Amult-Fuaction A Box laying method dya loess

专利摘要:
The present invention removes ocher and moisture, and removes odors, charcoal and kaolin to improve the firmness. Pulp to enhance the binding strength with clay. fiber. straw. By mixing styrofoam and pine needle starch, which gives cohesion, and wormwood, which gives off the smell of herbal odor, it is possible to prevent the various forms of ossuary from corruption and reduce the production cost of the ossuary. By using raw ocher and charcoal as a main source without baking, it prevents the deterioration of the crypt and gives a strong impact effect twice as much as that of ceramics in terms of impact, thereby making it possible to manufacture rugged, beautiful and environmentally friendly crypt in various forms. have. The present invention is 70% ocher weight, 5% charcoal weight, kaolin. 10% clay weight, pulp. fiber. straw. Styrofoam 13% by weight, remainder pine needles. Wormwood. It is added and mixed using 2% by weight of starch lamp, and then uniformly molded into a certain size of crypt and generates heat by instant heat treatment. In addition, the present invention may be applied to the dried container by applying an emulsion to smooth the sub-surface by heat treatment at 500 ℃, or may be dried by applying a urethane or the like, it is characterized by having a silk fiber attached.
公开号:KR20000049399A
申请号:KR1020000007211
申请日:2000-02-11
公开日:2000-08-05
发明作者:오주희；오성배
申请人:오주희；오성배；
IPC主号:

专利说明:

Manufacture of multipurpose crypts using loess {Amult-Fuaction A Box laying method dya loess}
The present invention relates to a method for manufacturing multipurpose crypts using ocher and charcoal, and more particularly, to facilitate its molding without baking the crypts molded using ocher and charcoal, and at the same time, the impact is greatly strengthened to cause cracks or crumbs. The present invention relates to a method for producing multipurpose crypts using ocher and char as a mixed method of preventing.
In general, ocher absorbs moisture when it is wet and discharges water when it is dry, so it is not only excellent in humidity control but also has various beneficial and antibacterial ingredients. Charcoal is also known for its excellent efficacy as a dehumidifying and deodorizing and disinfectant.
It is a large object of the present invention to bind the above-mentioned loess, charcoal and use the compound for multi-purpose.
Until now, the reason why it was not possible to manufacture the ossuary using ocher is because it is difficult to manufacture it without baking because the cracks or cracks occur when the ocher is dried due to the lack of adhesion of the ocher.
Therefore, the present invention invented in view of the problems as described above, and the direct contact with the antimicrobial properties due to the decay of oak, charcoal, and charcoal can be mixed with charcoal to remove moisture and odor removal and kaolin, clay mixed It provides firmness, and combines pine needle starch, which gives cohesive strength to pulp, fiber, straw, and styrofoam with scent, and scented mugwort to produce urine box. It is an object of the present invention to provide a method for manufacturing a multi-purpose coarse bin which can greatly reduce energy saving in a solar drying manufacturing process.
In addition, the present invention is to classify and shape the body and the lid as described above to attach the surface to the surface of the lid of a predetermined size with jade, stainless, glass, wood, etc., or smooth the surface by a heat treatment process of 500 ℃ with emulsion coating or urethane, etc. The purpose of the present invention is to provide a multi-purpose manufacturing method using ocher charcoal that can be applied to smooth and display the beauty.
The present invention for achieving the above object is a predetermined size after mixing 70% ocher weight, 5% charcoal weight, 10% kaolin weight, pulp, fiber, straw 13% by weight of pine needles, mugwort starch 2% After molding to the molding die of the heat treatment step and drying step is characterized in that carried out for a predetermined temperature and time.
The present invention is also mixed with more than 100% of moisture in the process of heat treatment and drying the molded crypt and then heat-treated at 250 ℃ for 20-30 minutes in the heat treatment process and dried for 24 hours at 60 ~ 90 ℃ in the drying process Complete after drying for 48 hours in drying.
In addition, the present invention can change the various colors by coating the outside, the inside has the characteristics of giving the efficacy of ocher antibacterial and true charcoal as raw ocher.
Hereinafter, the manufacturing method according to the present invention will be described.
First, ocher and charcoal are the main ingredients, and pulp, fiber, straw, and styrofoam are mixed at a predetermined ratio. -Pulp, fiber, straw, and styrofoam play a role of preventing cracks or chipping. Pine needles, starch, and ginkgo leaves give cohesion, wormwood gives fragrance, and kaolin, clay gives firmness and impact. Will give an effect.
Then, the mold is sprayed according to a predetermined amount with a water sprayer and simultaneously sprayed evenly according to a predetermined amount to a predetermined stirrer. On the other hand, the reason for heating the water is to facilitate the mixing of pulp, straw, fibers and the like and other residues.
After the mixture is uniformly mixed as described above, the mixture is placed in a mold and molded in a predetermined box, followed by heat treatment at 250 ° C. for 20 minutes in the first heat treatment step, followed by drying at 60-90 ° C. for 24 hours in a drying step, Dry for 48 hours.
Then, the dried ossuary is coated by heat-treating the outer surface with latex coating or coated with lacquer and urethane, and the glass is attached to the glass, stainless steel, wood, stone, etc. to show the beauty.
Example
70% cotton bottom loess, 5% charcoal weight, kaolin. 10% clay weight, pulp. fiber. straw. 13% weight of styrofoam, mugwort. Starch. 2% by weight of ginkgo biloba is mixed with water and then mixed uniformly in a stirrer.
Then, put the mixture into the mold, and put the mixture of the predetermined shape into the mold to prepare a box of the predetermined shape, heat-treated for 20 minutes at 250 ℃ in the heat treatment process, and dried for 24 hours at 60 ~ 90 ℃ in the drying process 48 Drying was completed for time.
At this time, the instantaneous surface frictional heat coating in the drying process.
Therefore, the present invention is a baking method by producing a mixture of ocher and charcoal, and kaolin to improve the firmness, clay, pulp, fiber, straw, styrofoam, styrofoam, pine needles, ginkgo leaves, starch, wormwood to give cohesion Energy saving, waste prevention from bacteria and insects encroachment, and the impact effect is more than twice as strong as ceramics, it is very useful to increase the demand of ossuary sugar, which increases day by day.
The present invention is not limited to the preferred embodiments of the above-described characteristics, and various modifications can be made by those skilled in the art without departing from the gist of the present invention as claimed above. And such changes will fall within the scope of the claims.

权利要求:
Claims (4)
[1" claim-type="Currently amended] 70% ocher weight, 10% clay, kaolin weight, lump, fiber, straw, styrofoam 13% weight, uniformly add and mix ginkgo biloba, pine needles, mugwort, starch, etc. It is characterized in that the drying process is carried out for a predetermined temperature and time.
[2" claim-type="Currently amended] The method of claim 1
After applying the latex to the surface of the dried brick, heat-treated and coated with 500 ℃, urethane, lacquer, etc., the oak, charcoal manufacturing method characterized in that using the ocher, charcoal
[3" claim-type="Currently amended] The method of claim 1
Method for producing multipurpose crypts using ocher and charcoal with a thermal friction coating of 300 ° C. on a dried surface.
[4" claim-type="Currently amended] The method of claim 1
A method for manufacturing multipurpose crypts using ocher and charcoal, characterized by attaching any one of stainless steel, glass, wood, and stone to the dried crypts surface.

类似技术:

---

公开号 | 公开日 | 专利标题

---

KR100591783B1|2006-06-26|Finishing material composition for interior material and method of preparing the same

---

CN101541703B|2013-10-16|The production method of building materials and vessels using environment-friendly yellow earth

---

CN105623326B|2017-12-12|A kind of nanometer oyster shell whiting ecological functions bullet applies coating

---

KR100709064B1|2007-04-18|Ceramic block and its process

---

KR100822073B1|2008-04-15|Forming material including charcoal and manufacturing method thereof

---

KR101458065B1|2014-11-07|TThe method of eco-friendly natural heulpan

---

KR100987117B1|2010-10-11|Environment-friendly red clay mortar composition and constructing method of packing materials by using same

---

KR20050098417A|2005-10-12|Loess mortar composition for construction materials and coating method thereof

---

KR100881070B1|2009-01-30|Oker korean paper plate and the construction method using natural pulp and loess

---

KR20040004806A|2004-01-16|Manufacture method of improvement brick

---

KR100605660B1|2006-07-31|Natural adhesive agent for manufacturing wallpapre and method of manufacturing the same

---

KR100492412B1|2005-06-03|The constructed method of Hwang-To plate, wall, ground, and ceiling for health residence.

---

KR100811602B1|2008-03-11|Eco-friendly interior materials for building and method of fabricating therof

---

CN104526811B|2016-04-13|A kind of method of modifying of straw

---

KR101033205B1|2011-05-06|Composition for environment-friendly functional paint using volcanic stone

---

CN1920165A|2007-02-28|Bamboo charcoal printing textile and manufacture method thereof

---

KR101418231B1|2014-07-10|The manufacturing method of environment-friendly yellow soil panels for construction

---

KR20060110386A|2006-10-25|Coating materials for surface finishing of construction

---

CN105060812A|2015-11-18|Functional diatom decorative material capable of being scrubbed

---

KR100774087B1|2007-11-06|It and method for manufacturing loess-board with inside charcoal

---

KR101672337B1|2016-11-04|Manufacturing method of glaze

---

KR100910213B1|2009-07-31|The method of maunfacturing a natural painting composite

---

KR20050119781A|2005-12-22|Coating material for building interior and exterior and production method thereof

---

KR100964917B1|2010-06-23|Loess korean paper manufactural system

---

CN1393324A|2003-01-29|Multi-kinds of boards and board compositions using broken grass and wood and clay and its manufacturing method

同族专利:

---

公开号 | 公开日

---

引用文献:

---

公开号 | 申请日 | 公开日 | 申请人 | 专利标题

---

法律状态:
2000-02-11|Application filed by 오주희, 오성배

---

2000-02-11|Priority to KR1020000007211A

---

2000-08-05|Publication of KR20000049399A

优先权:

---

申请号 | 申请日 | 专利标题

---

KR1020000007211A|KR20000049399A|2000-02-11|2000-02-11|Amult-Fuaction A Box laying method dya loess|