    The present invention relates to an apparatus and a method for producing a polymer latex resin powder, and according to one aspect of the present invention, there is provided an apparatus for producing a polymer latex resin powder comprising a first flocculation tank to which a polymer latex and a flocculant are each supplied, wherein the first flocculation tank is provided with a stirring part including a rotation axis and one or more impellers mounted on the rotation axis, and a discharge line, respectively and the first flocculation tank is provided so as to operate in a closed system upon operating the stirring part.
    公开号:EP3708248A1
    申请号:EP18875077.2
    申请日:2018-11-01
    公开日:2020-09-16
    发明作者:Jung Kee Jang；Hyun Jin Shin；Ye Hoon Im
    申请人:LG Chem Ltd；
    IPC主号:B01D21-00
    专利说明:
    [0001] The present invention relates to an apparatus and a method for producing a polymer latex resin powder.
    [0002] This application claims the benefit of priority based on Korean Patent Application No. 10-2017-0147939 filed on November 8, 2017 and Korean Patent Application No. 10-2018-0128632 filed on October 26, 2018 , the disclosures of which are incorporated herein by reference in their entirety. Background Art
    [0003] Generally, slow coagulation is used as a method for preparing a polymer latex as a powder in an emulsion polymerization process, and in this method, an aqueous solution of a flocculant such as an inorganic salt and an acid is divided in small amounts and added to break stability of an emulsifier, whereby the polymer in the latex is agglomerated.
    [0004] The slow coagulation method is capable of controlling the particle size as compared with a rapid coagulation method. A process of agglomerating polymer particles in the latex is called coagulation and one in which the polymer particles are agglomerated is called a slurry, where they are in a physically weakly bonded state, and thus show an easy break-up phenomenon by shear force by a stirrer (for example, an impeller).
    [0005] In addition, the primarily coagulated slurry is subjected to an aging process. The slurry thus generated is subjected to dehydrating and drying processes to finally obtain a powdery phase.
    [0006] Usually, in the polymer latex resin powder, fine particles having an average particle diameter of about 75µm or less are called "fine" particles and larger particles having an average particle diameter of about 800µm or more are called "coarse" particles. The fine particles deteriorate the performance of the dehydrator and the dryer of the latex resin powder and are easily scattered into the air, which cause many problems in transport and packing of the powder in the process, and the coarse particles have a problem of transport and storage and have a disadvantage that compatibility with other polymer resins is poor.
    [0007] Figure 1 is a conceptual diagram showing a conventional apparatus (10) for producing a polymer latex resin powder.
    [0008] Referring to Figure 1, the production apparatus (10) comprises a flocculation tank (11), a plurality of supply lines (12) for supplying a polymer latex, a flocculant and water, and the like into the flocculation tank, a stirring part (20) provided in the flocculation tank (11) and a discharge line (13). Here, the flocculation tank (11) has been provided so as to operate in an open system. Specifically, the flocculation tank (11) is maintained at a predetermined slurry level, and an air layer (14) is formed on the top of the flocculation tank (11).
    [0009] As described above, when the stirring part (20) is operated in the open system, coarse particles are generated by formation of vortexes (V) around the stirring part (20). Disclosure Technical Problem
    [0010] It is an object of the present invention to provide an apparatus and a method for producing a polymer latex resin powder capable of reducing fine and coarse particles.
    [0011] It is another object of the present invention to provide an apparatus and a method for producing a polymer latex resin powder capable of applying uniform shear force. Technical Solution
    [0012] To solve the above-described objects, according to one aspect of the present invention, there is provided an apparatus for producing a polymer latex resin powder comprising a first flocculation tank to which a polymer latex and a flocculant are each supplied, wherein the first flocculation tank is provided with a stirring part including a rotation axis and one or more impellers mounted on the rotation axis, and a discharge line, respectively and the first flocculation tank is provided so as to operate in a closed system upon operating the stirring part.
    [0013] The discharge line is connected to the top region of the first flocculation tank, whereby the first flocculation tank is provided so as to operate in a closed system upon operating the stirring part.
    [0014] Also, the discharge line is connected along the tangential direction to the first flocculation tank.
    [0015] Furthermore, the discharge line is connected to the first flocculation tank so as to be inclined at a predetermined angle based on the rotation axis of the stirring part. In addition, the angle may be 45°.
    [0016] Also, first and second supply lines, to which the polymer latex and the flocculant are each supplied, may be connected to the first flocculation tank.
    [0017] Furthermore, the first and second supply lines may be each connected to the bottom region of the first flocculation tank and may be provided so that the polymer latex and the flocculant are each supplied to the end side of the impeller.
    [0018] In addition, the apparatus for producing a polymer latex resin powder may further comprise a second flocculation tank into which the polymer slurry discharged from the first flocculation tank flows.
    [0019] At this time, the discharge line may be connected to the second flocculation tank at a height lower than the slurry level of the second flocculation tank.
    [0020] Also, the discharge line may comprise a first region connected to the first flocculation tank and a second region connected to the second flocculation tank.
    [0021] Furthermore, the boundary between the first region and the second region may be located above the uppermost end of the first flocculation tank.
    [0022] In addition, the first region and the second region of the discharge line may be connected at a predetermined angle.
    [0023] Also, it is preferable that both the first flocculation tank and the discharge line are each filled with the polymer slurry upon operating the stirring part.
    [0024] In addition, according to another aspect of the present invention, there is provided a method for producing a polymer latex resin powder, comprising steps of supplying a polymer latex and a flocculant to a first flocculation tank, stirring the polymer latex and flocculant in the first flocculation tank in a closed system and supplying the polymer slurry in the first flocculation tank into a second flocculation tank. Advantageous Effects
    [0025] As described above, the apparatus and method for producing a polymer latex resin powder related to at least one example of the present invention have the following effects.
    [0026] As the flocculation tank is provided so as to operate in a closed system upon stirring the polymer slurry, the fine and coarse particles can be reduced and the uniform shear force can be applied to the polymer slurry through the stirring part. Brief Description of Drawings
    [0027] Figure 1 is a conceptual diagram showing a conventional apparatus for producing a polymer latex resin powder. Figure 2 is a conceptual diagram showing an apparatus for producing a polymer latex resin powder related to one example of the present invention. Figure 3 is a diagram for explaining a connection structure of a discharge line. Figure 4 shows an analysis result of Area A in Figure 3. Figure 5 is a conceptual diagram showing an apparatus for producing a polymer latex resin powder related to another example of the present invention. Figure 6 is a graph showing the distribution ratio of the shear rate.Mode for Invention
    [0028] Hereinafter, an apparatus and a method for producing a polymer latex resin powder according to one example of the present invention will be described in detail with reference to the accompanying drawings.
    [0029] In addition, the same or similar reference numerals are given to the same or corresponding components regardless of reference numerals, of which redundant explanations will be omitted, and for convenience of explanation, the size and shape of each constituent member as shown may be exaggerated or reduced.
    [0030] Figure 2 is a conceptual diagram showing an apparatus (100) for producing a polymer latex resin powder (hereinafter, also referred to as a 'production apparatus') related to one example of the present invention.
    [0031] Also, Figure 3 is a diagram for explaining a connection structure of a discharge line, and Figure 4 is an analysis result of Area A in Figure 3.
    [0032] The production apparatus (100) comprises a first flocculation tank (110), a plurality of supply lines (111, 112), a stirring part (120) and a discharge line (130).
    [0033] Specifically, the production apparatus (100) comprises a first flocculation tank (110) to which a polymer latex and a flocculant are each supplied. Also, the first flocculation tank (110) is provided with a stirring part (120) including a rotation axis (121) and one or more impellers (122) mounted on the rotation axis (121), and a discharge line (130), respectively. In addition, the first flocculation tank (110) is provided so as to operate in a closed system when the stirring part (120) is operated. The first flocculation tank (110) may be composed of a flocculation tank operated in a closed system. The unexplained symbol C denotes the central axis of the first flocculation tank (110).
    [0034] In this document, the fact that the first flocculation tank (110) operates in a closed system means that the first flocculation tank (110) and the discharge line (130) are fully filled with the polymer slurry upon operating the stirring part (120). For example, the fact that the first flocculation tank (110) operates in a closed system may also mean that 90% or more of the volume of the first flocculation tank (110) is filled with the polymer slurry, preferably, may also mean that 95% or more of the volume of the first flocculation tank (110) is filled with the polymer slurry, and more preferably, may mean that 100% of the volume of the first flocculation tank (110) is filled with the polymer slurry.
    [0035] In addition, in the first flocculation tank (110), a supply part (102) may be provided in the bottom region. Specifically, in the first flocculation tank (110), a first and second supply lines (111, 112), to which a polymer latex and a flocculant are each supplied, may be connected to the bottom region. Each of the supply lines (111, 112) may be connected to one or more supply sources (101). The supply source may comprise, for example, a latex tank. Furthermore, water or the like may be further supplied to the first flocculation tank (110).
    [0036] On the other hand, the first and second supply lines (111, 112) may be connected to the bottom region of the first flocculation tank (110), respectively. Also, the first and second supply lines (111, 112) may be connected to the bottom region of the first flocculation tank (110) in parallel to the axial direction of the rotation axis (121), respectively. Furthermore, the first and second supply lines (111, 112) may be provided so that the polymer latex and the flocculant are each supplied to the end side of the impeller (122) (the impeller positioned at the bottom region of the first flocculation tank).
    [0037] The discharge line (130) is connected to the top region of the first flocculation tank (110). The discharge line (130) is connected to the top region of the first flocculation tank (110), whereby the first flocculation tank (110) can easily operate in a closed system.
    [0038] Also, the discharge line (130) of the first flocculation tank (110) may comprise a first region (131) connected to the first flocculation tank (110) and a second region (132) connected to the second flocculation tank (200). At this time, the first region (131) and the second region (132) may be connected at a predetermined angle.
    [0039] In addition, the boundary (133, connection) between the first region and the second region is located above the uppermost end (T) of the first flocculation tank (110). In this document, the boundary (133) between the first region and the second region is located above the uppermost end (T) of the first flocculating tank (110) based on the central axis (C) direction (y-axis direction) of the first flocculation tank. In this structure, when the first region (131) of the discharge line (130) is filled with the polymer slurry, 90% or more of the volume of the first flocculation tank (110) may be filled with the polymer slurry, preferably, 95% or more of the volume of the first flocculation tank (110) may be filled with the polymer slurry, and more preferably, 100% of the first flocculation tank (110) may be filled with the polymer slurry.
    [0040] Referring to Figure 3, the discharge line (130) is connected to the first flocculation tank (110) along the tangential direction. The first flocculation tank (110) may be in the form of a cylindrical cylinder. The first flocculation tank (110) may have a circular cross-section shape parallel to the x-axis direction in Figure 2. In this structure, the first region (131) is connected to the first flocculation tank (110) along the tangential direction. The tangential direction means that it is connected to the tangential direction of the first flocculation tank (110) based on the center axis (C) of the first flocculation tank (110).
    [0041] Also, the discharge line (130) is connected to the first flocculation tank (110) so as to be inclined at a predetermined angle based on the rotation axis (121) of the stirring part (120) (or the central axis of the first flocculation tank). Specifically, the first region (131) is connected to the first flocculation tank (110) so as to be inclined at a predetermined angle based on the rotation axis (121) of the stirring part (120) (or the central axis of the first flocculation tank).
    [0042] Furthermore, it is preferable that the angle (θ) is about 45° so that the flow of the polymer slurry can be performed in a state where the polymer slurry is filled in the discharge line (130). In addition, when the discharge line (130) is connected to the first flocculation tank (110) in a state of being inclined at a predetermined angle, the outlet flow rate can be maintained constant.
    [0043] In addition, the production apparatus (100) may further comprise a second flocculation tank (200) into which the polymer slurry discharged from the first flocculation tank (110) flows.
    [0044] At this time, the second flocculation tank (200) may have the general flocculation tank structure described through Figure 1. For example, the second flocculation tank (200) may comprise a housing (210) providing a stirring space, a stirring part (220) provided in the housing (210) and a discharge line (213) connected to the housing (210). In addition, the second flocculation tank (200) may be provided so as to operate in an open system.
    [0045] On the other hand, the discharge line (130) of the first flocculation tank (110) may be connected at a height lower than the slurry level (L) of the second flocculation tank (200).
    [0046] In such a structure, the first flocculation tank (110) and the discharge line (130) may be fully filled with the polymer slurry when the stirring part (120) is operated.
    [0047] Figure 5 is a conceptual diagram showing an apparatus for producing a polymer latex resin powder related to another example of the present invention.
    [0048] Referring to Figure 5, the apparatus for producing a polymer latex resin powder may comprise a plurality of first flocculation tanks (110, 110'). Also, two adjacent first flocculation tanks (110, 110') may be connected together to form a closed system.
    [0049] For example, the discharge line (130) of the first flocculation tank (110) connected to the supply source (101) is connected to the supply part (102') of the adjacent first flocculation tank (110'). At this time, in the discharge line (130) of the first flocculation tank (100) connected to the supply source (101), the first region (131) is drawn out from the top region of the first flocculation tank (110), and the second region (132) is connected to the supply part (102') of the bottom region of the adjacent first flocculation tank (110').
    [0050] A method for producing a polymer latex resin powder (hereinafter, also referred to as a 'production method') using the production apparatus (100) having such a structure will be described in detail.
    [0051] The production method comprises steps of supplying a polymer latex and a flocculant to a first flocculation tank (110), respectively, stirring the polymer latex and the flocculant in the first flocculation tank (110) in a closed system, and supplying the polymer slurry in the first flocculation tank to a second flocculation tank (200).
    [0052] Also, it is preferable that the polymer slurry in the first flocculation tank (110) is supplied at a height lower than the slurry level (L) of the second flocculation tank (200).
    [0053] In addition, it is preferable that the first flocculation tank (110) is filled with the polymer slurry at the time of stirring.
    [0054] Figure 6 is a graph showing the distribution ratio of the shear rate.
    [0055] Referring to Figure 6, a reference symbol E1 denotes existing coagulation, and a reference symbol E2 denotes new coagulation. At this time, the 'existing coagulation' represents the distribution ratio of the shear rate in the flocculation tank operating in the open system described in Figure 1, and the 'new coagulation' is the result using the production apparatus related to the present invention, which represents the distribution ratio of the shear rate in the flocculation tank operating in the closed system, and it can be confirmed that the distribution ratio of the shear rate is uniformly formed when the flocculation tank is operated in the closed system.
    [0056] The preferred examples of the present invention as described above are disclosed for illustrative purposes, which can be modified, changed and added within thought and scope of the present invention by those skilled in the art and it will be considered that such modification, change and addition fall within the following claims. Industrial Applicability
    [0057] According to the apparatus and method for producing a polymer latex resin powder related to at least one example of the present invention, as the flocculation tank is provided so as to operate in a closed system upon stirring the polymer slurry, the fine and coarse particles can be reduced and the uniform shear force can be applied to the polymer slurry through the stirring part.
    权利要求:
    Claims (7)
    [0001] An apparatus for producing a polymer latex resin powder comprising a first flocculation tank to which a polymer latex and a flocculant are each supplied,wherein the first flocculation tank is provided with a stirring part including a rotation axis and one or more impellers mounted on the rotation axis, and a discharge line, respectively,the discharge line is connected to the top region of the first flocculation tank,the first flocculation tank is provided so as to operate in a closed system upon operating the stirring part, andthe discharge line is connected along the tangential direction to the first flocculation tank, and connected to the first flocculation tank so as to be inclined at a predetermined angle based on the rotation axis of the stirring part.
    [0002] The apparatus for producing a polymer latex resin powder according to claim 1,wherein first and second supply lines, to which the polymer latex and the flocculant are each supplied, are connected to the first flocculation tank, andthe first and second supply lines are each connected to the bottom region of the first flocculation tank and provided so that the polymer latex and the flocculant are each supplied to the end side of the impeller.
    [0003] The apparatus for producing a polymer latex resin powder according to claim 1, wherein the angle is 45°.
    [0004] The apparatus for producing a polymer latex resin powder according to claim 1, further comprising a second flocculation tank into which the polymer slurry discharged from the first flocculation tank flows,wherein the discharge line is connected to the second flocculation tank at a height lower than the slurry level of the second flocculation tank.
    [0005] The apparatus for producing a polymer latex resin powder according to claim 4,wherein the discharge line comprises a first region connected to the first flocculation tank and a second region connected to the second flocculation tank, andthe first region and the second region are connected at a predetermined angle.
    [0006] The apparatus for producing a polymer latex resin powder according to claim 5,wherein the boundary between the first region and the second region is located above the uppermost end of the first flocculation tank.
    [0007] The apparatus for producing a polymer latex resin powder according to claim 4,wherein both the first flocculation tank and the discharge line are filled with the polymer slurry upon operating the stirring part.
    类似技术:
    公开号 | 公开日 | 专利标题
    Ziemecka et al.2011|Monodisperse hydrogel microspheres by forced droplet formation in aqueous two-phase systems
    CA1130795A|1982-08-31|Method and apparatus for reducing molecularagglomerate sizes in fluids
    CA2700239C|2015-06-09|Installation for enhanced oil recovery using water-soluble polymers, method implementing same
    JP5068163B2|2012-11-07|Solid-liquid contact apparatus and method
    CA2911924C|2016-10-18|Improvements relating to centrifugal pump impellers
    KR100743476B1|2007-07-30|Conical twin-screw extruder and dehydrator
    US20150315074A1|2015-11-05|Mixing and stirring device, mixing and stirring method, and method for manufacturing lightweight gypsum board
    US8794448B2|2014-08-05|Separation device
    EP2551021B1|2016-09-14|Centrifuge and discharge port member of a centrifuge for power reduction
    US20170368478A1|2017-12-28|Method for separating a feed material containing immiscible phases of different densities
    JP4966258B2|2012-07-04|Method and apparatus for dewatering organic sludge
    US7581872B2|2009-09-01|Gel mixing system
    US4529794A|1985-07-16|Method of rapidly dissolving polymers in water
    US20090065417A1|2009-03-12|Solid-liquid separator
    FI122057B|2011-08-15|Thickener and Thickening Method
    US20100059453A1|2010-03-11|System and method for de-watering waste drilling fluids
    Vieira et al.2010|Improvement of hydrocyclone separation performance by incorporating a conical filtering wall
    CN102497935B|2015-07-29|Device for flotation separation and method and utilize the manufacture method of goods
    JP4562737B2|2010-10-13|Treatment method and reactor by agglomeration
    SU1662342A3|1991-07-07|Mixer of liquid and solid particles
    CN2561501Y|2003-07-23|Dissolving mixers
    FI121621B|2011-02-15|Mixer for mixing sludge in metallurgical processes
    US8002991B2|2011-08-23|Dewatering method
    US6936178B2|2005-08-30|Apparatus for and method of settling of mineral slurries
    CN1222543C|2005-10-12|Preparation method of polymer latex resin pulverulent body
    同族专利:
    公开号 | 公开日
    EP3708248A4|2020-09-16|
    JP2021501065A|2021-01-14|
    CN111225738A|2020-06-02|
    US20200230525A1|2020-07-23|
    KR20190052613A|2019-05-16|
    引用文献:
    公开号 | 申请日 | 公开日 | 申请人 | 专利标题
    法律状态:
    2019-05-18| STAA| Information on the status of an ep patent application or granted ep patent|Free format text: STATUS: THE INTERNATIONAL PUBLICATION HAS BEEN MADE |
    2020-08-14| PUAI| Public reference made under article 153(3) epc to a published international application that has entered the european phase|Free format text: ORIGINAL CODE: 0009012 |
    2020-08-14| STAA| Information on the status of an ep patent application or granted ep patent|Free format text: STATUS: REQUEST FOR EXAMINATION WAS MADE |
    2020-09-16| A4| Supplementary search report drawn up and despatched|Effective date: 20200714 |
    2020-09-16| AK| Designated contracting states|Kind code of ref document: A1 Designated state(s): AL AT BE BG CH CY CZ DE DK EE ES FI FR GB GR HR HU IE IS IT LI LT LU LV MC MK MT NL NO PL PT RO RS SE SI SK SM TR |
    2020-09-16| AX| Request for extension of the european patent|Extension state: BA ME |
    2020-09-16| 17P| Request for examination filed|Effective date: 20200407 |
    2021-02-17| DAV| Request for validation of the european patent (deleted)|
    2021-02-17| DAX| Request for extension of the european patent (deleted)|
    优先权:
    申请号 | 申请日 | 专利标题
    [返回顶部]