    • 专利摘要:
    This biodegradable composition is composed of a plant material mainly composed of chaff and a binder of a biodegradable substance. The composition is formed into a container using the composition, and after use of the container, it is biodegradable by microorganisms, collapsed by sunlight or ultraviolet rays, and can be used as soil improving material after decomposition. Rice hulls can be blended with plant fibers such as straw and pulp. The binder consists of rosin, dharma, cow pearl, gelatin, starch, shellac, calcium carbonate, biodegradable plastics or mixtures thereof. This biodegradable material container is impregnated with a sheet woven fabric and / or nonwoven fabric, in particular, a slurry made of plant fiber powder material, shellac, titanium oxide, biodegradable wax, and calcium carbonate, and dried to produce a sheet member. It can be produced by laminating one or two or more, and pressing by heating and pressing.
    公开号:KR20000057885A
    申请号:KR1020000005153
    申请日:2000-02-02
    公开日:2000-09-25
    发明作者:카나야히사시；스에마스히데아키；카이요지；마츠오노리오；쿠보타유스케；하마치타츠야
    申请人:모리 테 쯔로오；세이부덴키 가부시키가이샤；오츠카 아키라；후쿠오카 카세이 코교 가부시키가이샤；
    IPC主号:
    专利说明:

    Biodegradable material composition, biodegradable container prepared from the composition and a method for producing the biodegradable container prepared by the composition {said biodegradable material composition, biodegradable container prepared by said composition and the manufacturing method of said container}
    The present invention relates to a biodegradable composition comprising a plant raw material such as chaff and a biodegradable material, a biodegradable container made from the biodegradable material composition and a method for producing the biodegradable container.
    Conventionally, it is known to use and discard a container (hereinafter referred to as a disposable container), which is made of a material in which straw or the like is added to a foamed styrene-based synthetic resin (for example, Japanese Patent Laid-Open No. 8-143695, Japanese Patent Laid-Open No. 8-81027).
    In addition, the biodegradable molding material disclosed in Japanese Patent Laid-Open No. 10-323810 is composed of 51 to 70% by weight of paper powder and 30 to 49% by weight of biodegradable aliphatic polyester resin, and has a high heat resistance temperature and steam. Vegetation pots that can be transplanted into soil can be formed in sterilized disposable containers, trays and seedlings. The biodegradable molding material has water resistance and collapses within a certain period of time when disposed after use.
    In addition, the manufacturing method of the decomposable container disclosed in Japanese Patent Laid-Open No. 7-205120 is a raw material of straw and rice hull which does not cause environmental pollution by disposal, and sterilizes straw and rice husk of grain at high temperature. After drying, it is cut fiber or pulverized powder in advance, while starch containing water is heated and gelatinized, and the mixed material mixed and stirred by both is heated and press-molded by a molding mold, and then a plastic film is applied to cover it. A layer is formed.
    Moreover, it is known that the disposable container which consists of a biodegradable nonwoven fabric as a tray and a case for foods displayed on the conveyance or showcase of foods, for example, is disclosed by Unexamined-Japanese-Patent No. 4-189740. The food tray is a fibrous web composed of cellulose-based natural fibers, cellulose-based regenerated or semi-synthetic fibers, or mixed fibers thereof, and is bonded with a binder between fibers mainly composed of chitosan salts, and with respect to 100 parts by weight of the fibers. It consists of a biodegradable nonwoven fabric having a weight of 200 g / m 2 or more with 1 to 10 parts by weight of a water repellent attached thereto, and is formed in the form of a plate press-molded to an apparent density of 0.2 g / cm 3 or more.
    However, in the conventional disposable container, in order to improve the fluidity during molding, a resin material which can only be biodegraded is added, so that environmental pollution occurs when these containers are disposed of. In addition, the conventional degradable container has a drawback in that it does not have sufficient mechanical properties such as sufficient rigidity, strength, shape retention properties and the like. In addition, the molded article produced by the method for producing a decomposable container can maintain the shape only when the cover layer is provided.
    On the other hand, the conventional disposable container does not have sufficient strength of the product, and in the case of being used as a food container, for example, in the case of transporting liquid or snow mono (cooked with vinegar) to the food container, the shape of the container itself is used. Problems such as swelling, weakening of the shape retention, and the container itself absorbing moisture caused discoloration of the surface.
    In addition, when molding using a biodegradable material including a sheet material in order to increase the strength of the container, the non-sheet material is coated on the sheet material, or the sheet is placed on the surface of the intermediate molded body which is a non-sheet material, and the like is molded. Since the sheet material and the non-sheet material were not integrated and molded, there was a problem in terms of weight reduction and thinning, and a problem such as deterioration in productivity occurred.
    An object of the present invention is to solve the above problems, and after the material constituting the article such as a container disposes the article, the article material decomposes in a short period of time by decomposing by microorganisms, sunlight, ultraviolet rays, etc. The present invention provides a biodegradable composition and a container made of the composition, which are decomposed, and the decomposition substance plays a role of a soil improving material and the like, and also has excellent mechanical properties such as rigidity, strength, shape retention, and the like.
    Another object of the present invention is to uniformly mix a raw material mixture obtained by grinding each plant raw material and a biodegradable material, or to add a sheet-like woven fabric and / or nonwoven fabric made of a biodegradable material to the raw material mixture, and in some cases, bleach sterilization. The container material is easily decomposed by microorganisms in a short time after disposal, without incineration of the composition constituting the molded container by compression molding by heating and pressing a material such as water resistance, heat resistance, etc. It decomposes and decomposes into H 2 O, CO 2 , etc. by action, sunlight, ultraviolet rays, etc., thereby decomposes into harmless soil, and the decomposed substance can act as a soil improving material, and at the same time, the weight of the container itself, weight reduction, productivity Biodegradable materials with excellent mechanical properties such as stiffness, strength, shape retention, water resistance and heat resistance It is to provide a method for producing a group.
    1 is a block diagram showing the manufacturing process of the container in the method for producing a biodegradable material container according to the present invention,
    Figure 2 is a schematic explanatory diagram showing a manufacturing apparatus used in the method for producing a biodegradable material container according to the present invention,
    Figure 3 is a block diagram showing an embodiment of the manufacturing process of the container in the method for producing a biodegradable material container according to the present invention,
    4 is an explanatory view showing a step of manufacturing a container made of a woven fabric and / or a nonwoven fabric in the method for producing a biodegradable material container according to the present invention;
    5 is a schematic explanatory diagram showing an embodiment in which a controller is installed in the manufacturing apparatus of FIG.
    Figure 6 is a block diagram showing another embodiment of the manufacturing process of the container in the method for producing a biodegradable material container according to the present invention,
    Figure 7 is a block diagram showing another embodiment of the manufacturing process of the container in the method for producing a biodegradable material container according to the present invention,
    8 is a schematic explanatory diagram showing an embodiment of a manufacturing apparatus for achieving a method for producing a biodegradable material container according to the present invention,
    9 is a schematic explanatory diagram showing an embodiment of a heating and pressing device in the production apparatus for achieving the method for producing a biodegradable material container according to the present invention;
    10 is a schematic explanatory diagram showing an embodiment of a manufacturing process by another material in the method of manufacturing a biodegradable material container according to the present invention;
    11 is an explanatory view showing a manufacturing process of another embodiment of the method for producing a biodegradable material container according to the present invention.
    The present invention relates to a biodegradable material composition composed of a mixture of a plant raw material comprising chaff as a main component and a biodegradable material including a binder.
    The blending ratio of the mixture is composed of 60 to 90% of the powder of the plant material and 10 to 40% of the biodegradable material. In addition, water may be added to the mixture.
    In addition, the biodegradable material is composed of shellac, rosin, dammar, copal, gelatin, starch, calcium carbonate, biodegradable plastics or mixed powder thereof. In the biodegradable material, the binder is composed of shellac, rosin, dharma, cow pearl, gelatin, starch or mixed powder thereof.
    This biodegradable composition is made at the same price as the market price compared to the materials used to make articles such as containers used in everyday life, and can be converted into harmless soil that is biodegradable and returned to the soil. Since the time for incineration, recycling, etc. after use can be omitted, and it can be used as a soil improvement material for crops, a container or a pot of low price can be provided as a whole.
    The mixed material may be mixed with an antioxidant preservative and / or bleach. In particular, the mixture is mixed with a woven and / or nonwoven made of a biodegradable material.
    The present invention also relates to a biodegradable material container produced by compression molding the biodegradable material composition by heating and pressing using the biodegradable material composition described above.
    On the other hand, the present invention is a process for producing a mixed raw material powder uniformly mixed with a biodegradable raw material powder obtained by grinding a biodegradable material including a plant raw material powder and a binder containing a chaff as a main ingredient, and then the mixed raw material The present invention relates to a method for producing a biodegradable material container, which comprises a step of compression molding a powder into a shape of a container by heating and pressing.
    The method for producing a biodegradable material container is prepared by heating and pressing the mixed raw material powder to produce an intermediate molded product, and then placing a woven and / or nonwoven fabric made of biodegradable material on the surface of the intermediate molded product to produce a molded product. In addition, the molded body may be compression molded into a predetermined shape by heating and pressing.
    Alternatively, in the method for producing a container for degradable material, the slurry made of the mixed raw material powder is applied to a woven fabric and / or a nonwoven fabric made of a biodegradable material to be dried to prepare a sheet material, and the mixed material is laminated on the sheet material. Compression molding by heat and pressure integrally.
    In addition, the present invention is applied to the deposition or precipitation of a sheet fiber woven and / or non-woven fabric consisting of biodegradable material of the plant fiber powder material, the shellac powder and / or shellac solution and / or biodegradable wax mainly composed of chaff The present invention relates to a method for producing a biodegradable material container made by impregnating and drying to prepare a sheet member, and then compressing the sheet member into a container having a predetermined shape by heating and pressing.
    To the slurry, inorganic fillers such as titanium oxide and calcium carbonate or talc and / or mica are added.
    In addition, the shellac powder and / or shellac solution at least function as a binder and a water resistant material. The titanium oxide functions at least as a deodorant and a bleach disinfectant, and the biodegradable wax at least functions as a water resistant material, a release material and a water repellent material. For example, when the container is used as a tableware or the like, it is effective to add titanium oxide as an odor remover or a sterilizing agent to remove or sterilize odors such as rice hulls.
    The sheet member to be compression molded is composed of one sheet or a plurality of stacked sheets. Further, in the step of laminating the sheet member, a filler including biodegradable materials such as the plant fiber powder material, the sheet-like woven fabric and / or nonwoven fabric is interposed between the sheet members, and the heat shield and heat resistance of the container are appropriately interposed. , Thickness and strength can be adjusted. For example, when the filler is made of a porous body, an air layer is formed in the porous portion, and heat shielding can be significantly improved.
    The biodegradable wax and the silicone coating agent are applied to the surface of the container in which the sheet member is hot-pressed.
    The plant fiber powder material is composed of pulverized powder pulverized into 50 ~ 350 mesh. In addition, the conditions for compression molding by heating and pressing of the sheet member may be set in a range of, for example, a temperature of 100 to 250 ° C., a pressure of 30 to 200 kg / cm 2, and a molding time of 3 to 60 seconds.
    The slurry is 40 to 90% of the plant fiber powder, 5 to 40% of the shellac solution, 1 to 30% of the titanium oxide, 1 to 40% of the biodegradable wax, 1 to 20% of the calcium carbonate and the balance of water or It is prepared by mixing organic solvents.
    In the plant fiber, the chaff has a raw material selected from plant materials such as bamboo, sugar cane, straw, palm trees, bagasse, squirrel, kenaf, cotton flakes, pulp, and mixtures of two or more thereof. Plant fiber materials, such as these, are added. In addition, the chaff can be used chaff separated from brown rice by the rice paddy of dry rice.
    The slurry is added with a binder selected from cow pearl, rosin, distilled toll oil, tall oil fatty acid, terpene polymer, starch, gelatin, casein, dharma, gum arabic, gilsonite and two or more kinds thereof.
    The step of impregnating the slurry into the sheet member is accomplished by passing the sheet member, which is sequentially released from the bobbin, in the state immersed in the slurry contained in the tank.
    The manufacturing method of this container manufactures a sheet member by drying the slurry containing at least the chaff-based plant fiber powder material, shellac powder, and / or shellac solution, and biodegradable wax, and then subjecting the sheet member to heat and pressure. By compression molding into a container having a predetermined shape.
    The process of manufacturing the sheet member by the slurry is accomplished by depositing a screen in the slurry contained in the tank, spreading the slurry onto the screen to pull the screen out of the tank, and drying the slurry.
    The chaff used here does not need to be washed or dried sterilized, and can be sufficiently sterilized at the time of the heat molding of the mixed material.
    The container preferably has a thickness of 0.5 mm or more in terms of strength and point of use, and preferably an inclination angle of 15 ° or more, but can be molded into a flat plate shape.
    In this method for producing a biodegradable container, for example, a slurry made of the mixed material is applied to the woven fabric and / or the nonwoven fabric and dried to produce a sheet, and the material obtained by laminating the mixed material on the sheet material has a predetermined shape. Press molding.
    This biodegradable material composition is composed entirely of biodegradable material, and in particular, can constitute a product having strength by the action of a woven fabric and / or a nonwoven fabric.
    This container is manufactured by bonding with a binder of a biodegradable material, which has a chaff as its main component, increases its strength with a woven fabric and / or a nonwoven fabric in an extremely simple manufacturing process.
    The biodegradable wax and the silicone coating agent are applied to the surface of the container in which the sheet member is hot-pressed. In addition, the biodegradable wax is added with a material selected from natural waxes such as animal and vegetable wax, mineral wax, petroleum wax and the like or two or more kinds thereof. The biodegradable wax generally does not have heat resistance to high temperatures, but in the field of use of the container, it is preferable to coat the surface of the container in order to improve water resistance.
    In this container manufacturing method, the step of manufacturing the sheet member from the slurry includes immersing a screen in the slurry contained in the tank, spreading the slurry onto the screen to pull the screen out of the tank, and By drying.
    The step of impregnating the slurry into the sheet member is accomplished by passing the sheet member, which is sequentially released from the bobbin, in the state immersed in the slurry contained in the tank.
    Since the manufacturing method of this biodegradable material container is comprised as mentioned above, since shellac (shellac powder and / or shellac solution) has water resistance and heat resistance, and since biodegradable wax has water resistance, it is used as a food container. The container can provide a preferable container without absorbing moisture and causing swelling without causing discoloration or deterioration.
    In addition, by laminating at least two sheets of sheet members impregnated with a slurry made of a biodegradable material, shape retention and strength of the container can be ensured, and a preferable container can be manufactured.
    That is, since it is also possible to manufacture a container by laminating | stacking 1 or 2 sheet members or more, it is possible to adjust the stacking number of sheets according to the use of a container, and to adjust the intensity | strength of a container or the degree of water resistance. In addition, since the biodegradable material can be sandwiched between the sheets to be laminated, the container can be made to have different functions, for example, heat shielding and heat resistance, depending on the properties of the material to be inserted while having a thickness in the container.
    On the other hand, the manufacturing method of this container adds a bleach disinfectant and a titanium oxide which has an odor removal effect, and a biodegradable wax which raises mold release property, water repellency, fluidity, or gloss as a biodegradable material, and can raise a characteristic of a container.
    The manufacturing method of this container is constructed as described above, and a sheet member impregnated with a slurry made of a biodegradable material is produced into a sheet member, or the slurry is filtered to produce a sheet member, and the sheet member is compressed by heating and pressing. Since the container is manufactured by molding, the strength can be improved compared to the conventional product, and the weight and thickness of the container can be reduced. In addition, in the production of the container, the effect of productivity is also obtained due to the convenience of handling.
    Moreover, this container can be used as a tableware, a dish tray, a vegetation pot, a container for storing various materials, and after being used as a food container, even if the container itself is left or discarded, the material constituting the container itself can be microorganisms. It can be biodegraded by light, or decayed by sunlight, especially ultraviolet light, and returned to the soil, so that it can be converted into harmless soil, water, or carbon dioxide. Therefore, there is no need to incinerate or recycle the container, and the processing thereof can be omitted. Biodegradable soils can also be used as soil improvers for crops.
    In addition, the container manufactured by this manufacturing method can provide a very cheap container as a whole because the container itself has the same function as the market price and has the above functions.
    Hereinafter, each Example of the biodegradable material composition which concerns on this invention, and the container shape | molded by this composition is demonstrated.
    The biodegradable composition according to the present invention can be used in containers for plant cultivation, such as pots, pots, vegetation pots, as well as tableware, containers, packaging boxes, bowls, sacks, plant raw material powder 60-90 It consists of the mixture which mixed 10-40% of biodegradable substances containing a binder with%, and the mixture which added water depending on a raw material. In addition, the material which is the main raw material constituting the biodegradable material composition is disintegrated by the decomposition action of the microorganisms, sunlight, ultraviolet rays and the like, converted into harmless soil, and can be used as a soil improving material.
    In addition, the plant raw material is added to the chaff, raw materials such as plant fiber material selected from bamboo, sugar cane, straw, pulp and two or more kinds of mixed raw materials thereof. That is, the plant raw material may be composed of only chaff, but may be blended with chaff, such as straw, pulp and plant fiber.
    Biodegradable materials may be rosin, dharma (natural resin), copearl (natural resin), gelatin, starch, shellac, biodegradable plastics, calcium carbonate or mixed powders thereof, among which rosin, dharma, cow pearl, Gelatin, starch and shellac function as binders.
    On the other hand, it is also possible to mix the oxidizing preservative and / or bleaching agent in the mixture consisting of plant raw materials and biodegradable raw materials. As rice hulls, rice husks separated from brown rice may be used by rice paddy of dried rice, and other drying treatments may be omitted.
    The chaff functions as an extender constituting an article such as a container, and they are themselves biodegradable and may be contained in a large amount at 60 to 90%, preferably 65 to 85% for cost reduction.
    Calcium carbonate contained in the biodegradable material composition has a natural decay, can reduce the cost, improve the heat resistance of the container and increase the hardness, but since the fluidity deteriorates in the molding, it is necessary to adjust the amount according to the product. There is a limit.
    The biodegradable plastics constituting the biodegradable material composition are composed of a biodegradable aliphatic polyester, a biodegradable aliphatic polyether, and the like, and for example, polycondensation of polyols such as 1,4-butanediol with dicarboxylic acids such as succinic acid and adipic acid. There is an aliphatic polyester obtained by the reaction.
    Shellac is a kind of natural resin, which has thermosetting properties, is naturally decomposed and biodegradable, and is used as a powder for uniformly mixing with plant raw materials. Shellac can be dissolved in alcohol and melted by heat, and can be used as an alcohol solution (25 to 50%) or an aqueous solution (25%), and can be used in a liquid phase.
    Rosin, which functions as a binder, is a natural resin and is naturally disintegratable. However, the rosin has a low bonding strength and heat resistance.
    Gelatin is a kind of animal protein and biodegradable. However, gelatin has low binding and heat resistance properties, and therefore, the amount of gelatin needs to be adjusted in consideration of this point.
    Starch is biodegradable and can be obtained inexpensively, but there is a property of low bonding strength and heat resistance. Therefore, it is necessary to adjust the amount of addition in consideration of this point.
    In this biodegradable material composition, the first embodiment consists of 80% of chaff as a plant material and 20% of starch as a biodegradable material as a blending ratio between the plant raw material and the biodegradable material. The second embodiment is composed of 70% chaff as a plant material, 20% starch as a biodegradable material and 10% calcium carbonate as a blending ratio between a plant material and a biodegradable material. The third embodiment consists of 80% chaff as a plant material and 20% shellac as a biodegradable material as a blending ratio between the plant raw material and the biodegradable material. The fourth embodiment is composed of 85% chaff as a plant material, 5% shellac as a biodegradable substance, and 10% such as calcium carbonate as a blending ratio between a plant raw material and a biodegradable substance. The shellac used here is a shellac solution dissolved in alcohol, which is coated on the surface of the rice hull molded body. The fifth embodiment is composed of 80% chaff as a plant material and 20% rosin as a biodegradable material as a blending ratio between a plant raw material and a biodegradable material. The sixth embodiment is composed of 80% chaff as a plant material and 20% gelatin as a biodegradable material as a blending ratio between the plant raw material and the biodegradable material. On the other hand, the seventh embodiment is composed of 70% chaff as a plant material, 20% aliphatic polyester as a biodegradable substance, and 10% calcium carbonate including a binder as a blending ratio between a plant raw material and a biodegradable substance.
    Next, with reference to FIG. 1 and FIG. 2, the Example of the manufacturing method of the biodegradable material container by this invention is demonstrated.
    The container 1 manufactured by this manufacturing method can be used in a container for plant cultivation, such as a flower pot, a vegetation pot, as well as a tableware, a container, a box for packaging, a container, a pouch, etc. It is manufactured. The material which is the main raw material which comprises the container 1 is disintegrated by microorganisms, daylight, ultraviolet rays, etc., and is converted into a harmless soil.
    The manufacturing method of the container (1) is a process for producing a mixed raw material powder in which the plant raw material powder containing chaff as a main component and the biodegradable raw material powder obtained by grinding the biodegradable material including a binder are uniformly mixed; Subsequently, the mixed raw material powder is pressurized by a press and press-molded into a container. First, a plant raw material mainly containing chaff is selected (step 10), and the selected plant material is pulverized into a 50 to 300 mesh using a grinder or the like (step 11) to prepare a plant raw powder (step 12). Meanwhile, a biodegradable material including a binder is selected (step 13), the selected biodegradable material is pulverized into a 50 to 300 mesh using a grinder or the like (step 14), and a biodegradable raw material powder is prepared (step 15).
    Subsequently, the plant raw material powder and the biodegradable raw material powder are blended at a predetermined ratio, and uniformly mixed by a mixer or the like to prepare a mixed raw material powder (step 16). At this time, the mixed raw material powder may be mixed at a blending ratio of 60-90% plant raw material and 10-40% biodegradable material in terms of maintaining the shape of the container, preferably 65-85% plant raw material and 15 biodegradable material It is preferable to mix at a compounding ratio of -35%.
    In preparing a mixed raw material powder when the mixed raw material powder is pressurized by compression using a molding apparatus, a predetermined amount of water may be added depending on the selected raw material. At this time, of course, some materials do not need to be added depending on the selected material. Next, the mixed raw material powder is filled between the upper mold 2 and the lower mold 3 using a predetermined molding apparatus such as a molding apparatus as shown in FIG. 2, and the upper mold 2 and the lower mold. While energizing the heater 4 provided with respect to the mold 3, the press 5 is operated, and a load P is applied to compress the molded raw powder by heating and pressing (step 17). At this time, the molding apparatus is preferably set so that the molding temperature is within a range of 100 to 200 ° C, a molding pressure of 20 to 80 kg / cm 2, and a molding time of 3 to 30 seconds. In addition, although the thickness of the container 1 formed by compression molding of the mixed raw material powder can be set in various ways, it is preferable to mold to a thickness of 0.5 mm or more in terms of mechanical properties such as strength and shape retention of the container 1. Preferred (step 18).
    Although the container 1 can manufacture a flat plate shape, when using it as a tableware, it is preferable for the strength and practical use to shape the inclination angle to 15 degrees or more.
    The biodegradable material comprising the plant raw material and the binder for producing the container 1 is the same as the material of the composition.
    Plant raw materials, such as rice hull, comprise the extender which comprises the container 1 here, and are biodegradable and can be contained in large quantities at 60 to 90%, preferably 65 to 85% for cost reduction.
    As a specific example of the raw material used by the manufacturing method of the container 1, the thing of 1st Example-7th Example of said biodegradable material composition can be used.
    Next, with reference to Figs. 3 to 5, another embodiment of a biodegradable material composition according to the present invention, a biodegradable material container made of the composition, and a method for producing the same will be described.
    The biodegradable composition of this embodiment is composed of a woven and / or nonwoven fabric composed of a plant material powder obtained by grinding a plant material mainly composed of chaff, a binder composed of a biodegradable material, and a biodegradable material. As the binder of the biodegradable material, one similar to the above embodiment can be used.
    The container 1 of this embodiment is manufactured using the biodegradable material composition.
    Since the container 1 can be increased in strength by adding a woven fabric and / or a nonwoven fabric, even if a thin thickness is formed, sufficient strength as a container can be secured, thus reducing the amount of the mixture itself composed of chaff and rosin. The weight of the container itself can be reduced, and the weight of the container can be achieved. The container 1 can also be used as a container for plant cultivation such as a flower pot, a vegetation pot, as well as a tableware, a container, a box for packing, a bowl and a pouch.
    The method for producing a biodegradable material container includes a woven fabric and / or a nonwoven fabric (8) made of a biodegradable substance on a mixture (7) in which a binder made of a biodegradable substance is added to a plant material powder obtained by grinding a plant raw material mainly composed of chaff. The material is manufactured by adding the material, and the material is press-molded into a predetermined shape to produce a container.
    The container 1 is, for example, coated with a woven fabric and / or non-woven fabric 8 shown in Figure 4 (A), as shown in Figure 4 (B) a slurry consisting of the mixture material 7, these are molded by pressing to dry the sheet Ash 9 is prepared. Subsequently, as shown in FIG. 4 (C), the mixed material 7 is laminated on the sheet material 9, and this is heated and press-molded into a predetermined shape to produce the container 1 shown in FIG. 4 (D).
    The manufacturing method of the container 1 consists of the raw material powder mixture 7 which mixed 60-90% of the plant raw material powders of the ground material which grind | pulverized the plant raw material which consists of rice hulls, and 10-40% of binders of a biodegradable substance. have. In some cases, it is composed of a slurry in which water is added to the mixed material 7. The main ingredient of the material constituting the vessel (1) is collapsed by or decomposed by the microorganisms, or daylight, UV light, which would call the soil a harmless, H 2 O, CO 2.
    In this embodiment, the conditions of the compression molding by the plant raw material powder and the heating press are the same as the above embodiment.
    Next, the manufacturing process of the container 1 is demonstrated with reference to FIG.
    This manufacturing method comprises the steps of preparing a mixed raw material powder obtained by uniformly mixing a raw material powder obtained by crushing a plant raw material containing chaff as a main component and a biodegradable raw material powder obtained by grinding a binder of a biodegradable substance, and then the mixed raw material powder It consists of the process of pressing by heating with a pressurization apparatus and compression molding into a container. In addition, a plant raw material mainly containing rice husk is prepared (step 20), and the prepared plant material is pulverized with a mill or the like in a 50 to 300 mesh (step 21) to prepare a plant raw material powder (step 22). Meanwhile, a binder of biodegradable material is prepared (step 23), and the prepared biodegradable material is pulverized with a mill or the like in a 50 to 300 mesh (step 24) to prepare a biodegradable raw material powder (step 25).
    Subsequently, the plant material powder and the biodegradable binder are blended in a predetermined ratio, and uniformly mixed by a mixer or the like to prepare a mixture 7 (step 26). In this case, the blending ratio of the mixed raw material powder is composed of 60 to 90% of the plant raw material and 10 to 40% of the binder from the viewpoint of maintaining the shape of the plant raw material powder of the rice hull and the raw material powder of the binder, preferably 65 to plant material It is preferable to comprise 85% and 15 to 35% of a binder. In this production method, when the mixed raw material powder is heated and pressurized to compression molding, a slurry is prepared by adding a predetermined amount of water, depending on the raw material selected in producing the mixed raw material powder. At this time, of course, some materials do not need to be added depending on the moisture content of the selected material.
    On the other hand, the woven fabric and / or the laminated nonwoven fabric 8 which consist of a biodegradable substance are prepared (step 27). And as shown to Fig.4 (A), the woven fabric and / or the laminated nonwoven fabric 8 are arrange | positioned on the lower mold | type 3, for example. As shown in Fig. 4B, a slurry of the mixed material 7 uniformly mixed is applied to the woven fabric and / or the laminated nonwoven fabric 8, and then the woven fabric and / or the laminated nonwoven fabric coated with the mixed material 7 are applied. The pressurizing device 5 is operated with respect to (8), a load P is applied to the upper die 2, and press molding is performed by pressing, and the press-formed sheet member 9 is dried and solidified (step 28). Subsequently, the mixed material 7 consisting of plant raw material and rosin is laminated on the dried sheet material 9. These are arranged on the lower mold 3, energize the heater 4 provided with the upper mold 2 and the lower mold 3, and simultaneously operate the pressurizing device 5, and apply a load P to the upper mold 2 Molding by heating and pressing (step 29), the biodegradable material container 1 is prepared (step 30).
    When rosin of biodegradable material is used as the binder, the rosin has low heat resistance, so that the pressurizing time and the forming temperature are controlled by the controller 6 in order to prevent melting and increasing the molding time.
    The molding temperature sets the heating temperature of the upper mold | type 2 of a metal mold | die to 160-170 degreeC, and the heating temperature of the lower mold | die 3 of a metal mold | die is 150-160 degreeC by the controller 6, for example. In this embodiment, although the upper mold | type 2 is set to higher temperature than the lower mold | type 3, since the molded article remains in the low temperature side mold | die at the time of heat-pressing the mixed material 7, in this embodiment, the molded article is a lower mold | type. Remain in (3). When the temperature of the upper mold (2) and the lower mold (3) is set to 150 ° C. or less, the adhesion reaction between the rice hull particles by rosin becomes slow, and the molding time becomes longer, and the bondability of the rice hull deteriorates. And the molded article may be defective. If the temperature of the upper mold | type 2 and the lower mold | type 3 is set to 170 degreeC or more, the phenomenon that a molded article will be pressed when a molding time becomes a little longer may arise. Therefore, as long as the molding time is about 30 seconds, the molding temperature is preferably about 150 to 170 ° C.
    The molding pressure is preferably about 10 to 80 kg / cm 2 in relation to the molding temperature of the mold and the molding time. On the other hand, although the thickness of the container 1 formed by the press molding of the mixed material 1 can be set in various ways, it is preferable to mold to the thickness of 0.5 mm or more, and the point of mechanical characteristics, such as strength of the container 1, shape maintenance, etc. Preferred at
    In addition, plant raw materials such as rice hull constituting the extender constituting the container, the same as the material of the composition can be used, and is biodegradable, for cost reduction, 60 to 90%, preferably 65 to 85 It can be contained in% by the tea.
    Next, with reference to FIG. 6, another Example of the manufacturing process of a container in the manufacturing method of this biodegradable material container is demonstrated.
    Since this embodiment is the same as the manufacturing process up to step 26 of the above embodiment, the description is omitted here. In step 26, the plant material powder and the biodegradable binder are blended in a predetermined ratio, and the mixture is uniformly mixed by a mixer or the like by heat and pressure molding to prepare an intermediate molded body (step 31). On the other hand, the woven fabric and / or the laminated nonwoven fabric 8 which consist of a biodegradable substance are prepared (step 32). For example, as shown in FIG. 5, the molded body is prepared by arranging the intermediate molded product on the lower mold 3 and the nonwoven fabric laminated and / or laminated on the intermediate molded product. Next, while energizing the heater 4 provided in the upper mold | type 2 and the lower mold | type 3, the pressurization apparatus 5 is operated, the load P is applied to the intermediate | mold body, the woven fabric, and / or the laminated nonwoven fabric. The heat press molding is carried out by heating and pressing (step 33) to prepare a biodegradable container 1 (step 34).
    Hereinafter, another embodiment of the method for producing a biodegradable material container according to the present invention will be described with reference to FIGS. 7 to 10.
    As shown in FIG. 7, the method for preparing the biodegradable material composition includes shellac powder and / or shellac solution as a plant fiber powder material, a binder, a water-resistant material, and a heat-resistant material, which is crushed at least chaff, and a biodegradable wax for improving water resistance. (Steps 41 to 43), and a mixture of them in a predetermined amount to knead to prepare a slurry (14). In this case, the slurry 14 can be added with odor remover, titanium oxide as a bleach disinfectant, and calcium carbonate (steps 44 and 45) as an extender. On the other hand, a sheet member made of a sheet-like woven fabric and / or nonwoven fabric made of a biodegradable material is prepared (step 47). The sheet member is applied to the slurry 14 by dipping or spraying (step 48), and the sheet member 11 in which the slurry 14 of the biodegradable material is impregnated into the sheet member is prepared (step 49). Subsequently, the sheet member 11 is dried (step 50), and the dried sheet member 11 is laminated in one sheet or two or more sheets (step 51). Subsequently, the laminated sheet member 11 is heated and press-molded into a predetermined shape (step 52), thereby producing a predetermined biodegradable material container 18 (step 53).
    In addition, in the process of laminating the sheet member 11, as shown in FIG. 10C, the filler 19 is appropriately interposed between the sheet members 11 to prevent heat shielding, heat resistance, thickness, and strength of the container 18. Can be adjusted. The filler 19 can be made of, for example, biodegradable materials such as plant fiber powder, sheet type woven fabric and / or nonwoven fabric, or mineral raw materials such as calcium carbonate, calcium hydroxide, calcium oxide, titanium oxide, mica powder and the like.
    Compression molding conditions by heating and pressing of the sheet member 11 vary depending on the mixing ratio of the material and the water content of the material. For example, the heating temperature is 100 to 250 ° C., the pressurization pressure is 30 to 200 kg / cm 2 and the molding time is 3 to 60. It can be set within the range of seconds and can be set similarly to the above embodiment.
    Slurry (14) consisting of a mixture of these raw materials has a blending ratio of 40 to 90% of plant fiber powder, 5 to 40% of shellac solution binder, 1 to 30% of odor removal and bleach disinfectant of titanium oxide, and 1 to 30% of biodegradable wax. It is prepared by mixing 40%, calcium carbonate 1-20% and the balance of water.
    Plant fiber powder is composed of pulverized powder pulverized to 50 ~ 350 mesh. In addition, to rice hulls, it is also possible to add a material selected from plant materials such as bamboo, sugar cane, straw, palm trees, vargas, wormwood, cotton crumb, kenaf (mallow and hibiscus), pulp, and mixtures of two or more thereof. It is possible. It is preferable to grind these plant materials into powder, but depending on the use of the container 18, the grinding | pulverization degree of a coarse state may be sufficient.
    Shellac may be added with a material selected from co-pearl, rosin, distilled toll oil, tall oil fatty acid, terpene polymer, starch, gelatin, casein, dharma, gum arabic, gilsonite and two or more kinds thereof as a binder.
    The sheet-like woven fabric and / or nonwoven fabric constituting the sheet member may be made of, for example, a cotton jet, cotton, hemp, jute, biodegradable resin, silk, or natural material such as a water jet, or a carbon fiber, It is made of glass fiber or the like. In addition, zeolite, activated carbon, etc. are added as an odor remover and a bleach disinfectant.
    Biodegradable waxes for enhancing the water resistance include, for example, materials selected from natural waxes such as animal and vegetable waxes, mineral waxes, petroleum waxes, and mixtures of two or more thereof. Biodegradable waxes are generally susceptible to heat and may dissolve upon contact with, for example, 100 ° C. or higher. Therefore, when coating the surface of the container 18, it is necessary to consider the use of the container 18. In the case where the biodegradable wax is applied to the surface of the container 18, it is preferable to use a silicone coating agent. In addition, an inorganic filler such as talc and / or mica is added to the slurry 14.
    In the process of impregnating the sheet member 11 with the slurry 14 prepared as described above, as shown in FIG. 8, the sheet member 11 is sequentially released from the bobbin 12 wound around the sheet member 11. This is accomplished by passing through the slurry 14 contained in the tank 13 in a state of being immersed. Moreover, the sheet member 11 immersed in the slurry 14 of the tank 13 is sent out by the feed roller 16, and is sent to the dryer 15 provided with the heater 27. As shown in FIG. In addition, the scraper 20 etc. can be provided in the vicinity of the front of the conveyance roller 16 etc. in order to adjust the thickness of the sheet member 11. By passing the sheet member 11 through the dryer 15, the slurry 14 impregnated into the sheet member 11 can be dried and solidified. What is necessary is just to advance the inside of the dryer 3 so that the sheet member 11 which impregnated the slurry 14 may be dried, for example at about 100 degreeC for 1-2 hours. As shown in FIG. 9, the dried sheet member 11 is controlled by the controller 26 by using a heat-forming press 17 formed of an upper mold 21 and a lower mold 22 having a heater 24. By controlling the temperature of the heater 24 and the pressing pressure by the pressurizing device 25, for example, under the conditions of the range of 100 to 250 ° C, 30 to 200 kg / cm 2 and 3 to 60 seconds, the press is repeated 1 to 3 times. It can shape | mold, Next, the edge part of the container 18 of a molded object is trimmed, and the container 18 is completed. At this time, the container 18 may be molded and taken out, and the remaining sheet member 11 may be disposed of or disposed of by winding in a bobbin.
    In the case of manufacturing the container 18, the container 18 can be manufactured by heating and pressing the sheet member 11, as shown in FIG. Or in the manufacturing method of this biodegradable material container, according to the container 18 used for the use which requires intensity | strength etc., as shown in FIG. (Two sheets in the drawing), the laminated sheet member 11 is heated and press-molded into a container 18 having a predetermined shape. The number of laminated sheets of sheets can be changed depending on the type of the container 18 to be manufactured. For example, it is also possible to laminate five sheets. Or in the manufacturing method of this biodegradable container, when manufacturing the container 18 which requires heat resistance, heat shielding, etc., the material which has such a function as shown in FIG. It is also possible to arrange between the sheet members 11 and to heat press-form the laminated sheet member 11 and the filler 19 at the same time. In addition, when the filler 19 is made of a porous material made of a fiber material or the like, air present in the porous portion forms a heat shielding layer, and the heat shielding properties can be significantly improved. For example, when a hot liquid or the like is put into the container 18, heat is removed from the outside of the container 18, and handling is easy.
    The container 18 can be used also for a container for plant cultivation, such as a flower pot and a vegetation pot, as well as a tableware, a container, a packaging box, a container, a bag, etc., for example. The material constituting the vessel 18 is decomposed by microorganisms, decomposed by sunlight, ultraviolet rays, or the like, converted to harmless soil, H 2 O, CO 2 , or returned to nature as a mineral.
    Next, another embodiment of the method for producing a biodegradable material container according to the present invention will be described with reference to FIG.
    This embodiment is a manufacturing method for forming the sheet member 30 by filtering the slurry itself into a sheet form without the use of a sheet-like woven fabric and / or a nonwoven fabric, for example, in the same manner as paper filtering. In other words, the method for producing the biodegradable container is dried by drying the slurry 14 containing at least a plant fiber powder material mainly composed of chaff, shellac powder and / or shellac solution, and biodegradable wax. ), And then the sheet member 30 is heated and press-molded into a container having a predetermined shape. In the manufacturing process of the biodegradable material container, for example, as shown in FIG. 11, the slurry 14 is placed in the tank 13 (step H), and the foot 13 is placed in the tank 13 in which the slurry 14 is contained. The screen 31 is immersed (step I), and a portion of the slurry 14 is moved to the diffusion state over the screen 31 by rocking the screen 31 (step J). The screen member 30 is lifted to attach the slurry 14 on the screen 31 in the form of a sheet to prepare a sheet member 30 (step K). Water is solidified by filtration from the sheet material 30 having the slurry attached to the screen 31 (step L), and the screen 31 is inverted to separate the sheet material 30 from the screen 31. The sheet member 20 is dried to manufacture the sheet member 11. The sheet member 30 is molded into the container 18 as shown in FIG.
    In this embodiment, as shown in FIG. 10C, the container 18 can be manufactured by stacking the sheet members 11 on which the sheet material 30 is dried. In the lamination step, the heat shielding, heat resistance, thickness and strength of the container 18 can be adjusted by appropriately interposing the filler 19 of the biodegradable material including at least the plant fiber powder material between the sheet members 11.
    According to the present invention, after a material constituting an article such as a container is disposed of the article, the article material is decomposed by harmless microorganisms, sunlight or ultraviolet rays and decomposed into harmless soil in a short period of time. A biodegradable composition and a container made from the composition are provided, which serve as ashes and also have excellent mechanical properties such as stiffness, strength and shape retention in use.
    权利要求:
    Claims (42)
    [1" claim-type="Currently amended] A biodegradable composition comprising a mixture of a plant raw material comprising chaff as a main component and a biodegradable substance including a binder.
    [2" claim-type="Currently amended] The biodegradable material composition according to claim 1, wherein the blending ratio of the mixture is composed of 60 to 90% of the powder of the plant material and 10 to 40% of the biodegradable material.
    [3" claim-type="Currently amended] The biodegradable material composition according to claim 1, wherein water is added to the mixture.
    [4" claim-type="Currently amended] The biodegradable material composition according to claim 1, wherein the plant raw material is blended with rice hulls, plant fiber which is a raw material selected from bamboo, sugar cane, straw, pulp and two or more kinds of mixed raw materials thereof.
    [5" claim-type="Currently amended] The biodegradable material composition according to claim 1, wherein the biodegradable material is made of rosin, dharma, cow pearl, gelatin, starch, shellac, calcium carbonate, biodegradable plastic, or a mixed powder thereof.
    [6" claim-type="Currently amended] [Claim 2] The biodegradable material composition according to claim 1, wherein in the biodegradable material, the binder is made of rosin, dharma, cow pearl, gelatin, starch, shellac or mixed powder thereof.
    [7" claim-type="Currently amended] The biodegradable material composition according to claim 1, wherein the mixed material is a mixture of an oxidizing preservative and / or a bleach.
    [8" claim-type="Currently amended] The biodegradable material composition according to claim 1, wherein the chaff is used as chaff separated from brown rice by rice paddy.
    [9" claim-type="Currently amended] The biodegradable material composition according to claim 1, wherein the mixed material contains a woven fabric and / or a nonwoven fabric made of a biodegradable material.
    [10" claim-type="Currently amended] A biodegradable material container produced by compression molding the biodegradable material composition according to any one of claims 1 to 9.
    [11" claim-type="Currently amended] A process of preparing a mixed raw material powder obtained by uniformly mixing a biodegradable raw material powder obtained by pulverizing a biodegradable material including a binder and a plant raw material comprising chaff as a main component, followed by heating and pressing the mixed raw material powder A method for producing a biodegradable material container comprising a process of compression molding into a shape of a container by using.
    [12" claim-type="Currently amended] The method of manufacturing a biodegradable material container according to claim 11, wherein water is added to the mixed raw material powder.
    [13" claim-type="Currently amended] 12. The method of claim 11, wherein the plant material powder and the biodegradable raw material powder are pulverized powders each pulverized into 50 to 300 mesh.
    [14" claim-type="Currently amended] The biodegradable material container according to claim 11, wherein the compression molding conditions of the mixed raw material powder are in the range of 100 to 200 DEG C, pressure of 20 to 80 kg / cm2, and molding time of 3 to 40 seconds. Manufacturing method.
    [15" claim-type="Currently amended] The method of manufacturing a biodegradable material container according to claim 11, wherein the thickness of the container formed by compression molding of the mixed raw material powder is 0.5 mm or more.
    [16" claim-type="Currently amended] The method of manufacturing a biodegradable material container according to claim 11, wherein the inclination angle of the container formed by compression molding of the mixed raw material powder is 15 ° or more.
    [17" claim-type="Currently amended] The method of manufacturing a biodegradable material container according to claim 11, wherein the mixed raw material powder is made by mixing 60 to 90% of the plant raw material and 10 to 40% of the biodegradable material.
    [18" claim-type="Currently amended] 12. The method for producing a biodegradable material container according to claim 11, wherein the plant raw material is blended with rice hulls, plant fiber which is a raw material selected from bamboo, sugar cane, straw, pulp and two or more kinds of mixed raw materials thereof. .
    [19" claim-type="Currently amended] 12. The method of claim 11, wherein the biodegradable material is shellac, rosin, dharma, cow pearl, gelatin, starch, calcium carbonate, biodegradable plastic, or a mixed powder thereof.
    [20" claim-type="Currently amended] 12. The method of claim 11, wherein the binder in the biodegradable material is shellac, rosin, dharma, cow pearl, gelatin, starch, or a mixed powder thereof.
    [21" claim-type="Currently amended] 12. The method of claim 11, wherein the mixed raw material powder is mixed with an oxidizing preservative and / or a bleaching agent.
    [22" claim-type="Currently amended] 12. The method for producing a biodegradable container according to claim 11, wherein the chaff is used as chaff separated from brown rice by rice paddy of dried rice.
    [23" claim-type="Currently amended] 12. The method of claim 11, wherein the mixed raw material powder is heated and press-molded to produce an intermediate molded body, and then a woven and / or nonwoven fabric made of biodegradable material is disposed on the surface of the intermediate molded body to prepare a molded body, and the molded body is A method for producing a biodegradable material container, characterized in that the compression molding by heating and pressing to a predetermined predetermined shape.
    [24" claim-type="Currently amended] The method of claim 11, wherein the slurry of the mixed raw material powder is applied to a woven fabric and / or non-woven fabric made of a biodegradable material and dried to prepare a sheet material, and the mixture is laminated on the sheet material to integrally have a predetermined shape Method for producing a biodegradable material container characterized in that the compression molding by heating and pressing.
    [25" claim-type="Currently amended] Plant fiber powder material consisting of chaff, shellac powder and / or slurry containing at least shellac solution and biodegradable wax is impregnated by sheet-like woven fabric and / or nonwoven fabric made of biodegradable material, followed by impregnation or drying. To produce a sheet member, and then press-molding the sheet member into a container having a predetermined shape by heating and pressing.
    [26" claim-type="Currently amended] The method of claim 25, wherein the slurry is added with inorganic filler such as titanium oxide and calcium carbonate.
    [27" claim-type="Currently amended] The shellac powder and / or shellac solution according to claim 26, wherein the shellac powder and / or shellac solution functions at least as a binder and a water resistant material, the titanium oxide at least functions as a deodorant and a bleach disinfectant, and the biodegradable wax is at least a water resistant material, a release material and a foot. A method for producing a biodegradable material container, which functions as a hand material.
    [28" claim-type="Currently amended] The method of manufacturing a biodegradable material container according to claim 25, wherein the compression molded sheet member is composed of one sheet or a plurality of stacked sheets.
    [29" claim-type="Currently amended] 29. The heat shielding property of a container according to claim 28, wherein in the step of laminating the sheet member, a filler including the plant fiber powder material, the sheet-like woven fabric and / or a biodegradable material of the nonwoven fabric is appropriately interposed between the sheet members. Method for producing a biodegradable material container, characterized in that to adjust the heat resistance, thickness and strength.
    [30" claim-type="Currently amended] The method for producing a biodegradable material container according to claim 25, wherein the biodegradable wax and the silicone coating agent are applied to the surface of the container in which the sheet member is hot-pressed.
    [31" claim-type="Currently amended] 26. The method of claim 25, wherein the plant fiber powder material is made of pulverized powder pulverized into 50 to 350 mesh.
    [32" claim-type="Currently amended] 27. The biodegradable material container according to claim 25, wherein the heat press forming conditions for the sheet member are in the range of 100 to 250 DEG C, pressure of 30 to 200 kg / cm < 2 > Manufacturing method.
    [33" claim-type="Currently amended] 27. The slurry of claim 25, wherein the slurry comprises 40 to 90% of the plant fiber powder, 5 to 40% of the shellac solution, 1 to 30% of the titanium oxide, 1 to 40% of the biodegradable wax, and 1 to 20 of the calcium carbonate. Method for producing a biodegradable material container, characterized in that it is prepared by mixing the% and the balance of water or organic solvent.
    [34" claim-type="Currently amended] 27. The material according to claim 25, wherein the chaff is added with a material selected from plant material such as bamboo, sugar cane, straw, palm tree, vargas, squirrel, kenaf, cotton crumb, pulp, and a mixture of two or more thereof. Method for producing a biodegradable container made of.
    [35" claim-type="Currently amended] The binder of claim 25, wherein a binder selected from co-pearl, rosin, distilled toll oil, tall oil fatty acid, terpene polymer, starch, gelatin, casein, dharma, gum arabic, gilsonite, and a mixture of two or more thereof is added thereto. Method for producing a biodegradable material container, characterized in that.
    [36" claim-type="Currently amended] 26. The method for producing a biodegradable container according to claim 25, wherein the slurry is added with a sterilizing agent for removing odor of zeolite and / or activated carbon.
    [37" claim-type="Currently amended] The method of claim 25, wherein the biodegradable wax is selected from natural waxes such as animal and vegetable waxes, mineral waxes, petroleum waxes, and mixtures of two or more thereof.
    [38" claim-type="Currently amended] 26. The method for producing a biodegradable container according to claim 25, wherein an inorganic filler such as talc and / or mica is added to the slurry.
    [39" claim-type="Currently amended] 26. The biodegradable material according to claim 25, wherein the step of impregnating the slurry into the sheet member is accomplished by passing the sheet member, which is sequentially released from the bobbin, in the state immersed in the slurry contained in the tank. Method for producing a container.
    [40" claim-type="Currently amended] A sheet member is prepared by drying a slurry comprising at least a chaff-based plant fiber powder material, a shellac powder and / or a shellac solution and a biodegradable wax, and then the sheet member has a predetermined shape by heating and pressing. A method for producing a biodegradable material container comprising compression molding into a container.
    [41" claim-type="Currently amended] 41. The method of claim 40, wherein in the step of laminating the sheet member, the heat shield, heat resistance, thickness, and strength of the container are adjusted by appropriately interposing a filler of biodegradable material including at least the plant fiber powder material between the sheet members. Method for producing a biodegradable material container, characterized in that.
    [42" claim-type="Currently amended] 41. The method of claim 40, wherein the manufacturing of the sheet member from the slurry comprises immersing a screen in the slurry contained in the tank, wherein the slurry diffuses over the screen, pulls the screen out of the tank, and dries the slurry. Method for producing a biodegradable material container characterized in that it is achieved by.
    类似技术:
    公开号 | 公开日 | 专利标题
    EP2608957B1|2017-05-03|Teabags and components of bi-component and mono-component pla and co-pla fibers
    EP1363981B1|2018-08-08|Compressed blends of coconut coir pith and non-coir/non-peat materials, and processes for the production thereof
    US8187514B2|2012-05-29|Biodegradable molded article
    EP0751855B1|2001-10-31|Process for the manufacture of shaped articles and product prepared therefrom
    TWI285585B|2007-08-21|Biodegradable or compostable containers
    US5354621A|1994-10-11|Biodegradable construction material and manufacturing method
    CN101095552B|2010-05-19|Tea container and method for preparing the same
    JP2012528008A|2012-11-12|Compressed biomass pellets and briquettes
    KR100566714B1|2006-04-03|Biodegradable molded article and manufacturing method thereof
    EP0474095B1|1995-11-02|Composition and process for forming biodegradable consumer products
    JP5224400B2|2013-07-03|Absorber, sanitary article using the absorber, and method for producing the same
    CN100404246C|2008-07-23|Biodegradable film
    CN101427648B|2011-06-01|Vegetation basis and method of production thereof
    EP1651727B1|2009-06-17|Naturally decomposing disposable tableware and manufacturing thereof
    CN100500748C|2009-06-17|Biodegradable starch bowl and method for preparing the same
    EP2862815B1|2017-03-22|Method for manufacturing a moulded fibre packaging and moulded fibre food packaging
    CN1284467A|2001-02-21|Bamboo container and its making process
    KR100574547B1|2006-04-27|Biodegradable composition having improved water resistance and method for producing same
    ES2281348T3|2007-10-01|Cellulosical and lignocellulic materials texturized and compositions and compounds of these.
    WO2014184273A1|2014-11-20|Biomaterial product based on sunflower seed shells and/or sunflower seed hulls
    CN102977623B|2015-11-25|The manufacture craft of a kind of vegetable fibre synthetic resin powder and plant-fiber product
    TW308576B|1997-06-21|
    JP2010124804A|2010-06-10|Granular excrement-treating material, and method for producing the same
    JP4796541B2|2011-10-19|Method for producing a natural binder for ink production
    KR101708156B1|2017-02-17|Bio cellulose sheet, articles for bio cellulose sheet, and manufacturing methods thereof
    同族专利:
    公开号 | 公开日
    TW426594B|2001-03-21|
    CN1268531A|2000-10-04|
    引用文献:
    公开号 | 申请日 | 公开日 | 申请人 | 专利标题
    法律状态:
    1999-02-10|Priority to JP99-033420
    1999-02-10|Priority to JP3342099A
    1999-02-10|Priority to JP3337899A
    1999-02-10|Priority to JP99-033378
    1999-06-16|Priority to JP11169495A
    1999-06-16|Priority to JP99-169495
    1999-09-09|Priority to JP25536099A
    1999-09-09|Priority to JP99-255360
    2000-02-02|Application filed by 모리 테 쯔로오, 세이부덴키 가부시키가이샤, 오츠카 아키라, 후쿠오카 카세이 코교 가부시키가이샤
    2000-09-25|Publication of KR20000057885A
    优先权:
    申请号 | 申请日 | 专利标题
    JP99-033420|1999-02-10|
    JP3342099A|JP2000229312A|1999-02-10|1999-02-10|Manufacture of container made of biodegradable material|
    JP3337899A|JP2000229311A|1999-02-10|1999-02-10|Biodegradable material composition, container made therefrom, and soil conditioning material utilizing the composition|
    JP99-033378|1999-02-10|
    JP99-169495|1999-06-16|
    JP11169495A|JP2000355008A|1999-06-16|1999-06-16|Biodegradable material composition, container of biodegradable material made of this composition and manufacture thereof|
    JP25536099A|JP2001079816A|1999-09-09|1999-09-09|Manufacture of container made of biodegradable material|
    JP99-255360|1999-09-09|
    [返回顶部]