Methods to recover cesium or rubidium from secondary ore

专利摘要:
A method to recover cesium, rubidium, or both from secondary ore is described and involves using scans and sorting techniques. Refined secondary ore is further described.
公开号:SE1551126A1
申请号:SE1551126
申请日:2014-02-28
公开日:2015-09-01
发明作者:Bart F Bakke；Claude Deveau
申请人:Cabot Corp；
IPC主号:

专利说明:

[1] [0001]This application claims the benefit under 35 U.S.C. §119(e) of prior U.S. Provisional Patent Application No. 61/772,946, filed March 5, 2013, which is incorporated in its entirety by reference herein.
[2] [0002]The present invention relates to cesium or rubidium or both and the recovery of these elements from secondary ore. The present invention further relates to a purified ore that contains cesium and a unique combination of others minerals and/or elements.
[3] [0003]Cesium salts, such as cesium formate, are increasingly being discovered as useful components or additives for a variety of industrial applications, such as in the hydrocarbon recovery areas. However, deposits of "primary- ore, that is, ore that contains high amounts of cesium with insignificant amounts of undesirable impurities, are rare, and operators have long sought techniques to enhance recovery of cesium and/or rubidium from known deposits of secondary ore containing cesium and/or rubidium.
[4] [0004]However, cesium-containing secondary ore, while available, presents major problems with regard to recovering the cesium from such ore. For instance, the expense of recovering significant amounts of cesium from low yield ore can be quite time consuming and expensive based on known methods. Also, with known techniques, it is very difficult and expensive to separate cesium from certain undesirable metals or minerals that can typically be found with deposits of cesium-containing secondary ore. For instance, many cesium-containing secondary ore deposits have significant lithium containing minerals, such as, but not limited to, phosphate minerals, such as Amblygonite, Montebrasite, and/or cesium-substituted Lithiophosphates. If the phosphate minerals which contain significant amounts of lithium, and frequently sodium, are not significantly separated from the secondary ore, the lithium can then present serious impediments WO 2014/13778PCT/US2014/01929 to the commercial use of the cesium-containing fraction of the secondary ore in a variety of industries, such as in the hydrocarbon recovery area with regard to fluids, such as drilling fluids, completion fluids, packer fluids, and the like.
[5] [0005]In more detail, one beneficial use of cesium is as cesium formate in solution to create high density well fluids which are extremely useful in deep drilling oil and gas wells. If the lithium is present at excessive levels in the fluids, the fluid cannot be manufactured with a sufficient amount of cesium in solution to achieve the high fluid density required for well drilling fluids. If the lithium levels exceed critical parameters, the cesium-containing salt will precipitate out of solution before reaching the needed density to work as a suitable well fluid, which will make the fluid unsuitable for hydrocarbon recovery.
[6] [0006]In using primary ore sources, the presence of lithium is not a significant problem because the cesium-containing primary ore deposits, namely, pollucite, can be recovered without any significant levels of lithium-containing phosphate minerals being present. Thus, this problem is unique to cesium-containing secondary ores. In addition, if the lithium is not substantially removed from the secondary ore before chemical processing to recover cesium, the lithium, as well as any sodium, can be excessively challenging to remove from the cesium during traditional downstream wet chemical processing of the ore (e.g., beginning with acid digestion). Adding to this challenge is the variable presence of the levels of these lighter alkalis, as introduced with the ore prior to wet chemical processing.
[7] [0007]These same problems also can exist with rubidium containing ore or ore containing cesium and rubidium.
[8] [0008]Accordingly, there is a need in the industry to develop methods for recovering the highly sought and valued minerals bearing cesium, rubidium, or both, from secondary ore, also referred to as cesium-containing secondary ore. There is a further need to create methods that will significantly reduce the content of minerals bearing lithium, and the other lighter alkali, WO 2014/13778PCT/US2014/01929 impurities and other mineral and/or metal impurities in the recovered cesium, rubidium, or both, so as to avoid the significant challenges of wet chemical processing, as well, the viability of brine products, as per those problems described above.
[9] [0009]A feature of the present invention is to provide a method to effectively recover cesium, rubidium, or both, from secondary ore.
[10] [0010]A further feature of the present invention is to provide methods to utilize the cesium, rubidium, or both, recovered from secondary ore in the production of cesium-containing fluids, such as cesium formate and the like.
[11] [0011]An additional feature of the present invention is to provide a method to recover cesium, rubidium, or both, from secondary ore and yet control the amount of lithium and/or metals or minerals that would be otherwise present in the recovered ore.
[12] [0012]A further feature of the present invention is to provide a crushed cesium-containing purified ore that contains high amounts of cesium and controlled amounts of lithium or lithium ions and having desirable cesium oxide-to-phosphorus oxide weight ratios.
[13] [0013]Additional features and advantages of the present invention will be set forth in part in the description that follows, and in part will be apparent from the description, or may be learned by practice of the present invention. The features and other advantages of the present invention will be realized and attained by means of the elements and combinations particularly pointed out in the description and appended claims.
[14] [0014]To achieve these and other advantages, and in accordance with the purposes of the present invention, as embodied and broadly described herein, the present invention relates to a method to recover cesium, rubidium, or both from secondary ore. The secondary ore can contain 25 wt% Cs20 or less based on overall weight of the secondary ore (such as 15 wt% or less or WO 2014/13778PCT/US2014/01929 wt% or less) and the majority of the secondary ore can include pieces having at least one dimension that is over 5 inches. The method can include crushing the secondary ore to obtain crushed ore comprising individual pieces. Each individual piece has a size capable of passing through a mesh/screen or bar/screen of 3 inches. Or, one can start with the crushed ore from a source or supplier. The method includes passing the crushed ore through a first sorter to conduct a first sorting at a feed rate of at least 1 ton/hour, wherein the first sorter determines whether each individual piece of crushed ore is a "Grade 1 piece" or "Grade 2 piece," based on the first sorter conducting at least one scan of each individual piece and determining or calculating atomic number and/or material density of each individual piece, wherein said "Grade 1 piece" is determined or calculated to comprise Cs20 in an amount of at least 20 wt% based on the weight of said individual piece. The method involves separating the Grade 1 pieces from the Grade 2 pieces, wherein % Cs20 of the total amount of Grade 1 pieces is at least 10% by weight higher than the total wt% Cs20 in the secondary ore. The method can optionally include extracting cesium, rubidium or both by subjecting the Grade 1 pieces to at least one acid treatment and/or other chemical treatment. It is recognized that the pollucite mineral, in nature, can have differing Cs20 wt% content due to the varying degree of lighter alkali molar substitution for Cs20. Pollucite comprising 44 wt% Cs20 would be about the maximum found in this mineral. For purposes of the present invention, a level of about 32 wt % Cs20 can be considered to represent "pure" pollucite mineral, and generally the pollucite mineral can contain no more than 32 wt% to 44 wt% Cs20.
[15] [0015]The present invention further relates to a crushed cesium-containing purified ore. For instance, the crushed cesium-containing purified ore can have the following: optionally, a pollucite and/or nanpingite and/or carnallite content in an amount of from 10 wt% to 90 wt%; a Cs20 content of from 5 wt% to about 32 wt%; WO 2014/13778PCT/US2014/01929 total phosphate mineral content of from 1 wt% to 10 wt%; a %P205 content of about less than 1.5% wt%; a %Cs20: %P205 weight ratio of at least 4:1; a Li20 content of from 0.5 wt% to 2 wt%; and an average crushed ore size or thickness of from 0.1 inch to 5 inches such as 0.5 to 2.5 inches, wherein all wt% are based on weight of purified ore. For this purified ore, a) the pollucite content is optional and further, instead of pollucite, any cesium bearing mineral(s) can be substituted in part or entirely, such as nanpingite and/or carnallite.
[16] [0016]The crushed cesium containing purified ore can additionally have one or more of the following: a SQUI content in an amount of from 0.5 wt% to 5 wt%; a quartz content in an amount of from 0.5 wt% to 5 wt%; a total Feldspar content of from 1 wt% to 10 wt%; an Albite content of from 0 wt% to 1 wt%; an Amphibolite content of from 0.1 wt% to 0.5 wt%; an Apatite content of from 0.5 wt% to 4 wt%; a Lepidolite content of from 2 wt% to 8 wt%; and/or an Amblygonite content of from 0 wt% to 1 wt%.
[17] [0017]It is to be understood that both the foregoing general description and the following detailed description are exemplary and explanatory only and are intended to provide a further explanation of the present invention, as claimed.
[18] [0018]The accompanying drawings, which are incorporated in and constitute a part of this application, illustrate some of the features of the present invention and together with the description, serve to explain the principles of the present invention. The descriptions are not intended to limit the scope or the spirit of the invention.
[19] [0019]Fig. 1 is a flow diagram showing one process of the present invention for recovering cesium, rubidium, or both, from secondary ore.
[20] [0020]Fig. 2 is a diagram showing the general set-up of the sorter that can be used in the methods of the present invention.
[21] [0021]Fig. 3 is a diagram showing a representation of a scan using a high channel and low channel signal scan with signal to image processing to create an image of the rocks to activate or achieve a mechanical separation of rock grades.
[22] [0022]Fig. 4 is a graph shows the effects of lithium with regard to the solubility of cesium in an aqueous fluid.
[23] [0023]According to the present invention, a method to recover cesium, rubidium, or both, from secondary ore (also known as cesium-containing secondary ore) is described. The present invention further relates to the recovered highly purified cesium-containing ore (also known as crushed cesium-containing purified ore). The present invention further relates to fluids or other material that contains the recovered cesium in the form of elemental cesium or a cesium compound (e.g., salt). Instead of cesium, the recovery and use of rubidium or a mixture of cesium and rubidium can be achieved. Further, the processes of the present invention can also be used to recover potassium from secondary ore. Also, to be clear, while less useful, the processes of the present invention can be used with primary ore alone, secondary ore alone, or a combination of primary and secondary ores. FIG. 1 provides a flow chart of steps that can be used. In all instances, the crushed cesium-containing purified ore contains an insufficient quantity of lithium-containing phosphate minerals to interfere with industrial uses of cesium, WO 2014/13778PCT/US2014/01929 rubidium, cesium compound, or rubidium compound obtained by further refinement of the crushed cesium-containing purified ore.
[24] [0024]In more detail, in the present invention, methods to recover cesium, rubidium, or both from secondary ore are provided. The secondary ore can comprise 25 wt% Cs20 or less based on overall weight of the secondary ore. The majority (by weight) of the secondary ore can comprise, consists essentially of, or consist of pieces having at least one dimension that is over 5 inches. Thus, over 50 wt% of the secondary ore has at least one dimension or two dimensions or all dimensions over 5 inches, such as over 60 wt%, over 70 wt%, over 80 wt%, over 90 wt%, over 95 wt%, over 99 wt% or about 100 wt%, based on the total weight of the starting secondary ore. Put another way, prior to crushing, a majority of the ore (by wt%) does not fall through a 5 inch U.S. mesh/screen.
[25] [0025]The secondary ore (overall) can be or include 20 wt% Cs20 or less, 15 wt% Cs or less, 10 wt% Cs20 or less, from 1 wt% to 15 wt% Cs20, from 1 wt% to 10 wt% Cs20, from 0.25 wt% to 5 wt% Cs20, less than 1 wt% Cs20, about 0.1 wt% Cs20 or more, from 0.1 wt% to 20 wt% Cs20, from 0.1 wt% to 18 wt% Cs20, from 0.1 wt% to 15 wt% Cs20, from 0.1 wt% to 10 wt% Cs20, from 0.1 wt% to 5 wt% Cs20, from 1 wt% to 20 wt% Cs20, from 1 wt% to 18 wt% Cs20, from 1 wt% to 15 wt% Cs20, or other low amounts of cesium containing ore, or other amounts within or outside of any one of these ranges based on the total wt% of the starting secondary ore.
[26] [0026]The secondary ore can include, comprise, consist essentially of, or consist of pollucite, nanpingite, carnallite, rhodozite, pezzottaite, rubicline, borate ramanite, beryls, voloshonite, cesstibtantite, avogadrite, margaritasite, kupletskite, nalivkinite, petalite, spodumene, lepidolite, biotite, mica, muscovite, feldspar, microcline, Li-muscovite, lithiophilite, amblygonite, illite, cookeite, albite, analcime, squi, amphiboles, lithian mica, amphibolite, lithiophospahe, apatite and/or londonite, or any combinations thereof The WO 2014/13778PCT/US2014/01929 secondary ore can comprise, consist essentially of, or consist of pollucite, an aluminosilicate mineral having the general formula (Cs>Na)[A1Si206]-120. The secondary ore can have at least 1 wt% pollucite based on the weight of the secondary ore, or from 1 to 5 wt% pollucite based on the weight of the secondary ore, or at least 3 wt% pollucite based on the weight of the secondary ore. Other amounts are from 1 wt% to 20 wt% or from 1 wt% to 15 wt%, or from 1 wt% to 10 wt%, or from 1 wt% to 5 wt% pollucite based on the weight of the secondary ore.
[27] [0027]In FIG. 1, a flow chart is provided to provide steps that can be used in the methods of the present invention. It is noted that this is simply exemplary of the present invention and is not intended to limit the steps or sequence of steps or which steps can be used or which steps can be optional. In FIG. 1, the ore can be crushed or crushed ore can be received (10) and then the crushed ore can be divided into various size fractions (12). At some point in time, the sorter that is used can be calibrated or trained with training sets of size fractions (14) based on the size fractions obtained in (12). It is noted that step (14) can be practiced at any point prior to running size fractions through the sorter and for instance, can be done minutes before passing size fractions through the sorter or hours or days or months beforehand. Then, the size fractions from the crushed ore are passed through the sorter that is calibrated and separated into Grade 1 or Grade 2 pieces (16). The Grade 1 pieces (18) are the pieces that contain high amounts of cesium oxide or have the potential to contain cesium oxide. The Grade 1 pieces (18) can then optionally be further crushed and/or calcined (22). The Grade 1 pieces can be optionally merged with the Grade 2A pieces (26). The Grade 1 pieces (18) can optionally be subjected to acid treatment with or without the Grade 2A pieces (34). The acid treatment (34) permits the separation of the cesium-containing product from the other materials (38). Conventional separation techniques known in the art can be used. Then, the recovered cesium can optionally be converted to cesium formate (42). The cesium WO 2014/13778PCT/US2014/01929 formate can then be made into a brine that contains cesium formate for a variety of uses (44). As a further option, after acid treatment (34) of the Grade 1 pieces, the recovered cesium product, such as Cs20 (36) can then be used to form one or more types of various cesium salts, such as cesium hydroxide, cesium sulphate, and the like (40). The Grade 2 pieces that are separated in step (16) can be recovered as Grade 2 pieces (20). These Grade 2 pieces can be optionally passed through a second sorter, which can be the same as the first sorter (24). This step separates the Grade 2 pieces into Grade 2A and Grade 2B pieces. The Grade 2A pieces (26) can optionally be merged with the Grade 1 pieces as described above, or the Grade 2A pieces can be calcined or further crushed (32) and then optionally subjected to acid treatment (34) for further processing. The Grade 2B pieces (28) can be considered tailings or can be recycled and passed through the sorter again for further recovery of desirable products (30).
[28] [0028]The method can comprise, consists essentially of, or consist of crushing the secondary ore to obtain crushed ore that is or includes individual pieces. Or in the alternative, crushed secondary ore can be obtained. Each individual piece can have a size capable of passing through a U.S. mesh/screen or bar/screen of 3 inches (e.g., or a U.S. mesh size of 2.5 inches, or 2 inches, or 1 inch, or smaller mesh size). The method further includes passing the crushed ore through a first sorter to conduct a first sorting at a feed rate of at least 1 ton/hour. The first sorter determines whether each individual piece of crushed ore is a "Grade 1 piece" or "Grade 2 piece", based on the first sorter conducting at least one scan of each individual piece and determining or calculating atomic number and/or material density of each individual piece. For purposes of the present invention, "the estimated atomic number" or "determining or calculating atomic number" can be atomic number or effective atomic number, also known as Zeff, which is the atomic number of a compound or material. For "material density", this can be considered "mass density". To avoid any doubt, when WO 2014/13778PCT/US2014/01929 "atomic number" or "estimated atomic number" is used throughout, this can be or include "effective atomic number" for instance using Mayneord's method. The "Grade 1 piece" is determined or calculated (based on the scan) to have Cs20 in an amount of at least 5 wt% (e.g., at least 5 wt%, at least 10 wt%, at least 15 wt%, at least 30 wt% from 5 wt% to 32 wt% or more) based on the weight of the individual piece. The method further includes separating the Grade 1 pieces from the Grade 2 pieces, wherein total wt% Cs20 of the total (combined) Grade 1 pieces is at least 10% by weight higher (e.g., at least 20 wt% higher, at least 30 wt% higher, at least 40 wt% higher, at least 50 wt% higher, at least 75 wt% higher, at least 100 wt% higher, at least 250 wt% higher, at least 400 wt% higher, at least 600 wt% higher, at least 800 wt% higher, at least 1000 wt% higher) than the total wt% Cs20 in the secondary ore before sorting.
[29] [0029]As another option, the Grade 1 pieces can be determined or calculated e.g., based on a scan, to comprise Cs20 in an amount and concentration, each by weight, of at least twice that present in the starting ore or secondary ore, and/or in an amount and concentration, each by weight, of at least twice that present in the Grade 2 pieces that are recovered (or separated from the Grade 1 pieces).
[30] [0030]With regard to the secondary ore as the starting material, the secondary ore can have at least one dimension, or at least two dimensions, or three dimensions that are over 5 inches in size. For instance, the starting secondary ore, prior to being crushed, can be 5.1 inches in at least one dimension, such as from 5.1 inches to 100 inches or more, such as from 10 inches to 75 inches, from 6 inches to 50 inches, and the like. Essentially, the secondary ore can be any size over 5 inches since it will be subjected to crushing to reduce the size as indicated herein prior to sorting.
[31] [0031]With regard to the crusher, any crusher can be used that can reduce large rocks into smaller rocks or individual pieces that can be scanned as described herein. Examples of WO 2014/13778PCT/US2014/01929 crushers that can be used include, but are not limited to, a jaw crusher, a gyratory crusher, a cone crusher, an impact crusher, such as a horizontal shaft impactor, hammer mill, or vertical shaft impactor. Other examples of crushers that can be used include compound crushers and mineral sizers. As an option, a rock breaker can be used before crushing to reduce oversized material too large for a crusher. Also, more than one crusher can be used and/or more than one type of crusher can be used in order to obtain desirable sizes and processing speeds.
[32] [0032]In the crushing step, prior to the first sort, the secondary ore can be crushed to obtain crushed ore that is or includes individual pieces, where each individual piece has a size capable of passing through a mesh/screen of 3 inches, or passing through a mesh/screen of 1 inch, or passing through a mesh/screen of 0.5 inch, or passing through a mesh/screen of 0.25 inch, or passing through a mesh/screen of 0.1 inch (all U.S. mesh sizes).
[33] [0033]The feed rate to the first sorter (and/or through the first sorter) can be at least 1 ton/hour or at least 2 ton/hour, at least 5 ton/hour, at least 8 ton/hour, at least 10 ton/hour, at least 15 ton/hour, at least 20 ton/hour, at least 25 ton/hour, at least 30 ton/hour, from 1 ton/hour to 35 ton/hour, from 5 ton/hour to 35 ton/hour, and the like.
[34] [0034]With regard to feeding the crushed ore to the first sorter, any means to convey this material can be used, such as a belt, chute, vibrating table, or other conveying devices used to move rocks or gravel to a location on a production line or mining operation.
[35] [0035]For purposes of the present invention, 'determining' atomic number and/or density can include 'calculating' or even estimating atomic number and/or density. With regard to the first sorter, the sorter is capable of performing at least one scan and, preferably, at least two scans of each individual piece and thereby calculating or determining an atomic number and/or material density of each individual piece or portions thereof. This calculating or determining based on one or more scans can be considered an estimate of atomic number and/or material density. The calculating or determining of the atomic density can be WO 2014/13778PCT/US2014/01929 considered an estimated atomic density. The calculating or determining of the material density can be considered an estimated material density. If more than one scan, the scans can be done simultaneously, almost simultaneously, or sequentially. The sorter can, by the scan, determine the estimated atomic number and/or material density of each individual piece or portions thereof, and this scan information, such as by X-ray scanning, can be used to determine which piece should be accepted or ejected. The scan information can be converted to optical images or pictures of each individual piece (or a portion(s) thereof) for subsequent use in the scanning operations. The optical images, as further explained elsewhere, can be color coded a) based on estimated atomic number and/or material density of the overall individual piece; b) based on the overall average estimated atomic number and/or average material density of the individual piece (where the average can be determined based on volume of each atomic number region and/or material density region measured), or c) based on where pixels or regions of an image of the individual pieces can be assigned different colors per estimated atomic number and/or material density of that pixel or region. Thus, an individual piece can have different zones that reflect different atomic numbers and/or material densities due to different minerals/elements present in the same individual piece. Based on the scan and the estimated atomic number and/or material density, different colors can be used to denote acceptable material or unacceptable material. Put another way, color codes can be associated with each individual piece or portions of each individual piece to signify individual pieces that contain Cs20 in sufficient amounts or pieces that do not contain sufficient amounts of Cs20, or contain an excessive amount of unacceptable material such as phosphates or lithium oxide.
[36] [0036]The sorter can be a dual energy X-ray transmission (DEXRT) sorter. For instance, a Commodas Ultrasort sorter can be used for the sorting. To obtain a more accurate sort as described herein, the sorter can be optionally "trained" or calibrated to understand WO 2014/13778PCT/US2014/01929 which types of minerals or rocks or fractions thereof would be considered as having the desired Cs20 amount and, thus, be a Grade 1 piece. Similarly, rock types can be used to train the sorter on which types of rock types or portions thereof would not be desirable and, therefore, would not contain high amounts of Cs20 and, therefore, be considered a "Grade 2 piece." When the sorter is being trained, generally, representative rocks or fractions thereof that are found in the location of the mining where the secondary ore is mined or otherwise recovered are used for training. Thus, in this optional "training" session, one would go to the mining location and collect representative rocks that reflect accurately the types of rocks or fractions thereof that are found. These rocks or fractions thereof are then identified by the user with respect to what type of rock that they are and/or whether the rock is a cesium containing rock which generally contains the mineral pollucite (and/or nanpingite and/or carnallite). The training session calibrates the sorter to better distinguish "Grade 1 pieces" from other rocks. The training can greatly increase the accuracy of identifying Grade 1 and Grade 2 pieces. When rocks of known composition are passed through the sorter for training or calibration, the scan can be studied to identify scan properties suitable for selection of Grade 1 pieces or pollucite containing pieces. While one option in the present application is to set the sorter to screen for a desired atomic number and/or material density, another option is to simply set the sorter's scan parameters to match the readings obtained from each training set. Put another way, if through the training sets, the sorter obtains a reading "X" for estimated atomic number and/or "Y" for a material density for a representative Grade 1 piece for a particular size fraction, then when the training is done, the sorter can be programmed to identify pieces that have this "X" atomic number and/or "Y" density number, or have an atomic number and/or material density that is within 5%, within 10%, within 15%, within 20%, or within 25% or some other designated percentage within the "X" and/or "Y" readings WO 2014/13778PCT/US2014/01929 from each size fraction in each training set. This would be done for each size fraction used in the training set.
[37] [0037]In training the sorter, various training sets can be used. For example, various identified or known minerals can be used, such as three to eight (or more) different mineral types, can be used to train. Each training set can comprise the same mineral types but have a different size fraction. The purpose of using different size fractions is to accurately calibrate the sorter to handle various sizes of rocks, or fractions thereof, when detection and sorting are based in part on overall averages determined for a volume of regions measured. For instance, one or more of the following five size fractions (U.S. Standard Sieve Size) can be used to calibrate or train the sorter: 2 inches + 1.5 inches 1.5 inches + 1 inch 1 inch + 0.5 inch 0.5 inch + 0.25 inch 0.25 inch + 0.125 inch.
[38] [0038]The rock types that can be included in each training set can be: Pollucite, Lepidolite, one or more pieces of Feldspar, Quartz, SQUI, Amblygonite, and/or Albite and/or one or more other mineral/rock types. Out of these rock types, the Grade 1 pieces are the pollucite mineral and the rest of the materials are, for the most part, Grade 2 pieces. Again, the rock types that are used during the training session are representative or are actual rocks obtained from the mining location so as to accurately reflect the rocks or fractions thereof that will be passed through the sorter during production of sorted ore. The training sets can contain Grade 1 pieces and/or Grade 2 pieces. The training set may contain desirable pieces (e.g., cesium containing pieces) and undesirable pieces (e.g., non-cesium containing pieces or where the cesium amount is very low).
[39] [0039]The following are further explanations of the type of rock types and one example of a training set used for purposes of "training" the sorter as described herein. The training set can comprise the following eight mineral types in different rock size fractions and/or grain sizes.
[40] [0040]Below is a further description of some of the minerals that can be found in secondary ore. One or more of these can be used in the "training" sets as described herein.
[41] [0041]Using the above size fractions, the crushed ore comprising individual pieces, for example, are separated into five (5) size fractions, namely, (a) -2 inches + 1.5 inches; (b) -1.5 inches + 1 inch; (c) -1 inch + 0.5 inch; (d) -0.5 inch + 0.25 inch; and (3) -0.25 inch + 0.125 inch. For purposes of the present invention, other size fractions of various size spreads also can be used to calibrate or train the sorter. Once the training is done for the sorter using various size fractions, it is to be understood that no further training is needed and the sorter is now calibrated. The sorter simply needs to be set to the desired size fraction that will then be passed through the sorter(s).
[42] [0042]When using the calibration or training sets or running the actual secondary ore through the sorter, the rocks or fractions thereof should only have a one layer thickness. In other words, the rocks or fractions thereof should not be on top of each other and this is so that a scan of each individual rock can occur and so that the scan can identify which rock is a Grade 1 piece or a Grade 2 piece.
[43] [0043]As an option, size fractions of the crushed ore that arc below 0.125 inch or less than 3 mm are not sorted through the sorter. In addition, as an option, size fractions above 3 inches, or above 2.5 inches, or above 2 inches are not passed through the sorter. The sizes above 3 inches or 2 inches can optionally be passed through the crushing step again to further reduce the size, such as below 2.5 inches or to below 2 inches.
[44] [0044]As an option, multiple size fractions can be used to train the sorter or calibrate the sorter and then be used to separate the crushed ore into these respective size fractions for passing through the sorter. The following formulas can be used to determine the various size fractions: Si = Sx to 50% S.
[45] [0045]As an option, the size fraction below 0.125 inch or below 3 mm can optionally not be passed through the sorter, and this small size fraction of crushed ore can simply be mixed with the "Grade 1 pieces" as an option. Through various experiments, it was determined that this small size fraction does not negatively affect quality of the "Grade 1 pieces" that are obtained and does not affect the desirable Cs20 amount. This was considered quite unexpected and surprising and permits a beneficial use for this very small size fraction.
[46] [0046]Using the training sets, the sorter can be better programmed (for instance by using the images of the training sets to know what is Grade 1 pieces and what are Grade 2 pieces) so as to better separate the Grade 1 pieces from the Grade 2 pieces. The sorter can be programmed using (at least in part) the images of the training sets to separate rubidium-bearing rocks, non-cesium containing rocks, low grade cesium-bearing rocks, and amphiboles from the Pollucite-containing Grade 1 pieces.
[47] [0047]The scan performed in the methods of the present invention can be a computer tomography type such as a dual energy computer tomography scan. The dual energy scan and the method involved can involve reconstructing the distribution function of the linear attenuation coefficient (LAC) within a chosen section, which can be planar (surface area) or volumetric. With the high energy scanner, LAC projections can be acquired, for instance, by measuring the current density of the transmitted energy ray for consecutive positions along a direction perpendicular to the incident radiation. The LAC distribution can be reconstructed from the scanned areas (the individual pieces) by means of a filtered back projection method, WO 2014/13778PCT/US2014/01929 iterative least square technique or algebraic reconstruction (see for instance, Kak et al (1999) Principles of Computerized Tomographic Imaging, IEEE Press, New York; Natterer (1986) The Mathematics of Computerized Tomography, J. Wiley & Sons, New York; Brooks et al (1976) Principles of computed assisted tomography CAT in radiography and radioisotopic imaging. Physics in Medicine and Biology 21, 689-752; and Censor et al (2001) Component averaging: an efficient iterative parallel algorithm for large and sparse unstructured problems, Parallel Computing 27, 777-808, all incorporated in their entirety by reference herein). The energy ray can be X-ray or a gamma-ray. For the dual energy scans, the lower energy scan (or low channel) should be at least 10 kV (or 10 keV) different from the higher energy scan (or high channel). Preferably, the lower energy scan is below 100 kV and the higher energy scan is above 100 kV. For instance, the lower energy scan can be 40 to 90 kV and the higher energy scan can be 120 to 200 kV. The image acquisition and processing can be automated with programming and software, such as, but not limited to, Accent Pro 2000 software such as Tomo software including the Data Acquisition Program and Tomogram Reconstruction Program; or Avizo Analysis Software for image acquisition and processing, all commercially available.
[48] [0048]For purposes of the present invention, the scans can determine the LAC of the individual pieces and this can represent the product between density p and the mass attenuation coefficient (MAC). The formula that can be used is described in Rizescu et al. (2001) Determination of local density (or material density) and effective atomic number by the dual-energy computerized tomography method with the 1921r radioisotope, Nuclear Instruments and Methods in Physics Research A. 465, 584-599, incorporated in its entirety by reference herein. With this determination, the photoelectric effect and Compton's inelastic scattering can be taken into account. With the dual energy scan in the present invention, a WO 2014/13778PCT/US2014/01929 determination of both material density and effective atomic numbers distribution functions through the individual pieces can be made.
[49] [0049]With X-rays, the transmitted radiations can be detected by means of sets of two different detectors separated by a metal shield, such as a thin (1 to 2 mm) copper shield. The metallic foil can act as a filter for the low energy X-rays, which modifies the spectral composition of the radiation detected by each set of detectors. This dual energy detection in in optional combination with the training sets (calibration sets) having known densities and atomic numbers, and by using suitable reconstruction algorithms, two different CAT or digital images of the individual pieces can be computed where one image can represent the material density and the other image can depict the Zeff distribution over the investigated pieces. As an option, the two different digital images, where one represents material density and the other depicts estimated atomic number or a Zeff distribution, can be merged or overlapped into a single image to reflect both computations. This combination of the two images, one for material density and one for atomic number, can be useful in determining or deciding whether an individual piece of crushed ore is a "Grade 1 piece" or "Grade 2 piece." This merging or combination of two images into one image can also be referred as an "effective atomic density." For purposes of sorting, and as an option, this "effective atomic density" can be used to determine if an individual piece of crushed ore is a "Grade 1 piece" or "Grade 2 piece" based on the percent of the individual piece that satisfies both the desired atomic number and desired material density that is used, for instance, based on the training or calibration sets for that particular size fraction.
[50] [0050]Various types of devices can be used to pass the individual pieces through the scanners, namely, the pieces can be directed to and pass through the scanner using a free-fall method without any rotating components or a belt can be used to achieve feeding of the individual pieces through the scanner. The sorter can have a feeder to form a monolayer of WO 2014/13778PCT/US2014/01929 individual pieces that pass the scanner, and this can be achieved with a vibratory feeder. A feed belt can then be used to feed the individual pieces between the X-ray source and the sensor. As stated, instead of a feed belt, a chute can be used without a belt. As the individual pieces pass between the source and sensor, preferably a dual energy X-ray, an image(s) of each rock (individual piece) is acquired and analyzed by an image processor.
[51] [0051]Then, a separation chamber can be used. The separation chamber is where the individual pieces proceed after being scanned and, based on the scan and image analysis, the individual pieces follow a separation plate onto a conveyor or bin. In the separation chamber, the Grade 1 pieces are separated from the Grade 2 pieces, and this can be done by using air jets to blast out the piece from the normal trajectory. The separation chamber can be set up either to blast out the Grade 1 pieces, which would then be considered ejected pieces, and the Grade 2 pieces can maintain their normal or natural trajectory and, therefore, be considered "accepted." The opposite can be set up as well, wherein the Grade 2 pieces are blasted out as ejected, and the Grade 1 pieces are left as accepted. Either setup is possible, depending upon user preferences.
[52] [0052]A broad-band electrical X-ray source(s) can be applied to the individual pieces to be sorted. The X-ray sensor system for instance, produces a digital image of the material being sorted, preferably using two different energy bands. The X-ray attenuation through the material is different in the two bands and depends on both the material's thickness and material density. An image transformation of the density images of the two bands can be done so as to classify each pixel according to atomic number and/or material density. In lieu of each pixel, a group of pixels or other region/zone can be classified collectively. A classification of the ore pieces (also known as individual pieces for this invention) is then made with regard to Cs20 content. As stated in more detail herein, the first sorter can be set such that the Grade 1 piece is determined based on having an estimated atomic number, for WO 2014/13778PCT/US2014/01929 instance, of at least 50 for a certain percentage volume of the individual piece (e.g., over 20%, over 30%, over 40%, over 50%, over 60%, over 70%). In other words, if the individual piece scanned is determined to contain a certain percentage of volume or surface area with an estimated atomic number of at least 50, this would be considered a Grade 1 piece that will be separated from the Grade 2 pieces. As an alternative or in addition, the individual piece can have the material density of the individual piece or portion thereof determined or calculated. For instance, if the scan determines that the individual piece or a significant volume of the individual piece, such as over 20% or over 30% or over 40% or over 50% or over 60% by volume, has a material density of at least 2.7 g/cm3 or at least 2.75 or at least 2.8 or at least 2.85 or at least 2.9, or has a density from 2.7 to 3.2 or a density from 2.7 to 3.2 or a density of 2.8 to 3.1 or a density of 2.7 to 3 or 2.8 to 3.1, the individual piece can be separated and considered a Grade 1 piece. Ideally, with two scans, the estimated atomic number and the material density can be both considered as criteria for determining if the piece is a Grade 1 piece or not. In other words, as an option, in order for a Grade 1 piece to be separated from Grade 2 pieces, the Grade 1 piece must have the desired estimated atomic number and the desired material density as described above and herein. Or, as an option, an individual piece can be considered a Grade 1 piece if one of two criteria are satisfied; meaning, the individual piece has either the desired estimated atomic number or the desired material density or both. Needless to say, if both criteria are required, the accuracy of recovering Grade 1 pieces increases significantly. Density (or material density) can be considered in units of g/cm3.
[53] [0053]The sensor's high spatial resolution can be 0.8 mm or 1 6 mm or other resolutions above or below these numbers or in between. The resolution permits the evaluation of particle shape, particle size, material thickness and texture of a grey-scale image (inclusions of various densities). The X-ray transmission image processing provides a highly efficient sensor system for classifying materials. The sorter can work with an electric X-ray source WO 2014/13778PCT/US2014/01929 featuring a maximum acceleration voltage of 160 KV and other acceleration voltages can be used.
[54] [0054]Fig. 3 provides one example of where the sorter does an X-ray scan (as shown in Fig. 2) using two different energies, and as shown in Fig. 3, a low channel image (50) can be created and a high channel image (55) can be created and then these two images can be subjected to image processing (58) to determine atomic number and material density per pixel or pixels or other desired volume or surface area. Further, the image processing can create images (66) of each piece and assign particular colors to particular ranges of atomic numbers and densities detected or determined or calculated and, as an option, the sorter can determine ejects and accepts based on the assigned atomic number and/or material density alone or it can determine ejects and accepts once the image is converted to a color image and color sorting can be used based on the digital image to sort, which is using an optical sorter method. For instance, a pixel or pixels or other volume having an effective atomic number above 50, for instance, from 50 to 80, can be assigned a black color. Different sub-ranges of effective atomic number within 50 to 80 can be assigned different colors, such as black (for one sub-range), blue (for a second sub-range), or green (for a third sub-range), depending upon where the effective atomic number lies with regard to this range of from 50 to 80. Effective atomic numbers that are below 50, for instance, can be assigned a color red or other color(s) and, therefore, the sorter, if one chooses, can be operated based on this color assignment as an optical sorting based on the image created, which reflects the estimated atomic number of the rock or portion thereof In addition or alternatively, the color designation can be used with material density using the same approach, and as described above, where a density of at least 2.7, or other ranges described earlier are used.
[55] [0055]The sorter, through the image processing, can further determine if the majority (by volume, for instance) of the individual piece primarily has an atomic number and/or material WO 2014/13778PCT/US2014/01929 density that would characterize it as a Grade 1 piece or a Grade 2 piece. For instance, if the individual piece contains at least 10% by volume, at least 20% by volume, at least 30% by volume or at least 40% by volume or at least 50% by volume (or surface area) of a desired atomic number (e.g. 50 to 80) and/or material density (e.g. 2.7 to 3.2 g/cm3), then the piece can be considered a Grade 1 piece. This determination can be adjusted based on user preferences.
[56] [0056]In the methods of the present invention, the first sorter can be set such that the Grade 1 piece is determined based on a determined or calculated atomic number of at least 50, or based on a determined or calculated atomic number of at least 52, or based on a determined or calculated atomic number of at least 53, or based on a determined or calculated atomic number of from 50 to 80 or from 50 to 70, or from 50 to 60, or from 51 to 60, or from 52 to 60, or from 53 to 60 for a certain percent volume of the individual piece, such as at least a 10% volume, at least a 20% volume, at least a 30% volume, or at least a 40% volume, or at least a 50% volume, or at least a 60% volume, or at least a 70% volume, or at least a 80% volume, or at least a 90% volume. The % volume can be determined based on the number of pixels having the desired atomic number. The % volume can be determined based on computed tomographic (CT) scans or slices. Or, the first order can be set such that the Grade 1 piece is determined based on a determined or calculated material density of at least 2.7, or based on a determined or calculated material density of at least 2.75, or based on a determined or calculated material density of at least 2.8, or based on a determined or calculated material density of at least 2.9, or based on a determined or calculated material density of from 2.7 to 3.2 or from 2.8 to 3.1 or 2.85 to 3.2 or 2.9 to 3 for a certain percent volume of the individual piece, such as at least a 10% volume, or at least a 20% volume, or at least a 30% volume, or at least a 40% volume, or at least a 50% volume, or at least a 60% volume, or at least a 70% volume, or at least an 80% volume, or at least a 90% volume. The WO 2014/13778PCT/US2014/01929 % volume can be determined based on the number of pixels having the desired atomic number. The % volume can be determined based on CT slices. As stated, in the methods of the present invention, the first sorter can be such that the Grade 1 piece is determined based on both the atomic number and material density as described herein using the various ranges described herein.
[57] [0057]As shown in Fig. 2, which is simply a schematic diagram of the operation in simplified format, the crushed ore enters a material feed 1 and this crushed ore then is fed to a vibratory pan 2, which spreads the particles into a monolayer, wherein the monolayer of crushed ore in the form of individual pieces can be fed by chute 3 or by a moving belt (not shown) and passes through a dual energy beam X-ray sensor 4 (or other energy scan). Cameras can be used or other sensors can be used including, but not limited to, X-ray transmission, X-ray fluorescence, X-ray fluorescence spectroscopy, conductivity, near infrared spectroscopy sensors, and the like. Upon passing through the scanners, a high speed image/signal processor 5 can process the scanned information to determine atomic number and/or material density of each individual piece and to then determine whether the piece is a Grade 1 piece or a Grade 2 piece. As stated, the determination of atomic number and/or material density can be done on a per pixel basis and then a determination can be made on whether a sufficient percent by volume of each individual piece has the desired atomic number and/or material density. As stated, this information can optionally be processed into the form of an image of the individual pieces and an array of high speed air jets can separate the individual pieces as Grade 1 pieces or Grade 2 pieces based on this processed information. The array of high speed air jet 6 can be used or other means to separate can be used. The separated process streams 7, namely the stream of Grade 1 pieces and the stream of Grade 2 pieces can then be fed to proper areas for further processing. For instance, the Grade 2 pieces can be designated as tailings and not be further used. Or, the Grade 2 pieces WO 2014/13778PCT/US2014/01929 can be re-introduced into the sorter again under the same sorting conditions or different sorting conditions. Or, the Grade 2 pieces can be processed through a different sorter. A remote user interface 8 can be in communication with the image/signal processor for purposes of controlling the overall sorter and for making any adjustments with regard to sort classifications and calibrations.
[58] [0058]A Grade 1 piece (for instance, from the first sort) can contain, based on the scan, at least about 4 wt%, at least about 6 wt%, at least about 8 wt%, at least 10 wt%, at least 15 wt%, at least 20 wt%, at least 25 wt%, at least 30 wt%, or from 4 wt% to 32 wt%, from 6 wt% to 30 wt%, from 8 wt% to 25 wt%, from 10 wt% to 20 wt%, from 15 wt% to 20 wt% Cs20 based on the weight of the individual piece.
[59] [0059]The method can optionally include calcining the Grade 1 pieces after separating, and generally before any optional acid treatment or other chemical treatment. The calcining can be at a calcining temperature of from about 800° C to about 1200° C, or other temperatures, for any amount of time, such as 10 minutes to 10 hours.
[60] [0060]In the methods of the present invention, at least about 40% by weight of available Cs20 present in the secondary ore can be captured or recovered, such as at least about 50%, at least about 60 wt%, at least about 70 wt%, at least about 80 wt%, at least about 90 wt%, such as from 40 wt% to 95 wt%, by weight of available Cs20 that was originally present in the secondary ore.
[61] [0061]In the methods of the present invention, as an option, at least about 10% by weight of available Rb20 present in the starting secondary ore can be captured or recovered, such as at least about 15% by weight of available Rb20 present in the secondary ore.
[62] [0062]The methods of the present invention can optionally include a second sorting.
[63] [0063]The second sorter can be set such that the Grade 2A piece is determined based on a determined or calculated atomic number of at least 25, or based on a determined or calculated atomic number of at least 30, or based on a determined or calculated atomic number of at least 35, or based on a determined or calculated estimated atomic number of from 25 to 45, for a certain percent volume of the individual piece, such as at least a 30% volume, or at least a 40% volume, or at least a 50% volume, or at least a 60% volume, or at least a 70% volume, or at least a 80% volume, or at least a 90% volume. The % volume can be determined based on the number of pixels having the desired atomic number. The % volume can be determined based on CT slices. It has been discovered that by having the second sort use different sorting conditions with regard to atomic number, additional Cs20 can be recovered with minimal impurities. The second sort can additionally or alternatively WO 2014/13778PCT/US2014/01929 include a scan for material density as in the first sorting using the same settings or different settings, such as reducing the minimum material density, for instance by 10% to 30% or some other amount. Equally useful, a significant level of rubidium in the form of Rb20 can be recovered using this second sorting technique, wherein the rejects of the first sorting are used and sorted through this second sorting. As an option, additional sorts can be used for the rejects of the second sort. Any number of additional sorts having the same or different conditions from the first sort or second sort can be used. The second sorting can capture at least about 1% by weight of available Cs20 present in the secondary ore, based on weight of the starting secondary ore, or at least about 15% by weight of available Cs20 present in the secondary ore, based on weight of the starting secondary ore, or at least about 50% by weight of available Cs20 present in the secondary ore, based on weight of the starting secondary ore.
[64] [0064]With regard to the second sorting, as an option, the Grade 2A pieces can be determined or calculated to comprise Rb20 in an amount and concentration, each by weight, of at least twice that present in the Grade 2 pieces, or in an amount and concentration, each by weight, of at least twice that present in the Grade 2B pieces.
[65] [0065]With regard to the second sorting, the second sorting can capture at least about % by weight of the available Cs20 present in the Grade 2 pieces, based on the weight of the Grade 2 pieces from the first sort. As an option, the second sorting can capture/recover at least 50% or at least about 70% by weight of the available Cs20 present in the Grade 2 pieces, based on the weight of the Grade 2 pieces from the first sort.
[66] [0066]As an option, the second sorting can capture at least about 30% by weight, at least 50% by weight, at least 65% by weight of the available Rb20 present in the starting ore, namely the secondary ore, based on the weight of the starting ore at the beginning of the process.
[67] [0067]As an option, the second sorting can capture at least about 35% by weight, at least WO 2014/13778PCT/US2014/01929 about 50% by weight, at least about 65% by weight, or at least about 80% by weight of the available Rb20 present in the Grade 2 pieces, based on the weight of the Grade 2 pieces from the first sort.
[68] [0068]As an option, the second sorting can capture at least about 20% by weight of available Rb20 present in the secondary ore, based on weight of the secondary ore prior to the first sorting, or at least about 30% by weight of available Rb20 present in the starting secondary ore, based on weight of the secondary ore prior to the first sorting, or at least about 40% by weight of available Rb20 present in the secondary ore, based on weight of the secondary ore at the start, or at least about 50% by weight of available Rb20 present in the secondary ore, based on weight of the starting secondary ore, or at least 1% by weight of available Cs20 present in the secondary ore, based on weight of the starting secondary ore, or at least 5% by weight of available Cs20 present in the starting secondary ore, based on weight of the secondary ore, or at least 10% by weight of available Cs20 present in the secondary ore, based on weight of the starting secondary ore.
[69] [0069]The first sorting and optional second sorting combined can capture at least 40% by weight of available Rb20 present in the secondary ore, based on weight of the starting secondary ore, or at least 50% by weight of available Rb20 present in the secondary ore, based on weight of the starting secondary ore, or at least 60% by weight of available Rb20 present in the secondary ore, based on weight of the starting secondary ore, or at least 65% by weight of available Rb20 present in the secondary ore, based on weight of the starting secondary ore.
[70] [0070]The first sorting and optional second sorting combined can capture at least 60% by weight of available Cs20 present in the secondary ore, based on weight of the starting secondary ore, and/or at least 40% by weight of available Rb20 present in the secondary ore, based on weight of the starting secondary ore, or at least 70% by weight of available Cs WO 2014/13778PCT/US2014/01929 present in the secondary ore, based on weight of the starting secondary ore, and/or at least 50% by weight of available Rb20 present in the secondary ore, based on weight of the starting secondary ore, or at least 80% by weight of available Cs20 present in the secondary ore, based on weight of the starting secondary ore, and/or at least 60% by weight of available Rb20 present in the secondary ore, based on weight of the starting secondary ore.
[71] [0071]With the methods of the present invention, the Grade 1 pieces can have or include at least 100% more Cs20 based on a comparison of total weight percent of Cs20 in the secondary ore to total weight percent of Cs20 in the Grade 1 pieces, such as at least 150% more Cs20, at least 200% more Cs20, or at least 300% more Cs20 (such as 100% to 1000% more by wt) based on a comparison of total weight percent of Cs20 in secondary ore to total weight percent of Cs20 in Grade 1 pieces.
[72] [0072]The method can optionally include extracting cesium, rubidium or both by subjecting the Grade 1 pieces to at least one acid treatment or acid digestion. The acid treatment can involve mixing the Grade 1 pieces with sulfuric acid, such as concentrated sulfuric acid, or other acids. Examples of acids that can be used include, but are not limited to, strong acid as that term is understood in the art. The acid(s) can be sulfuric acid, hydrochloric acid, hydrofluoric acid, nitric acid, and the like.
[73] [0073]In the present invention, the Grade 1 pieces can be subjected to an acid treatment which can involve leaching the Grade 1 pieces, which typically comprise pollucite and/or nanpingite and/or carnallite, with strong sulfuric acid to obtain an extract containing cesium alum which can be recovered by crystallization. Cesium alum is cesium aluminum sulfate hydrate. The sulfuric acid extracts can typically be contaminated with other metal ions, such as rubidium, sodium, potassium, magnesium, and iron. The processes described in U.S. Patent No. 6,436,879, can be used as part of the acid treatment to obtain a more highly pure cesium-containing material for such end uses as drilling fluids. This process, in summary, WO 2014/13778PCT/US2014/01929 involves treating the cesium starting material with a suitable reagent to dissolve at least a portion and preferably all or nearly all of the cesium contained therein and form a slurry. A base comprising slaked lime or calcium carbonate and an acid containing the anion of the pre-determined cesium compound can be added to the slurry and then the pre-determined cesium compound, once formed, can be separated.
[74] [0074]The Grade 1 pieces, alone or combined with the Grade 2A pieces, can be subjected to an acid treatment, such as sulfuric acid or other acids that would be considered equivalent. The acid:cesium weight ratio can be 4:1 or greater. The sulfuric acid treatment strength can be, for instance, at least 35% H2SO4, by weight. Other acids may be used at the same or similar acid strength. The acid treatment may be carried out at temperatures of 90° C or higher. The acid treatment can continue for 15 minutes or more, e.g., for 15 minutes to 2 hours or more.
[75] [0075]As an option, and at any part of the process, the Grade 1 and/or Grade 2A pieces can be subjected to further communition (one or more) to achieve any nominal sizing including sizes of less than 100 microns.
[76] [0076]In the present invention, the method can further include extracting cesium, rubidium or both by subjecting the Grade 2A pieces to at least one non-acid treatment. The non-acid treatment can involve calcining the pieces, for instance at a temperature of from about 800° C to about 1200° C, or other temperatures, for any amount of time, such as 10 minutes to 10 hours or more. 100771As an option, the Grade 1 pieces which now contain a much higher percentage of Cs20 can then be processed for a variety of uses. For instance, the Grade 1 pieces can be used to form cesium compounds, such as cesium formate. For instance, the Cs20 can be recovered and subjected to further recovery processes by reacting the Grade 1 pieces with at least one salt, where the salt is capable of recovering at least one metallic element, such as WO 2014/13778PCT/US2014/01929 cesium, to form a reaction product that includes at least one metallic element. For instance, the salt can be a sulfate salt. Details of this further processing step can be found in U.S. Patent No. 7,323,150, incorporated in its entirety by reference herein. By using this process, the cesium can be converted to a precursor salt, such as cesium sulfate, from which other cesium salts are produced. Other methodology similarly can produce alternative cesium salts from precursors like cesium hydroxide and cesium carbonate. As described, for instance, in U.S. Patent No. 7,759,273, the cesium can be formed into a cesium formate which subsequently can then be converted to a different cesium metal salt. Another process to form cesium salts is described in U.S. Patent No. 6,652,820, which is incorporated in its entirety by reference herein. This method involves forming a cesium salt by reacting cesium sulfate with lime to form cesium hydroxide which can then be converted to a cesium salt, such as cesium formate. As stated, the cesium compounds can be very desirable as drilling fluids or other fluids used for hydrocarbon recovery, such as completion fluids, packer fluids, and the like.
[78] [0078]The processes described in U.S. Patent No. 6,015,535 can also be used to form desirable cesium compounds, such as cesium formate. The various formulations and compositions described in the following patents can be used with the cesium or cesium compounds recovered by the processes of the present invention and each of these patents are incorporated in their entirety by reference herein: U.S. Patent No. 7,407,008; 7,273,832; 7,211,550; 7,056,868; 6,818,595; 6,656,989; and 6,423,802.
[79] [0079]As stated above and as shown in Fig. 4, a fluid comprising lithium, for instance a fluid comprising lithium formate, has a much lower saturation point than a fluid comprising cesium formate or rubidium formate. As shown in Fig. 4, cesium formate will remain in saturated solution until a maximum of 84% by weight cesium formate is present in only 16 wt% water. The same is true for a saturated rubidium formate solution. Also shown in Fig. 4 WO 2014/13778PCT/US2014/01929 is that these blends form a very desirable, high specific gravity solution, with a specific gravity ranging from 2.15 to 2.3 SG. However, a lithium formate solution is fully saturated at 16% by weight lithium formate, and any amounts above this will cause the lithium formate salt to precipitate from solution. Further, with lithium formate fluid, the maximum brine SG (specific gravity) is only about 1.14 SG, which generally is not useful for drilling fluids where high density fluids are desired. The presence of lithium formate in a cesium formate or rubidium formate fluid tends to destabilize the fluid, causing the maximum wt% of cesium formate or rubidium formate in solution at saturation to drop significantly. Thus, the presence of lithium in the higher specific gravity cesium formate brines is highly deleterious when attempting to produce stable oil field brines. Other, less stable, lighter alkalis of sodium and potassium, as illustrated in Fig. 4, also have a negative effect on the stability of high specific gravity alkali formate brine, but are not as deleterious as lithium. If the lithium content exceeds, for instance, over 3,000 ppm with regard to the refined, crushed ore processed into drilling fluids, this can result in an inadequate or sub-optimal cesium or rubidium formate drilling fluid or other high specific gravity, dense fluid. The acid treatment of cesium-containing ore to refine the ore and prepare cesium salts, such as cesium formate, cannot remove the lighter alkalis, including lithium, from the ore. This is a significant obstacle to refinement and use of secondary ore sources of cesium oxide for the manufacture of pure cesium or rubidium compounds, and high specific gravity fluids containing cesium or rubidium. As a result, the processes of the present invention are effective to significantly reduce the lithium levels in secondary ore in order to achieve a useful cesium-containing refined crushed ore intermediate product which can then be used to make high density drilling fluids or purified cesium compounds for other end uses. Prior ore refinement processes, such as flotation, acid treatment, color sorting, and the like, have not been effective to extract cesium and rubidium bearing minerals from cesium-containing secondary WO 2014/13778PCT/US2014/01929 ore containing lithium bearing phosphate minerals, without also extracting deleterious quantities of lithium. In contrast, the atomic number and/or material density sorting method of the present invention is effective in separating cesium and rubidium bearing minerals from cesium-containing secondary ore containing lithium bearing phosphate minerals, and from phosphate minerals containing deleterious quantities of lithium.
[80] [0080]As an option, the Grade 2 or Grade 2B pieces which contain high levels of lithium, potassium, and/or sodium can be further processed to recover the alkali metals for other industrial uses, such as batteries and other electrical applications.
[81] [0081]The present invention further relates to novel, purified, secondary ore which contains desirable levels of Cs20 and/or Rb20. The resulting sorted ore, after the first sort, is unique by itself or in combination with the sorted ore resulting from the second sort or further optional subsequent sorts, such as a third sort, and so on.
[82] [0082]The present invention further relates to a crushed, refined, cesium-containing ore.
[83] [0083]The crushed, refined, cesium containing ore can additionally have one or more of the following (based on the total weight of the ore): a) a SQUI content in an amount of from 0.5 wt% to 5 wt% (e.g., from 0.6 wt% to 5 wt%, from 0.7 wt% to 5 wt%, from 1 wt% to 5 wt%, from 1.2 wt% to 5 wt%, from 2 wt% to 5 wt%); b) a quartz content in an amount of from 0.5 wt% to 5 wt% (e.g., from 0.6 wt% to 5 wt%, from 0.7 wt% to 5 wt%, from 1 wt% to 5 wt%, from 1.2 wt% to 5 wt%, from 2 wt% to 5 wt%); c) a total Feldspar content of from 1 wt% to 10 wt% (e.g., from 2 wt% to 10 wt%, from 3 wt% to 10 wt%, from 4 wt% to 10 wt%, from 5 wt% to 10 wt%); d) an Albite content of from 0 wt% to 1 wt% (e.g., from 0.1 wt% to 1 wt%, from 0.2 wt% to 1 wt%, from 0.3 wt% to 1 wt%, from 0.4 wt% to 1 wt%); WO 2014/13778PCT/US2014/01929 an Amphibolite content of from 0.1 wt% to 0.5 wt% (e.g., from 0.2 wt% to 0.5 wt%, from 0.3 wt% to 0.5 wt%); an Apatite content of from 0.5 wt% to 4 wt% (e.g., from 0.6 wt% to 4 wt%, from 0.8 wt% to 4 wt%, from 1 wt% to 4 wt%); a Lepidolite content of from 2 wt% to 8 wt% (e.g., from 2.5 wt% to 8 wt%, from 4 wt% to 8 wt%, from 5 wt% to 8 wt%); and/or an Amblygonite content of from 0 wt% to 1 wt% (e.g., from 0.1 wt% to 1 wt%, from 0.2 wt% to 1 wt%, from 0.3 wt% to 1 wt%, from 0.5 wt% to 1 wt%).
[84] [0084]For instance, the above crushed, refined, ore (or recovered sorted ore) can be present after the first sort in the methods of the present invention (e.g., Grade 1 pieces).
[85] [0085]The present invention further relates to a crushed, refined, cesium-containing ore.
[86] [0086]The crushed, refined, cesium containing ore can additionally have one or more of the following (based on the weight of the ore): a SQUI content in an amount of from 2 wt% to 18 wt% (e.g., from 3 wt% to 15 wt%, from 5 wt% to 15 wt%, from 6 wt% to 10 wt%, from 3 wt% to 10 wt%, from 7 wt% to 10 wt%); a quartz content in an amount of from 1 wt% to 10 wt% (e.g., from 2 wt% to 10 wt%, from 3 wt% to 10 wt%, from 4 wt% to 10 wt%, from 5 wt% to 10 wt%, from 6 wt% to 10 wt%); a total Feldspar content of from 20 wt% to 70 wt% (e.g., from 25 wt% to 70 wt%, from 30 wt% to 70 wt%, from 35 wt% to 70 wt%, from 40 wt% to 70 wt%, from 50 wt% to 70 wt%); an Albite content of from 0 wt% to 2 wt% (e.g., from 0.1 wt% to 2 wt%, from 0.3 wt% to 2 wt%, from 0.5 wt% to 2 wt%, from 1 wt% to 2 wt%, from 0.75 wt% to 1. wt%); an Amphibolite content of from 0.5 wt% to 10 wt% (e.g., from 0.75 wt% to 10 wt%, from 1 wt% to 10 wt%, from 2 wt% to 10 wt%, from 3 wt% to 10 wt%, from 3 wt% to 7 wt%); an Apatite content of from 0 wt% to 1 wt% (e.g., from 0.1 wt% to 1 wt%, from 0.2 wt% to 1 wt%, from 0.3 wt% to 1 wt%, from 0.4 wt% to 1 wt%, from 0.5 wt% to 1 wt%); WO 2014/13778PCT/US2014/01929 a Lepidolite content of from 0.5 wt% to 15 wt% (e.g., from 0.75 wt% to 15 wt%, from 1 wt% to 15 wt%, from 2 wt% to 15 wt%, from 5 wt% to 15 wt%, from 7 wt% to 15 wt%); and/or an Amblygonite content of from 0.1 wt% to 3 wt% (e.g., from 0.2 wt% to 3 wt%, from 0.5 wt% to 3 wt%, from 1 wt% to 3 wt%, from 0.75 wt% to 2.5 wt%, from 1 wt% to 2 wt%).
[87] [0087]The above crushed, refined ore (or recovered sorted ore) can be formed or present from combining the first sort with the second sort (e.g., a combination of the Grade 1 pieces with the Grade 2A pieces). The present invention further relates to this combination. The first sort can comprise 20 wt% to 75 wt% of the combined sort, such as 25 wt% to 70 wt%, 30 wt% to 60 wt%, and the like, and the remaining wt% can be the second sort.
[88] [0088]The present invention further relates to a solution containing a cesium containing compound formed from or containing one or more of the purified ores mentioned herein.
[89] [0089]Representative examples of solutions containing a cesium containing compound formed from or containing one or more of the purified ores are described below. Two of the cesium salt solutions illustrated below reflect the processing of two of the purified ore streams. The first purified ore is a Grade 1 composition. The second purified ore stream reflects a weighted composition of Grade 1 plus Grade 2A streams. For comparison, the third cesium salt solution is constructed from the unpurified secondary ore.
[90] [0090]The three comparative alkali formate, oil-field brines presented were made with an uncalcined, sulfuric acid based extraction process.
[91] [0091]Using Grade 1 pieces (Fluid A), a fully saturated brine with the following composition was prepared from the ore (percents by weight of fluid): Cesium Formate: 78.54 wt% Lithium Formate: 0.51 wt% WO 2014/13778PCT/US2014/01929 Sodium Formate: 0.95 wt% Rubidium Formate: 0.56 wt% Potassium Formate: 0.43 wt% Water Content: 19.02 wt%.
[92] [0092]The alkali formate solutions Fluid A and Fluid B generated from sorted, purified ore fractions were capable of sustaining stable, high specific gravity, solids free, oil-field brines. The unpurified secondary ore processed into Fluid C was incapable of sustaining the required saturation weight to yield a useful specific gravity. There is an insufficient weight percentage of soluble cesium formate present. Too much water was required for alkali saturation to achieve WO 2014/13778PCT/US2014/01929 desired solution densities (over 2.0 SG and preferably over 2.1 SG) for brine stability. Also for perspective, the lithium fraction for this stream alone, viewed as a separate saturated entity, would represent a 25% aqueous based salt solution. For purposes of the present invention, SG is measured/normalized at a temperature 15.6°C.
[93] [0093]Formate-containing oil-field brine solutions are commonly buffered with soluble carbonate/bicarbonate. This soluble CO3 presence, in concert with a high degree of solution saturation, can further exacerbate formate brine instability by precipitating lithium carbonate, which can further seed and enable formate precipitation.
[94] [0094]The present invention will be further clarified by the following examples, which are intended to be exemplary of the present invention.
[95] [0095]In this example, a 789 kg quantity of secondary ore mined from Tanco granitic pegmatite at Bernic Lake, Manitoba, Canada was recovered. The secondary ore (with a U.S. mesh size of + 5 inch) had an estimated pollucite content of 45.72 wt% (wherein all wt% unless stated otherwise, are based on the weight of the starting secondary ore). The secondary ore was estimated to have a Cs20 content of about 9 wt%. The secondary ore also contained Lepidolite, Feldspar, Quartz, SQUI, Amblygonite, and Albite, and minor amounts of other mineral/rock types.
[96] [0096]For sorting, a dual energy X-ray transmission (DEXRT) sorter obtained from Commodas Ultrasort, GmbH, Wedel, Germany was used. The feed rate through the sorter was about 5 to 10 ton/hour. The sorter was calibrated using five (5) training sets of rocks from known ores. Each training set had the same mineral types but had a different size fraction. The following five size fractions were used to calibrate the sorter: WO 2014/13778PCT/US2014/01929 2 inches + 1.5 inches 1.5 inches + 1 inch 1 inch + 0.5 inch 0.5 inch + 0.25 inch 0.25 inch + 0.125 inch.
[97] [0097]The rock types in each training set were Pollucite, Lepidolite, Feldspar 4, Feldspar 3, Quartz, SQUI, Amblygonite, and Albite. These training sets were passed through the sorter to calibrate the sorter and to determine the scan parameters for atomic number and material density of the Pollucite for each size fraction.
[98] [0098]The starting secondary ore was crushed to a particle size such that it passed through a U.S. mesh of — 2.5 inches. The crushed ore was then divided into the same five size fractions identified above. Each of the size fractions were fed separately on a belt to the sorter and scanned. A dual energy scan of each individual piece of crushed ore was made and image processing was conducted to generate color images of each individual piece to reflect atomic number and material density. In the first sort, the sorter was set to eject any individual piece that had over 50% by volume of a determined or calculated atomic number of 50 or higher and a material density of from 2.7 to 3.2 g/cm3 from its normal trajectory by air jets as shown in Fig. 2. The ejected pieces were designed as useful, Grade 1 pieces.
[99] [0099]Then, the "accept" pieces not ejected from the first sort (the Grade 2 pieces) were collected and then passed through the same sorter. For the second pass, the settings of the sorter were adjusted to eject any individual piece that had over 50% by volume of a determined or calculated atomic number of 30 or higher and a material density of 2.5 to 3.2 g/cm3 from its normal trajectory by air jets to form the second ore stream (Grade 2A pieces).
[100] [00100] As can be seen in Table 1 below, in the method of the invention, the amount of Cs20 went from 9 wt% in the starting secondary ore to 19.2 wt% in the first sort, and 3 wt% in the second sort, with an overall low and acceptable phosphate and lithium content satisfactory for used in cesium compounds.
[101] [00101]The "Step 1 Ejects" refers to the results of the first sorting, which is also known as the "Grade 1 pieces." Table 1 shows the various weight per size fractions, the weight percent that this represents is based on the overall weight of the first sort and also shows the weight percent Cs20 per size fraction. The various amounts per size fraction, as well as for totals for the first sort with regard to Rb20, Li20, Na2O, and K20 are also reflected. Table 1 shows the same data for "Step 2 Ejects," the results of the second sorting, which passed Grade 2 pieces (Step 1 Accepts), through a second sorting step. As can be seen, after the second sorting, the Grade 2A pieces had 3.07 wt% Cs20, evidence that the first sorting did a very efficient job of recovering the cesium from the secondary ore, and the second sort yielded additional cesium missed by the first sorting. Table 1 further shows the "Step 2 Accepts", the Grade 2B pieces. The percent Cs20 for this remaining amount was significantly lower, at 0.58 wt% of the material in the Grade 2B pieces. Table 1 below further sets forth, by size fraction, the amount of the starting secondary ore, and the percent phosphates, which are highly undesirable minerals that typically contain lithium, which is unwanted in the cesium recoveries. Table 1 shows how the first sorting and second sorting steps recovered low phosphate level material, especially compared to the cesium level, and this is reflected in the Cs:P weight ratio. In this example and all examples here, the % Cs20, %P205, and %Ta205 were measured using x-ray fluorescence (XRF) and using fused and pressed pellets. %Rb20, K20, Na20, and Liz() were measured using Inductively Coupled Plasma (ICP) analytical technique. Unless stated otherwise, all other % measurement for the oxides or metals were done using XRF.
[102] [00102] In this example, the same procedures as in Example 1 were repeated, but with a different starting secondary ore to show the ability of the sorting techniques to process different cesium contents in the starting secondary ore. Also, different size fractions were used to calibrate and to sort. The results are set forth below in Table 2. In this example, besides the indicated mesh screen for size fraction, a bar screen was also used to allow rocks with a larger single dimension, for instance in length, to pass through and be processed. In Table 2 the first entry under Step 1 Ejects is crushed ore which would not pass through a 50 mm mesh screen which was passed through a 60 mm bar screen and collected on a 40 mm bar screen. Essentially, this was the bar screen fraction between 40 mm and 60 mm, which cannot pass through a 50 mm mesh screen. Typically this type of material has one dimension that is larger than 50 mm, but has remaining dimensions that are smaller than 50 mm and is sortable material using the technology of the present invention. The second entry in Table 2 under Step 1 Ejects refers to material that would not pass through a 50 mm mesh screen, but passes through a 40 mm bar screen. As seen in the data, the starting Cs20 content for the starting secondary ore was 4.65 wt% based on the weight of the starting secondary ore. After the first sorting, the amount of cesium (Cs20) in the first sort by weight was about 21 wt% Cs20, which was an incredible and surprising increase in the purity of the cesium in the first sort compared to the starting cesium content. The remaining recovery amounts are set forth in Table 2.
[103] [00103] As a result of the first sort, the ejects (Grade 1 pieces) had the following make-up (based on the weight of the first sorted rocks (Grade 1 pieces)): pollucite content in an amount of 67.1 wt%; a Cs20 content of 21.3 wt%; total phosphate mineral content of 0.49 wt%; WO 2014/13778PCT/US2014/01929 d) a %Cs20: %P205 weight ratio of at least 43.7:1; e) a Li20 content of 0.9 wt%; f) a Rb20 content of 0.88 wt%.
[104] [00104] As a result of the second sort, the ejects (Grade 2A pieces) had the following make-up (based on the weight of the second sorted rocks (Grade 2A pieces)): pollucite content in an amount of 0 wt%; a Cs20 content of 3 wt%; total phosphate mineral content of 0.79 wt%; a %Cs20: %P20 weight ratio of 1.34:1; a Liz() content of 1.06 wt%; and a Rb20 content of 1.66 wt% The second sort had a mineral content of: a SQUI content in an amount of 0.17 wt%; a quartz content in an amount of 1.97 wt%; a total Feldspar content of 79.78 wt%; an Albite content of 0 wt%; WO 2014/13778PCT/US2014/01929 an Amphibolite content of 2.09 wt%; an Apatite content of 0 wt%; a Lepidolite content of 1.25 wt%; and an Amblygonite content of 0.53 wt%.
[105] [00105] In this example, the same procedures as in Example 1 were repeated, but with a different starting secondary ore, and different size fractions were used to calibrate and to sort. Table 3 below further summarizes the results from Example 1 (identified as "feed 1" in Table 3) and in Example 2 (identified as "feed 2") in Table 3. "Feed 3" is Example 3. In Table 3, the feed grade is a reference to the weight percent of Cs20 in the starting secondary ore. As can be seen, the starting percent of cesium was 9% or lower. Table 3 further breaks down the starting amount of cesium per size fraction. Table 3 also provides the percent of Cs20 recovery based on the amount of available cesium that was present in the starting secondary ore. For instance, feed 1 shows a 93.4% Cs20 recovery which means that 93.4% of all available cesium oxide (by weight) that was available in the starting secondary ore was recovered by the sorting techniques of the present invention. The reference to wt% recovery is a reference to the weight percent of the first sort and second sort that was recovered as eject 1 and eject 2 (Grade 1 pieces and Grade 2A pieces) and which contained the Cs20. Referring to feed 1, the combined first and second sort comprised 45.72 wt% of the starting low-yield ore. Put another way, over half of the starting weight of the low-yield ore was discarded and yet the amount of available cesium recovered was 93.4% and the product grade (which is a reference to the percent purity/concentration of the Cs20) in the final sorted product was 18.56 percent by weight. Thus, referring to feed 1, the final sorted amount had a purity or concentration level of 18.56 wt% which was over a 100% increase from the starting Cs20 concentration. Similar results were seen for feed 2 which had an even lower starting Cs20 amount and yet resulted in a final Cs20 concentration of 21.26%. Feed 3, which is the third example, showed a starting cesium oxide content of 2.72% by weight and yet the finished sorted product had a cesium oxide concentration of 20.66 wt% wherein 92.14 wt% of the available cesium oxide (in the starting ore) was recovered by the sorting techniques.
[106] [00106]All of this shows the unexpected and superior ability of the present invention to recover cesium oxide from very low-yield ore to obtain a useful product for cesium applications.
[108] [00108] The present invention can include any combination of these various features or embodiments above and/or below as set forth in sentences and/or paragraphs. Any combination of disclosed features herein is considered part of the present invention and no WO 2014/13778PCT/US2014/01929 limitation is intended with respect to combinable features.
[109] [00109]Applicants specifically incorporate the entire contents of all cited references in this disclosure. Further, when an amount, concentration, or other value or parameter is given as either a range, preferred range, or a list of upper preferable values and lower preferable values, this is to be understood as specifically disclosing all ranges formed from any pair of any upper range limit or preferred value and any lower range limit or preferred value, regardless of whether ranges are separately disclosed. Where a range of numerical values is recited herein, unless otherwise stated, the range is intended to include the endpoints thereof, and all integers and fractions within the range. It is not intended that the scope of the invention be limited to the specific values recited when defining a range.
[110] [00110] Other embodiments of the present invention will be apparent to those skilled in the art from consideration of the present specification and practice of the present invention disclosed herein. It is intended that the present specification and examples be considered as exemplary only with a true scope and spirit of the invention being indicated by the following claims and equivalents thereof.

权利要求:
Claims (9)
[1] 1. WHAT IS CLAIMED IS: l . A method to recover cesium, rubidium, or both from secondary ore, Wherein said secondaryore comprises 25 Wt% CsgO or less based on overall Weight of said secondary ore and themajority of said secondary ore comprise pieces having at least one dimension that is over 5inches (l2.7 cm),said method comprising: obtaining crushed ore from said secondary ore and separating into two or more size fractions that are different from each other, Wherein said crushed ore comprising individual pieces, each individual piece having a size capable of passing through a U.S. standard sieve mesh/screen opening of 3 inches (76.2 mm); passing said crushed ore through a first sorter to conduct a first sorting at a feed rate of at least l ton/hour, Wherein said first sorter determines Whether each individual piece of crushed ore is a “Grade l piece” or “Grade 2 piece”, based on said first sorter conducting at least one scan of each individual piece and determining atomic number or material density orboth of each individual piece, Wherein said “Grade l piece” comprises CsgO, or CsgO and RbgO together, in an amount of at least 20 % based on the Weight of said individual piece; separating said Grade l pieces from said Grade 2 pieces, Whereby Wt % CsgO of said Grade l pieces is at least 10% by Weight higher than Wt % CsgO in said secondary ore and, optionally fiJrther comprising calcining said Grade l pieces after said separating.
[2] 2. The method of claim l , fiJrther comprising extracting cesium, rubidium orboth by subj ecting said Grade l pieces to at least one acid treatment.
[3] 3. The method of claim l, Wherein said secondary ore comprises 20 Wt% CsgO or less. The method of c1aim 1, Wherein said secondary ore comprises po11ucite. The method of c1aim 1, Wherein said first sorter detects and se1ects said Grade 1 piece based on an atomic number of from 80 to 150. The method of c1aim 1, Wherein said method captures at 1east about 40% by Weight ofaVai1ab1e CsgO present in said secondary ore and/or said method captures at 1east about 10% by Weight of aVai1ab1e RbgO present in said secondary ore. The method of c1aim 1, further comprising a second sorting step comprising passing saidGrade 2 pieces through a second sorter, Which is the same or different from said sorter,Wherein said second sorter determines Whether each indiVidua1 piece of said Grade 2 piecesis a “Grade 2A piece” or “Grade 2B piece”, based on said second sorter conducting at 1eastone scan of each indiVidua1 piece and deterrnining atomic number or material density orbothof each indiVidua1piece, Wherein said “Grade 2A piece” comprises CsgO and RbQO in anamount of at 1east 4 % based on the Weight of said indiVidua1piece, and said “Grade 2Bpiece” is any Grade 2 piece that is not a Grade 2A piece and then separating said Grade 2Apieces from said Grade 2B pieces and, optiona11y further comprising extracting cesium, rubidium or both by subjecting said Grade 2A pieces to at 1east one non-acid treatment. The method of c1aim 7, Wherein said second sorter is set such that said Grade 2A piece is deterrnined based on an atomic number of from 60 to 150. 10. 11. 12. 13. The method of claim 7, Wherein said second sorting captures at least about 10% by Weight ofavailable CsgO present in said secondary ore, based on Weight of said secondary ore at start,and/or Wherein said second sorting captures at least about 20% by Weight of available RbQO present in said secondary ore, based on Weight of said secondary ore at start. The method of claim 7, Wherein said first sorting and said second sorting combined captureat least 80% by Weight of available CsgO present in said secondary ore, based on Weight ofsaid secondary ore at start, and at least 60% by Weight of available RbgO present in said secondary ore, based on Weight of said secondary ore at start. The method of claim 1, Wherein said Grade 1 pieces comprise at least 100% more CsgObased on a comparison of Weight percent of CsgO in secondary ore to Weight percent of CsgO in Grade 1 pieces. The method of claim 1, Wherein said secondary ore comprises pollucite, nanpingite,carnallite, rhodozite, pezzottaite, rubicline, borate ramanite, beryls, voloshonite,cesstibtantite, avogadrite, margaritasite, kupletskite, nalivkinite, petalite, spodumene,lepidolite, biotite, mica, muscovite, feldspar, microcline, Li-muscovite, lithiophilite,amblygonite, illite, cookeite, albite, analcime, squi, amphiboles, lithian mica, amphibolite, lithiophospahe, apatite, londonite, or any combinations thereof The method of claim 1, Wherein said method fiJrther comprises crushing said secondary ore to obtain crushed ore comprising individual pieces, each individual piece having a size 1
[4] 4. 1
[5] 5. 1
[6] 6. 1
[7] 7. 1
[8] 8. 1
[9] 9. capab1e of passing through a U.S. standard sieve mesh/screen opening of 2 inches (50.8 mm) . The method of c1aim 1, Wherein said crushed ore comprising individual pieces, each individual piece having a size capab1e of passing through a mesh/screen of 1 inch. The method of c1aim 1, Wherein said first sorter is set such that Grade 1 piece is deterrnined based on a materia1 density of at 1east 2.5 g/cm3 . The method of c1aim 1, Wherein said first sorter conducts at 1east 2 scans of each individua1piece, Wherein one scan deterrnines atomic number and the other scan deterrnines materia1 density. The method of c1aim 7, Wherein said second sorter is set such that Grade 2A piece is deterrnined based on materia1 density of at 1east 2.5. The method of c1aim 7, Wherein second sorter is set such that said Grade 2A is deterrnined based on an atomic number of at 1east 30 and a materia1 density of at 1east 2.5. The method of c1aim 1, said method further comprising an initia1 ca1ibration step, Whereinbefore said passing of said crushed ore through said first sorter, passing through two or moresize fractions of known rocks and minera1s that are representative of the rocks and minera1sin said secondary ore to be sorted so as to ca1ibrate said first sorter, for each size fraction, With respect to What is representative of a “Grade 1 piece” or What is representative of a 20. 21. 22. “Grade 2 piece” or both based on scanned properties of atomic number or material density or both. The method of c1aim 19, Wherein said “Grade 1 piece” is deterrnined based on being Within10% of the scanned property of atomic number or materia1 density or both for the representatiVe Grade 1 piece for that size fraction. The method of c1aim 1, Wherein the size fractions are acquired by the forrnulas:S1 = SX to 50% SXS2 = S1 to 50% S1S3 = S2 to 50% S2, andoptiona11y S4 = S3 to 50% S3,Where SX is the maximum size fraction that is capab1e of passing through the sorter, and S1, S2, S3, and S4 are each a different size fraction. A refined crushed ore in the form of minera1 rocks comprising: a) a cesium bearing rock content in an amount of from 10 Wt% to 90 Wt%, Wherein saidcesium bearing rock is po11ucite, nanpingite, and/ or cama11i1te; b) a Cs2O content of from 5 Wt% to 32 Wt%; c) tota1phosphate minera1 content of from 1 Wt% to 10 Wt%; d) a %Cs2O: %P2O5 Weight ratio of at 1east 4:1; e) a Li2O content offrom 0.59 Wt% to 1.5 Wt%; f) a Rb2O content of from 0.5 Wt% to 1.8 Wt%; and g) an average crushed ore size of from 0.1 inch to 5 inches, Wherein all Wt% are based onWeight of refined crushed ore, and optionally fiJrther comprising at least one of thefollowing: a) a SQUI content in an amount of from 0.5 Wt% to 5 Wt%; b) a quartz content in an amount of from 0.5 Wt% to 5 Wt%; c) a total Feldspar content of from l Wt% to l0 Wt%; d) an Albite content of from 0 Wt% to l Wt%; e) an Amphibolite content of from 0.l Wt% to 0.5 Wt%; f) an Apatite content of from 0.5 Wt% to 4 Wt%; g) a Lepidolite content of from 2 Wt% to 8 Wt%; and/or h) an Amblygonite content of from 0 Wt% to l Wt%.

类似技术:

---

公开号 | 公开日 | 专利标题

---

CA2903410C|2018-10-30|Methods to recover cesium or rubidium from secondary ore

---

TWI405619B|2013-08-21|Method for separating mineral impurities from calcium carbonate-containing rocks by x-ray sorting

---

Marras et al.2017|Characterization methodology for re-using marble slurry in industrial applications

---

Ismail et al.2016|Chemical and mineralogical characterization of Malaysian low-grade manganese ore

---

JP5588589B2|2014-09-10|Production of asbestos-free high-purity natural scale minerals

---

Kirabira et al.2011|Beneficiation and Evaluation of Mutaka kaolin

---

US20210238426A1|2021-08-05|Process for making direct-run diatomite functional filler products

---

Szeliga et al.2016|Mineralogical and petrographic characteristic of basic types of Turonian flints from the north-eastern margin of the Holy Cross Mountains: a preliminary report

---

Mengason et al.2018|Potential of Standards-Based Energy Dispersive Spectrometry To Analysis of Rhyolitic Glass Particles For Tephrochronology in Ice Cores

---

Khonthu2012|Investigation of the flotation behaviour of ball mill and IsaMill products

---

Ekholm2021|Mineralogical characterization of oresamples of different pH in the Björkdal golddeposit, northern Sweden–implications formineral processing

---

Oliveira2021|The applicability of X-ray microtomography for mineral liberation determination

---

Gryffenberg2010|Mineralogical investigation of the Nepheline syenite Franspoort, South Africa for beneficiation

---

Tserendavga2015|Isolation and characterization of lost copper and molybdenum particles in the flotation tailings of Kennecott copper porphyry ores

---

Terashima et al.2003|The Preparation and Characterisation of Two New Geological Survey of Japan Geochemical Reference Materials: Copper ore JCu‐1 and Zinc ore JZn‐1

---

Gaft et al.2005|Minerals Radiometric Sorting

---

ELEMENT-MINERAL2008|CRCLEME

同族专利:

---

公开号 | 公开日

---

US9458524B2|2016-10-04|

---

CN105209645A|2015-12-30|

---

AU2014226278A1|2015-09-03|

---

CA2903410C|2018-10-30|

---

CA2903410A1|2014-09-12|

---

WO2014137785A1|2014-09-12|

---

BR112015021281A2|2017-07-18|

---

US20140255278A1|2014-09-11|

---

BR112015021281B1|2020-05-05|

---

CN105209645B|2017-10-31|

---

DE112014001140T5|2016-03-24|

---

US20140255694A1|2014-09-11|

---

US9045812B2|2015-06-02|

---

SE540164C2|2018-04-17|

引用文献:

---

公开号 | 申请日 | 公开日 | 申请人 | 专利标题

---

---

US4542648A|1983-12-29|1985-09-24|Shell Oil Company|Method of correlating a core sample with its original position in a borehole|

---

US4597955A|1985-05-01|1986-07-01|Carus Corporation|Process for recovering cesium from cesium ore|

---

US6015535A|1995-04-06|2000-01-18|Cabot Corporation|Process for producing purified cesium compound from cesium alum|

---

EP1192233A1|1999-05-21|2002-04-03|Cabot Corporation|Polymer compositions|

---

US6423802B1|1999-05-21|2002-07-23|Cabot Corporation|Water soluble copolymers and polymer compositions comprising same and use thereof|

---

US7211550B2|2000-07-14|2007-05-01|Cabot Corporation|Compositions for controlling scaling and completion fluids|

---

MY140701A|2001-02-14|2010-01-15|Cabot Specialty Fluids Inc|Drilling fluids containing an alkali metal formate|

---

US6652820B2|2001-04-02|2003-11-25|Cabot Corporation|Methods of making cesium salts and other alkali metal salts|

---

US7056868B2|2001-07-30|2006-06-06|Cabot Corporation|Hydrophobe associative polymers and compositions and methods employing them|

---

WO2003018708A2|2001-08-10|2003-03-06|Cabot Specialty Fluids, Inc.|Alkali metal tungstate compositions and uses thereof|

---

US7323150B2|2003-05-23|2008-01-29|Cabot Corporation|Methods for recovering at least one metallic element from ore|

---

US7759273B2|2005-04-20|2010-07-20|Cabot Corporation|Methods of forming an alkali metal salt|

---

US7407008B2|2006-05-10|2008-08-05|Cabot Specialty Fluids, Inc.|Weighted zero solids loss circulation, fluid loss and insulating annular space fluid systems|

---

BRPI0920320B1|2008-10-16|2019-07-09|Technological Resources Pty Limited|METHOD FOR CLASSIFYING MATERIAL AND METHOD FOR EXTRACTING MATERIAL|

---

AT521421T|2008-12-19|2011-09-15|Omya Development Ag|METHOD FOR SEPARATING MINERAL PURITY FROM CALCIUM-CARBONATE-CONTAINING STONES BY X-RAY GRADING|

---

US8610019B2|2009-02-27|2013-12-17|Mineral Separation Technologies Inc.|Methods for sorting materials|

---

WO2011064795A2|2009-11-24|2011-06-03|Goda Venkata Ramana|Device for sorting contaminants from minerals, and method thereof|

---

EP2550115A4|2010-03-23|2014-02-19|Tech Resources Pty Ltd|Sorting mined material on the basis of two or more properties of the material|

---

US20140225416A1|2011-07-08|2014-08-14|Technological Resources Pty. Limited|Sorting in a mining operation|

---

CN102744219A|2012-03-23|2012-10-24|内蒙古科技大学|Method for enriching niobium by using characteristic X ray|

---

CN102921638A|2012-11-16|2013-02-13|鞍钢集团矿业公司|Method for pretreating lean hematite and discarding tailings thereof by utilizing X-ray separators|

---

US9458524B2|2013-03-05|2016-10-04|Cabot Corporation|Methods to recover cesium or rubidium from secondary ore|NO2700456T3|2012-08-24|2018-02-24|

---

US9458524B2|2013-03-05|2016-10-04|Cabot Corporation|Methods to recover cesium or rubidium from secondary ore|

---

EP2859963A1|2013-10-11|2015-04-15|Sikora Ag|Method and device for sorting bulk material|

---

WO2015056264A1|2013-10-15|2015-04-23|Dead Sea Works Ltd.|Device, system and method for density measurements using gamma radiation|

---

WO2015070008A1|2013-11-08|2015-05-14|Schlumberger Canada Limited|Spectral analysis with spectrum deconvolution|

---

CN105154670B|2015-08-28|2018-01-12|武汉理工大学|A kind of method from separation and concentration rubidium in mine tailing containing rubidium|

---

WO2017109297A1|2015-12-23|2017-06-29|OutotecOy|A method and an arrangement for monitoring of a metallurgical separation process|

---

AR107476A1|2016-01-29|2018-05-02|Cascadero Copper Corp|CESSIO RECOVERY PROCESS OF MINERAL EPITERMAL DEPOSITS|

---

CN107413679A|2016-05-24|2017-12-01|湖南军芃科技股份有限公司|A kind of intelligent ore dressing device and method based on machine vision technique|

---

WO2019210351A1|2018-04-30|2019-11-07|Silica Technology Pty Ltd|Improved mica processing|

---

WO2019210350A1|2018-04-30|2019-11-07|Silica Technology Pty Ltd|Processing of silicate minerals|

---

CN109482334A|2018-11-26|2019-03-19|有研工程技术研究院有限公司|A kind of flotation combined beneficiation method of colour sorting-of mica containing rubidium-feldspar ore|

---

CN112024076A|2020-08-13|2020-12-04|张磊|Stone crushing and screening device for engineering construction based on Internet of things|

法律状态:

优先权:

---

申请号 | 申请日 | 专利标题

---

US201361772946P| true| 2013-03-05|2013-03-05|

---

PCT/US2014/019295|WO2014137785A1|2013-03-05|2014-02-28|Methods to recover cesium or rubidium from secondary ore|

---