    • 专利摘要:
    The invention relates to a process for the synthesis of a novel diene copolymer with a high content of phosphorus functional groups by free radical grafting of a poly (phosphorus) polymer carrying at the chain end a thiol function on a diene polymer according to the following steps: a) shaking at least one diene polymer in solution and at least one poly (phosphorus) polymer carrying a thiol functional group at the end of the chain in solution, b) heating the homogeneous reaction mixture obtained in the preceding step to the temperature of the grafting reaction, and c) adding the radical initiator concomitantly with one of the steps a) and b) or once the temperature of the grafting reaction reached.
    公开号:FR3017388A1
    申请号:FR1451037
    申请日:2014-02-11
    公开日:2015-08-14
    发明作者:Charlotte Dire；Rachid Matmour；Issam Blidi；Olivier Coutelier；Mathias Destarac
    申请人:Michelin Recherche et Technique SA Switzerland ；TOULOUSE, University of；Centre National de la Recherche Scientifique CNRS；Compagnie Generale des Etablissements Michelin SCA；Michelin Recherche et Technique SA France；Universite Paul Sabatier Toulouse III；
    IPC主号:
    专利说明:

    [0001] Process for the preparation of diene elastomers carrying phosphorus functional groups, products resulting from this process and composition containing them The present invention relates to diene elastomers bearing pendant phosphonate and / or phosphonic functions along the chain and to their process of preparation. The present invention also relates to rubber compositions containing diene elastomers carrying phosphonate and / or phosphonic functions, especially for application in vehicle tires.
    [0002] In order to modify the properties of the synthetic elastomers contained in the tire rubber compositions, different strategies are possible. Among these, the introduction of new chemical functions at the end or along the polymer chain is one of the methods used. The Applicants are particularly interested in the context of the invention in the functionalization along the diene polymer chain. Various types of reactions on unsaturations of diene polymers for functionalization are known in the literature. Diels-Alder reaction type [4 + 2] cycloaddition reactions can be mentioned between a dienophile (maleic anhydride, for example) and diene copolymers having conjugated dienes along the chain through the insertion of a conjugated triene comonomer (alloocimene) during the anionic copolymerization (EP2423239A1). We may also mention the hydrosilylation reactions of a hydrogenosilane carrying a function (epoxide, for example) on the pendant unsaturations of a diene polymer (FR 13/62946). 1,3-Dipolar cycloaddition reactions in the presence of nitrile oxide or nitrone (R. Huisgen, Angew Chem Int.Eng 1963, 2, 565-632, R. Huisgen, Angew Chem Int. Ed., 1963, 2, 633-645, JJ Tufariello, In 1,3-Dipolar Cycloaddition Chemistry, Padwa, A. Ed., Wiley-Interscience: New York, 1984, Chapter 9, p 83, KBG Torssell, Nitrile Oxides, Nitrones, and Nitronates, VCH Publishers Inc .: New York 1988, KV Gothelf, KV Jorgensen, Chem Rev 1988, 98, 863-909) are also known for functionalization (WO2012007441A1, WO2006045088A2) or diene polymer crosslinking ( FR1583406, WO2006081415A2). The radical grafting of functional or non-functional thiols via photochemical or chemical catalysts (with or without a radical initiator) is part of these functionalization reactions of diene polymers (natural and synthetic rubber) in the same way as the cycloaddition or hydrosilylation reactions mentioned. above (Angew Chem Int.Ed. 2010, 49, 1540-1573, J. Polym Sci .: Part A: Polym Chem 2004, 42, 5301-5338; Polym Chem, 2010, 1, 17-36, FR 13/62946). The Applicants are particularly interested within the scope of the invention in obtaining diene polymer carrying phosphonate and / or phosphonic functions along the chain. Indeed, phosphorus polymers have recently gained increasing interest because of their utility in a wide range of applications such as for example fuel cells (J. Fuel Cells, 2005, 5, (3), 355), membranes electrolytes (cation exchange membranes) (J.App.Poly Sci, 1999, 74, 83), flame retardants (Macromolecules, 1998, 31, 1010, Rhodia Chimie WO 2003076531), dental cement additives (J. Dent Res, 1974, 53, (4), 867), biomaterials (orthopedic applications) (J. Mater Sci Lett, 1990, 9, 1058, Macromol Rapid Commun 2006,20, 1719-24), solubilization of drugs (hydrogels for the release of drugs) (J. Appl.Polym Sci, 1998, 70, 1947), cell proliferation promoters (Fuji Photo Film Co. US 6218075; Biomaterials, 2005, 26, 3663; 3671) and corrosion inhibiting agents in cooling systems (Macromolecules, 1998, 31, 1010). The phosphonate or phosphonic function of these polymers can be either present in a monomer involved in the copolymerization with the other monomer or monomers constituting the polymer, or be obtained by the post-polymerization modification of the polymer.
    [0003] One of the methods of synthesis of diene phosphorus polymers known to those skilled in the art is the post-polymerization chemical modification of diene polymer by free radical grafting of functionalized thiols carrying a phosphorus function. The group of Pr. Boutevin (Polym Bull, 1998, 41, 145-151) describes the radical grafting of a thiol, diethyl 3-mercaptopropyl phosphonate (HS- (CH 2) 3 -PO 3 (Et) 2), on a hydroxy-telechelic polybutadiene (Mn = 1200 g / mol and 20% or 80% 1,2-butadiene unit) in THF with azobisisobutyronitrile (AIBN) as a radical initiator at 70 ° C for 6 hours. In order to have a real benefit related to the reactivity of the phosphonate and / or phosphonic functions of a diene polymer comprising them with a view to a significant modification of the properties of the polymer in its most diverse applications, it is necessary to use a polymer having high phosphonate and / or phosphonic function levels. In view of the existing methods of radical polymerization post-polymerization modification, an increase in the function rate on the polymer involves the use of a larger proportion of functionalised thiols carrying a phosphorus function. However, the use of functionalized thiol molecules bearing a phosphorus function to achieve high levels of graft functions leads to a significant change in the macrostructure of the resulting modified polymer. This macrostructure evolution observed in the context of radical grafting is generally due to secondary reactions (radical-radical bimolecular coupling, transfer reaction, etc.); the proportion of these side reactions increasing with the molar level of targeted graft functions.
    [0004] The technical problem that arises with respect to the state of the art is to have a simple and reproducible method for synthesizing a polymer having a high molar ratio of phosphonate and / or phosphonic functions while overcoming the drawbacks associated with the use of high proportions of thiol molecules carrying a phosphorus function.
    [0005] The present invention addresses this technical problem in that the inventors have developed, during their research, a new process for the preparation of diene polymers having a high molar ratio of phosphonate and / or phosphonic functions along the chain, while significantly limiting the evolution of macrostructure of the graft-related polymer with high proportions of functions. Indeed, the inventors have developed a process for preparing diene polymers carrying poly (phosphorus) grafts. A first subject of the invention is therefore a process for synthesizing a polymer with a high phosphonate and / or phosphonic function content by radical grafting of a poly (phosphorus) polymer carrying at the chain end a thiol function on a diene polymer. according to the following steps: a. shaking with at least one diene polymer and at least one poly (phosphorus) compound bearing a thiol end-chain function, each solubilized in a solvent, b. heating the homogeneous reaction mixture obtained in the preceding step to the temperature of the grafting reaction, and c. adding the radical initiator concomitantly with one of the steps a) and b) or once the temperature of the grafting reaction is reached. The subject of the invention is also a graft polymer comprising poly (phosphorus) grafts along the chain.
    [0006] The invention also relates to a reinforced rubber composition based at least on a reinforcing filler and an elastomeric matrix comprising at least one graft polymer comprising poly (phosphorus) grafts along the chain. In the present description, the term "graft" is understood to mean the poly (phosphorus) polymer chain bonded to the backbone of the polymer. In the present description, the term "phosphorus", whether it is the function or the polymer, means that a group or a polymeric unit, as the case may be, comprises at least one phosphonate function. , a phosphonic hemiacide function or a phosphonic diacid function.
    [0007] In the present description, the term "unit" of a polymer, any unit derived from a monomer of the backbone of the polymer in question. In the present description, the expression "terminated thiol" with reference to the poly (phosphorus) polymer is understood to mean carrying a thiol function at one end of the chain. In the present description, the number of moles of these units in the polymer relative to the total number of moles of the units present in said polymer is defined as the molar percentage or percentage of a unit in a polymer. In addition, the number of moles of graft in the polymer relative to the total number of moles of the diene units present in said starting polymer is defined as the mole rate or mole percentage of a graft in a polymer, or the degree of grafting. On the other hand, any range of values designated by the expression "between a and b" represents the range of values from more than a to less than b (i.e. terminals a and b excluded) while any range of values designated by the term "from a to b" means the range from a to b (i.e., including the strict limits a and b). By grafting yield is defined the amount of grafted thiol derivative relative to the amount of thiol introduced.
    [0008] The subject of the invention is therefore a process for synthesizing a polymer with a high content of phosphorus functional groups by free radical grafting of a poly (phosphorus) polymer carrying at the chain end a thiol function on a diene polymer. According to the invention, the polyphosphorus polymer carrying a thiol function at the end of the chain may be represented by the formula RP-SH, R representing an alkyl, acyl, aryl, alkenyl or alkynyl group, a saturated or unsaturated carbon cycle, optionally aromatic, a heterocycle, saturated or unsaturated, optionally aromatic; or a polymer chain, and P representing the polyphosphorus chain. As a poly (phosphorus) polymer carrying at the end of a thiol chain, there may be mentioned, according to certain variants of the invention, the compounds of general formula I: ## STR1 ## m denoting an integer greater than or equal to 1 and n denoting an integer greater than or equal to 0, provided that when n is other than 0, n and m may be identical or different, preferably each greater than 2, and preferably less than at 500. - R representing: (i) an alkyl, acyl, aryl, alkenyl or alkynyl group; (ii) a carbon cycle of groups (i), saturated or unsaturated, optionally aromatic; (iii) a heterocycle, saturated or unsaturated, optionally aromatic; these groups and rings (i), (ii) and (iii) may be substituted by substituted phenyl groups, substituted aromatic groups or groups: alkoxycarbonyl or aryloxycarbonyl (-COOR '), carboxy (-COOH), acyloxy (- 02CR '), carbamoyl (-CONR'2), cyano (-CN), alkylcarbonyl, alkylarylcarbonyl, arylcarbonyl, arylalkylcarbonyl, phthalimido, maleimido, succinimido, amidino, guanidimo, hydroxy (-OH), amino (-NR'2), halogen, allyl, epoxy, alkoxy (-OR '), S-alkyl, S-aryl, groups having a hydrophilic or ionic character such as the alkaline salts of carboxylic acids, the alkaline salts of sulfonic acid, the polyoxide chains alkylene (POE, POP), cationic substituents (quaternary ammonium salts), R 'representing an alkyl or aryl group; (iv) a polymer chain; X and X ', which are identical or different, representing a hydrogen atom, a halogen or a group R1, OR1, O2COR1, NHCOH, OH, NH2, NHR1, N (R1) 2, (R1) 2N + O-, NHCOR1, CO2H, CO2R1, CN, CONH2, CONHR1 or CON (R1) 2, wherein R1 is selected from alkyl, aryl, aralkyl, alkylaryl, alkene or organosilyl groups, optionally perfluorinated and optionally substituted with one or more carboxyl groups, epoxy, hydroxyl, alkoxy, amino, halogen or sulfonic acid; Y or Y ', which may be identical or different, are such that either Y, Y' or both comprise at least one phosphorus functional group -P (O) (OR 2) (OR 3) in which R 2 and R 3, which are identical or different, , represent a hydrogen atom or an alkyl radical, optionally haloalkyl.
    [0009] According to the invention, the term "alkyl" denotes a linear or branched hydrocarbon radical of 1 to 20 carbon atoms, such as methyl, ethyl, propyl, isopropyl, butyl, tert-butyl, isobutyl, pentyl, hexyl, heptyl or octyl. , nonyl, decyl, undecyl, dodecyl, tridecyl, tetradecyl, pentadecyl, hexadecyl, heptadecyl, octadecyl, nonadecyl or icosyl.
    [0010] By "alkenyl" is meant a linear or branched hydrocarbon chain of 2 to 20 carbon atoms comprising one or more double bonds. Examples of particularly preferred alkenyl groups are alkenyl groups carrying a single double bond such as -CH 2 -CH 2 -CH = C (CH 3) 2, vinyl or allyl.
    [0011] By "alkynyl" is meant a linear or branched hydrocarbon chain of 2 to carbon atoms comprising one or more triple bonds. Examples of particularly preferred alkynyl groups are alkynyl groups bearing a single triple bond such as -CH2-CH2-CECH. By "cycloalkyl" is meant saturated hydrocarbon groups which may be mono-or polycyclic and comprise from 3 to 12 carbon atoms, preferably from 3 to 8. Particularly preferred are monocyclic cycloalkyl groups such as cyclopropyl, cyclobutyl, cyclopentyl, cyclohexyl, cycloheptyl, cyclooctyl, cyclononyl, cyclodecyl, cycloundecyl and cyclododecyl.
    [0012] By "cycloalkenyl" is meant according to the invention a group derived from a cycloalkyl group as defined above, having one or more double bonds, preferably a double bond. By "cycloalkynyl" is meant according to the invention a group derived from a cycloalkyl group as defined above, having one or more triple bonds, preferably a triple bond. By "aryl" is meant an aromatic mono or bicyclic hydrocarbon group comprising 6 to 10 carbon atoms, such as phenyl or naphthyl.
    [0013] By "alkaryl" is meant an alkyl group as defined above, substituted with an aryl group. By "aralkyl" is meant an alkyl group as defined above, substituted with an aryl group.
    [0014] By "alkoxy" is meant an O-alkyl group generally having 1 to 20 carbon atoms, especially methoxy, ethoxy, propoxy and butoxy. The heterocyclic group (iii) denotes saturated or preferably unsaturated monocyclic or bicyclic carbon rings having 5 to 12 members and having 1, 2 or 3 endocyclic heteroatoms selected from O, N and S. These are generally derivatives of heteroaryl groups. Generally speaking, "heteroaryl" means 5- to 7-membered monocyclic aromatic groups or 6- to 12-membered bicycles comprising one, two or three endocyclic heteroatoms chosen from O, N and S. Examples are furyl groups, thienyl, pyrrolyl, oxazolyl, isoxazolyl, thiazolyl, isothiazolyl, imidazolyl, pyrazolyl, oxadiazolyl, triazolyl, thiadiazolyl, pyridyl, pyridazinyl, pyrazinyl and triazinyl. Preferably, the heterocycle when unsaturated comprises a single double bond. Preferred examples of unsaturated heterocycles are dihydrofuryl, dihydrothienyl, dihydropyrrolyl, pyrrolinyl, oxazolinyl, thiazolinyl, imidazolinyl, pyrazolinyl, isoxazolinyl, isothiazolinyl, oxadiazolinyl, pyranyl and mono-unsaturated derivatives of piperidine, dioxane, piperazine, trithiane, morpholine, dithiane, thiomorpholine, as well as tetrahydropyridazinyl, tetrahydropyrimidinyl, and tetrahydrotriazinyl. According to variants of the invention, R is as defined in WO 98/58974, WO 00/75207 and WO 01/42312 (definition of R1), WO 98/01478 and WO 99/31144 (definition of R ), or WO 02/26836 (definition of R1). Among these variants, R is more particularly a cyanomethyl group CNCH2-, 1-phenylethyl CH3 (C6H5) CH- or methylpropionyl CH3 (CO2CH3) CH-.
    [0015] The mole fraction of monomer units of the poly (phosphorus) polymer having X and X 'may be zero, and generally ranges from 0 to 0.5, preferably from 0 to 0.25, more preferably from 0 to 0.1.
    [0016] Among the monomers from which the units carrying phosphorus functional groups in Y and Y 'that are useful in the present invention are vinyl phosphonic acid, vinyl phosphonic acid dimethyl ester, bis (2-chloroethyl), and the like; vinyl phosphonic acid ester, vinylidene diphosphonic acid, vinylidene diphosphonic acid tetraisopropyl ester, alpha-styrene phosphonic acid, dimethyl-p-vinylbenzylphosphonate, diethyl-p-vinylbenzylphosphonate, dimethyl (methacryloyloxy) methyl phosphonate, diethyl (methacryloyloxy) methyl phosphonate, diethyl-2- (acrylamido) ethylphosphonate. More generally, any unsaturated styrene monomer, acrylate or methacrylate, acrylamido or methacrylamido, vinyl or allyl carrier of at least one dialkylphosphonate, phosphonic acid diacid or hemiacide-P (OH) (OR), or a mixture of these monomers. In a preferred manner, the dimethyl ester of vinylphosphonic acid and dimethyl-p-vinylbenzylphosphonate will be used. Among the comonomers from which the X and X 'substituted units useful in the present invention are derived, there may be mentioned hydrophilic (h) or hydrophobic (H) monomers selected from the following monomers. Among the hydrophilic monomers (h), mention may be made of: polyvinyl alcohol resulting from the hydrolysis of vinyl acetate units for example. neutral acrylamido monomers such as acrylamide, N, N-dimethylacrylamide and N-isopropylacrylamide. the cyclic amides of vinylamine, such as N-vinylpyrrolidone and vinylcaprolactam. ethylenically unsaturated mono- and di-carboxylic acids such as acrylic acid, methacrylic acid, itaconic acid, maleic acid, or fumaric acid. ethylenic monomers comprising a sulphonic acid group or an alkali metal or ammonium salt thereof, for example vinylsulphonic acid, vinylbenzene sulphonic acid, alpha-acrylamidomethylpropanesulphonic acid or 2-sulphoethylene methacrylate, or - the cationic monomers chosen from aminoalkyl (meth) acrylates, aminoalkyl (meth) acrylamides; monomers comprising at least one secondary, tertiary or quaternary amine functional group, diallyldialkyl ammonium salts such as dimethylaminoethyl (meth) acrylate, dimethylaminopropyl (meth) acrylate, dimethylaminopropyl (meth) acrylamide, 2- vinylpyridine, 4-vinylpyridine and diallyldimethylammonium chloride. Preferably, the hydrophilic monomeric units (h) are chosen from acrylic acid (AA), dimethylaminopropyl acrylamide, and N-vinylpyrrolidone. Among the monomers having a hydrophobic character (H), mention may be made of: styrenic derived monomers such as styrene, alpha-methylstyrene, para-methylstyrene or para-tert-butylstyrene, or acrylic acid esters or methacrylic acid with optionally fluorinated C1-C12, preferably C1-C8, alcohols, such as, for example, methyl acrylate, ethyl acrylate, propyl acrylate, n-butyl acrylate, isobutyl acrylate, 2-ethylhexyl acrylate, t-butyl acrylate, methyl methacrylate, ethyl methacrylate, n-butyl methacrylate, methacrylate isobutyl, - vinyl nitriles containing from 3 to 12 carbon atoms, and especially acrylonitrile or methacrylonitrile, - vinyl esters of carboxylic acids, such as vinyl acetate (VAc), vinyl versatate, or vinyl propionate, vinyl or vinylidene halides, for example chlorine vinylidene chloride and vinylidene fluoride; and diene monomers, for example butadiene or isoprene.
    [0017] Preferably, the hydrophobic monomer units (H) of the controlled-architecture copolymers of the invention are butadiene, isoprene, butyl acrylate and styrene.
    [0018] The poly (phosphorus) functional thiol polymer as defined above has an average number of units of at least 2 and at most equal to 1000. The poly (phosphorus) functional thiol polymer at the end of the chain may be any homopolymer obtained by polymerization of a monomer carrying at least one phosphorus functional group, or any copolymer of one or more monomers bearing at least one phosphorus functional group with one another or with one or more comonomers. According to variants of the invention, the poly (phosphorus) functional thiol polymer at the end of the chain can be obtained by controlled RAFT or MADIX (free radical controlled polymerization) of at least one monomer carrying at least one phosphorus functional group in the presence of a source of free radicals and a thiocarbonylthio chain transfer agent of general formula (II): RS (C = S) -Z (II) wherein R represents: (i) alkyl, acyl, aryl, alkenyl or alkynyl; (ii) a carbon cycle, saturated or unsaturated, optionally aromatic; (iii) a heterocycle, saturated or unsaturated, optionally aromatic; these groups and rings (i), (ii) and (iii) may be substituted by substituted phenyl groups, substituted aromatic groups or groups: alkoxycarbonyl or aryloxycarbonyl (-COOR '), carboxy (-COOH), acyloxy (- 02CR '), carbamoyl (-CONR'2), cyano (-CN), alkylcarbonyl, alkylarylcarbonyl, arylcarbonyl, arylalkylcarbonyl, phthalimido, maleimido, succinimido, amido, guanidimo, hydroxy (-OH), amino (-NR'2) halogen, allyl, epoxy, alkoxy (-OR '), S-alkyl, 5-aryl, hydrophilic or ionic groups such as the alkali metal salts of carboxylic acids, the alkaline salts of sulfonic acid, the chains polyalkylene oxide (POE, POP), cationic substituents (quaternary ammonium salts), R 'representing an alkyl or aryl group; (iv) a polymer chain; Z is an oxygen atom, a carbon atom, a sulfur atom, a nitrogen atom or a phosphorus atom, these atoms being substituted with one, two or three hydrocarbon radicals R ", so as to have a suitable valency, which may comprise at least one heteroatom, such that R "represents a group as defined above for R. According to variants of the invention, R and R" are as defined in the documents WO 98/58974. , WO 00/75207 and WO 01/42312 (definition of R1 respectively R2), WO 98/01478 and WO 99/31144 (definition of R respectively of Z and Ei), or WO 02/26836 (definition of R1 respectively the grouping According to variants of the invention, in the general formula (II), R is more particularly a cyanomethyl group CNCH2-, 1-phenylethyl CH3 (C6H5) CH- or methylpropionyl CH3 (CO2CH3) CH-. of the invention, in the general formula (II), Z denotes a group "OR" with R "denoting an alkyl radical e at C1-05, more preferably at C1-C2. Thus, according to variants of the invention, the poly (phosphorus) polymers of formula I can be obtained by RAFT or MADIX polymerization of monomers comprising Y and Y 'and, where appropriate, the monomers comprising X and X', in particular those listed above, in the form of homopolymers (where n = 0) or random or block copolymers. The preferred and variant aspects above are combinable with each other. The synthesis of a thiocarbonylthio transfer agent of the general formula (II) can be carried out in a manner known to those skilled in the art.
    [0019] The RAFT or MADIX polymerization initiator may be chosen from the initiators conventionally used in radical polymerization. Transfer agents or processes that are useful for carrying out the synthesis of the polyphosphorous polymer carrying a thiol function are described in particular in the following documents: the methods and agents of the applications WO 98/58974, WO 00/75207 and WO 01/42312 which carry out a radical polymerization controlled by xanthate control agents (-S- (C = S) -O- group), the process and the radical polymerization agents controlled by control agents. type dithioesters (-S- (C = S) -S-carbon group) or trithiocarbonates (-S- (C = S) -S-) group of the application WO 98/01478, the process and the radical polymerization agents controlled by dithiocarbamate type control agents (-S- (C = S) -Azote group) of the application WO 99/31144, the process and the radical polymerization agents controlled by dithiocarbazate control agents (group -S- (C = S) -Azote) of the application WO 02/26836, - the agents of the type xanthates, dithiocarbonates and / or trithiocarbonates described in documents WO002070571; W02001060792; W02004037780; WO2004083169; W02003066685; W02005068419; W02003062280; W02003055919; WO2006023790, and methods using them. One of the advantages of the RAFT or MADIX polymerization process is the ability to control the length of the poly (phosphorus) polymer by adjusting the molar ratio of the monomer and the transfer agent. The molar ratio of the monomer 20 to the transfer agent is generally at least 2. According to variants of the invention related to the choice of the phosphorus monomer, this ratio is at most 1000. At the end of polymerization, the product is predominantly of the general formula R-PS- (C = S) -Z, where P denotes the poly (phosphorus) polymer chain. The thiol derivative R-P-SH is obtained by chemical modification of this finished thiocarbonylthio product. Among the methods envisaged, advantageously the aminolysis reaction conducted in general with primary or secondary amine compounds. Even more advantageously, the poly (phosphorus) terminated thiol R-P-SH polymer is formed directly by thermolysis of particular thiocarbonylthio groups, for example xanthates derived from secondary alcohol.
    [0020] The process for synthesizing a polymer with a high phosphonate and / or phosphonic function by radical grafting of a poly (phosphorus) polymer onto a diene polymer according to the invention consists in grafting poly (phosphorus) polymers carrying a chain end thiol function as defined above for the grafting on unsaturations of the diene polymer. By diene polymer is meant according to the invention, any polymer in the sense known to those skilled in the art, derived at least in part (ie, a homopolymer or a copolymer) of monomers dienes (monomers carrying two carbon-carbon double bonds , conjugated or not).
    [0021] According to the invention, the diene polymers can be classified into two categories: "essentially unsaturated" or "essentially saturated". The term "essentially unsaturated" means a diene elastomer derived at least in part from conjugated diene monomers, having a proportion of units or units of diene origin (conjugated dienes) which is greater than 15% (°) / 0 in moles) . It is to this category of "essentially unsaturated" elastomers that the process according to the invention is more particularly directed. In the category of "essentially unsaturated" diene elastomers, the term "highly unsaturated" diene elastomer is particularly understood to mean a diene elastomer having a content of units of diene origin (conjugated dienes) which is greater than 50% (°) / 0 in mole). The term "substantially saturated" means a diene elastomer having a content of units or units of saturated type which is greater than 20% (°) / 0 in mole). The units or units of the saturated type may be units of structure equivalent to that obtained from an olefin-type monomer. In the category of "essentially saturated" diene elastomers, the term "highly saturated" diene elastomer is understood to mean a diene elastomer having a content of units or units of saturated type which is greater than 50% (°) / 0 in moles) . The term "diene elastomer" that may be used in the invention is more particularly understood to mean: (a) any homopolymer obtained by polymerization of a conjugated diene monomer having from 4 to 15 carbon atoms, for example 1,3-butadiene, 2-methyl-1,3-butadiene, 2,3-di (C 1 -C 5 alkyl) -1,3-butadienes, such as, for example, 2,3-dimethyl-1,3-butadiene, 3-diethyl-1,3-butadiene, 2-methyl-3-ethyl-1,3-butadiene, 2-methyl-3-isopropyl-1,3-butadiene, an aryl-1,3-butadiene, 1,3-pentadiene, 2,4-hexadiene; (b) any copolymer obtained by copolymerization of one or more of the conjugated dienes mentioned above, with one another or with one or more ethylenically unsaturated monomers. As ethylenically unsaturated monomers, mention may be made of: vinylaromatic compounds containing from 8 to 20 carbon atoms, for example styrene, ortho-, meta-, para-methylstyrene, para-tertiobutylstyrene or alpha-methylstyrene, the commercial mixture "vinyl-toluene", vinylmesitylene, divinylbenzene, vinylnaphthalene; vinyl nitrile monomers having 3 to 12 carbon atoms, for example acrylonitrile or methacrylonitrile; acrylic ester monomers derived from acrylic acid or methacrylic acid with alcohols having 1 to 12 carbon atoms, for example methyl acrylate, ethyl acrylate or propyl acrylate, n-butyl acrylate, isobutyl acrylate, 2-ethylhexyl acrylate, methyl methacrylate, ethyl methacrylate, n-butyl methacrylate, isobutyl methacrylate; The copolymers may contain between 99% and 20% by weight of diene units and between 1% and 80% by weight of vinylaromatic units, vinyl nitriles and / or acrylic esters. (c) a ternary copolymer obtained by copolymerization of ethylene, an α-olefin having 3 to 6 carbon atoms with a non-conjugated diene monomer having from 6 to 12 carbon atoms, for example elastomers obtained from ethylene, of propylene with a non-conjugated diene monomer of the aforementioned type, such as in particular 1,4-hexadiene, vinyl norbornene, ethylidene norbornene, norbornadiene, dicyclopentadiene; (d) a copolymer of isobutene and isoprene (butyl rubber), as well as the halogenated, in particular chlorinated or brominated, versions of this type of copolymer; (e) natural rubber; (f) a copolymer of a conjugated diene monomer selected from C4 to C8 conjugated diene monomers and an olefin / alpha-olefin monomer selected from ethylene or C3 to C20 alpha-olefins; (g) a mixture of several of the elastomers defined in (a) to (f) between them. The diene elastomers that can be used according to the invention can be obtained according to conventional polymerization techniques well known to those skilled in the art which is a function of the nature, the macrostructure and the microstructure of the elastomer. The elastomers may have any microstructure which is a function of the polymerization conditions used, in particular the presence or absence of a modifying and / or randomizing agent and the amounts of randomizing modifying agent used. The elastomers can be, for example, block, random, sequence, microsequential, and be prepared in dispersion, in emulsion or in solution; they may be coupled and / or starred or functionalized with a coupling agent and / or starring or functionalization. Among the elastomers used in the context of the grafting process according to the invention, non-exclusive examples include polybutadiene, polyisoprene, polychloroprene and their hydrogenated versions, polyisobutylene, block copolymers of butadiene and polyisobutylene. isoprene with styrene, as well as their hydrogenated versions such as poly styrene-b-butadiene (SB), poly styrene-b-butadiene-b-styrene (SBS), poly styrene-b-isoprene-b-styrene (SIS) ), poly styrene-b- (isoprene-stat-butadiene) -b-styrene or poly styrene-b-isoprene-b-butadiene-b-styrene (SIBS), hydrogenated SBS (SEBS), poly styrene-b -butadiene-b-methyl methacrylate (SBM), as well as its hydrogenated version (SEBM), random copolymers of butadiene with styrene (SBR) and acrylonitrile (NBR) and their hydrogenated versions, statistical copolymers of isoprene with styrene (SIR) and their hydrogenated versions, copolymers isoprene and butadiene styrene statistics (SBIR) and their hydrogenated versions, butyl or halogenated rubbers, ethylene-propylene-diene copolymers (EPDM), ethylene-diene copolymers and mixtures thereof. Among these, the diene elastomer (s) used in the invention are very particularly chosen from the group of diene elastomers consisting of polybutadiene (abbreviated as "BR"), synthetic polyisoprene (IR) and natural rubber (NR). ), butadiene copolymers, isoprene copolymers and mixtures of these elastomers. Such copolymers are more preferably selected from the group consisting of butadiene-styrene copolymers (SBR), isoprene-butadiene copolymers (BIR), isoprene-styrene copolymers (SIR), isoprene-copolymers of butadiene styrene (SBIR) and ethylene-butadiene copolymers (EBR), as well as mixtures thereof. According to variants of the invention, the diene elastomer or elastomers used in the process of the invention are chosen from elastomers having a mass ratio of units bearing pendant unsaturation along the chain, in particular of the vinyl type (for example type-1,2 and -3,4 units), in the diene part, greater than 20%, preferably at least 40% and more preferably still at least 50%. According to the invention, the diene polymer bearing poly (phosphorus) grafts is obtained by carrying out the following steps: a. stirring at least one diene polymer in solution and at least one poly (phosphorus) polymer carrying a thiol end-chain function in solution, b. heating the homogeneous reaction mixture obtained in the preceding step at the temperature of the grafting reaction, and c. add the radical initiator concomitantly with one of the steps a) and b) or preferably once the temperature of the grafting reaction reached. The process according to the invention involves contacting at least one diene polymer in solution and at least one poly (phosphorus) polymer carrying a thiol functional group at the end of the chain in solution. This implies the prior solubilization of the different polymers in appropriate solvents. According to one embodiment, the diene elastomer is dissolved in a first solvent and is mixed, with stirring, preferably mechanically, with the poly (phosphorus) functionalized thiol polymer at the end of the chain dissolved in a second solvent. Or conversely, the poly (phosphorus) functionalized end-thiol polymer in solution in a solvent is mixed with stirring, preferably mechanically, the diene elastomer in solution in another solvent with stirring.
    [0022] Thus, in step a), the reaction mixture comprises a solvent which is constituted according to the invention of a mixture comprising at least one solvent of the diene polymer and at least one solvent of the poly (phosphorus) polymer. Preferably, the two solvents are miscible. According to a variant of the process of the invention, the solvents are identical.
    [0023] As a solvent for the poly (phosphorus), it is possible to use any polar solvent such as a ketone, a sulfoxide, a THF (tetrahydrofuran) type ether or dioxane, a halogenated solvent of chloroform type, dichloromethane, dichloroethane, tetrachloroethane, 1, 2-dichlorobenzene, etc., and mixtures thereof. Preferably, 1,2-dichlorobenzene or THF is used.
    [0024] As a solvent for the diene elastomer, any inert hydrocarbon solvent which may be for example an aliphatic or alicyclic hydrocarbon such as pentane, hexane, heptane or iso, may be used according to the process according to the invention. octane, cyclohexane, methylcyclohexane or an aromatic hydrocarbon such as benzene, toluene, xylene, and mixtures thereof, or a polar ether-type solvent such as THF, dioxane and their mixture. Preferably, methylcyclohexane, toluene or THF is used. According to the variant in which the solvents of the different polymers are identical, THF is preferably used.
    [0025] One variant of the process of the invention consists in using a mixture of poly (phosphorus) polymers functionalized at the end of the chain as defined above as molecules to be grafted onto the diene polymer. The process according to the invention comprises the step of heating the homogeneous reaction mixture obtained in the preceding step to the temperature of the grafting reaction. The grafting reaction temperature is at least 20 ° C, preferably at least 50 ° C and even more preferably 60 ° C. The grafting reaction temperature is at most 120.degree. C., preferably at most 100.degree. C. and even more preferably at most 90.degree.
    [0026] The process according to the invention comprises the step of adding a radical initiator, which, once the temperature of the grafting reaction is reached, results in the grafting of the poly (phosphorus) functionalized thiol polymer at the end of the chain onto the units. polymer having unsaturations. As a radical initiator, any initiator known to those skilled in the art can be used according to the invention. There may be mentioned, for example, azobisisobutyronitrile or else peroxides generally such as lauroyl peroxide or peroxypivalate. The radical initiator may be added, in part or in whole, to the reaction mixture at any time of steps a), b) or once the grafting temperature has been reached. The addition of the radical initiator after heating the medium, once the grafting temperature has been reached, constitutes a preferred variant of the process of the invention. The radical initiator may be added to the reaction mixture in any customary form, however, preferably in the form of a solution in a solvent. Preferably, the solvent of the radical initiator is identical to at least one of the polar and apolar solvents used to solubilize respectively the polymer to be grafted and the diene elastomer. As such a solvent, there may be mentioned THF. Preferably, the molar ratio of the poly (phosphorus) terminated thiol polymer to the radical initiator is at least 5, preferably at least 10, or even at least 45, and is at most 100, preferably at most 60. More preferably still, the The molar ratio of the poly (phosphorus) terminated thiol polymer to the radical initiator is at least 45 and at most 55.
    [0027] Preferably, the amount of total solvent, or solvent of the reaction medium, is such that the mass concentration of elastomer is between 1 and 50%, preferably between 2 and 20% and even more preferably between 3 and 10% in said solvent.
    [0028] The grafting reaction is carried out according to a mechanism known to those skilled in the thiol-ene reaction art, ie a hydrothiolation of a carbon-carbon double bond. It should be noted that in the context of the invention the variants and the preferred aspects described above are combinable with each other.
    [0029] At the end of this grafting reaction, a certain percentage of double bonds carried by the diene polymer was consumed by the reaction, essentially the pendant double bonds along the chain, in particular the double bonds of vinyl origin. The final polymer is characterized by its molar fraction in phosphorus functional groups, itself linked to the molar fraction of poly (phosphorus) grafts as well as to the degree of polymerization of the poly (phosphonate) graft. Those skilled in the art will understand that it is not possible to quantify this molar level in phosphorus functions since it can vary for the same elastomer, or the same diene part, in a range which is limited in value low to a low level. grafting with poly (phosphorus) polymers having a low proportion of phosphorus units, at least two, and a high value at 100% grafting rate by poly (phosphorus) polymers having a high proportion of phosphorus units m, m being preferably at most 500. The radical grafting method according to the invention can be carried out continuously or discontinuously. Those skilled in the art will understand that depending on its implementation, the process steps, in particular steps a), b) and c), then take place simultaneously or in succession. After grafting, the reaction is stopped in a conventional manner known to those skilled in the art, for example by adding to the grafted elastomer obtained an antioxidant, such as 4,4'-methylene bis-2,6-tert-butylphenol or any other suitable agent. This antioxidant may be added as a solution in an organic solvent, such as toluene or methylcyclohexane, which is then evaporated. According to variants of the invention, according to which poly (phosphorus) polymers comprising phosphonate functions are grafted along the polymer chain, at the end of the grafting reaction, the phosphonate functions can advantageously be converted by means of methods known to those skilled in the art, in part or in whole, phosphonic acid functions (for example by reaction with TMSiBr / MeOH) or phosphonic hemiacide functions (for example by reaction with sodium iodide Nal) Another The subject of the invention is the grafted diene polymer bearing poly (phosphorus) grafts along the chain that can be synthesized by the method described above. The grafted diene polymer according to the invention comprises a main chain derived from the diene polymer and side chains, or grafts, derived from the poly (phosphorus) terminated thiol polymer. According to some variants, the grafted diene polymer corresponds to formula (III): P [- G (III) in which - P represents the polymer chain derived from the diene polymer, - G represents the poly (phosphorus) graft derived from the poly polymer (Phosphorus) terminated thiol of formula I described above, and - i represents the number of grafted units. P represents the polymer chain derived from the diene polymer. The latter is as described above, encompassing all its variants. G represents the poly (phosphorus) graft derived from the poly (phosphorus) terminated thiol polymer described above. G comprises the sulfur atom that binds it to the polymer. According to variants, G encompasses all the variant definitions of formula I relating to R and the monomer units from which the poly (phosphorus) polymer is derived. i represents the number of grafted units. It is a number at least equal to 1. According to one variant of the invention, i is at most equal to 10,000 in the same graft polymer molecule. The polymer according to the invention has the particularity of being able to contain a high level of phosphorus functions. Indeed, the molar fraction in phosphorus functions, depends on the molar fraction of poly (phosphorus) grafts, as well as the degree of polymerization of the poly (phosphorus) part of the graft.
    [0030] According to variants of the invention, the degree of polymerization of the poly (phosphorus) portion of the graft varies from 2 to 500. The molar fraction of poly (phosphorus) grafts is itself dependent on the yield of the grafting reaction and the unsaturations rate. According to variants of the invention, the molar ratio of poly (phosphorus) grafts relative to the diene portion of the diene polymer is at least 0.05%, preferably 0.2% and even more preferably 0.3% and it is at most 30%, preferably 15% and even more preferably 10%. The diene polymers carrying poly (phosphorus) grafts according to the invention can be used as such or in mixtures with one or more other compounds. The presence of phosphonate or phosphonic groups along the chain makes it possible to envisage use in applications similar to those of modified diene polymers in general, and polymers bearing phosphonate or phosphonic functions in particular. For example, it is known for the optimization of the interactions between the elastomer and the reinforcing filler within a reinforced rubber composition, to modify the nature of the diene polymers in order to introduce functional groups therein. Thus, the particular structure of the graft polymer according to the invention makes it possible to envisage its use in the manufacture of various products based on reinforced rubber.
    [0031] Another object of the invention is therefore a rubber composition comprising a reinforcing filler and an elastomer as described above or prepared by radical grafting according to the method described above. The rubber composition according to the invention has the characteristic of comprising a reinforcing filler, for example carbon black, a reinforcing inorganic filler such as silica with which a coupling agent is associated in known manner, or a mixture of these two types of load. According to an advantageous variant of the invention, the reinforcing filler is predominantly other than carbon black, that is to say that it preferably comprises more than 50% by weight of the total weight of the filler, one or several fillers other than carbon black, especially a reinforcing inorganic filler such as silica, or it consists exclusively of such a filler. According to this variant, when carbon black is also present, it may be used at a level of less than 20 phr, more preferably less than 10 phr (for example between 0.5 and 20 phr, in particular between 2 and 10 phr). Preferably, the content of total reinforcing filler (carbon black and / or other reinforcing filler such as silica) is between 10 and 200 phr, more preferably between 30 and 150 phr, the optimum being in a known manner different according to the particular applications targeted. Another characteristic of the rubber composition according to the invention is to comprise the grafted diene polymer carrying poly (phosphorus) grafts. According to variants of the invention, the composition may, in addition to this graft polymer, comprise at least one conventional diene elastomer. This or these diene elastomers are then present in the elastomer matrix in proportions of between 0 and 60 phr (the limits of this range being excluded), preferably at most 50 phr, even more preferably at most 30 phr. In the case of a blend with at least one conventional diene elastomer, the mass fraction of the diene polymer grafted in the elastomeric matrix is predominant and preferably greater than 40 phr; more preferably still this rate is at least 50 phr, in particular at least 70 phr.
    [0032] As conventional diene elastomer are more particularly suitable polybutadienes (BR), butadiene copolymers, polyisoprenes (PI), isoprene copolymers and mixtures of these elastomers. Such copolymers are more preferably chosen from the group consisting of copolymers of butadiene and a vinylaromatic monomer, more particularly butadiene-styrene copolymer (SBR), isoprene-butadiene copolymers (BIR), copolymers of isoprene and a vinylaromatic monomer, more particularly the isoprene-styrene copolymer (SIR) and the isoprene-butadiene-styrene copolymers (SBIR).
    [0033] According to variants of the invention, the conventional diene elastomer may be star-shaped, coupled, functionalized or otherwise, in a manner known per se, by means of functionalising, coupling or starring agents known to man of the art. 'art. The rubber compositions in accordance with the invention may also comprise all or part of the usual additives normally used in elastomer compositions intended for the manufacture of tires, for example pigments, protective agents such as anti-ozone waxes, chemical antiozonants, anti-oxidants, anti-fatigue agents, reinforcing or plasticizing resins, acceptors (for example phenolic novolac resin) or methylene donors (for example HMT or H3M) as described, for example, in the application WO 02/10269, a crosslinking system based on either sulfur, or sulfur and / or peroxide and / or bismaleimide donors, vulcanization accelerators, vulcanization activators, adhesion promoters such as compounds based on cobalt, plasticizing agents, preferably non-aromatic or very weakly aromatic selected from the group consisting of naphthenic, paraffinic oils, MES oils, TDAE oils, ethers plasticizers, ester plasticizers, hydrocarbon resins having a high Tg, preferably greater than 30 ° C, as described for example in the applications WO 2005/087859, WO 2006 / 061064 and WO 2007/017060, and mixtures of such compounds.
    [0034] In the field of tires, especially for vehicles, the use of such a rubber composition is particularly appropriate. Therefore, a tire including one of these components comprises a rubber composition based on a grafted diene polymer described above by its structure or its method of synthesis, is also an object of the invention. The aforementioned features of the present invention, as well as others, will be better understood on reading the following description of several embodiments of the invention, given by way of illustration and not limitation.
    [0035] EXAMPLE OF CARRYING OUT THE INVENTION Measurements used The elastomers are characterized, before cooking, as indicated below.
    [0036] Size Exclusion Chromatography The number average molecular weights Mn of the polymers and their dispersions were obtained by size exclusion chromatography (SEC) with tetrahydrofuran (THF) as eluent at 1 ml / min. Calibration is carried out with polystyrene (PS) standards having molar masses of between 1200 and 512800 g mol-1. The CES chain is equipped with a Waters 2414 RI detector and a set of 2 columns (Shodex KF-802.5 and KF-804) thermostatically controlled at 35 ° C.
    [0037] Glass transition temperature The glass transition temperature determination analyzes were carried out with a Netzsch DSC (Phoenix) device.
    [0038] An aluminum crucible comprising 5 to 10 mg of sample is deposited on a platinum boat. The rate of temperature rise used for all the samples is 10 ° C.min-1. The analyzes were conducted under nitrogen.
    [0039] Nuclear Magnetic Resonance Spectroscopy 1 H NMR, 31 P NMR, and 13 C NMR were recorded on a 300 MHz Bruker spectrometer at room temperature and using CDCl 3 as a solvent. The chemical shifts are indicated in ppm. The monomer conversions are determined by 1 H NMR and 31 P NMR.
    [0040] EXAMPLES OF EMBODIMENT OF THE INVENTION EXAMPLE 1 Synthesis of Cyanomethyl Functioning Xanthate C4-Scheme Diagram 1. Synthesis of Xanthate with Cyanomethyl C4 Function In a 500 ml flask, 6 g (6.81 × 10 -2 mol) of 3 -methylbutanol are solubilized in 45 mL of THF. A solution of BuLi (1.6 M in hexane) (46.5 mL, 7.44 × 10 -2 mol) is added dropwise at 0 ° C. to the reaction mixture. The reaction is stirred for 30 minutes. Carbon disulfide (30 ml, 4.96 × 10 -3 mol) is added dropwise at 0 ° C. to the reaction medium. The reaction mixture is then kept under magnetic stirring for 30 minutes at 0 ° C. (11.6 g, 13.62 10 -2 mol) of bromoacetonitrile is added dropwise to the reaction mixture and the solution is stirred for 15h. After evaporation of THF, the residue is purified by CH 2 Cl 2 / water (1: 1) extraction. The CH 2 Cl 2 solution is evaporated under vacuum. After purification on a chromatographic column (eluent: petroleum ether / ethyl acetate, 95/5) and evaporation, the product is obtained in the form of a yellowish oil with a final yield of 86%. 1 H NMR (300 MHz, CDCl3, b = ppm): 5.58 (1H, m, 0-CHCH3), 3.85 (2H, s, NC-CH2-SC = S), 2.02 (1H, m, (-CH (CH3) 2), 1.33 (3H, d, O-CHCH3), 0.96 (6H, d, (-CH (CH3) 2) 13C NMR (300 MHz, CDCl3, b = ppm): 208.6 (S = CSCH-), 115.5 (NC-CH2-SC = S), 87.8 (O-CHCH3), 32.7 ((-CH (CH3) 2), 21 , 1 (NC-CH2-SC = S), 18.1 (-CH (CH3) 2), 17.9 (O-CHCH3), 15.8 (O-CHCH3) n-BuLi / THF CS2 excess Example 2: Synthesis of DMVP-C4 Dimethyl Vinylphosphonate Monoadduct - C2H4Cl2 DLP Reaction Scheme Figure 2. Synthesis of DMVP-C4 Monoadduct In a 25 mL flask surmounted by a coolant, C4 xanthate (2.76 g, 13, 59.10-2 mol), dimethyl vinylphosphonate (1 g, 7.35 × 10 -3 mol) and the solvent 1,2-dichloroethane (6 ml), the mixture is degassed with argon for 15 minutes. maintained at reflux of the solvent (95 ° C.) and with magnetic stirring for 7 hours 5 mol% of dilauroyl peroxide are added every 60 minutes to 25 mol% After purification on a chromatographic column (eluent ethyl acetate) and evaporation, the final yield of the synthesis is 65%. 1H NMR (300 MHz, CDCl3, b = ppm): 5.58 (1H, m, O-CHCH3), 4.35 (1H, m, NC-CH2-CH2-CH1-SC = S), 3, 82 (3H, s, P = (OCH3) 2), 2.62 (2H, m, NC-CH2-CH2-CH1-SC = S), 2.45-2.21 (2H, m, NC-CH2) -CH2-CHI-SC = S), 2.03 (-CH (CH3) 2), 1.35 (3H, d, O-CHCH3), 0.95 (6H, d, (-CH (CH3) 2 31 P NMR (300 MHz, CDCl3, b = ppm): 24.6 (1 P, d, P = (OCH3) 2) 13C-NMR (300 MHz, CDCl3, b = ppm): 210.7 (S = CSCH) -), 119.1 (NC-CH2-CH2-CH1-SC = S), 88.0 (O-CHCH3), 54.2 (P = (OCH3) 2), 44.4 and 42.6 (NC- CH2-CH2-CH1-SC = S), 32.7 ((-CH (CH3) 2), 26.6 (NC-CH2-CH2-CHI-SC = S), 19.1 (- CH (CH3) 2), 16.4 (O-CHCH3), 15.1 (NC-CH2-CH2-CH2-SC = S) Example 3: Aminolysis of the DMVP-C4 Monoadduct - Scheme Diagram 3. Aminolysis of the DMVP-monoadduct C4 In a 25mL flask, 200mg (2.94.104 mol) DMVP-C4 monoadduct are solubilized in 6 mL of dichloromethane The flask is placed in an ice bath, degassed with argon for 15 minutes and then stored protected from light in an inert atmosphere until solubilization n full of monoadduit. A second solution containing 1 ml of propylamine in 40 ml of dichloromethane is prepared and then degassed with argon for 15 minutes. From this stock solution, 1 ml (2.94 × 10 -4 mol) is added dropwise at 0 ° C. to the reaction mixture containing the monoadduct. The reaction is stirred for 60 minutes. After purification on a chromatographic column (eluent ethyl acetate) and evaporation, the final yield of the aminolysis is 35%. 31 P NMR (300 MHz, CDCl 3, b = ppm): 26.3 (1 P, s, P = (OCH 3) 2). EXAMPLE 4 Thermolysis of the DMVP-C4 Monoadduct 20-Scheme S 0 Dichlorobenzene 0 200 Diagram 4. Thermolysis of the DMVP-C4 Monoadduct The DMVP-C4 Monoadduct (250 mg, 7.37 × 10 4 mol) and the 1,2-dichlorobenzene solvent ( 3 ml) are introduced into a 25 ml flask surmounted by a condenser. The reaction mixture is degassed with argon for 15 minutes and then refluxed with the solvent (200 ° C) in the dark and for 5 minutes. The yield of the thermolysis is 70%. 31 P NMR (300 MHz, CDCl 3, b = ppm): 26.3 (1 P, s, P = (OCH 3) 2).
    [0041] EXAMPLE 5 Synthesis of the oligomers of PDMVP MeO MeO 2 P = O - Reaction Scheme o MeO AIBN Dioxane Scheme 5. Synthesis of the oligomer PDMVP-C4 The polymerization is carried out according to the following protocol: Xanthate C4 (470 mg, 2, 31.10-3 mol), dimethyl vinylphosphonate (3 g, 2.2 × 10 -2 mol), AIBN (72 mg, 4.38 × 10 -4 mol) and 4.6 g of 1,4-dioxane are placed in a Schlenk tube. The solution is degassed with argon for 15 minutes and then placed in a bath previously heated to 70 ° C. The reaction is stirred for 24 hours. The reaction mixture was purified by drying under reduced pressure at 80 ° C and washing with dichloromethane to remove residual monomer and dioxane. The conversion obtained is 50% and the molar mass, determined by 31 P NMR, is 720 g / mol (Mn theo = 750 g / mol). Example 6: Thermolysis of PDMVP-C4 Oligomers - Dichlorobenzene Reaction Scheme 200 ° C Scheme 6. Thermolysis of PDMVP-C4 oligomers The PDMVP-C4 (250 mg, 3.47 × 10 -4 mol) and the 1,2-solvent dichlorobenzene (3 ml) are introduced into a 25 ml flask surmounted by a coolant. The reaction mixture is degassed with argon for 15 minutes and then kept at reflux of the solvent (200 ° C) in the dark and for 15 minutes. The yield of the thermolysis was 72% (determined by 31 P NMR).
    [0042] Example 7: Thermolysis of DMVP-C4 Monoadduct followed by Grafting on SBR-Scheme Scheme 7. Synthesis of SBR-g-DMVP The DMVP-C4 monoadduct (250 mg, 7.37 × 10 4 mol) and the 1,2-dichlorobenzene solvent (3 ml) are introduced into a 50 ml flask surmounted by a refrigerant. The mixture is degassed with argon for 15 minutes and then kept at reflux of the solvent (200 ° C) in the absence of light and for 5 minutes. 500 mg of SBR (Mn = 235,900 g / mol, dispersity D (Mw / Mn) = 1.24, 75% of PB) are dissolved in 15 ml of methylcyclohexane. The latter SBR is already antioxidized with A02246 (2,2'-methylenebis (4-methyl-6-tert-butylphenol) This second solution is added to the monoadduct then the reaction medium is degassed with argon for 15 minutes. The solution is then heated to 75 ° C. A solution of 10 mg of DLP in 20 ml of methylcyclohexane is prepared and then degassed with argon for 15 minutes.This stock solution, (1 ml, 1.25 × 10 -6 mol) is The reaction mixture is cooled down and then precipitated in methanol, the reaction mixture is solubilized in dichloromethane and then antioxidized with 1 ml of a 10 g / l solution of A02246. The polymer is then dried under vacuum at 60 ° C. The grafting yield is 37.5% (determined by 1 H NMR) Table 1 below summarizes the characteristics of the polymers synthesized by grafting DMVP.
    [0043] DLP MCH / Dichlorobenzene 32 Table 1: Synthesis of SBR-g-DMVP by thiol-ene grafting. [SBR] o = 1.3.10-4 mol L-1, [DLP] o = 0.2μ) / 0 / [DMVP] o, T = 75 ° C, t = 3h Example 7 [DMVP-C41% graft target /% graft exp / Rdt gra% consom- Fraction molaire Mn b (g ID Tg mmol L-1 unsaturations unsaturations a exp (%) a mation phosphonate a / mol1) (° C) unsaturations a diene polymer (PS) SBR No. 00 00 00 00 00 00 00 235900 1.24 -19.8 grafted SBR 7a 6.3 1.36 0.925 68 2.95 3.6 250800 1.23 -21.1 SBR 7b 57.9 12.5 4, 37.5 16.33 18.2 400600 1.44 -23.8 5 Determination by -NHM 1H, b. CES-RI determination in THF with PS standards. Example 8: Thermolysis of PDMVP-C4 followed by grafting on SBR - Reaction Scheme O OMe OMe MeO MeO 2 P = O MeO-P = O Med Dichlerobenzene 200 ° C MeO MoO 2 P = O MeO-P. Figure 8. Synthesis of SBR-g-PDMVP The PDMVP-C4 oligomer (250 mg, 3.47 × 10 4 mol) and the 1,2-dichlorobenzene solvent (3 ml) are introduced into a 50 ml flask surmounted. refrigerant. The mixture was degassed with argon for 15 minutes and then refluxed with the solvent (200 ° C) in the dark and for 5 minutes. 500 mg of SBR (Mn = 235,900 g / mol, D = 1.24, 75% of PB) are dissolved in 15 ml of methylcyclohexane. The latter SBR is already antioxidized with A02246 (2,2'-methylenebis (4-methyl-6-tert-butylphenol) This second solution is added to the solution of PDMVP and the reaction medium is degassed with argon for 30 minutes. The solution is then heated to 75 ° C. A solution of 10 mg of DLP in 20 ml of methylcyclohexane is prepared and then degassed with argon for 15 minutes. 6 mol) is added via a syringe into the reaction medium After 3 hours of reaction, the mixture is cooled and then precipitated in methanol The polymer is solubilized in dichloromethane and then antioxidized with 1 ml of a solution of A02246 at 10 g The polymer is then dried under vacuum at 60 ° C. The grafting yield is 48.5% (determined by 1H NMR) Table 2 below summarizes the characteristics of the polymers synthesized by grafting DMVP. 2: Synthesis of SBR-g-PDMVP by Th Grafting iol-ene [SBR] o = 1.3.10-4 mol L-1, [PDMVP-C4] o = 29.2.10-3 mol L-1, [DLP] o = 0.2`) / 0 / [ PDMVP] o, T = 75 ° C, t = 3h. EXAMPLE 8 [PDMVP-% targeted graft /% graft exp / yield grafting% molar fraction Mn b (g mol- ') D Tg C4] 0 unsaturations at (%) a mation phosphonate a / (PS) (°) C) mmol Ll unsaturations diene polymer SBR no 00 00 00 00 00 00 235900 1.24 -19.8 grafted SBR 8a 3.7 1.05 0.7 66.5 2.2 12.2 239800 1.25 SBR 8b 23.1 6.6 3.2 48.5 8.1 55.8 243000 1.26 -34.1 a 1H NMR determination b CES-RI determination in THF with PS standards. Results Compared with the use of a thiol-terminated monophosphonate (Example 7), the grafting of thiol-terminated poly (phosphonates) (Example 8) makes it possible to obtain modified phosphonate diene polymer having high phosphonate functions without having to aim for high grafting rates. The use of phosphonate functional thiol small molecules such as those described in Example 7 has the disadvantage of an evolution of the macrostructure 10 in the case of high grafting rates. In the case where a low grafting rate of the unsaturations of the diene elastomer is aimed at, we observe a conservation of the macrostructure of the final polymer (entry 2, table 1 of example 7). However, in this case the molar fraction of phosphonate functions in the final polymer is low (3.6%). In order to obtain a diene polymer having high phosphonate function levels, we have aimed at a high degree of grafting of the unsaturations of the diene elastomer. The final polymer thus has a large molar fraction of phosphonate functions (18.2%). In this case, however, the grafting reaction is accompanied by an evolution of the macrostructure which is due to the secondary reactions (bimolecular coupling, transfer reaction, etc.) and the proportion of which increases with the rate of grafts targeted. This is illustrated by the excessive evolution of the Mn (400600 g mol-1), the dispersity (0 = 1.44) and the consumption of the double bonds of the diene elastomer (Table 1 entry 3 of the Example 7). Advantageously, the use of a poly (phosphonate) graft carrying a thiol function at the end of the chain makes it possible to overcome the disadvantages associated with the use of the small thiol functionalized phosphonate molecules. In fact, the use of the poly (phosphonate) s makes it possible to obtain a modified diene polymer having a high molar ratio of phosphonate functions along the chain by aiming for low grafting levels and without modifying the final polymer macrostructure.
    [0044] This is illustrated in Table 2, entry 2 of Example 8. In fact, we succeed in grafting high molar levels of phosphonate functions (12.2%) without having to target a high level of unsaturations of the diene elastomer. . In this case, the grafting makes it possible to preserve the final polymer macrostructure (Mn = 239800 g mol-1, D = 1.25). We can also increase the molar fraction of the phosphonate functions in the final diene polymer to reach a very high level of 55.8% (Table 2, entry 3 of Example 8) without observing a change in the macrostructure of the final polymer (Mn = 243000 g mol-1, D = 1.26) which was not the case with the monophosphonate carrying the thiol function of Example 7.
    权利要求:
    Claims (4)
    [0001]
    REVENDICATIONS1. Process for synthesizing a polymer with a high phosphonate and / or phosphonic function by free radical grafting of a poly (phosphorus) polymer carrying at the chain end a thiol function on a diene polymer according to the following steps: a. shaking at least one diene polymer in solution and at least one poly (phosphorus) polymer carrying a thiol function at the end of the chain in solution, b. heating the homogeneous reaction mixture obtained in the preceding step to the temperature of the grafting reaction, and c. adding the radical initiator concomitantly with one of the steps a) and b) or once the temperature of the grafting reaction has been reached.
    [0002]
    2. Method according to claim 1, characterized in that the solvent of the poly (polyphosphorus) polymer is 1,2-dichlorobenzene or THF. 20
    [0003]
    3. Method according to claim 1 or 2, characterized in that the solvent of the diene polymer is methylcyclohexane, toluene or THF.
    [0004]
    4. A process according to any one of the preceding claims, characterized in that the poly (phosphorus) chain-endolated polymer of a thiol function is represented by the general formula I: 1-12 X 1 [1-12 ## EQU1 ## where - m denotes an integer greater than or equal to 1 and n denotes an integer greater than or equal to 0, provided that when n is not equal to 0, n and m may be the same or different, preferably greater than 2, and preferably less than 500. - R representing: (i) an alkyl, acyl, aryl, alkenyl or alkynyl group, (ii) a carbon ring, saturated or unsaturated optionally aromatic; (iii) a heterocycle, saturated or unsaturated, optionally aromatic; or wherein said groups and rings (i), (ii) and (iii) may be substituted by substituted phenyl groups, substituted aromatic groups or: alkoxycarbonyl or aryloxycarbonyl (-COOR '), carboxy (-COOH), acyloxy ( - 02CR '), carbamoyl (-CONR'2), cyano (-CN), alkylcarbonyl, alkylarylcarbonyl, arylcarbonyl, arylalkylcarbonyl, phthalimido, maleimido, succinimido, amidino, guanidimo, hydroxy (-OH), amino (-NR'2) , halogen, allyl, epoxy, alkoxy (-OR '), S-alkyl, S-aryl, hydrophilic or ionic groups such as the alkaline salts of carboxylic acids, the alkaline salts of sulfonic acid, the chains alkylene polyoxide (POE, POP), the cationic substituents (quaternary ammonium salts), R 'representing an alkyl or aryl group, (iv) a polymer chain, X and X', which may be identical or different, representing an atom hydrogen, a halogen or a group R1, OR1, O2COR1, NHCOH, OH, NH2, NHR1, N (R1) 2, (R1) 2N + O-, NHCOR1, CO2H, CO2R1, CN, CONH2, CONHRI or CON (R1) 2, in which R1 is chosen from alkyl, aryl, aralkyl, alkylaryl, alkene or organosilyl groups, optionally perfluorinated and optionally substituted with one or more carboxyl, epoxy or hydroxyl groups, alkoxy, amino, halogen or sulfonic acid. Y or Y ', which may be identical or different, are such that either Y, Y' or both comprise at least one phosphorus functional group -P (O) (OR 2) (OR 3) in which R 2 and R 3, which may be identical or different, represent a hydrogen atom or an alkyl radical, optionally haloalkyl. Process according to Claim 4, characterized in that in formula I, R is a cyanomethyl group of formula CNCH2-, 1-phenylethyl of formula CH3 (C6H5) CH- or methylpropionyl of formula CH3 (CO2CH3) CH-. Process according to Claim 4 or 5, characterized in that the molar fraction of monomer units of the poly (phosphorus) polymer containing X and X 'ranges from 0 to 0.5, preferably from 0 to 0.25, more preferably between 0 and 0.1. Process according to any one of the preceding claims, characterized in that the poly (phosphorus) polymer carrying a thiol function at the chain end has a number of units of at least 2 and at most equal to 1000. any of the preceding claims, characterized in that the diene polymer is chosen from diene elastomer elastomers consisting of polybutadiene (abbreviated as "BR"), synthetic polyisoprene (IR), natural rubber (NR), copolymers of butadiene-styrene (SBR), isoprene-butadiene copolymers (BIR), isoprene-styrene copolymers (SIR) and isoprene-butadiene-styrene copolymers (SBIR), ethylene-butadiene copolymers ( EBR) and mixtures of these elastomers. 9. Process according to any one of the preceding claims, characterized in that the diene polymer is chosen from elastomers having a mass content of vinylic units in the diene part, greater than 20%, preferably of at least 40%. 10. Process according to any one of the preceding claims, characterized in that the molar ratio of the poly (phosphorus) polymer carrying a thiol function at the chain end to the radical initiator is at least 5.5. 6. 7. 8.preferentially at least 10, or even at least 45, and is at most 100, preferably at most 60.. 11. Grafted diene polymer having phosphonate and / or phosphonic functions consisting of a main polymer chain derived from a diene polymer which comprises units grafted with poly (phosphorus) grafts bound thereto via a sulfur atom, which grafted diene polymer is obtainable by the process as defined in at least one of claims 1 to 10. 12. Polymer according to claim 11, characterized in that the main polymeric chain is derived from an elastomer among a polybutadiene (BR), a synthetic polyisoprene (IR), a natural rubber (NR), a butadiene and / or isoprene copolymer, in particular a butadiene-styrene copolymer (SBR), a copolymer of isoprene-butadiene (BIR), an isoprene-styrene copolymer (SIR), an isoprene-butadiene-styrene copolymer (SBIR), and ethylene-butadiene copolymers (EBR), as well as mixtures thereof. 13. Polymer according to claim 11 or 12, characterized in that the polymer chain poly (phosphorus) of the graft is any homopolymer obtained by polymerization of a monomer carrying at least one phosphonate function, or any copolymer of one or several monomers carrying at least one phosphonate function with one another or with one or more comonomers. 14. Polymer according to any one of claims 11 to 13, the grafted diene polymer corresponds to formula (III): P [- G]; (III) in which - P represents the polymer chain derived from the diene polymer, G represents the poly (phosphorus) graft derived from the poly (phosphorus) terminated thiol polymer of formula (I), i represents the number of grafted units of the chain polymer derived from the diene polymer of the general formula (I): ## STR1 ## where m is an integer greater than or equal to 2 and n denotes an integer greater than or equal to 0; provided that when n is not 0, n and m may be the same or different, preferably greater than 2 and preferably less than 500. - R representing: (i) an alkyl, acyl, aryl, alkenyl or alkynyl group; (ii) a carbon ring of a group (i), saturated or unsaturated, optionally aromatic; (iii) a heterocycle, saturated or unsaturated, optionally aromatic; or wherein said groups and rings (i), (ii) and (iii) may be substituted by substituted phenyl groups, substituted aromatic groups or: alkoxycarbonyl or aryloxycarbonyl (-COOR '), carboxy (-COOH), acyloxy ( - 02CR '), carbamoyl (-CONR'2), cyano (-CN), alkylcarbonyl, alkylarylcarbonyl, arylcarbonyl, arylalkylcarbonyl, phthalimido, maleimido, succinimido, amidino, guanidimo, hydroxy (-OH), amino (-NR'2) , halogen, allyl, epoxy, alkoxy (-OR '), S-alkyl, S-aryl, hydrophilic or ionic groups such as the alkaline salts of carboxylic acids, the alkaline salts of sulfonic acid, the chains alkylene polyoxide (POE, POP), the cationic substituents (quaternary ammonium salts), R 'representing an alkyl or aryl group, (iv) a polymer chain, X and X', which may be identical or different, representing an atom hydrogen, a halogen or a group R1, OR1, O2COR1, NHCOH, OH, NH2, NHR1, N (R1) 2, (R1) 2N + O-, NHCOR1, CO2H, CO2R1, CN, CONH2, CONHRI or CON (R1) 2, in which R1 is chosen from alkyl, aryl, aralkyl, alkylaryl, alkene or organosilyl groups, optionally perfluorinated and optionally substituted with one or more carboxyl, epoxy or hydroxyl groups, alkoxy, amino, halogen or sulfonic acid. Y or Y ', which may be identical or different, are such that either Y, Y' or both comprise at least one phosphorus functional group -P (O) (OR 2) (OR 3) in which R 2 and R 3, which are identical or different, , represent a hydrogen atom or an alkyl radical, optionally haloalkyl. 15. Polymer according to any one of claims 11 to 14, characterized in that the poly (phosphonate) graft has a number of units of at least 2 and at most equal to 1000. 16. Polymer according to any one Claims 13 to 15, characterized in that the molar fraction of monomer units comprising X and X 'with respect to the polymer chain derived from the poly (phosphorus) polymer ranges from 0 to 0.5, preferably from 0 to 0 , 25, more preferably between 0 and 0.1. 17. Polymer according to any one of the preceding claims, characterized in that the molar level of grafted poly (phosphonate) grafts relative to the diene portion of the diene polymer is at least 0.05%, preferably 0.2 and more preferably 0.3%, and it is at most 30%, preferably 15% and even more preferably 10%. 18. A rubber composition based on at least one reinforcing filler and at least one elastomer comprising phosphonate and / or phosphonic functions as prepared according to the process defined in any one of claims 1 to 10 or as defined in any one of claims 11 to 17. 19. A tire of which one of its constituent elements comprises a rubber composition according to claim 18.
    类似技术:
    公开号 | 公开日 | 专利标题
    FR3017388A1|2015-08-14|PROCESS FOR THE PREPARATION OF DIAGNOSTIC ELASTOMERS WITH PHOSPHOROUS FUNCTIONS, PRODUCTS THEREOF AND COMPOSITION CONTAINING SAME
    EP2935341B1|2017-04-19|Process for radical grafting of a diene elastomer
    FR2861394A1|2005-04-29|PROCESS FOR THE PREPARATION OF POLYALCOAXYMINES AS BEGINNERS FOR THE RADICAL POLYMERIZATION OF POLYFUNCTIONAL | POLYMERS
    Mazzolini et al.2010|Thiol-end-functionalized polyethylenes
    FR2987838A1|2013-09-13|TELECHELIC POLYOLEFIN AND PROCESS FOR OBTAINING THE SAME
    WO2019007883A1|2019-01-10|Composition on the basis of at least one specific polyaromatic compound
    EP3105260A1|2016-12-21|Polyphosphorus polymer that is thiol-functionalised at the chain ends and production method thereof
    EP3648989A1|2020-05-13|Polymer carrying specific pendant imidazolidinone functional groups
    WO2015121228A1|2015-08-20|Phosphorus diene block copolymer, method for the synthesis thereof and rubber composition containing same
    EP1527105A2|2005-05-04|Synthesis of statistical microgels by means of controlled radical polymerisation
    EP3212678B1|2019-09-04|Method for synthesizing a polymer bearing a hydroxyaryl group
    FR3017389A1|2015-08-14|POLYMER CARRYING PHOSPHOROUS FUNCTIONS AND AT LEAST ONE AZOTUR FUNCTION, METHOD OF SYNTHESIS AND USE THEREOF
    EP3221373A1|2017-09-27|Rubber composition comprising a phosphonate-functionalized polyene copolymer, and use of such a copolymer for improving filler-diene elastomer interactions
    FR3012455A1|2015-05-01|
    FR3027904A1|2016-05-06|PROCESS FOR THE SYNTHESIS OF A HYDROXYARYL GROUP-CARRYING POLYMER, PRODUCT THEREOF AND COMPOSITION CONTAINING THE SAME
    WO2012007443A1|2012-01-19|Graft polymer to which combined nitrogen molecules are grafted
    FR3040058B1|2019-07-19|PROCESS FOR THE SYNTHESIS OF A POLYMER CARRIER OF A FUNCTIONAL GROUP, PRODUCT THEREOF AND COMPOSITION CONTAINING SAME
    WO2021023948A1|2021-02-11|Polymer having specific n-substituted imidazolidinone pendant functional groups
    WO2022003279A1|2022-01-06|Grafted elastomer bearing epoxy pendant groups
    WO2020070406A1|2020-04-09|Method for synthesising a thermoplastic elastomer comprising at least one poly| block
    WO2021023949A1|2021-02-11|Composition based on at least one compound having an n-substituted imidazolidinone function
    WO2017109316A1|2017-06-29|Method for synthesising a polymer bearing at least one phosphonate group, polymer obtained by said method and composition containing same
    FR2889702A1|2007-02-16|New silane compounds useful as a precursor for the syntheses of compounds, particularly polymers containing silane groups
    MXNL04000104A|2006-06-19|Method for the preparation of segmented copolymers comprising polydienic segments.
    同族专利:
    公开号 | 公开日
    WO2015121224A1|2015-08-20|
    US20170022296A1|2017-01-26|
    CN105940028A|2016-09-14|
    EP3105269A1|2016-12-21|
    FR3017388B1|2016-02-12|
    引用文献:
    公开号 | 申请日 | 公开日 | 申请人 | 专利标题
    WO2004096865A2|2003-04-29|2004-11-11|Societe De Technologie Michelin|Method for obtaining an elastomer graft with functional groups along the chain and rubber compositions|
    WO2007100719A1|2006-02-23|2007-09-07|Commonwealth Scientific And Industrial Research Organisation|Process for synthesizing thiol terminated polymers|
    EP2607102A1|2011-12-21|2013-06-26|The Goodyear Tire & Rubber Company|Method of making a graft polymer, copolymer and tire|FR3045610A1|2015-12-21|2017-06-23|Michelin & Cie|PROCESS FOR THE SYNTHESIS OF A POLYMER CARRIER OF AT LEAST ONE PHOSPHONATE GROUP, POLYMER THEREFROM AND COMPOSITION CONTAINING THE SAME|US7279532B2|2002-03-01|2007-10-09|Asahi Kasei Chemicals Corporation|Modified hydrogenated copolymer|
    US8048960B2|2007-04-18|2011-11-01|Styron Europe Gmbh|Monovinylidene aromatic polymers comprising sulfanylsilane functionalized elastomeric polymers|FR3037588B1|2015-06-19|2017-05-19|Michelin & Cie|THERMOPLASTIC ELASTOMERIC COPOLYMER BASED ON DIENE ELASTOMER AND POLYPROPYLENE, COMPOSITIONS COMPRISING THE SAME, AND PROCESS FOR PREPARING THE SAME|
    FR3056214A1|2016-09-16|2018-03-23|Compagnie Generale Des Etablissements Michelin|COMPOSITE BASED ON METAL COMPONENT AND FUNCTIONAL POLYMER MATRIX.|
    CN109627359B|2017-10-06|2021-11-19|台橡股份有限公司|Modified rubber containing silicon and phosphorus, composition and manufacturing method thereof|
    EP3713773A1|2017-11-21|2020-09-30|Compagnie Générale des Etablissements Michelin|Rubber composition|
    JP2020084146A|2018-11-30|2020-06-04|Ｔｏｙｏ Ｔｉｒｅ株式会社|Modified diene polymer and method for producing the same|
    法律状态:
    2015-02-19| PLFP| Fee payment|Year of fee payment: 2 |
    2016-02-18| PLFP| Fee payment|Year of fee payment: 3 |
    2017-02-17| PLFP| Fee payment|Year of fee payment: 4 |
    2018-02-23| PLFP| Fee payment|Year of fee payment: 5 |
    2019-10-25| ST| Notification of lapse|Effective date: 20191006 |
    优先权:
    申请号 | 申请日 | 专利标题
    FR1451037A|FR3017388B1|2014-02-11|2014-02-11|PROCESS FOR THE PREPARATION OF DIAGNOSTIC ELASTOMERS WITH PHOSPHOROUS FUNCTIONS, PRODUCTS THEREOF AND COMPOSITION CONTAINING SAME|FR1451037A| FR3017388B1|2014-02-11|2014-02-11|PROCESS FOR THE PREPARATION OF DIAGNOSTIC ELASTOMERS WITH PHOSPHOROUS FUNCTIONS, PRODUCTS THEREOF AND COMPOSITION CONTAINING SAME|
    US15/118,035| US20170022296A1|2014-02-11|2015-02-10|Method for producing diene polymers bearing phosphorus functional groups, products resulting from said method and composition containing same|
    PCT/EP2015/052702| WO2015121224A1|2014-02-11|2015-02-10|Method for producing diene polymers bearing phosphorus functional groups, products resulting from said method and composition containing same|
    CN201580006314.5A| CN105940028A|2014-02-11|2015-02-10|Method for producing diene polymers bearing phosphorus functional groups, products resulting from said method and composition containing same|
    EP15703586.6A| EP3105269A1|2014-02-11|2015-02-10|Method for producing diene polymers bearing phosphorus functional groups, products resulting from said method and composition containing same|
    [返回顶部]