    • 专利摘要:
    Provided is a laminate that includes a thin glass film and is hence excellent in flexibility, and that is excellent in puncture resistance . A laminate for an image display apparatus of the present invention includes: a glass film; and a resin layer arranged on one side of the glass film, wherein the glass film has a thickness of more than 50 µm and 150 µm or less, wherein the laminate for an image display apparatus has a puncture strength measured in conformity with JIS Z 1707 : 1997 of more than 2 kg and 50 kg or less, and wherein the laminate for an image display apparatus has a bending radius of from 15 mm to 200 mm.
    公开号:EP3705290A1
    申请号:EP18872596.4
    申请日:2018-10-25
    公开日:2020-09-09
    发明作者:Takeshi Murashige；Junichi Inagaki；Akiko Sugino；Tetsuro Ikeda
    申请人:Nitto Denko Corp；
    IPC主号:B32B17-00
    专利说明:
    [0001] The present invention relates to a laminate for an image display apparatus. Background Art
    [0002] In recent years, the weight reductions and thinning of display and lighting elements each using a liquid crystal display element or an organic EL, and of a solar cell have been advancing from the viewpoints of conveyability, storability, and a design property, and development toward continuous production by a roll-to-roll process has also been advancing. Under such situations, extremely thin glass (glass film) has heretofore been proposed as a method of imparting flexibility to glass. The glass film can be wound in a roll shape, and hence can be processed by the roll-to-roll process. For example, a method including processing a transparent electrode or the like from glass by the roll-to-roll process has heretofore been known.
    [0003] Meanwhile, a touch sensor function is incorporated into a display element, in particular an apparatus, such as a mobile device or a laptop PC, and its outermost surface layer is required to have durability against pen hitting or the like. A resin material subjected to a high-hardness surface treatment called hard coating has heretofore been used in the outermost surface layer of such device. In reality, however, sufficient durability has not been obtained. In addition, the frequency of the use of tempered glass called cover glass for significantly improving the strength of such device has been increasing. However, the tempered glass is as thick as 500 µm or more, and hence there is a circumstance in which the tempered glass is hardly applicable to a device having a certain area or more, such as a laptop PC or a monitor, owing to demands for thinning and a weight reduction. In addition, the tempered glass is not suitable for curved display because the glass cannot follow the shape of a curved surface. Under such situations, an attempt has been made to use a thin glass film in the outermost surface layer. However, the glass film is thin and easy to deform, and hence there remains a problem in that the film is liable to break in, for example, the case where its surface is hit with an acute protrusion, such as a pen. Citation ListPatent Literature
    [0004] [PTL 1] WO 2013-175767 A1 Summary of InventionTechnical Problem
    [0005] The present invention has been made to solve the conventional problems, and an object of the present invention is to provide a laminate that includes a thin glass film and is hence excellent in flexibility, and that is excellent in puncture resistance. Solution to Problem
    [0006] According to one embodiment of the present invention, there is provided a laminate for an image display apparatus, including: a glass film; and a resin layer arranged on one side of the glass film, wherein the glass film has a thickness of more than 50 µm and 150 µm or less, wherein the laminate for an image display apparatus has a puncture strength measured in conformity with JIS Z 1707: 1997 of more than 2 kg and 50 kg or less, and wherein the laminate for an image display apparatus has a bending radius of from 15 mm to 200 mm.
    [0007] In one embodiment, the laminate for an image display apparatus includes the glass film, an adhesive layer, the resin layer, and a pressure-sensitive adhesive layer in the stated order.
    [0008] In one embodiment, the laminate for an image display apparatus has a strength P represented by the following equation (1) of 500 (10-4 (µm)3(GPa)2) or more: P = tg 2 × Eg ta 1 × Ea 1 + tp × Ep 50 + ta 2 × Ea 2
    [0009] In one embodiment, the resin layer is a polarizing plate.
    [0010] In one embodiment, the polarizing plate includes a polarizer and a protective film arranged on one side of the polarizer, and the protective film and the polarizer are arranged in the stated order from a glass film side.
    [0011] In one embodiment, the resin layer has a modulus of elasticity at 23°C of from 1.5 GPa to 10 GPa.
    [0012] In one embodiment, the adhesive layer has a modulus of elasticity at 23°C of from 0.5 GPa to 15 GPa.
    [0013] In one embodiment, the pressure-sensitive adhesive layer has a modulus of elasticity at 23°C of from 0.00001 GPa to 10 GPa.
    [0014] In one embodiment, a ratio (modulus of elasticity of the adhesive layer/modulus of elasticity of the pressure-sensitive adhesive layer) of a modulus of elasticity of the adhesive layer at 23°C to a modulus of elasticity of the pressure-sensitive adhesive layer at 23°C is from 1 to 1,000. Advantageous Effects of Invention
    [0015] According to the present invention, the laminate that includes a thin glass film and is hence excellent in flexibility, and that is excellent in puncture resistance can be provided. Brief Description of Drawings
    [0016] FIG. 1 is a schematic sectional view of a laminate for an image display apparatus according to one embodiment of the present invention. FIG. 2 is a schematic sectional view of a laminate for an image display apparatus according to another embodiment of the present invention. Description of Embodiments A. Overall Configuration of Laminate for Image Display Apparatus
    [0017] FIG. 1 is a schematic sectional view of a laminate for an image display apparatus according to one embodiment of the present invention. A laminate 100 for an image display apparatus illustrated in FIG. 1 includes a glass film 10 and a resin layer 30 arranged on one side of the glass film 10. The laminate 100 for an image display apparatus preferably further includes an adhesive layer 20 between the glass film 10 and the resin layer 30. In addition, the laminate 100 for an image display apparatus preferably further includes a pressure-sensitive adhesive layer 40 on the side of the resin layer 30 opposite to the glass film 10. In one embodiment, the adhesive layer 20 and the pressure-sensitive adhesive layer 40 may be arranged on the resin layer 30 directly (i.e., without any other layer being interposed) . In addition, the adhesive layer 20 may be directly arranged on the glass film 10. The term "adhesive layer" as used herein refers to a layer capable of bonding substances to each other by being interposed between the substances. Therefore, when an adherend bonded to the adhesive layer is peeled, the adhesive layer is free of any practical adhesive strength. In addition, the term "pressure-sensitive adhesive layer" refers to a substance that has an adhesive property at normal temperature, and that is bonded to an adherend with a light pressure. Therefore, even when the adherend bonded to the pressure-sensitive adhesive layer is peeled, the pressure-sensitive adhesive layer holds a practical pressure-sensitive adhesive strength.
    [0018] In one embodiment, the resin layer may be a polarizing plate. FIG. 2 is a schematic sectional view of a laminate for an image display apparatus according to another embodiment of the present invention. A laminate 200 for an image display apparatus illustrated in FIG. 2 includes the glass film 10 and a polarizing plate 30' arranged on one side of the glass film10. In one embodiment, as illustrated in FIG. 2 , the polarizing plate 30' includes a polarizer 32 and a protective film 31 arranged on at least one side of the polarizer 32. When the protective film 31 is arranged only on one side of the polarizer 32, the protective film 31 and the polarizer 32 are preferably arranged in the stated order from the glass film 10 side. When the protective film 31 is arranged at such position, a laminate for an image display apparatus excellent in puncture strength can be obtained. The protective film may be arranged on each of both surfaces of the polarizer as required. Similarly to the laminate for an image display apparatus illustrated in FIG. 1 , the laminate 200 for an image display apparatus preferably further includes the adhesive layer 20 between the glass film 10 and the polarizing plate 30'. In addition, the laminate 200 for an image display apparatus preferably further includes the pressure-sensitive adhesive layer 40 on the side of the polarizing plate 30' opposite to the glass film 10. In one embodiment, the adhesive layer 20 and the pressure-sensitive adhesive layer 40 may be arranged on the polarizing plate 30' directly (i.e., without any other layer being interposed) . In addition, the adhesive layer 20 may be directly arranged on the glass film 10.
    [0019] The laminate 100 for an image display apparatus of the present invention has a high hardness because the laminate includes the glass film10. In addition, the laminate 100 for an image display apparatus of the present invention includes the resin layer 30 (the polarizing plate 30') on one side of the glass film 10. Accordingly, the breakage of the glass film 10 can be prevented, and hence the laminate is excellent in puncture resistance. In the present invention, the laminate is considered to be excellent in puncture resistance as described above because point compression applied to the surface of the glass film 10 (surface opposite to the polarizer) can be effectively caused to escape toward the resin layer 30.
    [0020] The puncture strength of the laminate for an image display apparatus of the present invention measured in conformity with JIS Z 1707:1997 is more than 2 kg and 50 kg or less, preferably from 4 kg to 30 kg, more preferably from 4 kg to 20 kg. When the puncture strength falls within such range, both of the bendability and puncture strength of the laminate can be achieved.
    [0021] The bending radius of the laminate for an image display apparatus of the present invention is from 15mm to 200 mm, preferably from 30 mm to 150 mm, more preferably from 50 mm to 100 mm. When the bending radius falls within such range, the above-mentioned effect becomes significant. The "bending radius" may be measured by: preparing poles having different outer diameters; and pressing and bending the laminate for an image display apparatus along the curved surfaces of the poles. The "bending radius" corresponds to the outer diameter of any one of the polls when the laminate for an image display apparatus is maximally bent to the extent that the laminate is not damaged. The "bending radius" is measured under a state in which the glass film is convex (i.e., the glass film faces outward and the resin layer faces inward).
    [0022] The thickness of the laminate for an image display apparatus of the present invention is preferably from 50 µm to 500 µm, more preferably from 100 µm to 400 µm, still more preferably from 120 µm to 300 µm.
    [0023] In one embodiment, the laminate for an image display apparatus of the present invention has a strength P represented by the following equation (1) of 500 (10-4 (µm)3(Gpa)2) or more: P = tg 2 × Eg ta 1 × Ea 1 + tp × Ep 50 + ta 2 × Ea 2
    [0024] In one embodiment, when the adhesive layer 20 and the pressure-sensitive adhesive layer 40 are directly arranged on the resin layer 30, 30', and the adhesive layer 20 is directly arranged on the glass film 10, the strength P of a laminate having the configuration "glass film 10/adhesive layer 20/resin layer 30, 30'/pressure-sensitive adhesive layer 40" is 500 (10-4 (µm)3(GPa)2) ormore. Without beingboundby anyparticular theory, a relationship among the glass film serving as the outermost surface layer, the adhesive layer, the resin layer, and the pressure-sensitive adhesive layer may be considered to be as described below. The puncture strength of the glass film is weighted by the puncture strengths of the three respective layers, that is, the adhesive layer, the pressure-sensitive adhesive layer, and the resin layer serving as coefficients therefor. Equations representing the weights are obtained from consistency with experimental results . The fact that the parameter is specified by the thicknesses and the moduli of elasticity is valid when the parameter is considered in terms of mechanical strength.
    [0025] In this description, the moduli of elasticity of the glass film, the resin layer, and the adhesive layer may be measured with an autograph (details about a measurement method are described later) . In addition, the modulus of elasticity of the pressure-sensitive adhesive layer may be measured with a viscoelasticity-measuring apparatus (details about a measurement method are described later) .
    [0026] The laminate for an image display apparatus of the present invention may further include other layers. Examples of the other layers include an antiref lection layer, an antiglare layer, an antistatic layer, and a conductive layer. A separator may be arranged on a surface of the pressure-sensitive adhesive layer. The separator can protect the pressure-sensitive adhesive layer until the laminate for an image display apparatus is put into practical use. In one embodiment, no other layer is arranged on the surface of the glass film opposite to the resin layer (i.e., the glass film is exposed). In addition, in order to prevent, for example, the adhesion of foreign matter to the surface of the exposed glass film, any appropriate protective material may be temporarily arranged on the surface of the glass film.
    [0027] The laminate for an image display apparatus of the present invention may be used in, for example, the substrate of a display element for an image display apparatus . In another aspect of the present invention, an image display apparatus including the laminate for an image display apparatus is provided. In one embodiment, the laminate for an image display apparatus of the present invention may be arranged on the outermost side on the viewer side of the image display apparatus. The laminate for an image display apparatus arranged as described above may function as a front surface protective plate for the image display apparatus. B. Glass Film
    [0028] Any appropriate glass film may be adopted as the glass film. According to classification based on composition, examples of the glass film include soda-lime glass, borate glass, aluminosilicate glass, and quartz glass films. In addition, according to classification based on an alkali component, examples of the glass film include alkali-free glass and low-alkali glass films. The content of an alkali metal component (e.g., Na2O, K2O, Li2O) in the glass is preferably 15 wt% or less, more preferably 10 wt% or less.
    [0029] The thickness of the glass film is preferably from 30 µm to 300 µm, more preferably more than 50 µm and 300 µm or less, still more preferably from 70 µm to 150 µm, particularly preferably from 80 µm to 120 µm. When the thickness falls within such range, a laminate for an image display apparatus having the following features can be obtained: the laminate is excellent in flexibility; and the glass film hardly breaks, and hence the laminate is excellent in productivity.
    [0030] The glass film preferably has a light transmittance at a wavelength of 550 nm of 85% or more. The glass film preferably has a refractive index at a wavelength of 550 nm of from 1.4 to 1.65.
    [0031] The glass film has a density of preferably from 2.3 g/cm3 to 3.0 g/cm3, more preferably from 2.3 g/cm3 to 2.7 g/cm3. When the glass film has a density falling within the range, a lightweight laminate for an image display apparatus is obtained.
    [0032] Any appropriate method may be adopted as a forming method for the glass film. The glass film is typically produced by melting a mixture containing a main raw material, such as silica or alumina, a fining agent, such as salt cake or antimony oxide, and a reducing agent, such as carbon, at a temperature of from 1, 400°C to 1, 600°C, and forming the molten mixture into a thin sheet shape, followed by cooling. Examples of the forming method for the glass film include a slot down-draw method, a fusion method, and a float method. The glass film formed in a sheet shape by any one of those methods may be chemically polished with a solvent, such as hydrofluoric acid, as required, in order to reduce its thickness or enhance its smoothness. C. Resin Layer
    [0033] Examples of the resin layer include a polarizing plate, a retardation plate, an isotropic film, and a conductive film. The resin layer may include a single layer, or may include a plurality of layers.
    [0034] Any appropriate material is used as a material for forming the resin layer. Examples of the material for forming the resin layer include a polyolefin-based resin, a cyclic olefin-based resin, a polycarbonate-based resin, a cellulose-based resin, a polyester-based resin, a polyamide-based resin, a polyimide-based resin, a polyether-based resin, a polystyrene-based resin, a (meth)acrylic resin, a (meth)acrylic urethane-based resin, a polysulfone-based resin, an acetate-based resin, an epoxy-based resin, a silicone-based resin, a polyarylate-based resin, a polysulfone-based resin, a polyetherimide-based resin, an epoxy-based resin, a urethane-based resin, a silicone-based resin, and a polyvinyl alcohol (PVA)-based resin.
    [0035] The thickness of the resin layer is preferably from 25 µm to 300 µm, more preferably from 30 µm to 250 µm, still more preferably from 50 µm to 200 µm, particularly preferably from 50 µm to 100 µm.
    [0036] The modulus of elasticity of the resin layer at 23°C is preferably from 2 GPa to 10 GPa, more preferably from 2 GPa to 5 GPa, still more preferably from 2 GPa to 4 GPa. When the modulus of elasticity falls within such range, a laminate for an image display apparatus excellent in puncture resistance can be obtained. C-1. Polarizing Plate
    [0037] As described above, in one embodiment, the resin layer is a polarizing plate. The polarizing plate includes a polarizer and a protective film arranged on at least one side of the polarizer. The thickness of the polarizing plate is preferably from 5 µm to 300 µm, more preferably from 10 µm to 250 µm, still more preferably from 25 µm to 200 µm, particularly preferably from 25 µm to 100 µm. C-1-1. Polarizer
    [0038] The thickness of the polarizer is not particularly limited, and an appropriate thickness may be adopted depending on purposes. The thickness is typically from about 1 µm to about 80 µm. In one embodiment, a thin polarizer is used, and the thickness of the polarizer is preferably 20 µm or less, more preferably 15 µm or less, still more preferably 10 µm or less, particularly preferably 6 µm or less. With the use of such thin polarizer, a thin laminate for an image display apparatus can be obtained.
    [0039] The polarizer preferably exhibits absorption dichroism at any wavelength in the wavelength range of from 380 nm to 780 nm. The polarizer has a single axis transmittance of preferably 40.0% or more, more preferably 41.0% or more, still more preferably 42. 0% or more, particularly preferably 43.0% or more. The polarizer has a polarization degree of preferably 99.8% or more, more preferably 99.9% or more, still more preferably 99.95% or more.
    [0040] The polarizer is preferably an iodine-based polarizer. More specifically, the polarizer may be formed of an iodine-containing polyvinyl alcohol-based resin (hereinafter referred to as "PVA-based resin") film.
    [0041] Any appropriate resin may be adopted as a PVA-based resin for forming the PVA-based resin film. Examples of the resin include polyvinyl alcohol and an ethylene-vinyl alcohol copolymer. The polyvinyl alcohol is obtained by saponifying polyvinyl acetate. The ethylene-vinyl alcohol copolymer is obtained by saponifying an ethylene-vinyl acetate copolymer. The saponification degree of the PVA-based resin is typically from 85 mol% to 100 mol%, preferably from 95.0 mol% to 99.95 mol%, more preferably from 99.0 mol% to 99.93 mol%. The saponification degree may be determined in conformity with JIS K 6726-1994. The use of the PVA-based resin having such saponification degree can provide a polarizer excellent in durability. When the saponification degree is excessively high, gelling may occur.
    [0042] The average polymerization degree of the PVA-based resin may be appropriately selected depending on purposes. The average polymerization degree is typically from 1, 000 to 10, 000, preferably from 1,200 to 5, 000, more preferably from 1,500 to 4,500. The average polymerization degree may be determined in conformity with JIS K 6726-1994.
    [0043] A production method for the polarizer is, for example, a method (I) including stretching and dyeing a PVA-based resin film alone, or a method (II) including stretching and dyeing a laminate (i) having a resin substrate and a polyvinyl alcohol-based resin layer. Detailed description of the method (I) is omitted because the method is well known and commonly used in the art. The production method (II) preferably includes the step of stretching and dyeing the laminate (i) having the resin substrate and the polyvinyl alcohol-based resin layer formed on one side of the resin substrate to produce a polarizer on the resin substrate. The laminate (i) maybe formed by applying an application liquid containing a polyvinyl alcohol-based resin onto the resin substrate and drying the applied liquid. In addition, the laminate (i) may be formed by transferring a polyvinyl alcohol-based resin film onto the resin substrate. For example, details about the production method (II) are described in JP 2012-73580 A , which is incorporated herein by reference. C-1-2. Protective Film
    [0044] Any appropriate resin film may be adopted as the protective film. As a material for forming the protective film, there are given, for example: a polyester-based resin, such as polyethylene terephthalate (PET); a cellulose-based resin, such as triacetylcellulose (TAC); a cycloolefin-based resin, such as a norbornene-based resin; an olefin-based resin, such as polyethylene or polypropylene; and a (meth)acrylic resin. Of those, polyethylene terephthalate (PET) is preferred. The term "(meth)acrylic resin" refers to an acrylic resin and/or a methacrylic resin.
    [0045] In one embodiment, a (meth)acrylic resin having a glutarimide structure is used as the (meth)acrylic resin. The (meth)acrylic resin having a glutarimide structure (hereinafter sometimes referred to as glutarimide resin) is described in, for example, JP 2006-309033 A , JP 2006-317560 A , JP 2006-328329 A , 2006-328334 A , JP 2006-337491 A , JP 2006-337492 A , JP 2006-337493 A , JP 2006-337569 A , JP 2007-009182 A , JP 2009-161744 A , and JP 2010-284840 A . The descriptions thereof are incorporated herein by reference.
    [0046] The protective film and the polarizer are laminated via any appropriate adhesive layer. The resin substrate used at the time of the production of the polarizer may be peeled before the lamination of the protective film and the polarizer, or after the lamination.
    [0047] The thickness of the protective film is preferably from 4 µm to 250 µm, more preferably from 5 µm to 150 µm, still more preferably from 10 µm to 100 µm, particularly preferably from 10 µm to 50 µm.
    [0048] The modulus of elasticity of the protective film at 23°C is preferably from 1 GPa to 10 GPa, more preferably from 2 GPa to 7 GPa, still more preferably from 2 GPa to 5 GPa. When the modulus of elasticity falls within such range, a laminate for an image display apparatus excellent in puncture resistance can be obtained. In this description, the modulus of elasticity of the protective film may be measured with an autograph (details about a measurement method are described later). D. Adhesive Layer
    [0049] The adhesive layer is formed of any appropriate adhesive. Examples of the adhesive include a polyester-based adhesive, a polyurethane-based adhesive, a polyvinyl alcohol-based adhesive, and an epoxy-based adhesive. Of those, an epoxy-based adhesive is preferred. This is because particularly satisfactory adhesiveness can be obtained.
    [0050] When the adhesive is a thermosetting adhesive, the adhesive can exhibit a peel-resisting force by being cured (solidified) through heating. In addition, when the adhesive is a photocurable adhesive, such as a UV-curable adhesive, the adhesive can exhibit a peel-resisting force by being cured through irradiation with light, such as UV light. In addition, when the adhesive is a moisture-curable adhesive, the adhesive may react with, for example, moisture in air to cure. Accordingly, the adhesive can cure to exhibit a peel-resisting force even by being left to stand.
    [0051] For example, a commercial adhesive may be used as the adhesive, or the adhesive may be prepared as an adhesive solution (or dispersion liquid) by dissolving or dispersing various curable resins in a solvent.
    [0052] The thickness of the adhesive layer is preferably from 1 µm to 30 µm, more preferably from 1 µm to 20 µm, still more preferably from 5 µm to 10 µm. When the thickness falls within such range, a laminate for an image display apparatus that is excellent in flexibility and is excellent in puncture resistance can be obtained.
    [0053] The modulus of elasticity of the adhesive layer at 23°C is preferably from 0.5 GPa to 15 GPa, more preferably from 0.8 GPa to 10 GPa, still more preferably from 1 GPa to 5 GPa. When the modulus of elasticity falls within such range, a laminate for an image display apparatus that is excellent in flexibility and is excellent in puncture resistance can be obtained.
    [0054] The ratio (modulus of elasticity of the adhesive layer/modulus of elasticity of the pressure-sensitive adhesive layer) of the modulus of elasticity of the adhesive layer at 23°C to the modulus of elasticity of the pressure-sensitive adhesive layer at 23°C is preferably from 1 to 1,000, more preferably from 10 to 500. When the ratio falls within such range, a laminate for an image display apparatus that is excellent in puncture resistance and is excellent in puncture strength can be obtained. E. Pressure-sensitive Adhesive Layer
    [0055] The pressure-sensitive adhesive layer is formed of any appropriate adhesive. A pressure-sensitive adhesive containing, for example, an acrylic polymer, a silicone-based polymer, polyester, polyurethane, polyamide, polyether, or a fluorine-based or rubber-based polymer as a base polymer is used as the pressure-sensitive adhesive. Of those, an acrylic pressure-sensitive adhesive is preferably used. This is because the acrylic pressure-sensitive adhesive is excellent in optical transparency, shows moderate wettability, moderate cohesiveness, and a moderate pressure-sensitive adhesive characteristic, such as an adhesive property, and may be excellent in, for example, weatherability and heat resistance. An acrylic pressure-sensitive adhesive formed of an acrylic polymer having 4 to 12 carbon atoms is particularly preferred.
    [0056] The thickness of the pressure-sensitive adhesive layer is preferably from 1 µm to 100 µm, more preferably from 3 µm to 80 µm, still more preferably from 3 µm to 50 µm. When the thickness falls within such range, a laminate for an image display apparatus that is excellent in flexibility and is excellent in puncture resistance can be obtained.
    [0057] The modulus of elasticity of the pressure-sensitive adhesive layer at 23°C is preferably from 0.00001 GPa to 10 GPa, more preferably from 0.001 GPa to 8 GPa, still more preferably from 0.001 GPa to 5 GPa. When the modulus of elasticity falls within such range, a laminate for an image display apparatus that is excellent in flexibility and is excellent in puncture resistance can be obtained. A method of measuring the modulus of elasticity of the pressure-sensitive adhesive layer is described later.
    [0058] In one embodiment, when the thickness of the glass film is 70 µm or more, the modulus of elasticity of the pressure-sensitive adhesive layer at 23°C is preferably from 0.00001 GPa to 1 GPa, more preferably from 0.00001 GPa to 0.1 GPa. In another embodiment, when the thickness of the glass film is less than 70 µm, the modulus of elasticity of the pressure-sensitive adhesive layer at 23°C is preferably from 0.5 GPa to 8 GPa, more preferably from 1 GPa to 4 GPa. When the modulus of elasticity of the pressure-sensitive adhesive layer is regulated in accordance with the thickness of the glass film, a laminate for an image display apparatus that is excellent in flexibility and is excellent in puncture resistance can be obtained. F. Others
    [0059] In the present invention, in order to set the puncture strength measured in conformity with JIS Z 1707:1997 to more than 2 kg and 50 kg or less, and to set the bending radius to from 15 mm to 200 mm, elements described in the section B to the section E can be appropriately combined to achieve such settings; for example, the settings may be preferably achieved by any one of the following embodiment modes. Embodiment Mode (1)
    [0060] When the thickness of the glass film is 30 µm or more and 60 µm or less, a laminate for an image display apparatus is produced by: setting the modulus of elasticity of the adhesive layer at 23°C to 1 GPa or more and 5 GPa or less; setting the thickness of the polarizing plate to 25 µm or more and 200 µm or less; setting the thickness of the pressure-sensitive adhesive layer to 3 µm or more and 50 µm or less; and setting the modulus of elasticity of the pressure-sensitive adhesive layer at 23°C to 1 GPa or more and 4 GPa or less. Embodiment Mode (2)
    [0061] When the thickness of the glass film is 70 µm or more and 120 µm or less, a laminate for an image display apparatus is produced by: setting the modulus of elasticity of the adhesive layer at 23°C to 1 GPa or more and 5 GPa or less; setting the thickness of the polarizing plate to 25 µm or more and 200 µm or less; setting the thickness of the pressure-sensitive adhesive layer to 3 µm or more and 50 µm or less; and setting the modulus of elasticity of the pressure-sensitive adhesive layer at 23°C to 0.00001 GPa or more and 0.1 GPa or less. Examples
    [0062] The present invention is specifically described below by way of Examples, but the present invention is not limited to these Examples. In addition, in Examples, "part(s)" and "%" are by weight unless otherwise specified. [Production Example 1] Preparation of Polarizing Plate A(Preparation of Polarizer)
    [0063] First, a laminate obtained by forming a 9-micrometer thick PVA layer on an amorphous PET substrate was subjected to in-air auxiliary stretching at a stretching temperature of 130°C to produce a stretched laminate. Next, the stretched laminate was subjected to dyeing to produce a colored laminate. Further, the colored laminate was subjected to in-boric-acid-solution stretching at a stretching temperature of 65°C so that the total stretching ratio became 5.94 times. Thus, an optical film laminate including a 4-micrometer thick PVA layer stretched together with the amorphous PET substrate was produced. Such two-stage stretching was able to produce an optical film laminate including the 4-micrometer thick PVA layer, the layer forming such a high-function polarizer that the PVA molecules of the PVA layer formed on the amorphous PET substrate were aligned in a high order, and iodine caused to adsorb to the polarizer by the dyeing was aligned as a polyiodide ion complex in one direction in a high order. (Preparation of Acrylic Film)
    [0064] A methacrylic resin pellet having a glutarimide ring unit was dried at 100.5 kPa and 100°C for 12 hours, and was extruded from the T-die of a uniaxial extruder at a die temperature of 270°C to be formed into a film shape. The film was stretched in its conveying direction (MD direction) under an atmosphere having a temperature higher than the Tg of the resin by 10°C. Next, the film was stretched in the direction (TD direction) perpendicular to the film-conveying direction under an atmosphere having a temperature higher than the Tg of the resin by 7°C. Thus, an acrylic film having a thickness of 40 µm was obtained. (Preparation of Curable Adhesive)
    [0065] 35 Parts by weight of N-hydroxyethyl acrylamide HEAA (manufactured by Kohjin Co., Ltd.), 45 parts by weight of N-acryloylmorpholine ACMO (manufactured by Kohjin Co., Ltd.), 25 parts by weight of polypropylene glycol diacrylate TPGDA (manufactured by Toagosei Co., Ltd., product name: "ARONIX M-220"), 3 parts by weight of a photopolymerization initiator (manufactured by Ciba Specialty Chemicals, product name: "IRGACURE 184"), and 1.5 parts by weight of another photopolymerization initiator (manufactured by Nippon Kayaku Co., Ltd., product name: "KAYACURE DETX-S") were added as an adhesive. (Production of Polarizing Plate)
    [0066] The curable adhesive was applied in an application thickness of about 1 µm onto the polarizer produced on the PET substrate. Next, the acrylic film having a thickness of 40 µm was bonded to the adhesive layer. The adhesive was irradiated with UV light having a peak UV irradiance of 1,600 mW/cm2 and a UV integrated light quantity of 1,000 mJ/cm2 (wavelength: from 380 nm to 440 nm), which had been emitted from a conveyor-type UV irradiation apparatus (manufactured by FUSION UV SYSTEMS), from the PET substrate side to be cured, and the cured adhesive was dried at 70°C for 2 minutes. Finally, the PET substrate was peeled from the laminate obtained by laminating the acrylic film, the polarizer, and the PET substrate. Thus, a laminate (a polarizing plate A having a thickness of 44 µm) of the acrylic film (protective film) and the polarizer was obtained. [Production Example 2] Preparation of Polarizing Plate B
    [0067] A polyvinyl alcohol film (PVA) having a thickness of 80 µm was stretched at up to 3 times between rolls having different speed ratios while being dyed in an iodine solution at 30°C having a concentration of 0.3% for 1 minute. After that, the film was stretched so that the total stretching ratio became 6 times while being immersed in an aqueous solution at 60°C containing boric acid at a concentration of 4% and potassium iodide at a concentration of 10% for 0.5 minute. Next, the film was washed by being immersed in an aqueous solution at 30°C containing potassium iodide at a concentration of 1.5% for 10 seconds. After that, the film was dried at 50°C for 4 minutes to provide a polarizer having a thickness of 20 µm. A 40-micrometer thick triacetylcellulose film (TAC) subjected to a saponification treatment was bonded to one surface of the polarizer with a polyvinyl alcohol-based adhesive, and a 33-micrometer thick norbornene-based film was bonded to the other surface thereof with the adhesive. Thus, a polarizing plate B (thickness: 93 µm) was obtained. [Production Example 3] Preparation of Polarizing Plate C
    [0068] A polarizing plate C (thickness: 137 µm) was obtained in the same manner as in Production Example 2 except that: the thickness of the TAC film was changed to 100 µm; and the thickness of the polarizer was changed to 4 µm. [Production Example 4] Preparation of Polarizing Plate D
    [0069] A TAC film (thickness: 100 µm) was bonded to the surface of the polarizer of the polarizing plate Aprepared in Production Example 1 opposite to the acrylic film (protective film) via an adhesive layer (thickness: 5 µm) including an adhesive prepared in Production Example 7 below. Thus, a polarizing plate D (thickness: 149 µm) having the configuration "acrylic film/polarizer/TAC film" was obtained. [Production Example 5] Preparation of Polarizing Plate E
    [0070] A TAC film (thickness: 100 µm) was bonded to the surface of the polarizer of the polarizing plate Aprepared in Production Example 1 opposite to the acrylic film (protective film) via an adhesive layer (thickness: 20 µm) including a pressure-sensitive adhesive prepared in Production Example 6 below. Thus, a polarizing plate E (thickness: 164 µm) having the configuration "acrylic film/polarizer/TAC film" was obtained. [Production Example 6] Preparation of Pressure-sensitive Adhesive(Preparation of Acrylic Polymer)
    [0071] 100 Parts by weight of butyl acrylate, 5 parts by weight of acrylic acid, and 0.075 part by weight of 2-hydroxyethyl acrylate, 0.2 part by weight of 2,2'-azobisisobutyronitrile serving as a polymerization initiator, and 200 parts by weight of ethyl acetate serving as a polymerization solvent were loaded into a four-necked flask including a stirring blade, a temperature gauge, a nitrogen gas-introducing tube, and a condenser. After air in the flask had been sufficiently purged with nitrogen, the mixed liquid, whose temperature in the flask was kept at around 55°C, was subjected to a polymerization reaction for 10 hours while being stirred in a streamof nitrogen. Thus, an acrylic polymer solution was prepared. The acrylic polymer had a weight-average molecular weight of 2,200,000. (Preparation of Pressure-sensitive Adhesive Composition)
    [0072] 100 Parts by weight of the solid content of the acrylic polymer solution was uniformly mixed with 0.2 part by weight of dibenzoyl peroxide (NYPER BMT, manufactured by Nippon Oil & Fats Co., Ltd.) serving as a peroxide, 0.05 part by weight of diglycidylaminomethylcyclohexane (manufactured by Mitsubishi Gas Chemical Company, Inc., TETRAD-C) serving as an epoxy-based cross-linking agent, 0.1 part by weight of a trimethylolpropane-tolylene diisocyanate adduct (manufactured by Nippon Polyurethane Industry Co., Ltd., CORONATE L) serving as an isocyanate-based cross-linking agent, and 0.075 part by weight of a silane coupling agent (manufactured by Shin-Etsu Chemical Co., Ltd., KBM-403), followed by stirring. Thus, an acrylic pressure-sensitive adhesive (solid content: 10.9 wt%) was prepared. [Production Example 7] Preparation of Adhesive(Preparation of Epoxy Adhesive)
    [0073] 70 Parts by weight of CELLOXIDE 2021P (manufactured by Daicel Chemical Industries, Ltd.), 5 parts by weight of EHPE 3150, 19 parts by weight of ARON OXETANE OXT-221 (manufactured by Toagosei Co., Ltd.), 4 parts by weight of KBM-403 (manufactured by Shin-Etsu Chemical Co., Ltd.), and 2 parts by weight of CPI-101A (manufactured by San-Apro Ltd.) were compounded to prepare an epoxy adhesive. [Example 1]
    [0074] A glass film (manufactured by Nippon Electric Glass Co., Ltd., product name: "OA-10G", thickness: 100 µm) and the polarizing plate A produced in Production Example 1 were bonded to each other via an adhesive layer (thickness: 5 µm) including the adhesive prepared in Production Example 7. At this time, the polarizing plate A was arranged so that its protective film was on the glass film side. Next, the adhesive layer was irradiated with UV light (500 mJ/cm2) from a high-pressure mercury lamp. Thus, the adhesive layer was cured.
    [0075] Further, a pressure-sensitive adhesive layer (thickness: 20 µm) including the pressure-sensitive adhesive prepared in Production Example 6 was formed on the polarizer side of the polarizing plate. Thus, a laminate for an image display apparatus was obtained.
    [0076] The pressure-sensitive adhesive layer was formed as follows:(i) the pressure-sensitive adhesive was applied onto a silicone-treated polyethylene terephthalate film (manufactured by Mitsubishi Chemical Polyester Film Co., Ltd., thickness: 38 µm), and was heated at 155°C for 1 minute to form the pressure-sensitive adhesive layer having a thickness after the drying of 20 µm; and (ii) the pressure-sensitive adhesive layer was transferred from the polyethylene terephthalate film onto the polarizer to provide the laminate for an image display apparatus including the pressure-sensitive adhesive layer. [Example 2]
    [0077] A laminate for an image display apparatus was obtained in the same manner as in Example 1 except that the polarizing plate B was used instead of the polarizing plate A. [Example 3]
    [0078] A laminate for an image display apparatus was obtained in the same manner as in Example 1 except that the polarizing plate C was used instead of the polarizing plate A. [Example 4]
    [0079] A laminate for an image display apparatus was obtained in the same manner as in Example 1 except that the polarizing plate D was used instead of the polarizing plate A. The polarizing plate D was arranged so that its TAC film was on the glass film side. [Example 5]
    [0080] A laminate for an image display apparatus was obtained in the same manner as in Example 2 except that a glass film (manufactured by Nippon Electric Glass Co., Ltd., product name: "OA-10G", thickness: 70 µm) was used instead of the glass film (manufactured by Nippon Electric Glass Co., Ltd., product name: "OA-10G", thickness: 100 µm). [Comparative Example 1]
    [0081] A laminate for an image display apparatus was obtained in the same manner as in Example 1 except that a glass film (manufactured by Nippon Electric Glass Co., Ltd., product name: "OA-10G", thickness: 50 µm) was used instead of the glass film (manufactured by Nippon Electric Glass Co., Ltd., product name: "OA-10G", thickness: 100 µm). [Comparative Example 2]
    [0082] A laminate for an image display apparatus was obtained in the same manner as in Comparative Example 1 except that the polarizing plate B was used instead of the polarizing plate A. [Comparative Example 3]
    [0083] A laminate for an image display apparatus was obtained in the same manner as in Comparative Example 1 except that the polarizing plate C was used instead of the polarizing plate A. [Comparative Example 4]
    [0084] A glass film (manufactured by Nippon Electric Glass Co., Ltd., product name: "OA-10G", thickness: 100 µm), a pressure-sensitive adhesive layer (thickness: 20 µm) including the pressure-sensitive adhesive prepared in Production Example 6, the polarizing plate A, and another pressure-sensitive adhesive layer (thickness: 20 µm) including the pressure-sensitive adhesive prepared in Production Example 6 were laminated in the stated order to provide a laminate for an image display apparatus . The polarizing plate A was arranged so that its protective film was on the glass film side. [Comparative Example 5]
    [0085] A laminate for an image display apparatus was obtained in the same manner as in Comparative Example 4 except that a glass film (manufactured by Nippon Electric Glass Co., Ltd., product name: "OA-10G", thickness: 200 µm) was used instead of the glass film (manufactured by Nippon Electric Glass Co., Ltd., product name: "OA-10G", thickness: 100 µm). [Comparative Example 6]
    [0086] A glass film (manufactured by Nippon Electric Glass Co., Ltd., product name: "OA-10G", thickness: 50 µm), a pressure-sensitive adhesive layer (thickness: 20 µm) including the pressure-sensitive adhesive prepared in Production Example 6, a TAC film (thickness: 100 µm), and another pressure-sensitive adhesive layer (thickness: 20 µm) including the pressure-sensitive adhesive prepared in Production Example 6 were laminated in the stated order to provide a laminate for an image display apparatus. [Comparative Example 7]
    [0087] A TAC film (thickness: 100 µm), a pressure-sensitive adhesive layer (thickness: 20 µm) including the pressure-sensitive adhesive prepared in Production Example 6, the polarizing plate E, and another pressure-sensitive adhesive layer (thickness: 20 µm) including the pressure-sensitive adhesive prepared in Production Example 6 were laminated in the stated order to provide a laminate for an image display apparatus. The polarizing plate E was arranged so that its TAC film was on the glass film side. <Evaluation>
    [0088] The laminates for image display apparatus obtained in Examples, Comparative Examples, and Reference Example were subjected to the following evaluations. The results are shown in Table 1. 1. Modulus of Elasticity(Modulus of Elasticity of Pressure-sensitive Adhesive Layer)
    [0089] The storage modulus of elasticity of a pressure-sensitive adhesive layer at 23°C was measured with a viscoelasticity-measuring apparatus ARES (manufactured by TA Instruments, Inc.). That is, the pressure-sensitive adhesive layer was formed into a sheet shape having a thickness of 2 mm, and the sheet was punched into a shape in accordance with parallel plates each having a diameter of 25 mm, followed by its mounting between the chucks of the apparatus. Then, the temperature of the layer was increased from -70°C to 150°C at a rate of temperature increase of 5°C/min while strain was applied thereto at a frequency of 1 Hz, followed by the measurement of its storage modulus of elasticity at 23°C. (Moduli of Elasticity of Adhesive Layer, Polarizing Plate, Resin Layer, and Glass Film)
    [0090] A strip-shaped sample having a thickness of 50 µm, a width of 2 cm, and a length of 15 cm was produced, and its modulus of elasticity was measured with an autograph (manufactured by Shimadzu Corporation, AG-I) from the elongation of the strip-shaped sample in its lengthwise direction and a stress. Test conditions were as follows: a chuck-to-chuck distance was set to 10 cm, and a tensile rate was set to 10 mm/min. 2. Bendability
    [0091] Vinyl chloride-made poles having different outer diameters were prepared so that their radii ranged from 20 mm to 100 mm in increments of 10 mm. A bending test was performed by: bending a sample along any one of the poles so that its glass film side (in each of Comparative Examples 7 and 8, its TAC film side serving as the outermost surface layer) faced outward; confirming the degree of bending of the sample on the basis of whether both sides thereof couldbe or couldnot be fixedwith CELLOTAPE (trademark) manufactured by Nichiban Co., Ltd. (CT405AP-24, pressure-sensitive adhesive strength: 3.93 N/10 cm), or the sample broke; and measuring the bending radius thereof. A sample size was as follows: the length of its short side was set to 20 mm, and the length of its long side was set to the radius of the outer diameter of each pole. 3. Method of evaluating Puncture Strength
    [0092] A 5-centimeter square laminate was bonded to a glass plate to provide an evaluation sample. A jig for a film puncture test (TKS-20N/250N (in conformity with JIS Z 1707:1997, manufactured by Imada Co., Ltd.)) was attached to a motorized vertical force gauge stand (manufactured by Nidec-Shimpo Corporation). The evaluation sample was placed on the stage of the stand, and the sample was punctured with a puncture rod (ϕ0.5 mm) at a rate of 20 mm/min. An indentation load when the glass broke was measured with the force gauge and adopted as the puncture strength of the sample. 4. Pencil Hardness
    [0093] The pencil hardness of the surface of a laminate for an image display apparatus opposite to its pressure-sensitive adhesive layer (i.e., the surface of its glass film or the surface of its TAC film) was measured in conformity with the pencil hardness test of JIS K 5600-5-4 (provided that a load of 500 g was applied thereto). 5. Strength P
    [0094] A strength P described in the section A was calculated.
    [0095] 10glass film 20adhesive layer 30resin layer 30'polarizing plate 31protective film 32polarizer 40pressure-sensitive adhesive layer 100, 200laminate for image display apparatus
    权利要求:
    Claims (9)
    [0001] A laminate for an image display apparatus, comprising:
    a glass film; and
    a resin layer arranged on one side of the glass film,
    wherein the glass film has a thickness of more than 50 µm and 150 µm or less,
    wherein the laminate for an image display apparatus has a puncture strength measured in conformity with JIS Z 1707:1997 of more than 2 kg and 50 kg or less, and
    wherein the laminate for an image display apparatus has a bending radius of from 15 mm to 200 mm.
    [0002] The laminate for an image display apparatus according to claim 1, wherein the laminate for an image display apparatus comprises the glass film, an adhesive layer, the resin layer, and a pressure-sensitive adhesive layer in the stated order.
    [0003] The laminate for an image display apparatus according to claim 2, wherein the laminate for an image display apparatus has a strength P represented by the following equation (1) of 500 (10-4 (µm)3(Gpa)2) or more: P = tg 2 × Eg ta 1 × Ea 1 + tp × Ep 50 + ta 2 × Ea 2
    [0004] The laminate for an image display apparatus according to any one of claims 1 to 3, wherein the resin layer is a polarizing plate.
    [0005] The laminate for an image display apparatus according to claim 4,wherein the polarizing plate includes a polarizer and a protective film arranged on one side of the polarizer, andwherein the protective film and the polarizer are arranged in the stated order from a glass film side.
    [0006] The laminate for an image display apparatus according to any one of claims 1 to 5, wherein the resin layer has a modulus of elasticity at 23°C of from 2 GPa to 10 GPa.
    [0007] The laminate for an image display apparatus according to any one of claims 2 to 6, wherein the adhesive layer has a modulus of elasticity at 23°C of from 0.5 GPa to 15 GPa.
    [0008] The laminate for an image display apparatus according to any one of claims 2 to 7, wherein the pressure-sensitive adhesive layer has a modulus of elasticity at 23°C of from 0.00001 GPa to 10 GPa.
    [0009] The laminate for an image display apparatus according to any one of claims 2 to 8, wherein a ratio (modulus of elasticity of the adhesive layer/modulus of elasticity of the pressure-sensitive adhesive layer) of a modulus of elasticity of the adhesive layer at 23°C to a modulus of elasticity of the pressure-sensitive adhesive layer at 23°C is from 1 to 1,000.
    类似技术:
    公开号 | 公开日 | 专利标题
    US10534199B2|2020-01-14|Functional sheet and lens using same
    KR101727871B1|2017-04-17|Set of polarizing plates and front plate-integrated liquid crystal display panel
    US9169423B2|2015-10-27|Adhesive optical film, manufacturing method for the same and image display device using the same
    KR102215376B1|2021-02-10|Photocurable adhesive composition, polarizer and process for producing same, optical member, and liquid-crystal display device
    KR101673037B1|2016-11-04|Adhesive polarization plate, image display device and methods for manufacturing adhesive polarization plate and image display device
    US7622055B2|2009-11-24|Polarizing plate and image display including the same
    KR100973677B1|2010-08-04|Polarizing plate and adhesive composition for polarizing plate
    JP4928529B2|2012-05-09|Manufacturing method of polarizing plate, polarizing plate, optical film, and image display device
    KR101819787B1|2018-01-17|Composite polarizing plate and liquid crystal display device
    KR101985994B1|2019-06-04|Polarizing film production method
    US7929086B2|2011-04-19|Laminated film
    JP5874159B2|2016-03-02|GLASS-RESIN LAMINATE, GLASS ROLL WASTING THE SAME, AND GLASS ROLL MANUFACTURING METHOD
    US9880419B2|2018-01-30|Optical laminate for front surface of in-cell touch panel liquid crystal element and in-cell touch panel liquid crystal display device using same
    KR101780570B1|2017-09-21|Light-diffusing adhesive and optical member and polarizing plate using said light-diffusing adhesive
    KR101912493B1|2018-10-26|Adhesive sheet for optical film, process for production of the adhesive sheet, adhesive optical film, and image display device
    KR20150104175A|2015-09-14|Circular polarizing plate and bendable display device
    US7911564B2|2011-03-22|Polarizing plate, image display, and method of manufacturing polarizing plate
    JP6136527B2|2017-05-31|Optical laminate for front surface of in-cell touch panel liquid crystal element and in-cell touch panel type liquid crystal display device using the same
    CN104250524B|2020-02-21|Adhesive composition, adhesive and adhesive sheet
    TWI551895B|2016-10-01|Double-sided transparent adhesive sheet with linear polarization function
    US20140160406A1|2014-06-12|Polarizing plate
    KR101719883B1|2017-03-24|Photocurable adhesive composition, polarizer and process for producing same, optical member, and liquid-crystal display device
    US9684096B2|2017-06-20|Unit for image display device having adhesive layer, and image display device using the unit
    JP4807774B2|2011-11-02|Liquid crystal panel and liquid crystal display device
    JP5268234B2|2013-08-21|Liquid crystal panel and liquid crystal display device
    同族专利:
    公开号 | 公开日
    KR20200060463A|2020-05-29|
    TW201922492A|2019-06-16|
    JPWO2019087938A1|2020-11-19|
    WO2019087938A1|2019-05-09|
    CN111315573A|2020-06-19|
    引用文献:
    公开号 | 申请日 | 公开日 | 申请人 | 专利标题
    法律状态:
    2019-05-11| STAA| Information on the status of an ep patent application or granted ep patent|Free format text: STATUS: THE INTERNATIONAL PUBLICATION HAS BEEN MADE |
    2020-08-07| STAA| Information on the status of an ep patent application or granted ep patent|Free format text: STATUS: REQUEST FOR EXAMINATION WAS MADE |
    2020-08-07| PUAI| Public reference made under article 153(3) epc to a published international application that has entered the european phase|Free format text: ORIGINAL CODE: 0009012 |
    2020-09-09| 17P| Request for examination filed|Effective date: 20200423 |
    2020-09-09| AK| Designated contracting states|Kind code of ref document: A1 Designated state(s): AL AT BE BG CH CY CZ DE DK EE ES FI FR GB GR HR HU IE IS IT LI LT LU LV MC MK MT NL NO PL PT RO RS SE SI SK SM TR |
    2020-09-09| AX| Request for extension of the european patent|Extension state: BA ME |
    2021-02-17| DAV| Request for validation of the european patent (deleted)|
    2021-02-17| DAX| Request for extension of the european patent (deleted)|
    2021-08-04| A4| Supplementary search report drawn up and despatched|Effective date: 20210706 |
    2021-08-04| RIC1| Information provided on ipc code assigned before grant|Ipc: B32B 17/10 20060101AFI20210630BHEP Ipc: B32B7/023 20190101ALI20210630BHEP Ipc: B32B 27/00 20060101ALI20210630BHEP Ipc: C03C 17/32 20060101ALI20210630BHEP Ipc: B32B7/12 20060101ALI20210630BHEP Ipc: B32B 27/30 20060101ALI20210630BHEP Ipc: B32B 27/32 20060101ALI20210630BHEP |
    优先权:
    申请号 | 申请日 | 专利标题
    [返回顶部]