    US20180173040A1|2018-06-21|
    WO2016025446A2|2016-02-18|
    CN106663717A|2017-05-10|
    WO2016025446A3|2016-08-04|
    US9927667B2|2018-03-27|
    US20160041418A1|2016-02-11|
    US10613397B2|2020-04-07|
    SE542703C2|2020-06-30|
    引用文献:
    公开号 | 申请日 | 公开日 | 申请人 | 专利标题
    EP0707320A1|1994-10-13|1996-04-17|AT&T Corp.|Transparent conductors comprising zinc-indium-oxide and methods for making films|
    US20050140283A1|2002-02-13|2005-06-30|Lau Silvanus S.|Multilayer structure to form an active matrix display having single crystalline drivers over a transmissive substrate|
    KR101220102B1|2004-12-06|2013-01-14|가부시키가이샤 한도오따이 에네루기 켄큐쇼|Display device|
    US8018563B2|2007-04-20|2011-09-13|Cambrios Technologies Corporation|Composite transparent conductors and methods of forming the same|
    KR20100096255A|2008-01-24|2010-09-01|가부시키가이샤 아루박|Process for producing liquid crystal display device|
    JP5352878B2|2008-03-31|2013-11-27|公立大学法人高知工科大学|Display substrate, method for manufacturing the same, and display device|
    US20120037502A1|2009-05-01|2012-02-16|Ulvac, Inc.|Sintered Body for ZnO-Ga2O3-Based Sputtering Target and Method of Producing the Same|
    MX2012002156A|2009-08-24|2012-04-02|First Solar Inc|Doped transparent conductive oxide.|
    CN101845614B|2010-05-07|2011-09-21|中国科学院宁波材料技术与工程研究所|Method for preparing zinc oxide-based sputtering target material|
    CN102586736B|2012-02-23|2013-10-16|西北稀有金属材料研究院|Doped ZnO-based sputtering target material and preparation method thereof|
    EP2904128A1|2012-10-08|2015-08-12|Corning Incorporated|Sputtered transparent conductive aluminum doped zinc oxide films|
    CN103014675B|2012-11-26|2015-03-25|中山市创科科研技术服务有限公司|Device for forming AZO film on substrate|
    CN103866264B|2012-12-10|2017-05-10|中国科学院微电子研究所|Phosphorus-doped zinc oxide film preparation method|
    KR20150092777A|2014-02-05|2015-08-17|삼성디스플레이 주식회사|Display device and method of manufacturing a display device|US8563573B2|2007-11-02|2013-10-22|Vertex Pharmaceuticals Incorporated|Azaindole derivatives as CFTR modulators|
    CN106353917B|2016-11-28|2019-02-19|深圳市华星光电技术有限公司|Liquid crystal display device|
    法律状态:
    优先权:
    申请号 | 申请日 | 专利标题
    US201462035790P| true| 2014-08-11|2014-08-11|
    US201562153818P| true| 2015-04-28|2015-04-28|
    US14/822,514|US9927667B2|2014-08-11|2015-08-10|Display having a transparent conductive oxide layer comprising metal doped zinc oxide applied by sputtering|