    • 专利摘要:
    The present invention relates to a tire whose tread comprises a rubber composition based on at least one elastomer matrix comprising more than 50% by weight of an SBR solution which carries a silanol function and an amine function, a reinforcing filler. at a content of between 40 and 80 phr, which reinforcing filler comprises between 40 and 80 phr of a silica, a coupling agent for coupling the silica with the SBR solution, 10 to 50 phr of a hydrocarbon resin having a higher Tg at 20 ° C., 0 to less than 5 phr of a liquid plasticizer. Such a tire has a good compromise of performance between rolling resistance and wet grip.
    公开号:FR3021971A1
    申请号:FR1455096
    申请日:2014-06-05
    公开日:2015-12-11
    发明作者:Philippe Labrunie；Gaudemaris Benoit De
    申请人:Michelin Recherche et Technique SA Switzerland ；Compagnie Generale des Etablissements Michelin SCA；Michelin Recherche et Technique SA France；
    IPC主号:
    专利说明:

    [0001] The field of the invention is that of tires with low rolling resistance.
    [0002] A tire must obey in known manner a large number of technical requirements, often antinomic, among which low rolling resistance, high wear resistance, as well as high adhesion on dry and wet roads.
    [0003] This compromise of properties, in particular from the point of view of rolling resistance and wear resistance, has been improved in recent years on "green tires" with low energy consumption, especially for passenger vehicles. , thanks in particular to the use as tread of new weakly hysteretic rubber compositions having the characteristic of being reinforced mainly by specific inorganic fillers qualified as reinforcing agents, in particular highly dispersible silicas known as "HDS" (Highly Dispersible Silica), capable of to compete, from the point of view of reinforcing power, with conventional pneumatic grade carbon blacks.
    [0004] Treads for tire with low rolling resistance can be obtained by the joint use of silica and functional elastomers whose function is interactive with silica. By way of example, mention may be made of patents or patent applications EP 0 778 311 B 1, EP 0877 047 B 1 and WO 2008/141702, WO 2006/050486. A constant concern of tire manufacturers is to further reduce the rolling resistance of tires with low rolling resistance. It is possible to reduce the rate of reinforcing filler, especially silica, in the rubber composition of the tread of the tire to further improve the rolling resistance performance of the tire. But this solution generally has the disadvantage of reducing the wet grip of the tire.
    [0005] The Applicants have found a solution to this problem by specifically combining in a rubber composition reinforced with a tread silica a certain elastomer matrix, a specific reinforcing filler and a particular plasticizer system.
    [0006] Thus, the subject of the invention is a tire tread which comprises a rubber composition based on at least: an elastomer matrix comprising more than 50% by weight of an SBR solution which carries a silanol function and a function amine, P10-3330 - 2 - - a reinforcing filler present at a level greater than 40 phr and less than or equal to 80 phr, which reinforcing filler comprises between 40 and 80 phr of a silica, - a coupling agent, - 10 to 50 phr of a hydrocarbon resin having a Tg greater than 20 ° C, 0 to less than 5 phr of a liquid plasticizer. The invention also relates to a method for the tire according to the invention. The tires of the invention are particularly intended to equip tourism-type motor vehicles, as well as two-wheeled vehicles. The invention as well as its advantages will be readily understood in the light of the description and the following exemplary embodiments.
    [0007] DETAILED DESCRIPTION OF THE INVENTION In the present description, unless expressly indicated otherwise, all the percentages (%) indicated are% by weight. The abbreviation "pce" means parts by weight per hundred parts of the elastomeric matrix which consists of all of the elastomers present in the rubber composition. All values of glass transition temperature "Tg" are measured in a known manner by DSC (Differential Scanning Calorimetry) according to ASTM D3418 (1999). On the other hand, any range of values designated by the expression "between a and b" represents the range of values from more than a to less than b (i.e. terminals a and b excluded) while any range of values designated by the term "from a to b" means the range from a to b (i.e., including the strict limits a and b). I-1. Elastomer matrix: The SBR solution is a copolymer of styrene and butadiene prepared in solution. It has the essential characteristic of carrying a silanol function and an amine function. As SBR commercial solution carrying a silanol function and an amine function, mention may be made of the HPR340 elastomer from the company JSR.
    [0008] In general, a function carried by a solution SBR can be located on the elastomeric chain either at the end of the chain or inside the chain (that is to say outside the chain ends). The first case occurs for example when the SBR is prepared using a polymerization initiator carrying the function or using a functionalizing agent. The second case occurs for example when the SBR is modified by the use of a coupling agent or starring carrying the function. According to a preferred embodiment of the invention, the silanol function and the amine function are located outside the chain ends of the solution SBR.
    [0009] According to any of the embodiments of the invention, the amine function carried by the SBR solution is preferably a pendant group. The pendant position of the amine function means, in a known manner, that the nitrogen atom of the amine function does not interconnect between the carbon-carbon bonds of the elastomer chain of the SBR solution.
    [0010] According to a first variant of the invention, the silanol function carried by the SBR solution is a pendant group, which is to say that the silicon atom of the silanol function does not intercalate between the carbon-carbon bonds of the elastomer chain of the SBR solution. An SBR solution carrying a silanol pendant function can for example be prepared by hydrosilylation of the elastomeric chain with a silane bearing an alkoxysilane group, followed by hydrolysis of the alkoxysilane function in the silanol function. According to a second variant of the invention, the silanol function carried by the SBR solution is not a pendant group, but is located in the elastomeric chain, which amounts to saying that the silicon atom of the silanol function is intercalates between the carbon-carbon bonds of the elastomer chain of the SBR solution. Such an SBR solution may be prepared by coupling reaction of the elastomeric chains with a coupling agent bearing an alkoxysilane function and an amine function according to the procedure described in patent application EP 2 285 852, followed by hydrolysis of the function. alkoxysilane in silanol function. Suitable coupling agents are, for example, N, N-dialkylaminopropyltrialkoxysilanes, the dialkyl groups being C 1 -C 10, preferably C 1 -C 4, the compounds 3- (N, N-dimethylaminopropyl) trimethoxysilane, 3- (N, N) -dimethylaminopropyl) triethoxysilane, 3- (N, N-diethylaminopropyl) trimethoxysilane, 3- (N, N-diethylaminopropyl) triethoxysilane being more particularly preferred irrespective of the embodiment of the invention. This second variant is preferred and applies to any of the embodiments of the invention. According to the first or the second variant, the hydrolysis of the alkoxysilane function carried by the SBR solution in silanol function can be carried out according to the procedure described in the patent application EP 2,266,819 A1 or else by a step of stripping the solution containing the SBR solution. According to a preferred embodiment of the invention, the amine function is a tertiary amine. As tertiary amine function, there may be mentioned amines substituted by alkyl radicals in C1-C10, preferably alkyl in C1-C4, more preferably a methyl or ethyl radical whatever the embodiment of the invention. It is understood that the SBR solution may consist of a mixture of SBR solution, the SBR solution differing from each other by the chemical nature of the amine function, by their microstructure or by their macrostructure.
    [0011] According to any of the embodiments of the invention, the SBR solution preferably has a glass transition temperature below -40 ° C, more preferably between -70 ° C and -40 ° C.
    [0012] When the elastomer matrix of the composition of the tread according to the invention comprises a second elastomer, this second elastomer is preferably a diene elastomer. By elastomer (or indistinctly "rubber", the two terms being considered synonymous) of the "diene" type, it is to be understood in a known manner (one or more) elastomer derived at least in part (ie, a homopolymer or a copolymer) of monomers dienes (monomers bearing two carbon-carbon double bonds, conjugated or otherwise).
    [0013] These diene elastomers can be classified into two categories: "essentially unsaturated" or "essentially saturated". The term "essentially unsaturated" is generally understood to mean a diene elastomer derived at least in part from conjugated diene monomers, having a level of units or units of diene origin (conjugated dienes) which is greater than 15% (mol%); Thus, diene elastomers such as butyl rubbers or copolymers of dienes and alpha-olefins of the EPDM type do not fall within the above definition and may in particular be described as "essentially saturated" diene elastomers ( low or very low diene origin, always less than 15%). In the category of "essentially unsaturated" diene elastomers, the term "highly unsaturated" diene elastomer is particularly understood to mean a diene elastomer having a content of units of diene origin (conjugated dienes) which is greater than 50%. Although it applies to any type of diene elastomer, one skilled in the art of the tire will understand that the invention is preferably carried out with essentially unsaturated diene elastomers.
    [0014] These definitions being given, the term "diene elastomer" that may be used in the compositions according to the invention is understood to mean: (a) - any homopolymer obtained by polymerization of a conjugated diene monomer, preferably having from 4 to 12 carbon atoms; P10-3330 - (b) - any copolymer obtained by copolymerization of one or more conjugated dienes with each other or with one or more vinyl aromatic compounds preferably having from 8 to 20 carbon atoms.
    [0015] By way of conjugated dienes 1,3-butadiene, 2-methyl-1,3-butadiene, 2,3-di (C 1 -C 5 alkyl) -1,3-butadienes, such as for example 2 3-dimethyl-1,3-butadiene, 2,3-diethyl-1,3-butadiene, 2-methyl-3-ethyl-1,3-butadiene, 2-methyl-3-isopropyl 3-butadiene, aryl-1,3-butadiene, 1,3-pentadiene, 2,4-hexadiene. Suitable vinylaromatic compounds are, for example, styrene, ortho-, meta-, para-methylstyrene, the commercial "vinyl-toluene" mixture, para-tert-butylstyrene, methoxystyrenes, chlorostyrenes, vinylmesitylene, divinylbenzene, vinylnaphthalene. The second elastomer, when diene, is different from the SBR solution in that it does not carry both silanol function and amine function. Nevertheless it may have a microstructure or a macrostructure which may be identical to or different from that of the SBR solution. The second elastomer, whether diene or not, is used in a proportion of between 0 and 50%, preferably between 0 and 25%, more preferably between 0 and 10% of the mass of the elastomer matrix. In other words, the elastomer matrix comprises more than 50%, preferably more than 75% solution, even more preferably more than 90% by weight of the SBR solution, the 100% complement being constituted by the second elastomer. These preferred ranges apply to any of the embodiments of the invention. The second diene elastomer is selected from the group consisting of polybutadienes, natural rubber, synthetic polyisoprenes, butadiene copolymers, isoprene copolymers and mixtures of these elastomers.
    [0016] I-2. Reinforcing filler The rubber composition comprises any type of so-called reinforcing filler known for its ability to reinforce a rubber composition that can be used for the manufacture of a tread for tires. The level of reinforcing filler is greater than 40 phr and less than or equal to 80 phr. Such a reinforcing filler typically consists of nanoparticles whose average size (in mass) is less than one micrometer, generally less than 500 nm, the most often between 20 and 200 nm, in particular and more preferably between 20 and 200 nm. between 20 and 150 nm. The reinforcing filler has the essential characteristic of comprising between 40 and 80 phr of a silica. The silica used may be any reinforcing silica known to those skilled in the art, in particular any precipitated or fumed silica having a BET surface and a CTAB specific surface both less than 450 m 2 / g, preferably from 30 to 400 m 2 / g, especially between 60 and 300 m2 / g. As highly dispersible precipitated silicas (called "HDS"), mention may be made, for example, of the "Ultrasil" 7000 and "Ultrasil" 7005 silicas of the Degussa company, the "Zeosil" 1165MP, 1135MP and 1115MP silicas of the Rhodia company. "Hi-Sil" silica EZ150G from the company PPG, the "Zeopol" silicas 8715, 8745 and 8755 from the Huber Company, the silicas with a high specific surface area as described in the application WO 03/16387. The person skilled in the art will understand that, as the equivalent silica filler described in this paragraph, could be used a reinforcing filler of another nature, in particular organic such as carbon black, since this reinforcing filler would be covered of a silica. By way of example, mention may be made, for example, of carbon blacks for tires as described for example in documents WO 96/37547 and WO 99/28380. According to a particular embodiment of the invention, the silica content is in a range from 50 to 70 phr. According to this particular embodiment of the invention, the level of reinforcing filler preferably varies between 50 and 75 phr, more preferably between 55 and 70 phr. According to one embodiment of the invention, the rubber composition may comprise carbon black. Suitable carbon blacks are all carbon blacks, especially blacks conventionally used in tires or their treads (so-called pneumatic grade blacks). Among the latter, there will be mentioned more particularly the reinforcing carbon blacks of the series 100, 200, 300, or the series blacks 500, 600 or 700 (ASTM grades), such as, for example, the blacks N115, N134, N234, N326, N330. , N339, N347, N375, N550, N683, N772). These carbon blacks can be used in the isolated state, as commercially available, or in any other form, for example as a carrier for some of the rubber additives used. The carbon black, when present, is preferably used at a level of less than 10 phr, more preferably less than or equal to 5 phr. These preferred ranges P10-3330 - 7 - apply to any of the embodiments of the invention. In the ranges indicated, it benefits from the coloring properties (black pigmentation agent) and anti-UV carbon blacks, without otherwise penalizing the typical performance provided by the reinforcing inorganic filler.
    [0017] A coupling agent, generally a silane (or binding agent), is used in a well-known manner to ensure a sufficient chemical and / or physical connection between the silica (surface of its particles) and one of the elastomers of the the elastomer matrix, in particular the SBR solution. This coupling agent is at least bifunctional. In particular, organosilanes or at least bifunctional polyorganosiloxanes are used. In particular, polysulfide silanes, called "symmetrical" or "asymmetrical" silanes according to their particular structure, are used, as described, for example, in claims WO 03/002648 (or US 2005/016651) and WO 00/002649 (or US 2005/016650).
    [0018] Particularly suitable, but not limited to, polysulfide silanes having the following general formula (I): (I) Z - A - Sx - A - Z, wherein: - x is an integer of 2 at 8 (preferably from 2 to 5); the symbols A, which are identical or different, represent a divalent hydrocarbon radical (preferably a C1-C18 alkylene group or a C6-C12 arylene group, more particularly a C1-C10 alkylene, especially a C1-C4 alkylene, in particular propylene); the symbols Z, which are identical or different, correspond to one of the following three formulas: ## STR2 ## in which: the radicals R 1, substituted or unsubstituted, identical or different from each other, represent a C 1 -C 18 alkyl, C 5 -C 18 cycloalkyl or C 6 -C 18 aryl group (preferably C 1 -C 6 alkyl, cyclohexyl or phenyl groups, especially C 1 -C 4 alkyl groups, more particularly methyl and / or ethyl). the radicals R2, substituted or unsubstituted, which are identical to or different from one another, represent a C1-C18 alkoxyl or C5-C18 cycloalkoxyl group (preferably a C1-C8 alkoxyl group and a cycloalkoxyl group); C5-C8, more preferably still selected from C1-C4 alkoxyl, especially methoxyl and ethoxyl).
    [0019] In the case of a mixture of polysulfurized alkoxysilanes corresponding to formula (I) above, in particular common commercially available mixtures, the average value of "x" is a fractional number preferably of between 2 and 5, more preferably close to 4. But the invention can also be advantageously used for example with disulfide alkoxysilanes (x = 2).
    [0020] By way of examples of polysulphide silanes, mention may be made more particularly of bis (C 1 -C 4) alkoxy (C 1 -C 4) alkylsilylalkyl (C 1 -C 4) polysulfides (especially disulfides, trisulphides or tetrasulfides), for example by polysulfides of bis (3-trimethoxysilylpropyl) or bis (3-triethoxysilylpropyl). Among these compounds, bis (3-triethoxysilylpropyl) tetrasulfide, abbreviated TESPT, of formula [(C2H50) 3Si (CH2) 3S212 or bis (triethoxysilylpropyl) disulfide, abbreviated TESPD, of formula (C2H50) 3Si (CH2) 3S] 2. Mention may also be made, by way of preferred examples, of polysulfides (in particular disulphides, trisulphides or tetrasulfides) of bis- (C 1 -C 4 monoalkoxyl) dialkyl (C 1 -C 4) silylpropyl), more particularly bis-monoethoxydimethylsilylpropyl tetrasulfide as described in US Pat. patent application WO 02/083782 cited above (or US 7,217,751). By way of examples of coupling agents other than a polysulfide alkoxysilane, mention may be made in particular of bifunctional POS (polyorganosiloxanes) or hydroxysilane polysulfides (R 2 = OH in formula I above) as described, for example in patent applications WO 02/30939 (or US Pat. No. 6,774,255), WO 02/31041 (or US 2004/051210), and WO2007 / 061550, or else silanes or POS bearing functional azo-dicarbonyl groups, such as described for example in patent applications WO 2006/125532, WO 2006/125533, WO 2006/125534.
    [0021] As examples of other sulphurized silanes, mention may be made, for example, of silanes carrying at least one thiol function (-SH) (called mercaptosilanes) and / or of at least one blocked thiol function, as described for example in patents or patent applications US 6,849,754, WO 99/09036, WO 2006/023815, WO 2007/098080.
    [0022] Of course, it would also be possible to use mixtures of the coupling agents described above, as described in particular in the aforementioned application WO 2006/125534. The content of coupling agent is advantageously less than 10 phr, it being understood that it is generally desirable to use as little as possible. Its level is preferably P10-3330 between 0.5 and 8 phr, more preferably between 2 and 8 phr. This level is easily adjusted by those skilled in the art according to the level of silica used in the composition. .1-3. Hydrocarbon resin: The hydrocarbon resin, present in the rubber composition at a content ranging from 10 to 50 phr, has a glass transition temperature, Tg, of greater than 20 ° C. The term "resin" is hereby reserved, by definition known to those skilled in the art, to a compound which is solid at room temperature (23 ° C), as opposed to a liquid plasticizer such as an oil. Hydrocarbon resins are polymers well known to those skilled in the art, essentially based on carbon and hydrogen but may include other types of atoms, used in particular as plasticizers or tackifiers in polymeric matrices. They are inherently miscible (i.e., compatible) with the rates used with the polymer compositions for which they are intended, so as to act as true diluents. They have been described, for example, in the book "Hydrocarbon Resins" by R. Mildenberg, M. Zander and G. Collin (New York, VCH, 1997, ISBN 3-527-28617-9), chapter 5 of which is devoted their applications, in particular pneumatic rubber (5.5 "Rubber Tires and Mechanical Goods"). They can be aliphatic, cycloaliphatic, aromatic, hydrogenated aromatic, aliphatic / aromatic type that is to say based on aliphatic and / or aromatic monomers. They may be natural or synthetic, whether or not based on petroleum (if so, also known as petroleum resins). Their Tg is preferably greater than 0 ° C., especially greater than 20 ° C. (most often between 30 ° C. and 95 ° C.). In a known manner, these hydrocarbon resins can also be described as thermoplastic resins in that they soften by heating and can thus be molded. They can also be defined by a point or softening point (in English, "softening point"). The softening temperature of a hydrocarbon resin is generally about 50 to 60 ° C. higher than its Tg value. The softening point is measured according to ISO 4625 ("Ring and Ball" method). The macrostructure (Mw, Mn and Ip) is determined by size exclusion chromatography (SEC) as indicated below. As a reminder, the SEC analysis, for example, consists in separating the macromolecules in solution according to their size through columns filled with a porous gel; the molecules are separated according to their hydrodynamic volume, the larger ones being eluted first.
    [0023] The sample to be analyzed is simply solubilized beforehand in a suitable solvent, tetrahydrofuran at a concentration of 1 g / liter. Then the solution is filtered on a 0.45 μm porosity filter before injection into the apparatus. The equipment used is for example a "Waters alliance" chromatographic chain according to the following conditions: elution solvent: tetrahydrofuran, temperature 35 ° C .; - concentration 1 g / liter; flow rate: 1 ml / min; volume injected: 100111; - Moore calibration with polystyrene standards; - set of 3 columns "Waters" in series ("Styragel HR4E", "Styragel HR1" and "Styragel HR 0.5") - detection by differential refractometer (for example "WATERS 2410") that can be equipped with an operating software (eg "Waters Millenium").
    [0024] A Moore calibration is conducted with a series of low Ip (less than 1.2) polystyrene commercial standards of known molar masses covering the field of masses to be analyzed. The mass-averaged molecular weight (Mw), the number-average molecular weight (Mn) and the polymolecularity index (Ip = Mw / Mn) are deduced from the recorded data (mass distribution curve of the molar masses).
    [0025] All the molar mass values indicated in the present application are therefore relative to calibration curves made with polystyrene standards. According to a preferred embodiment of the invention, the hydrocarbon resin has at least any one, more preferably all of the following characteristics: a Tg greater than 25 ° C. (in particular between 30 ° C. and 100 ° C.) more preferably greater than 30 ° C (in particular between 30 ° C and 95 ° C); a softening point greater than 50 ° C. (in particular between 50 ° C. and 150 ° C.); a number-average molar mass (Mn) of between 400 and 2000 g / mol, preferably between 500 and 1500 g / mol; - A polymolecularity index (Ip) of less than 3, preferably 2 (recall: Ip = Mw / Mn with Mw weight average molar mass).
    [0026] By way of examples of such hydrocarbon resins, mention may be made of homopolymer or copolymer resins of cyclopentadiene (abbreviated as CPD), homopolymer or copolymer resins of dicyclopentadiene (abbreviated to DCPD), homopolymer or copolymer resins terpene, C5 homopolymer or copolymer resins, C9 homopolymer or copolymer resins, alpha-methyl-styrene homopolymer or copolymer resins, or mixtures of these resins. Among the above copolymer resins, mention may be made more particularly of (D) CPD / vinylaromatic copolymer resins, (D) CPD / terpene copolymer resins, terpene phenol copolymer resins, copolymer resins. (D) CPD / C5 cut, (D) CPD / C9 cut copolymer resins, terpene / vinylaromatic copolymer resins, terpene / phenol copolymer resins, C5 / vinylaromatic cut copolymer resins, or blends thereof resins. The term "terpene" here combines in a known manner the alpha-pinene, betapinene and limonene monomers; preferably, a limonene monomer is used which is present in a known manner in the form of three possible isomers: L-limonene (laevorotatory enantiomer), D-limonene (dextrorotatory enantiomer), or the dipentene, racemic of the dextrorotatory and levorotatory enantiomers. . Examples of suitable vinyl aromatic monomers are styrene, alpha-methylstyrene, ortho-methylstyrene, metamethylstyrene, para-methylstyrene, vinyl-toluene, para-tert-butylstyrene, methoxystyrenes, chlorostyrenes and hydroxystyrenes. vinylmesitylene, divinylbenzene, vinylnaphthalene, any vinylaromatic monomer from a C9 cut (or more generally from a Cs to Cm cut). More particularly, mention may be made of homopolymer resins (D) CPD, copolymer resins (D) CPD / styrene, polylimonene resins, limonene / styrene copolymer resins, limonene / D copolymer resins (CPD) , C5 / styrene cut copolymer resins, C5 / C9 cut copolymer resins, or mixtures of these resins.
    [0027] All the resins above are well known to those skilled in the art and commercially available, for example sold by the company DRT under the name "Dercolyte" for polylimonene resins, by the company Neville Chemical Company under the name "Super Nevtac ", by Kolon under the name" Hikorez "or by the company Exxon Mobil under the name" Escorez "with regard to C5 / styrene resins or C5 / C9 cut resins or by Struktol under the name" 40 MS "or" 40 NS "(mixtures of aromatic and / or aliphatic resins). According to any of the embodiments of the invention, the resin is preferably a terpene resin such as a homopolymer or a copolymer of limonene, or a C5 cutting and C9 cutting copolymer. The resin is used at a level ranging from 10 to 50 phr in the rubber composition. According to the particular embodiment where the proportion of silica in the rubber composition is from 50 to 70 phr, the level of resin is preferably in a range from 20 to 40 phr. P10-3330 - 12 - .1-4. Liquid plasticizer: The liquid plasticizer preferably has a glass transition temperature of less than -20 ° C, more preferably less than -40 ° C. As liquid plasticizer, any extender oil, whether of aromatic or non-aromatic nature, any liquid plasticizer known for its plasticizing properties vis-à-vis diene elastomers, is usable. At room temperature (23 ° C.), these plasticizers or these oils, more or less viscous, are liquids (that is to say, as a reminder, substances having the capacity to eventually take on the shape of their container) , in contrast in particular to hydrocarbon plasticizing resins which are inherently solid at room temperature.
    [0028] Particularly suitable as liquid plasticizers are naphthenic oils, paraffinic oils, DAE oils, MES (Medium Extracted Solvates) oils, Treated Distillate Aromatic Extracts (TDAE) oils, Residual Aromatic Extract Oils (RAE) oils, TRAE oils ( Treated Residual Aromatic Extract) and SRAE oils (Safety Residual Aromatic Extract oils), mineral oils, vegetable oils, ethers plasticizers, ester plasticizers, phosphate plasticizers, sulphonate plasticizers and mixtures of these compounds. I-5. Various additives: The rubber compositions of the treads of the tires in accordance with the invention may also comprise all or part of the usual additives normally used in elastomer compositions intended for the manufacture of tire treads, in particular pneumatic tires, fillers other than those mentioned above, for example non-reinforcing fillers such as chalk or lamellar fillers such as kaolin, talc, pigments, protective agents such as anti-ozone waxes, chemical antiozonants, anti-oxidants, reinforcing resins (such as resorcinol or bismaleimide), acceptors (for example phenolic novolac resin) or methylene donors (for example HMT or H3M) as described, for example, in application WO 02/10269, a crosslinking system with either sulfur or sulfur and / or peroxide and / or bismaleimide, accelerators or retarders vulcanization, vulcanization activators. These compositions may also contain coupling activators when a coupling agent is used, inorganic filler recovery agents or, more generally, processing aids which can be used in a known manner, using P10-3330. - improving the dispersion of the filler in the rubber matrix and lowering the viscosity of the compositions, to improve their ability to implement in the green state; these agents are for example hydrolysable silanes such as alkylalkoxysilanes, polyols, polyethers, amines, hydroxylated or hydrolysable polyorganosiloxanes. I-6. Preparation of rubber compositions: The compositions used in the treads of the tires of the invention may be manufactured in appropriate mixers, using two successive preparation phases well known to those skilled in the art: a first phase of work or thermomechanical mixing (so-called "non-productive" phase) at high temperature, up to a maximum temperature of between 110 ° C. and 190 ° C., preferably between 130 ° C. and 180 ° C., followed by a second phase of mechanical work (so-called "productive" phase) up to a lower temperature, typically below 110 ° C, for example between 40 ° C and 100 ° C, finishing phase during which the crosslinking system is incorporated. The process for preparing such compositions comprises, for example, the following steps: thermomechanically kneading (for example in one or more times) the elastomer matrix, the reinforcing filler, the coupling agent, the hydrocarbon resin, where appropriate the liquid plasticizer up to a maximum temperature between 110 ° C and 190 ° C (so-called "non-productive" phase); - cool all at a temperature below 100 ° C; - Then incorporate, in a second step (called "productive"), a crosslinking system; - mix everything up to a maximum temperature of less than 110 ° C. By way of example, the non-productive phase is carried out in a single thermomechanical step in the course of which, in a suitable mixer such as a conventional internal mixer, all of the basic constituents (the elastomer matrix) are first introduced. , the hydrocarbon resin, optionally the liquid plasticizer, the reinforcing filler and the coupling agent), then in a second step, for example after one to two minutes of mixing, the other additives, any load-collecting agents, or of complementary implementation, with the exception of the crosslinking system. The total mixing time in this non-productive phase is preferably between 1 and 15 minutes.
    [0029] After cooling the mixture thus obtained, it is then incorporated in an external mixer such as a roll mill, maintained at low temperature (for example between 40 ° C and 100 ° C), the crosslinking system. The whole is then mixed (productive phase) for a few minutes, for example between 2 and 15 min.
    [0030] Whatever the embodiment of the invention, the crosslinking system itself is preferably based on sulfur and a primary vulcanization accelerator, in particular a sulfenamide type accelerator. To this vulcanization system are added, incorporated during the first non-producing phase and / or during the production phase, various known secondary accelerators or vulcanization activators such as zinc oxide, stearic acid, guanidine derivatives (especially diphenylguanidine), etc. The sulfur content is preferably between 0.5 and 3.0 phr, that of the primary accelerator is preferably between 0.5 and 5.0 phr.
    [0031] It is possible to use as accelerator (primary or secondary) any compound capable of acting as a vulcanization accelerator for diene elastomers in the presence of sulfur, especially thiazole type accelerators and their derivatives, thiuram type accelerators, zinc dithiocarbamates. These accelerators are more preferably selected from the group consisting of 2-mercaptobenzothiazyl disulfide (abbreviated "MBTS"), N-cyclohexyl-2-benzothiazyl sulfenamide (abbreviated "CBS"), N, Ndicyclohexyl-2-benzothiazyl sulfenamide ( abbreviated "DCBS"), N-tert-butyl-2-benzothiazylsulfenamide (abbreviated as "TBBS"), N-tert-butyl-2-benzothiazylsulfenimide (abbreviated as "TBSI"), zinc dibenzyldithiocarbamate (abbreviated to " ZBEC ") and mixtures of these compounds. Preferably, a primary accelerator of the sulfenamide type is used.
    [0032] The final composition thus obtained can then be calendered or extruded, for example to form a rubber profile used for the manufacture of a tire tread, especially for passenger vehicles.
    [0033] The invention relates to the tires previously described both in the green state (that is to say, before firing) and in the fired state (that is to say, after crosslinking or vulcanization). The invention also relates to a method for preparing the tread according to the invention, which method comprises the following steps: thermomechanically kneading the elastomer matrix, the reinforcing filler, the coupling agent, the hydrocarbon resin, up to reach a maximum temperature between 110 ° C and 190 ° C; - cool all at a temperature below 100 ° C; - Then incorporate, in a second step, a crosslinking system; - mix everything up to a maximum temperature below 110 ° C; - Calender or extrude the composition thus obtained. The invention also applies to cases where the rubber compositions described above form only part of composite or hybrid treads, in particular those consisting of two radially superposed layers of different formulations (so-called "cap-base"), both carved and intended to come into contact with the road during the rolling of the tire, during the life of the latter. The portion based on the previously described formulation may then constitute the radially outer layer of the tread intended to come into contact with the ground from the beginning of the rolling of the new tire, or on the contrary its radially inner layer intended to come into contact with the ground later. The aforementioned features of the present invention, as well as others, will be better understood on reading the following description of exemplary embodiment of the invention, given by way of illustration and not limitation. II-EXAMPLES OF CARRYING OUT THE INVENTION IL1-Preparation of Compositions A, B, C and D: The formulations (in phr) of compositions A, B, C and D are described in Table I. The elastomeric matrices of compositions A and C are identical and comprise more than 50% by weight of an SBR solution which carries a silanol function and an amine function, in particular tertiary, which functions are positioned outside the ends of the elastomeric chain. The elastomer matrices of compositions B and D are identical and comprise more than 50% by weight of a SBR solution bearing a silanol function at the end of the elastomeric chain devoid of amine function. Compositions C and D differ from each other solely in the nature of the elastomer which constitutes the elastomer matrix. Composition C is in accordance with the invention while composition D is not so because of the nature of the elastomeric matrix. The compositions A and B differ from one another solely in the nature of the elastomer which constitutes the elastomer matrix and are both not in accordance with the invention, because of the degree of reinforcing filler, the silica content, the resin content and the level of liquid plasticizer. The following procedures are carried out for the production of these compositions: an internal mixer (final filling ratio: approximately 70% by volume) is introduced, the initial vessel temperature of which is approximately 60 ° C., successively the elastomer matrix , the reinforcing filler, the coupling agent, the hydrocarbon resin, if appropriate the liquid plasticizer and the various other ingredients with the exception of the vulcanization system. Thermomechanical work (non-productive phase) is then carried out in one stage, which lasts a total of 5 minutes, until a maximum temperature of 165 ° C is reached.
    [0034] P10-3330 - 16 - The mixture thus obtained is recovered, it is cooled and then sulfur and a sulfenamide type accelerator are incorporated on a mixer (homo-finisher) at 23 ° C., mixing the whole (productive phase) for a period of time. appropriate (for example between 5 and 12 min).
    [0035] The compositions A, B, C and D thus obtained are vulcanized, and their properties in the fired state are presented in Table I. 11.2 - Results: The dynamic properties tan (8) max are measured on a viscoanalyzer (Metravib VA4000) according to ASTM D 5992-96. The response of a sample of vulcanized composition (cylindrical specimen 4 mm in thickness and 400 mm 2 in section), subjected to a sinusoidal stress in alternating simple shear, at the frequency of 10 Hz, at 0 ° C., is recorded. A constant strain strain sweep is performed at 0.7MPa. The higher the value of tan (8) at 0 ° C, the better the grip of the tire on wet ground. The delta tan values at 0 ° C. of the compositions C and D are much lower than the compositions A and B, and this because of the lower rate of reinforcing filler. As expected, a decrease in the reinforcing filler content is accompanied by a decrease in the wet grip performance of the tires whose treads consist respectively of the composition C and the composition D. But unexpectedly it is observed that this decrease in wet adhesion performance is less for composition C than for composition D. Indeed, the tan delta value at 0 ° C. of composition C is 10% greater than that of D. Consequently, a tire whose tread consists of the composition C has a better wet grip performance than a tire whose tread is composed of the composition D. The tire according to the invention offers a good performance compromise between rolling resistance and wet grip. P10-3330 - 17 - Table I Compositions ABCD SBR1 (1) 100 - 100 - SBR2 (2) - 100 - 100 carbon black (3) 3 3 3 3 silica (4) 80 80 60 60 resin (5) 36 36 Liquid plasticizer (6) 7 7 - - antiozone wax 1.8 1.8 1.8 1.8 antioxidant (7) 2.7 2.7 2.7 2.7 silane (8) 6.4 6.4 4.8 4.8 Stearic acid 2 2 2 2 CBS (9) 2.3 2.3 2.3 2.3 DPG (10) ) 2 2 2 2 sulfur 1 1 1 1 ZnO 1 1 1 1 Cooking properties Tg delta 0 ° c 0.61 0.62 0.33 0.30 (1) SBR1: SBR with 27% styrene and 24% 1.2 of the part butadiene (Tg = -48 ° C) carrying a silanol function and a tertiary amine pendant function, which functions are located outside the ends of the elastomeric chain; (2) SBR with 27% of styrene unit and 24% of 1.2 unit of the butadiene part (Tg = -48 ° C) carrying a silanol function at the end of the elastomeric chain; (3) ASTM grade N234 (Cabot company); (4) "Zeosil 1165 MP" silica of Rhodia type "HDS" (5) C5 cut resin / C9 cut ECR-373 from Exxon; (6) Sunflower oil 85% by weight of oleic acid, "Lubrirob Tod 1880" from Novance (7) N- (1,3-dimethylbutyl) -N'-phenyl-p-phenylenediamine, company Flexsys (8) TESPT ("Si69" from Degussa); (9) N-cyclohexyl-2-benzothiazol sulfenamide ("Santocure CBS" from Flexsys) (10) Diphenylguanidine ("Perkacit" DPG from Flexsys).
    [0036] P10-3330 - 18 -
    权利要求:
    Claims (12)
    [0001]
    REVENDICATIONS1. A tire whose tread comprises a rubber composition based on at least: an elastomer matrix comprising more than 50% by weight of an SBR solution which carries a silanol function and an amine function, a reinforcing filler present at a rate of between 40 and 80 phr, which reinforcing filler comprises between 40 and 80 phr of a silica, a coupling agent for coupling silica to the SBR solution, 10 to 50 phr of a hydrocarbon resin having a Tg greater than 20. ° C., 0 to less than 5 phr of a liquid plasticizer.
    [0002]
    2. A tire according to claim 1 wherein the silanol function and the amine function are located outside the chain ends of the first diene elastomer.
    [0003]
    3. A tire according to any one of claims 1 to 2 wherein the amine function is a tertiary amine function.
    [0004]
    4. A tire according to any one of claims 1 to 3 wherein the solution SBR has a glass transition temperature of less than -40 ° C.
    [0005]
    5. A tire according to claim 4 wherein the solution SBR has a glass transition temperature of between -70 ° C and -40 ° C.
    [0006]
    A tire according to any one of claims 1 to 5, wherein the elastomeric matrix comprises more than 75% by weight of the SBR solution.
    [0007]
    The tire of any one of claims 1 to 6, wherein the hydrocarbon resin is a terpene resin or a C5 / C9 cut copolymer.
    [0008]
    8. A tire according to any one of claims 1 to 7 wherein the silica content is from 50 to 70 phr.
    [0009]
    9. A tire according to claim 8 wherein the hydrocarbon resin content varies from 20 to 40 phr. - 19 - 3021971
    [0010]
    10. A tire according to any one of claims 8 to 9 wherein the reinforcing filler content varies between 50 phr and 75 phr.
    [0011]
    11. A tire according to any one of claims 1 to 10 wherein the reinforcing filler comprises a carbon black at a rate of less than 10 phr, preferably at most 5 phr.
    [0012]
    A process for preparing a tire according to any one of claims 1 to 11 which comprises the following steps: thermomechanically kneading the elastomeric matrix, the reinforcing filler, the coupling agent, the hydrocarbon resin, until a temperature is reached maximum between 110 ° C and 190 ° C; cool the assembly to a temperature below 100 ° C; - Then incorporate, in a second step, a crosslinking system; Kneading everything to a maximum temperature of less than 110 ° C .; - Calender or extrude the composition thus obtained.
    类似技术:
    公开号 | 公开日 | 专利标题
    EP3152066B1|2018-05-02|Tyre with low rolling resistance
    EP3105066B1|2018-02-07|Tyre tread
    EP2643403B1|2020-08-19|Tire tread
    EP2643401B1|2020-10-14|Tire tread having enhanced wet grip
    EP2643400B1|2020-05-06|Tread for winter tyre
    EP3152239B1|2018-09-26|Tyre with low rolling resistance
    EP2760929A1|2014-08-06|Tyre with improved grip on wet ground
    EP2655494A1|2013-10-30|Tyre the tread of which comprises a thermoplastic polyurethane block copolymer
    WO2013045482A1|2013-04-04|Tyre with improved grip on wet ground
    WO2011120966A1|2011-10-06|Tyre, the tread of which comprises a rubber composition comprising a polyvinyl ester resin
    EP3393823B1|2021-12-01|Tire for vehicles transporting heavy loads comprising a new tread
    WO2012084847A1|2012-06-28|Tyre, the tread of which comprises a poly| resin
    WO2012152702A1|2012-11-15|Tyre with a tread comprising an emulsion sbr having a high trans content
    EP2844501A1|2015-03-11|Tyre tread
    WO2016131704A1|2016-08-25|Tyre, the tread of which includes a phenolic compound
    WO2019073145A1|2019-04-18|Tyre provided with a tread including at least one butyl rubber and a butadiene and styrene copolymer
    EP3558715A1|2019-10-30|Tyre for a vehicle carrying heavy loads, comprising a new tread
    同族专利:
    公开号 | 公开日
    US20170204256A1|2017-07-20|
    JP2017518422A|2017-07-06|
    EP3152066A1|2017-04-12|
    CN106414590B|2021-05-18|
    JP6641300B2|2020-02-05|
    FR3021971B1|2016-06-03|
    EP3152066B1|2018-05-02|
    CN106414590A|2017-02-15|
    WO2015185394A1|2015-12-10|
    引用文献:
    公开号 | 申请日 | 公开日 | 申请人 | 专利标题
    WO2009077837A1|2007-12-14|2009-06-25|Petroflex Industria E Comercio S.A.|A1,3-butadiene and styrene copolymer product, functionalized at the extremities of its polymeric chains, and the preparation process|
    EP2213688A1|2009-01-29|2010-08-04|The Goodyear Tire & Rubber Company|Tire with a tread of a spatially defined elastomer composition|
    FR2951178A1|2009-10-08|2011-04-15|Michelin Soc Tech|FUNCTIONALIZED DIENIC ELASTOMER AND RUBBER COMPOSITION CONTAINING SAME.|
    WO2012069567A1|2010-11-26|2012-05-31|Societe De Technologie Michelin|Tyre tread|WO2018079800A1|2016-10-31|2018-05-03|Compagnie Generale Des Etablissements Michelin|A tire comprising a tread|FR2740778A1|1995-11-07|1997-05-09|Michelin & Cie|SILICA-BASED RUBBER COMPOSITION AND FUNCTIONALIZED DIENE POLYMER HAVING TERMINAL SILANOL FUNCTION|
    FR2744127A1|1996-01-26|1997-08-01|Michelin & Cie|RUBBER COMPOSITION BASED ON A DIENE POLYMER HAVING A SILANOL FUNCTION AND COMPRISING AN ORGANOSILANE DERIVATIVE|
    FR2763074B1|1997-05-07|1999-06-25|Michelin & Cie|RUBBER COMPOSITION BASED ON CARBON BLACK HAVING SILICA ATTACHED TO ITS SURFACE AND OF DYENIC POLYMER FUNCTIONALIZED OR MODIFIED BY SILANOL FUNCTIONS|
    AT239737T|1997-08-21|2003-05-15|Crompton Corp|BLOCKED MERCAPTOSILANES AS A CLUTCH FOR FILLED RUBBER COMPOSITION|
    JP5357371B2|2000-07-31|2013-12-04|コンパニーゼネラールデエタブリッスマンミシュラン|Tire tread|
    CN1263792C|2000-10-13|2006-07-12|米其林技术公司|Rubber composition comprising as coupling agent polyfunctional organosilane|
    CN1257171C|2000-10-13|2006-05-24|米其林技术公司|Polyfunctional organosilane as coupling agent and method for obtaining same|
    FR2823215B1|2001-04-10|2005-04-08|Michelin Soc Tech|TIRE AND TIRE TREAD COMPRISING AS COUPLING AGENT A BIS-ALKOXYSILANE TETRASULFURE|
    AT465208T|2001-06-28|2010-05-15|Michelin Soc Tech|TIRE RUNNING REINFORCED BY SILICA WITH LOW SPECIFIC SURFACE|
    WO2003002649A1|2001-06-28|2003-01-09|Societe De Technologie Michelin|Tyre tread reinforced with silica having a very low specific surface area|
    AT266669T|2001-08-06|2004-05-15|Degussa|ORGANOSILICON COMPOUNDS|
    RU2004107514A|2001-08-13|2005-10-10|Сосьете Де Текноложи Мишлен |COMPOSITION BASED ON DIENE RUBBER FOR PNEUMATIC TIRES, INCLUDING SPECIAL SILICON DIOXIDE AS A REINFORCING FILLER|
    FR2866028B1|2004-02-11|2006-03-24|Michelin Soc Tech|PLASTICIZING SYSTEM FOR RUBBER COMPOSITION|
    US7928258B2|2004-08-20|2011-04-19|Momentive Performance Materials Inc.|Cyclic diol-derived blocked mercaptofunctional silane compositions|
    EP1773938B1|2004-07-29|2011-04-20|Société de Technologie Michelin|Zinc-free or practically zinc-free rubber composition|
    FR2877348B1|2004-10-28|2007-01-12|Michelin Soc Tech|PLASTICIZING SYSTEM FOR RUBBER COMPOSITION|
    ES2534483T3|2004-11-02|2015-04-23|Bridgestone Corporation|Polyhedral Modified Polymer|
    FR2883568B1|2005-03-24|2007-05-18|Michelin Soc Tech|RUBBER COMPOSITION COMPRISING ITACONIMIDOMALEIMIDE|
    FR2886304B1|2005-05-26|2007-08-10|Michelin Soc Tech|RUBBER COMPOSITION FOR PNEUMATIC COMPRISING AN ORGANOSILICIC COUPLING SYSTEM|
    FR2886305B1|2005-05-26|2007-08-10|Michelin Soc Tech|PNEUMATIC RUBBER COMPOSITION COMPRISING AN ORGANOSILICALLY COUPLED AGENT AND AN INORGANIC CHARGE RECOVERY AGENT|
    FR2886306B1|2005-05-26|2007-07-06|Michelin Soc Tech|PNEUMATIC RUBBER COMPOSITION COMPRISING AN ORGANOSILOXANE COUPLING AGENT|
    DE102005037453A1|2005-08-09|2007-02-15|Uwe Gmbh|radiator device|
    KR20080068868A|2005-11-16|2008-07-24|다우 코닝 코포레이션|Organosilanes and their preparation and use in elastomer compositions|
    US7510670B2|2006-02-21|2009-03-31|Momentive Performance Materials Inc.|Free flowing filler composition based on organofunctional silane|
    FR2910901B1|2006-12-27|2010-06-25|Michelin Soc Tech|RUBBER COMPOSITION COMPRISING A POLYMALEIMIDE COMPOUND|
    FR2915202B1|2007-04-18|2009-07-17|Michelin Soc Tech|MONOMODAL COUPLED DIENIC ELASTOMER HAVING CHAIN SILANOL FUNCTION, PROCESS FOR OBTAINING THE SAME, AND RUBBER COMPOSITION CONTAINING SAME.|
    JP4354512B2|2007-10-17|2009-10-28|住友ゴム工業株式会社|Rubber composition for tread and tire having tread comprising the same|
    CN102026826B|2008-03-10|2015-01-14|株式会社普利司通|Method for producing modified conjugated diene polymer/copolymer, modified conjugated diene polymer/copolymer, and rubber composition and tier using the same|
    JP5756248B2|2008-04-28|2015-07-29|株式会社ブリヂストン|tire|
    FR2930554B1|2008-04-29|2012-08-17|Michelin Soc Tech|ELASTOMERIC MIXTURE COMPRISING MAJORITARILY AN AMINO-ALCOXYSILANE GROUP-COUPLED DIENE ELASTOMER, RUBBER COMPOSITION COMPRISING SAME AND METHODS OF OBTAINING SAME|
    JP5134592B2|2008-08-08|2013-01-30|住友ゴム工業株式会社|Rubber composition for cap tread and tire having cap tread comprising the same|
    JP4881362B2|2008-11-05|2012-02-22|住友ゴム工業株式会社|Rubber composition and tire|
    FR2951186B1|2009-10-12|2012-01-06|Michelin Soc Tech|RUBBER COMPOSITION BASED ON GLYCEROL AND A FUNCTIONALIZED ELASTOMER AND TIRE TREAD FOR PNEUMATIC|
    FR2955582B1|2010-01-28|2012-03-09|Michelin Soc Tech|METHOD FOR MANUFACTURING SELF-BREAKING ELASTOMER COMPOSITION|
    JP5351244B2|2011-04-22|2013-11-27|住友ゴム工業株式会社|Rubber composition for tire and pneumatic tire|
    CA2797904C|2011-12-20|2015-01-27|Heraeus Medical Gmbh|Paste-like bone cement|
    FR2980481B1|2011-09-26|2013-10-11|Michelin Soc Tech|PNEUMATIC WITH IMPROVED ADHERENCE TO WET SOIL|
    CN104220506B|2012-03-30|2018-02-02|米其林集团总公司|Tire tread for improved abrasive nature|
    FR2996851B1|2012-10-15|2014-11-28|Michelin & Cie|INNER TIRE GUM.|
    US20140135437A1|2012-11-15|2014-05-15|The Goodyear Tire & Rubber Company|Tire with rubber tread containing combination of resin and vegetable oil, particularly soybean oil|FR3038320A1|2015-07-02|2017-01-06|Michelin & Cie|RUBBER COMPOSITION COMPRISING A VERY HIGH SPECIFIC SURFACE SILICA AND A HYDROCARBONATED RESIN WITH LOW VITREOUS TRANSITION TEMPERATURE|
    EP3469022B1|2016-06-09|2020-09-23|Compagnie Générale des Etablissements Michelin|A tire comprising a tread|
    JP6869333B2|2016-09-02|2021-05-12|株式会社ブリヂストン|Preparation of cis-1,4-polydiene with multiple silane functional groups prepared by in-situ hydrosilylation of polymer cements|
    FR3061185A1|2016-12-22|2018-06-29|Compagnie Generale Des Etablissements Michelin|RUBBER COMPOSITION COMPRISING A SPECIFIC HYDROCARBON RESIN|
    FR3061184A1|2016-12-22|2018-06-29|Compagnie Generale Des Etablissements Michelin|RUBBER COMPOSITION COMPRISING A SPECIFIC HYDROCARBON RESIN|
    US20200001650A1|2017-01-31|2020-01-02|Compagnie Generale Des Etablissements Michelin|A tire comprising a rubber composition|
    WO2018182042A1|2017-03-31|2018-10-04|Compagnie Generale Des Etablissements Michelin|A tire comprising a tread|
    EP3630504A1|2017-05-31|2020-04-08|Compagnie Générale des Etablissements Michelin|A tire comprising a tread|
    DE102017221236A1|2017-11-28|2019-05-29|Continental Reifen Deutschland Gmbh|Sulfur crosslinkable rubber compound, vulcanizate of the rubber mixture and vehicle tires|
    CN111491999A|2017-12-19|2020-08-04|米其林集团总公司|Tire tread with crosslinking system based on organic peroxide|
    FR3081161B1|2018-05-17|2020-07-10|Compagnie Generale Des Etablissements Michelin|TIRE TREAD OF WHICH THE CROSSLINKING SYSTEM IS BASED ON ORGANIC PEROXIDE|
    US11214667B2|2019-07-29|2022-01-04|The Goodyear Tire & Rubber Company|Pneumatic tire|
    法律状态:
    2015-06-19| PLFP| Fee payment|Year of fee payment: 2 |
    2015-12-11| PLSC| Publication of the preliminary search report|Effective date: 20151211 |
    2016-06-27| PLFP| Fee payment|Year of fee payment: 3 |
    2017-06-21| PLFP| Fee payment|Year of fee payment: 4 |
    2018-06-20| PLFP| Fee payment|Year of fee payment: 5 |
    2020-03-13| ST| Notification of lapse|Effective date: 20200206 |
    优先权:
    申请号 | 申请日 | 专利标题
    FR1455096A|FR3021971B1|2014-06-05|2014-06-05|TIRE WITH LOW ROLLING RESISTANCE|FR1455096A| FR3021971B1|2014-06-05|2014-06-05|TIRE WITH LOW ROLLING RESISTANCE|
    US15/315,601| US20170204256A1|2014-06-05|2015-05-27|Tire with low rolling resistance|
    JP2016571334A| JP6641300B2|2014-06-05|2015-05-27|Tire with low rolling resistance|
    CN201580029591.8A| CN106414590B|2014-06-05|2015-05-27|Tire with low rolling resistance|
    EP15725597.7A| EP3152066B1|2014-06-05|2015-05-27|Tyre with low rolling resistance|
    PCT/EP2015/061625| WO2015185394A1|2014-06-05|2015-05-27|Tyre with low rolling resistance|
    [返回顶部]