    • 专利摘要:
    The invention relates to a bioreactor obtained by compression of a mixture of an enzyme, a conductor and chitosan. The conductor may consist of carbon nanotubes. This bioreactor can be manufactured according to the following steps: preparing a mixture of powders in which the proportion of enzyme powder relative to a carbon nanotube powder is of the order of 50/50 by weight; prepare a viscous solution of chitosan in a ratio of 5 to 15 (in mg) of 0.75 to 1.25 chitosan (in ml) of acetic acid diluted to 0.4 to 0.6% by volume in water; add to the powder mixture the viscous chitosan in a weight ratio of 3 to 5 for the powder at 5 to 10 for chitosan; make a first compression then a light grinding; perform a second compression to make a pellet; and dry at room temperature.
    公开号:FR3019384A1
    申请号:FR1452534
    申请日:2014-03-25
    公开日:2015-10-02
    发明作者:Ichi Sarra El；Donald K Martin；Philippe Cinquin；Abdelkader Zebda
    申请人:Universite Joseph Fourier (Grenoble 1)；
    IPC主号:
    专利说明:

    [0001] The present invention relates to an implantable reactor in vivo, at which a reaction between elements confined in this reactor and compounds present in the host organism is likely to occur. This reaction may for example lead to a deformation of the reactor, to the generation of an electrical potential, or to the chemical transformation of the compound interacting with the reactor. A reactor leading to the generation of an electrical potential may constitute an electrode of a biopile or a biosensor, of the sugar-oxygen type, for example glucose-oxygen type. A reactor leading to the chemical transformation of a compound interacting with the reactor will, for example, be a glucose killer, for example by transforming glucose into a compound that will be eliminated by the body. Although the invention and the state of the art are described herein primarily in the case of bioelectrodes of a biopile, it will be understood that the invention is generally applicable to any implantable reactor in vivo.
    [0002] B13302 2 Discussion of the Prior Art Various types of glucose-oxygen biopiles are described in the prior art, for example in PCT / FR2009 / 050639 (B8606). In these known biopiles, each electrode, anode and cathode, corresponds to an enclosure containing a liquid medium in which an electrode wire plunges. The anode and cathode enclosures are delimited by membranes that can be traversed by hydrogen and oxygen but avoiding the circulation of other heavier elements.
    [0003] The anode comprises in a solution an enzyme and a redox mediator. The enzyme is capable of catalyzing the oxidation of sugar and is for example selected from the group comprising glucose oxidase if the sugar is glucose and lactose oxidase if the sugar is lactose. The redox mediator has a low redox potential capable of exchanging electrons with the anode enzyme and is for example selected from the group comprising: ubiquinone (UQ) and ferrocene. The cathode also comprises in a solution an enzyme and preferably a redox mediator. The enzyme is capable of catalyzing the reduction of oxygen and is for example selected from the group comprising: polyphenol oxidase (PPO), laccase and bilirubin oxidase. The redox mediator has a high redox potential capable of exchanging electrons with the cathode enzyme and is for example chosen from the group comprising: hydroquinone (QH2) and 2,2'-azinobis- (3-ethylbenzo-thiazoline-6) -sulfonate) (ABTS). The following type of reaction occurs at the anode and the cathode: Cathode: QH2 + 1/2 02 PPO> Q + H2O Anode: glucose + UQ GKEK> gluconolactone + UQH2 Cathode: Q + 2H + + 2e - * QH2 Anode: UQH2- ÷ UQ + 2H + + 2e- these reactions being given in the particular case where the sugar is glucose, the anode enzyme is glucose oxidase B13302 3 (GOX), the mediator Anode redox is ubiquinone (UQ), the cathode enzyme is polyphenol oxidase (PPO), and the redox cathode mediator is quinhydrone (QH2). An anode potential of 20 mV and a cathode potential of 250 mV are then obtained, which leads to a zero current potential difference of the 230 mV biopile. Such biocells function well, but particularly with regard to the biopile disclosed in patent application PCT / FR2009 / 050639, require anode and cathode conductors to be immersed in enclosures containing suitable liquids, which constitutes a problem. inconvenient practice in many cases and makes it particularly difficult if not impossible to implant such biopiles in a living being. Indeed, it seeks to implant such biocells 15 in living beings, including to supply various actuators, such as pacemakers, artificial sphincters, or even artificial hearts. Solid electrode biopiles have been proposed. However, biopiles using such electrodes, especially when implanted in a living being, have shown a short life. An in vivo oxygen implantable oxygen glucose biopile is described in particular in the European patent EP 2,375,481 of the applicant (B10272). In this patent, it is proposed to make anode and cathode pellets of a biopile from a compression of a conductor such as graphite and an enzyme to which a redox mediator is added. The cathode and the anode, and preferably all of the anode and the cathode, are surrounded by a semi-permeable enclosure, for example of the type used in dialysis, to pass glucose and oxygen. and do not let enzymes and redox mediators pass. The conductive material from which the anode compression and cathode compression is performed is indicated as being graphite or a conductive polymer. Figure 1 attached reproduces Figure 2 of this prior patent. It shows an anode pellet A and a cathode pellet K integral respectively conductors 1 and 3. The anode is surrounded by a semipermeable membrane 11, the cathode of a semipermeable membrane 12 and the The assembly is surrounded by a semipermeable membrane 13. Satisfactory in vivo experimental results have been obtained with the biopile electrodes described in this patent. However, it is desirable to further improve the life of the electrodes, i.e. the operating time of the biopile and to maximize the biocompatibility of this cell. More generally, it is desirable to improve the life of bioreactors as defined above. Thus, a bioreactor obtained by compression of a mixture of an enzyme, a conductor and chitosan is provided. According to one embodiment, the conductor consists of carbon nanotubes. There is also provided a process for producing a bioreactor comprising the following steps: preparing a powder mixture in which the proportion of enzyme powder relative to a carbon nanotube powder is of the order of 50/50 in weight; prepare a viscous solution of chitosan in a ratio of 5 to 15 (in mg) of 0.75 to 1.25 chitosan (in ml) of acetic acid diluted to 0.4 to 0.6% by volume in the water ; add to the powder mixture the viscous chitosan in a weight ratio of 3 to 5 for the powder at 5 to 10 for chitosan; B13302 make a first compression then a light grinding; perform a second compression to make a pellet; and dry at room temperature. According to one embodiment, the pressure applied during the second compression is in a range of 2000 to 6000 kPa. According to one embodiment, the solution comprises from 0.002 to 0.005% by weight per volume of genipin. According to one embodiment, the solution comprises from 0.001 to 0.005% by weight per volume of caffeic acid. A bioreactor is also provided in which a porous chitosan membrane is placed on the active side and adhered to the periphery thereof. According to one embodiment, the bioreactor is a lozenge-shaped bioelectrode in which a conductor is bonded via a conductive adhesive to the face of the tablet opposite to the active face. According to one embodiment, the membrane comprises pores with an average diameter of the order of 1 to 10 nanometers. According to one embodiment, the membrane comprises a smooth face facing the pellet and a rough face facing outwards. There is also provided a method of making a porous membrane for a bioreactor, comprising the steps of: preparing a solution in a ratio of 5 to 15, (in mg) 0.75 to 1.25 chitosan (in ml ) acetic acid diluted to 0.4 to 0.6% in water; shake ; pour on a smooth support; and dry for 2 to 4 days at room temperature.
    [0004] B13302 BRIEF DESCRIPTION OF THE DRAWINGS These features and advantages, as well as others, will be set forth in detail in the following description of particular embodiments in a non-limiting manner with reference to the accompanying figures in which: FIG. Figure 2 of European Patent EP 2,375,481; Figs. 2A and 2B are respectively a sectional view and a top view of an embodiment of an electrode; and Figure 3 shows current characteristics versus time of various biocells. DETAILED DESCRIPTION Firstly, it is intended here to manufacture a bioelectrode tablet 15 not from the compression of only one conductor and an enzyme, but from a compression of chitosan, an enzyme and a conductive and possibly a redox mediator and other additives. The conductor may advantageously consist of multiwall carbon nanotubes (MWCNT - MultiWalled Carbon NanoTubes). A mixture of powders of an enzyme and carbon nanotubes is initially prepared, the proportion of enzyme powder relative to the carbon nanotube powder being of the order of 50/50 by weight, this proportion being variable. around 20 %. A viscous chitosan solution is also prepared by adding chitosan powder in acetic acid diluted to 0.5 volume%, heated to 50 ° C, and stirring for 2 hours at room temperature. To the powder mixture is added the viscous chitosan in a weight ratio of 2 for the powder to 3 for chitosan. For a pellet, for example, 0.04 gram of powder and 0.06 gram of chitosan will be used. The powder and chitosan are mixed in the viscous state and the first compression is carried out and then the mixture is lightly milled. A second compression is then carried out at a pressure selected in a range of 2000 to 6000 kPa to provide a pellet, followed by drying for two to four days at room temperature (20 to 30 ° C) for the whole polymerize. It is possible to add to the initial mixture a crosslinking agent, for example genipin at 0.0045% by weight per volume (g / 100 ml) in the viscous solution of chitosan after 2 hours of stirring. The genipin is first solubilized in a solution of 12% dimethylsulfoxide (DMSO) and 88% water (H 2 O). It is also possible to improve the acidic membrane resistance by adding to the initial mixture a product such as caffeic acid in a proportion of 0.0032% by weight per volume (g / 100 ml) in the viscous chitosan solution.
    [0005] The caffeic acid is previously solubilized at 4% in ethanol. The solution is allowed to stir for 30 min before taking 3 g to spread on the smooth support for drying as previously described. A feature of the process described herein is that during the second compression and drying, the chitosan is made into interconnected long fibers with a diameter of about 30 nm. It will be emphasized that a three-dimensional nanofibrous and nanoporous network is obtained simply by compression of the polymer with the powder and evaporation of the solvent at room temperature. As a result, the enzyme and carbon nanotubes are immobilized in the chitosan fiber matrix and do not migrate out of the pellet. This has a significant advantage because the enzyme, trapped by the fiber matrix, remains protected and active for a long time. In addition, it is necessary to trap carbon nanotubes, questions currently posed on the possible harmfulness of carbon nanotubes in vivo. A biocathode comprising only a conductor and an enzyme, as described in the above-mentioned prior patent, has a 1-month stability in batch operation. A biocathode based on chitosan-MWCNT-laccase, as described herein, has a stability greater than 2 months in continuous operation. In vitro measurements show that the discontinuous operation stability of the biocathode described here exceeds six months. In addition, this stability is also ensured in vivo for a period greater than 200 days. This demonstrates that the bioelectrode described here provides the enzyme with a protective environment for its activity but also retains the enzyme within the electrode pellet and near the carbon nanotubes for electrical conduction. The porosity of the three-dimensional matrix of chitosan allows a good diffusion of the substrates of the enzyme. Alternatively, instead of using carbon nanotubes, graphene, gold powder or a conductive polymer such as polyaniline may be used as the conductor. Particular embodiments have been described. Various variations and modifications will be apparent to those skilled in the art. In particular, the polymer may be chitosan or other biocompatible polymer, for example: polyvinyl alcohol, poly (methylmethacrylate), gelatin, dextran, or copolymers such as chitosan-polyethylene glycol or a mixture of these polymers. The method of manufacturing the conductive polymer and enzyme electrodes can be applied to the cathode or the anode. Different enzymes can be immobilized in this structure laccase, bilirubin oxidase, polyphenol oxidase, glucose oxidase, glucose dehydrogenase, catalase, peroxidase. According to another aspect of the present invention, there is provided a particular filter membrane for an enzymatic bioelectrode as above or any other enzymatic bioelectrode obtained by compression of a conductor, an enzyme and possibly a redox mediator. the redox mediator is not indispensable in the cathode.
    [0006] B13302 9 As illustrated in FIGS. 2A and 2B, the electrode is in the form of a tablet 20 having for example a circular shape in top view, a diameter of 0.5 to 1 cm and a thickness of 0, 5 to 2 mm. On the underside of the pad 20 is fixed a conductive strip 22 for example by a conductive adhesive, for example a carbon paste 24 itself coated with a protective layer of silicone adhesive 25, selected from biocompatible glues. On the upper face of the pellet 20 is placed - and not deposited - a membrane 26 bonded at its periphery to the pellet by a ring of silicone adhesive 28. It is intended here to use for the membrane 26 a membrane based of chitosan. This membrane is for example obtained starting from a solution in a ratio of 5 to 15, for example 10 (in mg) of chitosan at 0.75 to 1.25, for example 1 (in ml) of acetic acid. diluted to 0.4 to 0.6% by volume in water and heated to 50 ° C. In one test, 200 mg of chitosan were dissolved in 20 ml of acetic acid diluted to 0.5% by volume in water. This mixture is stirred for two hours. Then, 3 g of this mixture were taken and spread on a non-adhesive smooth support (diameter 28 cm), for example an antistatic polystyrene cup, and dried for 2 to 4 days at room temperature, by example at a temperature of 20 to 30 ° C. In one test, it was dried for three days at 25 ° C. A flexible nanoporous film is thus obtained. Experiments carried out by the applicant have shown that this flexibility is related to the fact that the drying is carried out for a long time at ambient temperature. This characteristic is not obtained for example if drying temperatures above 40 ° C are used. For a film thickness of the order of 7 to 15 μm, for example 10 μm, a porous membrane with average pore diameters of the order of 1 to 10 nanometers has been obtained. It will be preferred to use conditions where this average diameter is in the range of 5 to 8 nm to allow glucose to pass and to filter larger compounds. As in the context of making a pellet, it is possible to add to the initial mixture a crosslinking agent, for example genipin, and an acid-resistance agent, for example caffeic acid. The film obtained has a difference in roughness between the two faces which is due to the fact that one of the faces (the rougher) has been in contact with the air and not the support (smooth face). During assembly, the rough surface will preferably be placed outwards with respect to the surface of the bioelectrode pellet. Indeed, the difference in roughness on a thin film influences the ion diffusion and consequently the electrical resistivity. The inventors have shown that the chitosan film has good ionic conductivity (10-4 S.cm-1). This ionic conductivity is better than that obtained with commercial membranes such as Nafion or cellulose acetate. The chitosan film described herein allows, by its mechanical properties including its flexibility and its adequate swelling rate, to confer mechanical stability to the electrode by marrying the surface of the pellet after swelling thereof in the liquid. It confers a biocompatible interface to the tissue contact after implantation of the biopile. It constitutes an effective barrier against a possible release of the constituents of the electrode on the one hand, and against the biological molecules coming from the extracellular liquid. The pore diameter can be adjusted by changing: the concentration of the chitosan in the solvent (acetic acid), the chitosan ratio / crosslinking agent, the molecular weight of the powdered chitosan put into the initial acetic acid solution. Figure 3 shows a current characteristic in mA / m1 (milliliters corresponding to pellet volume) versus time in days for various biocells.
    [0007] B13302 11 Curve A corresponds to the case where a cellulose acetate membrane was used, curve B to the case where a Nafion membrane was used, and curve C to the case where a chitosan membrane was used. as previously described. It can be seen that the (negative) current is much larger in the case of the chitosan membrane and that the characteristics of the biocell do not degrade, quite the opposite, as a function of time. On the other hand, it is noted that for cellulose acetate, the characteristic starts from a value of -0.15 and falls to a value of about -0.05 after about 70 days. With a Nafion membrane, a relatively constant characteristic is obtained but current densities two to three times lower than with a chitosan-based membrane.
    [0008] Although the invention and the state of the art are described here mainly in the case of a bioelectrode, it will be understood that the invention applies generally to any implantable bioreactor in vivo, as defined at the beginning of the this description.
    权利要求:
    Claims (7)
    [0001]
    REVENDICATIONS1. Bioreactor obtained by compression of a mixture of an enzyme, a conductor and chitosan.
    [0002]
    2. Bioreactor according to claim 1, wherein the conductor consists of carbon nanotubes.
    [0003]
    3. A method of manufacturing a bioreactor according to claim 1 or 2, comprising the steps of preparing a mixture of powders in which the proportion of enzyme powder relative to a carbon nanotube powder is of the order of 50. / 50 by weight; prepare a viscous chitosan solution in a ratio of 5 to 15 (in mg) of chitosan at 0.75 to 1.25 (in ml) of acetic acid diluted to 0.4 to 0.6% by volume in water; add to the powder mixture the viscous chitosan in a weight ratio of 3 to 5 for the powder at 5 to 10 for chitosan; make a first compression then a light grinding; perform a second compression to make a pellet; and dry at room temperature.
    [0004]
    The method of claim 3, wherein the pressure applied during the second compression is in the range of 2000 to 6000 kPa.
    [0005]
    The method of manufacturing a membrane according to claim 3 or 4, wherein the solution comprises from 0.002 to 0.005 wt.% By volume of genipin.
    [0006]
    The method of manufacturing a membrane according to claim 3 or 4, wherein the solution comprises from 0.001 to 0.005% by weight per volume of caffeic acid. 30
    [0007]
    A bioreactor according to claim 1 or 2, wherein a porous membrane (26) based on chitosan is placed on an active side of the bioreactor and adhered to the periphery thereof. B13302 13 Bioreactor according to claim 7 constituting a pellet-shaped bioelectrode (20), wherein a conductor (22) is bonded via a conductive adhesive (24) to the face of the pellet opposite to the active face. 9. Bioreactor according to claim 7 or 8, wherein the membrane comprises pores with an average diameter of the order of 1 to 10 nanometers. 10. Bioreactor according to any one of claims 7 to 9, wherein the membrane comprises a smooth face facing towards the pellet and a rough face facing outwards. A process for producing a porous membrane for a bioreactor according to any one of claims 7 to 9, comprising the steps of: preparing a solution in a ratio of 5 to 15, (in mg) of chitosan at 0, 75 to 1.25 (in ml) acetic acid diluted to 0.4 to 0.6% in water; shake ; pour on a smooth support; and drying for 2 to 4 days at room temperature.
    类似技术:
    公开号 | 公开日 | 专利标题
    EP3123544B1|2019-06-19|Implantable biocompatible reactor
    Chen et al.2015|PVDF-Nafion nanomembranes coated microneedles for in vivo transcutaneous implantable glucose sensing
    JP4878756B2|2012-02-15|Immobilization of enzymes used in biofuel cells and sensors
    Wang et al.2005|A novel glucose biosensor based on the nanoscaled cobalt phthalocyanine–glucose oxidase biocomposite
    Krishnan et al.2017|Chitosan-covered Pd@ Pt core–shell nanocubes for direct electron transfer in electrochemical enzymatic glucose biosensor
    FR2673289A1|1992-08-28|SENSOR FOR MEASURING THE QUANTITY OF A COMPONENT IN SOLUTION.
    EP2965335A1|2016-01-13|Biocompatible electrochemical supercapacitor
    IL234190A|2019-09-26|Improved spacer membrane for an enzymatic in-vivo sensor
    EP2351048B1|2018-01-03|Electrically conductive fibres for bioelectrochemically systems, electrodes comprising the fibres and systems comprising these electrodes
    EP3560021B1|2021-01-27|Bioelectrode for detecting and/or oxidising glucose and method for the production thereof and device comprising same
    Suzuki et al.2016|Long-term continuous operation of FAD-dependent glucose dehydrogenase hydrogel-modified electrode at 37° C
    EP3353836B1|2021-04-21|Electrochemical reactor block
    El Ichi et al.2014|Biocompatible implantable biofuel cell
    WO2015193624A1|2015-12-23|Biocompatible implantable reactor
    Slaughter et al.2012|Vertically aligned Pd nanowires for Glucose Oxidase Bioanode
    FR3082359A1|2019-12-13|BIOPILE WITH A BIOFUEL TANK
    EP3728700A1|2020-10-28|Implantable device for producing hydrogen
    FR3009209A1|2015-02-06|FUEL BIOPILE
    WO2018091815A1|2018-05-24|Bioelectrode for detecting and measuring metabolites, and preparation process
    US20170224879A1|2017-08-10|Method for manufacturing a conductive film from an electrochemical bioreactor
    Chen2019|Bioelectrocatalytic oxidation and reduction of different substrates using carbon nanostructured electrodes
    WO2019175426A1|2019-09-19|Nanostructured bioelectrode for glucose oxidation, from electrogenerated aromatic compounds
    Narvaez Villarrubia2015|GLUCOSE/OXYGEN-BASED BIOFUEL CELL FOR BIOMEDICAL APPLICATIONS: ELECTRODE DESIGNS INTEGRATING CARBON COMPOSITE
    同族专利:
    公开号 | 公开日
    CA2943392A1|2015-10-01|
    EP3123544A2|2017-02-01|
    EP3123544B1|2019-06-19|
    FR3019384B1|2018-01-12|
    WO2015145054A3|2016-08-11|
    US10316284B2|2019-06-11|
    WO2015145054A2|2015-10-01|
    US20170081626A1|2017-03-23|
    引用文献:
    公开号 | 申请日 | 公开日 | 申请人 | 专利标题
    US20110039164A1|2006-11-06|2011-02-17|Akermin, Inc.|Bioanode and biocathode stack assemblies|
    FR2958801A1|2010-04-08|2011-10-14|Univ Joseph Fourier|BIOPILE A GLUCOSE|
    FR2963989A1|2010-08-19|2012-02-24|Univ Joseph Fourier|BIOPILE WITH DIRECT TRANSFER|
    WO2013130145A2|2011-11-30|2013-09-06|The Regents Of The University Of California|Printed biofuel cells|WO2016156612A1|2015-04-03|2016-10-06|Universite Grenoble Alpes|Implantable intestinal reactor|
    WO2019122441A1|2017-12-22|2019-06-27|Universite Grenoble Alpes|Implantable device for producing hydrogen|ZA827728B|1981-11-17|1983-08-31|Nestle Sa|A process for the production of enzymatically active biocatalysts and the products obtained|
    US5885609A|1997-05-23|1999-03-23|Northeastern University|Biocompatible articles and method for making same|
    CA2809372A1|2010-08-30|2012-03-08|President And Fellows Of Harvard College|A high strength chitin composite material and method of making|
    TWI526534B|2014-12-01|2016-03-21|國立台灣科技大學|A glucose oxidase/ potassium hexacyanoferrate electrospun nanofibrous membrane and a disposable glucose biosensor thereof|WO2017212304A1|2016-06-07|2017-12-14|Universite Grenoble Alpes|Bioelectrode coated with a gel of modified polysaccharide|
    ES2781376B2|2019-02-28|2021-01-27|Consejo Superior Investigacion|Wireless, portable and reusable biosensor|
    法律状态:
    2016-03-25| PLFP| Fee payment|Year of fee payment: 3 |
    2017-03-10| TQ| Partial transmission of property|Owner name: UNIVERSITE GRENOBLE ALPES, FR Effective date: 20170207 |
    2017-03-23| PLFP| Fee payment|Year of fee payment: 4 |
    2018-03-19| PLFP| Fee payment|Year of fee payment: 5 |
    2019-03-26| PLFP| Fee payment|Year of fee payment: 6 |
    2020-03-26| PLFP| Fee payment|Year of fee payment: 7 |
    2021-03-29| PLFP| Fee payment|Year of fee payment: 8 |
    优先权:
    申请号 | 申请日 | 专利标题
    FR1452534A|FR3019384B1|2014-03-25|2014-03-25|BIOCOMPATIBLE IMPLANTABLE REACTOR|
    FR1452534|2014-03-25|FR1452534A| FR3019384B1|2014-03-25|2014-03-25|BIOCOMPATIBLE IMPLANTABLE REACTOR|
    PCT/FR2015/050725| WO2015145054A2|2014-03-25|2015-03-23|Implantable biocompatible reactor|
    US15/126,236| US10316284B2|2014-03-25|2015-03-23|Implantable biocompatible reactor|
    CA2943392A| CA2943392A1|2014-03-25|2015-03-23|Implantable biocompatible reactor|
    EP15718517.4A| EP3123544B1|2014-03-25|2015-03-23|Implantable biocompatible reactor|
    [返回顶部]