    • 专利摘要:
    A lithium secondary battery includes: a cathode, an anode; and an electrolyte between the cathode and the anode, wherein the cathode includes a cathode active material represented by Formula 1 below, and the electrolyte includes a lithium salt, a nonaqueous solvent, and a compound represented by Formula 2, where x, y, z, M, A, L1, a1, and R<sub>1</sub>to R<sub>4</sub>are defined as described in the disclosure.         Formula 1     Li<sub>x</sub>Ni<sub>y</sub>M<sub>1-y</sub>O<sub>2-z</sub>A<sub>z</sub>
    公开号:EP3699985A1
    申请号:EP20157630.3
    申请日:2020-02-17
    公开日:2020-08-26
    发明作者:Wonseok Cho；Pavel Shatunov；Olga Tsay；Younghye Kang；Aeran Kim；Hyejin Park；Jeongmin Shin；Myungheui Woo；Duckjae YOU；Taejin Lee；Harim Lee；Jinhyeok LIM；Hyunbong CHOI
    申请人:Samsung SDI Co Ltd；
    IPC主号:H01M4-00
    专利说明:
    [0001] Embodiments of the present disclosure relate to a lithium secondary battery including a phosphine-based additive. 2. Description of Related Art
    [0002] Lithium secondary batteries are used as power sources for driving portable electronic appliances such as, for examples, video cameras, mobile phones, and notebook computers. Rechargeable lithium secondary batteries have three times higher energy density per unit weight than existing lead-acid batteries, nickel-cadmium batteries, nickel metal hydride batteries, and nickel-zinc batteries, and may be charged at high speed.
    [0003] Non-aqueous electrolytes including organic solvents are generally used for lithium secondary batteries. The electrolyte further includes a lithium salt which is dissolved in the organic solvent. The organic solvent should be stable at a high voltage, should have high ionic conductivity and a high dielectric constant, and should have low viscosity.
    [0004] However, LiPF6, which may be used as a lithium salt of the electrolyte, may react with the solvent and to promote the depletion of the solvent thereby generating a large amount of gas. When LiPF6 is decomposed, LiF and PF5 are produced, which causes the depletion of the electrolyte in the battery, resulting in deterioration of high temperature performance and poor safety.
    [0005] As the cathode active material contained in the cathode of the lithium secondary battery, a lithium-containing metal oxide may be used. For example, a composite oxide of lithium and a metal selected from cobalt (Co), manganese (Mn), nickel (Ni), and a combination thereof may be used. Among these, in the case of high-Ni-content cathode active materials, studies have recently been conducted on such materials because they may realize a higher capacity battery as compared with existing lithium cobalt oxide.
    [0006] However, in the case of a high-Ni-content cathode active material, lifetime characteristics are poor due to the weak surface structure of a cathode.
    [0007] Accordingly, a lithium secondary battery that suppresses or reduces the side reaction of the aforementioned electrolyte and having improved lifetime characteristics and high-temperature stability should be provided. SUMMARY
    [0008] According to an aspect of an embodiment, there is provided a new lithium secondary battery.
    [0009] Additional aspects of embodiments will be set forth in part in the description which follows and, in part, will be apparent from the description, or may be learned by practice of the presented embodiments of the disclosure.
    [0010] According to the present disclosure, there is provided a lithium secondary battery, including: a cathode; an anode; and an electrolyte between the cathode and the anode, wherein the cathode includes a cathode active material represented by Formula 1, and the electrolyte includes: a lithium salt; a non-aqueous solvent; and a compound represented by Formula 2:         Formula 1     LixNiyM1-yO2-zAz in Formula 1, 0.9≤x≤1.2, 0.6≤y≤0.98, and 0≤z<0.2 are satisfied, M is at least one element selected from Al, Mg, Mn, Co, Fe, Cr, V, Ti, Cu, B, Ca, Zn, Zr, Nb, Mo, Sr, Sb, W, and Bi, and A is an element having an oxidation number of -1 or -2; and
    [0011] The above, and other aspects and features, of certain embodiments of the disclosure will be more apparent from the following description taken in conjunction with the accompanying drawings, in which:FIG. 1 is a schematic view of a lithium secondary battery according to an embodiment; FIG. 2A is a graph illustrating the anode cyclic voltage currents of the electrolytes according to Preparation Example 1 and Comparative Preparation Example 1 measured using a cyclic voltammetry (CV), and FIG. 2B is an enlarged graph of FIG. 2A; FIG. 3 is a graph illustrating the changes in discharge capacity per cycle at 25 °C of the lithium secondary batteries according to Examples 1 to 5 and Comparative Examples 1 and 2; FIG. 4 is a graph illustrating the changes in discharge capacity per cycle at 45 °C of the lithium secondary batteries according to Examples 1 to 5 and Comparative Examples 1 and 3; FIG. 5 is a graph illustrating the changes in resistance (DCIR) at 60 °C of the lithium secondary batteries according to Examples 1 to 5 and Comparative Examples 1 and 2; and FIG. 6 is a graph illustrating the changes in resistance (DCIR) at 60 °C of the lithium secondary batteries according to Examples 1 to 5 and Comparative Examples 1 and 3. DETAILED DESCRIPTION
    [0012] Reference will now be made in more detail to embodiments, examples of which are illustrated in the accompanying drawings, wherein like reference numerals refer to like elements throughout. In this regard, the present embodiments may have different forms and should not be construed as being limited to the descriptions set forth herein. Accordingly, the embodiments are merely described below, by referring to the figures, to explain aspects of embodiments of the present description. As used herein, the term "and/or" includes any and all combinations of one or more of the associated listed items. Expressions such as "at least one of," when preceding a list of elements, modify the entire list of elements and do not modify the individual elements of the list.
    [0013] Hereinafter, an additive for lithium secondary batteries, an organic electrolyte including the additive, and a lithium secondary battery employing the electrolyte according to embodiments will be described in more detail.
    [0014] As used herein, "a" and "b" in "Ca-Cb" refer to the number of carbon atoms in a functional group. For example, the functional group may include "a" to "b" carbon atoms. Therefore, for example, the term "C1-C4 alkyl group" refers to an alkyl group having 1 to 4 carbon atoms, such as CH3-, CH3CH2-, CH3CH2CH2-, (CH3)2CH-, CH3CH2CH2CH2-, CH3CH2CH(CH3)-, or (CH3)3C-.
    [0015] Certain radical nomenclature used herein may include mono-radicals or di-radicals depending on the context. For example, when one substituent requires two connection points in the remaining molecule, it is to be understood that the substituent is a di-radical.
    [0016] As used herein, the term " C1-C30 alkylene group" refers to an unbranched aliphatic group having 1 to 30 carbon atoms. The alkylene group may be substituted. For example, an alkylene group includes di-radicals such as -CH2-, -CH2CH2-, or -CH2CH(CH3)CH2-.
    [0017] As used herein, the term "C2-C30 alkenylene group" refers to an unbranched hydrocarbon group having 2 to 30 carbon atoms including at least one carbon-carbon double bond. The alkenylene group may be substituted.
    [0018] As used herein, the term "C2-C30 alkynylene group" refers to an unbranched hydrocarbon group having 2 to 30 carbon atoms including at least one carbon-carbon triple bond. The alkynylene group may be substituted.
    [0019] As used herein, the term "C2-C30 alkoxyalkylene group" refers to a structure in which two unbranched aliphatic hydrocarbon groups are connected by an oxygen atom (O). Examples of the alkoxyalkylene group include a methoxymethylene group, a methoxyethylene group, a methoxypropylene group, a methoxybutylene group, a methoxypentylene group, a methoxyhexylene group, an ethoxymethylene group, an ethoxyethylene group, an ethoxypropyenel group, an ethoxypentylene group, and an ethoxyhexylene group. The alkoxyalkylene group may be substituted.
    [0020] As used herein, the term " C1-C30 alkyl group" refers to a branched or unbranched aliphatic hydrocarbon group having 1 to 30 carbon atoms. The alkyl group may be substituted or unsubstituted. Examples of the alkyl group include a methyl group, an ethyl group, a propyl group, an isopropyl group, a butyl group, an isobutyl group, a tert-butyl group, a pentyl group, a hexyl group, a cyclopropyl group, a cyclopentyl group, a cyclohexyl group, and a cycloheptyl group. In another embodiment, each of these alkyl groups may be selectively substituted. In another embodiment, the alkyl group may include 1 to 6 carbon atoms. Examples of the alkyl group having 1 to 6 carbon atoms include a methyl group, an ethyl group, a propyl group, an iso-propyl group, a butyl group, an iso-butyl group, a sec-butyl group, a pentyl group, a 3-pentyl group, and a hexyl group.
    [0021] As used herein, the term "C2-C30 alkenyl group" refers to a hydrocarbon group having 2 to 30 carbon atoms including at least one carbon-carbon double bond, and examples thereof include an ethenyl group (or vinyl group), a 1-propenyl group, a 2-propenyl group, a 2-methyl-1-propenyl group, a 1-butenyl group, a 2-butenyl group, a cyclopropenyl group, a cyclopentenyl group, a cyclohexenyl group, and a cycloheptenyl group. In some embodiments, the alkenyl group may be substituted or unsubstituted.
    [0022] As used herein, the term "C2-C30 alkynyl group" refers to a hydrocarbon group having 2 to30 carbon atoms including at least one carbon-carbon triple bond, and examples thereof include an ethynyl group, a 1-propynyl group, a 2-propynyl group, a 1-butynyl group, and a 2-butynyl group. In some embodiments, the alkynyl group may be substituted.
    [0023] As used herein, the term "C2-C30 alkoxyalkyl group" refers to a structure in which two branched or unbranched aliphatic hydrocarbon groups are connected by an oxygen atom (O), wherein the group includes 2 to 30 carbon atoms. Examples of the alkoxyalkyl group include a methoxymethyl group, a methoxyethyl group, a methoxypropyl group, a methoxyisopropyl group, a methoxybutyl group, a methoxytert-butyl group, a methoxypentyl group, a methoxyhexyl group, a methoxycyclopentyl group, a methoxycyclohexyl group, a methoxycycloheptyl group, an ethoxymethyl group, an ethoxyethyl group, an ethoxypropyl group, an ethoxyisopropyl group, an ethoxytert-butyl group, an ethoxypentyl group, an ethoxyhexyl group, an ethoxycyclopropyl group, an ethoxycyclopentyl group, an ethoxycyclohexyl group, and an ethoxycycloheptyl group. In some embodiments, each of them may be selectively substituted.
    [0024] As used herein, the term "vinyl group" refers to a structure represented by "CH2=CH-*"(where, * is a bonding site with neighboring atoms).
    [0025] As used herein, a substituent is derived from an unsubstituted parent group. Here, at least one hydrogen atom is substituted with another atom or functional group. Unless otherwise expressed, when a functional group is described as "substituted", it means that the functional group is substituted with at least one substituent selected from a C1-C20 alkyl group, a C2-C20 alkenyl group, a C2-C20 alkynyl group, a C1-C20 alkoxy group, halogen, a cyano group, a hydroxy group, and a nitro group. When it is described herein that one functional group is "selectively substituted", the functional group may be substituted with any one of the aforementioned substituents.
    [0026] A lithium secondary battery according to the present disclosure includes a cathode, an anode, and an electrolyte interposed between the cathode and the anode.wherein the cathode includes a cathode active material represented by Formula 1 below, andthe electrolyte includes: a lithium salt; a non-aqueous solvent; and a compound represented by Formula 2:         Formula 1     LixNiyM1-yO2-zA,
    [0027] The compound represented by Formula 2 is added to the electrolyte to improve the lifetime characteristics and high-temperature stability of the lithium secondary battery.
    [0028] In Formula 2 above, L1 is selected from *-N(R5)-*', *-O-*', *-S-*',a substituted or unsubstituted C1-C30 alkyl group, a substituted or unsubstituted C2-C30 alkenyl group, a substituted or unsubstituted C2-C30 alkynyl group, and a substituted or unsubstituted C2-C30 alkoxyalkyl group.
    [0029] In an embodiment, in Formula 2 above, L1 may be selected from a methylene group, an ethylene group, a propylene group, a butylene group, a pentylene group, a hexylene group, and a heptylene group; anda methylene group, an ethylene group, a propylene group, a butylene group, a pentylene group, a hexylene group, and a heptylene group, each of which is substituted with at least one selected from a methyl group, an ethyl group, a propyl group, a vinyl group, -F, -CI, - Br, -I, a cyano group, a hydroxy group, and a nitro group.
    [0030] For example, in Formula 2 above, L1 may be selected from a methylene group and an ethylene group; and a methylene group and an ethylene group, each of which is substituted with at least one selected from a methyl group, an ethyl group, a propyl group, and vinyl group, but the present disclosure is not limited thereto.
    [0031] In Formula 2 above, a1 may be an integer of 0 to 3, and the L1s may be the same as or different from each other when a1 is 2 or more,
    [0032] For example, in Formula 2 above, a1 may be 1 or 2, but the present disclosure is not limited thereto.
    [0033] In an embodiment, in Formula above,a1 may be 1, and L1 may be an ethylene group; ora1 may be 2, and L1 may be a methylene group. However, the present disclosure is not limited thereto.
    [0034] In Formula 2 above, R1 to R5 are each independently selected from a substituted or unsubstituted C1-C30 alkyl group, a substituted or unsubstituted C2-C30 alkenyl group, and a substituted or unsubstituted vinyl group. However, at least one of R1 to R4 is selected from a substituted or unsubstituted C1-C30 alkyl group, a substituted or unsubstituted C2-C30 alkenyl group, and a substituted or unsubstituted vinyl group.
    [0035] According to an embodiment, in Formula 2 above, R1 to R4 may be each independently selected from a C1-C30 alkyl group; a vinyl group; and a C1-C30 alkyl group substituted with at least one selected from a methyl group, an ethyl group, a propyl group, a butyl group, - F, -CI, -Br, -I, a cyano group, a hydroxy group, and a nitro group.
    [0036] For example, in Formula 2 above, R1 to R4 may be each independently a C1-C30 alkyl group, but the present disclosure is not limited thereto.
    [0037] For example, in Formula 2 above, R1 to R4 may be each independently a methyl group.
    [0038] For example, in Formula 2 above, R5 may be hydrogen.
    [0039] In an embodiment, the compound represented by Formula 2 above may be Compound 1 below.
    [0040] The reason why the compound is added to an electrolyte to improve the performance of a lithium secondary battery will be described in more detail below.
    [0041] Because the compound represented by Formula 2 above includes an ORn (n=1 to 4) group having excellent electrical and chemical reactivity at both ends thereof, the decomposition of an organic solvent such as ethylene carbonate (EC) may be suppressed or reduced to thereby reduce the subsequent generation of gas, and thus, a resistance increase rate may be lowered.
    [0042] Further, if LiPF6 may be used as the lithium salt included in an electrolyte, it has to be reminded that LiPF6 has a limited thermal stability and may be easily hydrolyzed even by traces of water. However, when the additive including the compound represented by Formula 2 is added to an electrolyte, reaction products of the decomposition process may be captured by the -ORn groups, for example -OMe groups of the compound represented by Formula 2, thereby suppressing or reducing for example the hydrolysis reaction of LiPF6 by water. As a result, the generation of gas in the lithium secondary battery is suppressed or reduced to thereby improve cycle lifetime characteristics. Further, the swelling phenomenon of a battery may be prevented or reduced due to the suppression or reduction of gas generation.
    [0043] In addition, the -ORn groups located at the end of the compound represented by Formula 2 may form a stable thin film on the surface of a metal substrate through a complexing reaction with metal ions, for example, copper ions (Cu2+) eluted from the metal substrate. Due to the formation of such a thin film, the additional elution of metal from the metal substrate is suppressed or reduced, and thus, the overdischarging of a battery during the storage of the battery may be suppressed or reduced to thereby improve battery characteristics.
    [0044] During the initial charging of the lithium secondary battery, the decomposition reaction of an electrolyte occurs on the surface of an anode due to the reduction potential of the electrolyte being relatively higher than that of lithium. This decomposition reaction of an electrolyte may form a solid electrolyte interphase (SEI) on the surface of an electrode to suppress or reduce the movement of electrons required for a reaction between an anode and an electrolyte, thereby preventing or reducing the additional decomposition of the electrolyte. Thus, the performance of a battery may depend on the characteristics of a film formed on the surface of an anode. Considering this, it is required to form an SEI layer that is more rigid and has excellent electrical characteristics should be formed through the introduction of an electrolyte additive that is decomposed before the electrolyte during a charging reaction.
    [0045] The compound represented by Formula 2 according to an embodiment includes -ORn groups having excellent electrochemical reactivity at both ends thereof during a charging reaction, and thus, the compound represented by Formula 2 is decomposed before the decomposition of the organic solvent of the electrolyte, thereby forming an SEI film that is rigid and has excellent electrical characteristics on the surface of an anode.
    [0046] Further, because the -ORn group has excellent electrochemical reactivity, the -ORn groups may form a donor-acceptor bond with a transition metal oxide exposed to the surface of the cathode active material, and thus, a protective layer may be formed in the form of a composite.
    [0047] For example, the weight content of the compound represented by Formula 2 may be 0.05 wt% or more and less than 5 wt% based on the total weight of the electrolyte. The content (e.g., an amount or weight) thereof may be suitably or appropriately selected within the range that does not deteriorate (or does not substantially deteriorate) the characteristics of a battery. For example, the content of the compound represented by Formula 2 may be in a range of 0.1 wt% to 4 wt% based on the total weight of the electrolyte. For example, the content of the compound represented by Formula 2 may be in a range of 0.1 wt% to 3 wt% based on the total weight of the electrolyte. For example, the content of the compound represented by Formula 2 may be in a range of 0.1 wt% to 2 wt% based on the total weight of the electrolyte.
    [0048] When the content (e.g., an amount or weight) of the compound represented by Formula 2 exceeds the above content range, for example, exceeds 5 wt% based on the total weight of the electrolyte, the compound represented by Formula 2 acts as a resistance, so that battery lifetime may be deteriorated due to an increase of an interfacial resistance, and resistance may be increased. In contrast, when the content (e.g., an amount or weight) of the compound represented by Formula 2 is less than 0.05 wt%, high-temperature storage characteristics are deteriorated or reduced.
    [0049] In an embodiment, the lithium salt may include at least one selected from LiPF6, LiBF4, LiSbF6, LiAsF6, LiClO4, LiCF3SO3, Li(CF3SO2)2N, LiC4F9SO3, LiAlO2, LiAlCl4, LiN(CxF2x-1SO2)(CyF2y-1SO2) (0≤x≤20, 0≤y≤20), LiCI, Lil, lithium bis(oxalate) borate (LiBOB), and LiPO2F2. For example, the lithium salt may include lithium bis(fluorosulfonyl) imide (LiN(FSO2)2). Any suitable lithium salt generally used in the art may be used.
    [0050] The concentration of the lithium salt in the electrolyte may be in a range of 0.01 M to 5.0 M. Any suitable or appropriate concentration may be used as needed or desired. Within the above concentration range, further improved battery characteristics may be obtained. For example, the concentration of the lithium salt in the electrolyte may be 0.01 M to 4.0 M. For example, the concentration of the lithium salt in the electrolyte may be 0.01 M to 3.0 M. For example, the concentration of the lithium salt in the electrolyte may be 0.01 M to 2.0 M.
    [0051] According to an embodiment, the non-aqueous solvent may include at least one selected from ethyl methyl carbonate (EMC), methyl propyl carbonate, ethyl propyl carbonate, dimethyl carbonate (DMC), diethyl carbonate (DEC), dipropyl carbonate, propylene carbonate (PC), ethylene carbonate (EC), fluoroethylene carbonate (FEC), vinylene carbonate (VC), vinylethylene carbonate (VEC), butylene carbonate, ethyl propionate, ethyl butyrate, dimethyl sulfoxide, dimethyl formamide, dimethylacetamide, gamma-valerolactone, gamma-butyrolactone, and tetrahydrofuran.
    [0052] The electrolyte may be in a liquid or gel state. The electrolyte may be prepared by adding the lithium salt and the additive to the organic solvent.
    [0053] The form of the lithium battery is not limited, and includes a lithium secondary battery such as a lithium ion battery, a lithium ion polymer battery, and a lithium sulfur battery, as well as a lithium primary battery.
    [0054] The operating voltage of the lithium secondary battery may be 4.2 V or more, for example, 4.3 V or more, or, for example, 4.45 V or more.
    [0055] For example, the lithium secondary battery may be manufactured by the following method.
    [0056] First, a cathode is prepared.
    [0057] For example, a cathode active material composition in which a cathode active material, a conductive material, a binder, and a solvent are mixed is prepared. A cathode plate is prepared by coating a cathode current collector with the cathode active material composition. In some embodiments, the cathode plate may be prepared by casting the cathode active material composition onto a separate support, separating a film from the support and then laminating the separated film on a metal current collector. The cathode is not limited to the above-described form, but may have a form other than the above-described form.
    [0058] The cathode includes a cathode active material represented by Formula 1 above. For example, in Formula 1 above, A may be halogen or S.
    [0059] For example, in Formula 1 above, y represents a content (e.g., an amount or weight) of Ni in the cathode active material, and 0.6≤y≤0.98 may be satisfied. For example, in Formula 1 above, 0.6<y≤0.98 may be satisfied. For example, in Formula 1 above, 0.6<y≤0.88 may be satisfied. For example, in Formula 1 above, 0.7<y≤0.98 may be satisfied. For example, in Formula 1 above, 0.8<y≤0.9 may be satisfied. For example, in Formula 1 above, 0.8<y≤0.88 may be satisfied. When the content of Ni in the cathode active material is less than 60% or the cathode active material containing no Ni is included, because an increase in surface resistance is not large because surface reactivity at a voltage of 4.2 V or less is not high, the effect of the surface modification due to the compound represented by Formula 2 is insignificant (or not substantial), such that an improvement in performance may not observed, and high capacitance may not be exhibited.
    [0060] For example, in Formula 1 above, M may be at least one element selected from Al, Mn, and Co.
    [0061] For example, the cathode active material may be represented by Formula 3 or 4 below:         Formula 3     Lix'Niy'Co1-y'-zAlz'O2          Formula 4     Lix'Niy'CO1-y'-z'Mnz'O2 in Formulae 3 and 4, 0.9≤x'≤1.2, 0.6≤y'≤0.98, 0<z'≤0.2, and 0<1-y'-z'≤0.2 are satisfied. For example, the cathode active material may be LiNi0.6Co0.2Mn0.2O2, LiNi0.6Co0.2Al0.2O2, LiNi0.8Co0.1Mn0.1O2, LiNi0.8Co0.1Al0.1O2, LiNi0.88Co0.105Mn0.015O2, or LiNi0.88Co0.105Al0.015O2.
    [0062] In one or more embodiments, a compound having a coating layer on the surface of the compound may be used, or a mixture of the compound and a compound having a coating layer may be used. The coating layer may include a coating element compound of an oxide of the coating element, a hydroxide of a coating element, an oxyhydroxide of the coating element, an oxycarbonate of the coating element, or a hydroxycarbonate of the coating element. The compound constituting this coating layer may be amorphous or crystalline. As the coating element included in the coating layer, Mg, Al, Co, K, Na, Ca, Si, Ti, V, Sn, Ge, Ga, B, As, Zr, or a mixture thereof may be used. In the process of forming the coating layer, any suitable coating method generally used in the art as a method that does not adversely affect the properties (e.g., chemical and/or physical properties) of the cathode active material (for example, spray coating, dipping or the like) may be used. Such a coating method should be readily apparent to those skilled in the art upon review of the present disclosure, such that a detailed description thereof is not necessary here.
    [0063] The conductive material may be carbon black or graphite particles. Any suitable conductive material generally used in the art may be used.
    [0064] Examples of the binder may include, but are not limited to, a vinylidene fluoride / hexafluoropropylene copolymer, polyvinylidene fluoride (PVDF), polyacrylonitrile, polymethylmethacrylate, polytetrafluoroethylene and mixtures thereof, and a styrene butadiene rubber-based polymer. Any suitable binder generally used in the art may be used.
    [0065] As the solvent, N-methylpyrrolidone, acetone, water, or the like may be used. Any suitable solvent generally used in the art may be used.
    [0066] The content (e.g., an amount or weight) of the cathode active material, the content (e.g., an amount or weight) of the conductive material, the content (e.g., an amount or weight) of the binder, and the content (e.g., an amount or weight) of the solvent may be any suitable level generally used in the art in a lithium secondary battery. At least one of the conductive material, the binder, and the solvent may be omitted depending on the use and configuration of the lithium secondary battery.
    [0067] Next, an anode is prepared.
    [0068] For example, an anode active material composition in which an anode active material, a conductive material, a binder, and a solvent are mixed is prepared. An anode plate is prepared by directly coating an anode current collector with the anode active material composition and drying the anode active material composition. In some embodiments, the anode plate may be prepared by casting the anode active material composition onto a separate support, separating a film from the support and then laminating the separated film on a metal current collector.
    [0069] The anode active material may be used without limitation. Any suitable anode active material generally used in the art may be used. For example, the anode active material may include at least one selected from a lithium metal, a metal alloyable with lithium, a transition metal oxide, a non-transition metal oxide, and a carbon-based material.
    [0070] For example, the metal alloyable with lithium may be Si, Sn, Al, Ge, Pb, Bi, Sb, a Si-Y' alloy (Y' is an alkaline metal, an alkaline earth metal, a group 13 element, a group 14 element, a transition metal, or a combination thereof, and not Si), or a Sn-Y' alloy (Y' is an alkaline metal, an alkaline earth metal, a group 13 element, a group 14 element, a transition metal, or a combination thereof, and not Sn). The element Y' may be Mg, Ca, Sr, Ba, Ra, Sc, Y, Ti, Zr, Hf, Rf, V, Nb, Ta, Db, Cr, Mo, W, Sg, Tc, Re, Bh, Fe, Pb, Ru, Os, Hs, Rh, Ir, Pd, Pt, Cu, Ag, Au, Zn, Cd, B, Al, Ga, Sn, In, Ti, Ge, P, As, Sb, Bi, S, Se, or Te.
    [0071] For example, the transition metal oxide may be lithium titanium oxide, vanadium oxide, lithium vanadium oxide, or the like.
    [0072] For example, the non-transition metal oxide may be SnO2, SiOx (0<x<2), or the like.
    [0073] The carbon-based material may be crystalline carbon, amorphous carbon, or a mixture thereof. The crystalline carbon may be graphite such as natural graphite or artificial graphite having an amorphous, plate-like, flake-like, spherical or fibrous form. The amorphous carbon may be soft carbon (low-temperature fired carbon), hard carbon, mesophase pitch carbide, or fired coke.
    [0074] The conductive material, binder and solvent in the anode active material composition may be the same (e.g., substantially the same) as those in the cathode active material composition.
    [0075] The content (e.g., an amount or weight) of the anode active material, the content of the conductive material, the content (e.g., an amount or weight) of the binder, and the content (e.g., an amount or weight) of the solvent may be any suitable level generally used in the art in a lithium secondary battery. At least one of the conductive material, the binder, and the solvent may be omitted depending on the use and configuration of the lithium secondary battery.
    [0076] Next, a separator to be inserted between the anode and the cathode is prepared.
    [0077] As the separator, any suitable separator generally used in the art in a lithium battery may be used. A separator having low resistance to the movement of ions in the electrolyte and superior in electrolyte wettability may be used. For example, the separator may include any one selected from glass fiber, polyester, Teflon, polyethylene, polypropylene, polytetrafluoroethylene (PTFE), and combinations thereof, and may be made in the form of nonwoven fabric or woven fabric. For example, a windable separator including polyethylene, polypropylene, or the like may be used in a lithium ion battery, and a separator having good electrolyte impregnation ability may be used in a lithium ion polymer battery. For example, the separator may be produced by the following method.
    [0078] A polymer resin, a filler, and a solvent are mixed to prepare a separator composition. The separator composition is directly applied on an electrode and dried to form a separator. In some embodiments, the separator composition is cast on a support and dried, a separation film is separated from the support, and then the separation film is laminated on the electrode to form a separator.
    [0079] The polymer resin used in the production of the separator is not limited, and any suitable material generally used in the art for a binder of an electrode plate may be used in the production of the separator. For example, as the polymer resin, a vinylidene fluoride/hexafluoropropylene copolymer, polyvinylidene fluoride (PVDF), polyacrylonitrile, polymethyl methacrylate, or a mixture thereof may be used.
    [0080] Next, the above-described electrolyte for a lithium secondary battery is prepared.
    [0081] As shown in FIG. 1, the lithium secondary battery 1 includes a cathode 3, an anode 2, and a separator 4. The anode 2, the cathode 3, and the separator 4 are wound or folded and accommodated in a battery case 5. Then, an electrolyte is injected into the battery case 5, and the battery case 5 is sealed with a cap assembly 6 to complete the manufacture of the lithium secondary battery 1. The battery case 5 may have a cylindrical shape, a rectangular shape, or a thin film shape. For example, the lithium secondary battery 1 may be a large-sized thin-film battery. The lithium secondary battery 1 may be a lithium ion battery.
    [0082] The separator 4 may be located between the anode 2 and the cathode 3 to form a battery structure. The battery structure is laminated as a bi-cell structure and then impregnated with an electrolyte, and the resulting product is accommodated in a pouch and sealed to complete a lithium ion polymer battery.
    [0083] Further, the plurality of battery structures may be laminated to form a battery pack, and this battery pack may be used in any suitable appliances utilizing high capacity and high power. For example, the battery pack may be used in notebooks, smart phones, electric vehicles, and the like.
    [0084] Further, because the lithium secondary battery is excellent in lifetime characteristics and high rate characteristics, it may be used in electric vehicles (EV). For example, the lithium secondary battery may be used in hybrid vehicles such as plug-in hybrid electric vehicles. Further, the lithium secondary battery may be used in fields requiring a large amount of electric power storage. For example, the lithium secondary battery may be used in electric bicycles, electric tools, and the like.
    [0085] Hereinafter, embodiments of the present disclosure will be described in more detail with reference to Examples and Comparative Examples. Preparation of electrolytePreparation Example 1
    [0086] 1.15 M LiPF6 was added to a non-aqueous solvent in which ethylene carbonate (EC), ethyl methyl carbonate (EMC), and dimethyl carbonate (DMC) were mixed to a volume ratio of 2:1:7, to prepare a mixed solution.
    [0087] 0.1 wt% of Compound 1 above was added to the mixed solution based on the total weight of an electrolyte to prepare an electrolyte for a lithium secondary battery. Preparation Example 2
    [0088] An electrolyte for a lithium secondary battery was prepared in substantially the same manner as in Preparation Example 1, except that 0.25 wt% of Compound 1 was added. Preparation Example 3
    [0089] An electrolyte for a lithium secondary battery was prepared in substantially the same manner as in Preparation Example 1, except that 0.5 wt% of Compound 1 was added. Preparation Example 4
    [0090] An electrolyte for a lithium secondary battery was prepared in substantially the same manner as in Preparation Example 1, except that 1 wt% of Compound 1 was added. Preparation Example 5
    [0091] An electrolyte for a lithium secondary battery was prepared in substantially the same manner as in Preparation Example 1, except that 2 wt% of Compound 1 was added. Comparative Preparation Example 1
    [0092] An electrolyte for a lithium secondary battery was prepared in substantially the same manner as in Preparation Example 1, except that Compound 1 was not added. Comparative Preparation Example 2
    [0093] An electrolyte for a lithium secondary battery was prepared in substantially the same manner as in Preparation Example 1, except that 5 wt% of Compound 1 was added. Evaluation Example 1: Evaluation of CV characteristics
    [0094] In order to evaluate the electrochemical stability of the electrolytes according to Preparation Example 1 and Comparative Preparation Example 1, measurement thereof was performed by cyclic voltammetry (CV), and the results thereof are shown in FIGS. 2A and 2B.
    [0095] An anode CV measurement was performed by using a three electrode electrochemical cell in which a graphite anode is used as a working electrode and Li metal electrodes are used as a reference electrode and a counter electrode. In this case, scanning was performed from 3 V to 0 V and from 0 V to 3 V for 3 cycles, and scanning speed was 0.1 mV/sec.
    [0096] As shown in FIGS. 2A and 2B, in the cyclic voltage-current curve of the three electrode cell including the electrolyte according to Preparation Example 1, reduction peaks appeared in one cycle. In contrast, in the cyclic voltage-current curve of the three electrode cell including the electrolyte according to Comparative Preparation Example 1, reduction peaks did not appear. In view of these results, it is believed that, in the lithium secondary battery including the electrolyte prepared in Preparation Example 1, an initial SEI film is formed on the anode over a wide voltage range before solvent decomposition occurs during the charging process in which lithium ions are intercalated into the anode. Accordingly, it is believed that the lithium secondary battery employing the electrolyte according to Preparation Example 1 of the present disclosure has excellent battery performance as compared with the lithium secondary battery employing the electrolyte according to Comparative Preparation Example 1, in which the initial SEI film is not formed. Manufacture of lithium secondary batteryExample 1
    [0097] 98 wt% of artificial graphite (BSG-L, Tianjin BTR New Energy Technology Co., Ltd.), 1.0 wt% of styrene-butadiene rubber (SBR) binder (ZEON), and 1.0 wt% of carboxymethyl cellulose (CMC, manufactured by NIPPON A&L) were mixed, introduced into distilled water, and then stirred for 60 minutes using a mechanical stirrer to prepare an anode active material slurry. The slurry was applied onto a copper current collector having a thickness of 10 µm to a thickness of about 60 µm using a doctor blade, dried at 100 °C for 0.5 hours using a hot air dryer, further dried in vacuum at 120 °C for 4 hours, and then roll-pressed to prepare an anode plate. Preparation of cathode
    [0098] 97.45 wt% of LiNi0.88Co0.105Mn0.015O2, 0.5 wt% of artificial graphite (SFG6, Timcal) powder, 0.7 wt% of carbon black (Ketjenblack, ECP), 0.25 wt% of modified acrylonitrile rubber (BM-720H, manufactured by Zeon Corporation), 0.9 wt% of polyvinylidene fluoride (PVdF, S6020, Solvay), and 0.2 wt% of polyvinylidene fluoride (PVdF, S5130, Solvay) were mixed, introduced into an N-methyl-2-pyrrolidone solvent, and then stirred for 30 minutes using a mechanical stirrer to prepare a cathode active material slurry. The slurry was applied onto an aluminum current collector having a thickness of 20 µm to a thickness of about 60 µm using a doctor blade, dried at 100 °C for 0.5 hours using a hot air dryer, further dried in vacuum at 120 °C for 4 hours, and then roll-pressed to prepare a cathode plate.
    [0099] A lithium secondary battery was manufactured by using a polyethylene separator having a thickness of 14 µm and coated with ceramic on a side facing the anode and using the electrolyte prepared in Preparation Example 1. Example 2
    [0100] A lithium secondary battery was manufactured in substantially the same manner as in Example 1, except that the electrolyte prepared in Preparation Example 2 was used instead of the electrolyte prepared in Preparation Example 1. Example 3
    [0101] A lithium secondary battery was manufactured in substantially the same manner as in Example 1, except that the electrolyte prepared in Preparation Example 3 was used instead of the electrolyte prepared in Preparation Example 1. Example 4
    [0102] A lithium secondary battery was manufactured in substantially the same manner as in Example 1, except that the electrolyte prepared in Preparation Example 4 was used instead of the electrolyte prepared in Preparation Example 1. Example 5
    [0103] A lithium secondary battery was manufactured in substantially the same manner as in Example 1, except that the electrolyte prepared in Preparation Example 5 was used instead of the electrolyte prepared in Preparation Example 1. Comparative Example 1
    [0104] A lithium secondary battery was manufactured in substantially the same manner as in Example 1, except that the electrolyte prepared in Comparative Preparation Example 1 was used instead of the electrolyte prepared in Preparation Example 1. Comparative Example 2
    [0105] A lithium secondary battery was manufactured in substantially the same manner as in Example 1, except that the electrolyte prepared in Comparative Preparation Example 2 was used instead of the electrolyte prepared in Preparation Example 1. Comparative Example 3
    [0106] A lithium secondary battery was manufactured in substantially the same manner as in Example 1, except that, as the cathode active material, LiCoO2 was used instead of LiNi0.88Co0.105Mn0.015O2. Evaluation Example 2: Evaluation of cycle lifetime characteristics (25 °C)
    [0107] Processes of charging the lithium secondary batteries according to Examples 1 to 5 and Comparative Examples 1 and 2 at 25 °C under CC-CV 4A, 4.2 V, 100 mA cut-off and then discharging these secondary batteries at 25 °C under CC 10 A, 2.5 V cut-off was repeated for 1 cycle to 500 cycles to evaluate cycle lifetime characteristics, and the change in capacity up to 500 cycles is shown in FIG. 3.
    [0108] Referring to FIG. 3, it can be seen that the discharge cycle characteristics of the lithium secondary batteries of Examples 1 to 5 according to embodiments of the present disclosure is excellent as compared with those of the lithium secondary batteries of Comparative Examples 1 and 2, and that the lithium secondary battery including the compound represented by Formula 2 as an electrolyte additive exhibits excellent lifetime characteristics.
    [0109] Referring to the lithium secondary battery according to Comparative Example 2, it was found that, even when this lithium secondary battery includes the compound represented by Formula 2 as an additive, lifetime characteristics is rather deteriorated when the content (e.g., an amount or weight) of the additive is 5 wt% or more based on the total weight of the electrolyte. Evaluation Example 3: Evaluation of cycle lifetime characteristics (45 °C)
    [0110] Processes of charging the lithium secondary batteries according to Examples 1 to 5 and Comparative Examples 1 and 3 at 45 °C under CC-CV 4A, 4.2V, 100 mA cut-off and then discharging these secondary batteries at 25 °C under CC 10 A, 2.5 V cut-off was repeated for 1 cycle to 500 cycles to evaluate cycle lifetime characteristics, and the change in capacity up to 500 cycles is shown in FIG. 4 and Table 1. Table 1 Content of Compound 1 Number of cycles Cycle capacity retention rate (%) at 45 °C Example 3 0.5 wt% 500 74.2 Comparative Example 3 0.5 wt% 500 71.2
    [0111] Referring to FIG. 4 and Table 1, it may be found that the discharge cycle characteristics of the lithium secondary batteries of Examples 1 to 5 according to embodiments of the present disclosure is excellent as compared with those of the lithium secondary batteries of Comparative Examples 1 and 3, and that the lithium secondary battery including the compound represented by Formula 2 as an electrolyte additive exhibits excellent lifetime characteristics.
    [0112] Referring to the lithium secondary battery according to Comparative Example 3, it was found that, even when this lithium secondary battery includes the compound represented by Formula 2 as an additive, lifetime characteristics is rather deteriorated when the cathode active material is not a Ni-based active material satisfying Formula 1. Evaluation Example 4: Resistance test in high-temperature storage (at 60 °C for 30 days)
    [0113] The resistances (DCIR) of the lithium secondary batteries manufactured in Examples 1 to 5 and Comparative Examples 1 to 3 were measured at the first day at which they were stored high temperature (60 °C), and were measured after they were stored for 30 days. Then, resistance increase rates (%) were calculated. The results thereof are shown in Table 2 below and FIGS. 5 and 6. Table 2 Initial DCIR (mΩ) DCIR (mΩ) after 30 days DCIR increase rate (%) Example 1 19.18 26.12 136.2 Example 2 19.12 25.81 135.0 Example 3 19.02 24.88 130.8 Example 4 18.87 26.41 140.0 Example 5 19.34 26.57 137.3 Comparative Example 1 18.84 26.66 141.5 Comparative Example 2 18.69 28.51 152.6 Comparative Example 3 19.25 27.48 142.8
    [0114] As shown in Table 2 and FIGS. 5 and 6, it is found that the high-temperature resistance increase rate of each of the lithium secondary batteries of Examples 1 to 5 is lower than that of the lithium secondary battery of Comparative Example 1 not including Compound 1 even when they were stored at high temperature for a long period of time. It is considered that this is because the -OMe groups of Compound 1 effectively suppresse or reduce the side reaction of LiPF6.
    [0115] Further, it is found that, although the lithium secondary battery according to Comparative Example 2 includes the compound represented by Formula 2 as an additive, resistance characteristics are rather deteriorated when the content (e.g., an amount or weight) of the additive is 5 wt% or more based on the total weight of the electrolyte. Although the present disclosure is not limited by any particular mechanism or theory, it is believed that this is because the Compound 1 added in excess acts as a resistor.
    [0116] Further, it is found that, although the lithium secondary battery according to Comparative Example 3 includes the compound represented by Formula 2 as an additive, resistance characteristics are rather deteriorated when this lithium secondary battery includes a compound other than the compound represented by Formula 1 as the cathode active material. This shows that the resistance characteristic improving effect of the present disclosure is a remarkably improved effect according to the combination of the cathode active material represented by Formula 1 and the electrolyte additive represented by Formula 2. Evaluation Example 5: Measurement of high-temperature storage characteristics
    [0117] Each of the lithium secondary batteries manufactured according to Examples 1 to 5 and Comparative Examples 1 to 2 was left at 60 °C for 10 days, 20 days, or 30 days in a state of charge (SOC) of 100%, and the storage characteristics thereof at high temperature (60 °C) were evaluated. The results thereof are given in Table 3 below.
    [0118] In an initial formation condition, during a first cycle, each of the lithium secondary batteries was CC charged up to 3.6 V by a current of 0.2 C and then discharged up to 2.6 V. During a second cycle, each of the lithium secondary batteries was CC charged up to 4.2 V by a current of 0.2 C and then discharged up to 2.6 V. Thus, an oxide film was formed on the surface of an electrode.
    [0119] Initial capacities and capacities after 10 days, 20 days, and 30 days were measured after CC(constant current)-CV(constant voltage) charging each of the lithium secondary batteries up to 4.2 V by a current of 1 C and then discharging each of the lithium secondary batteries up to a cut off of 2.6 V by a current of 3 C.
    [0120] The capacity retention rate (%) is a percentage value of the retention capacity after 10 days, 20 days, and 30 days with respect to initial capacity.
    [0121] The capacity recovery rate (%) is a percentage value of the recovery capacity after 10, 20, or 30 days with respect to initial capacity. Table 3 After 10 days After 20 days After 30 days Capacity retention rate (%) Capacity recovery rate (%) Capacity retention rate (%) Capacity recovery rate (%) Capacity retention rate (%) Capacity recovery rate (%) Example 1 92 96 93 95 91 93 Example 2 92 97 92 94 91 93 Example 3 92 97 93 95 91 94 Example 4 93 98 94 96 92 93 Example 5 91 96 92 94 90 92 Comparative Example 1 91 96 92 94 92 92 Comparative Example 2 91 96 93 95 92 93
    [0122] Referring to Table 3, it is found that the lithium secondary batteries of Examples 1 and 2 are not particularly deteriorated in terms of capacity retention rate and capacity recovery rate as compared with the lithium secondary batteries of Comparative Examples 1 and 2.
    [0123] The content of nickel in the cathode active material may be increased to maximize the capacity of the lithium secondary battery, and the electrolyte then includes the alkoxy phosphine-based compound to improve the high-temperature stability and lifetime characteristics of the lithium secondary battery.
    权利要求:
    Claims (12)
    [0001] A lithium secondary battery (1), comprising:
    a cathode (2);
    an anode (3); and
    an electrolyte between the cathode (2) and the anode (3),
    wherein the cathode comprises a cathode active material represented by Formula 1, and
    the electrolyte includes a lithium salt, a non-aqueous solvent, and a compound represented by Formula 2:         Formula 1>     LixNiyM1-yO2-zAz wherein, in Formula 1,
    0.9≤x≤1.2, 0.6≤y≤0.98, and 0≤z<0.2 are satisfied,
    M is at least one element selected from Al, Mg, Mn, Co, Fe, Cr, V, Ti, Cu, B, Ca, Zn, Zr, Nb, Mo, Sr, Sb, W, and Bi, and
    A is an element having an oxidation number of -1 or -2; and
    [0002] The lithium secondary battery of claim 1, wherein,in Formula 2, L1 is selected from a methylene group, an ethylene group, a propylene group, a butylene group, a pentylene group, a hexylene group, and a heptylene group; anda methylene group, an ethylene group, a propylene group, a butylene group, a pentylene group, a hexylene group, and a heptylene group, each of which is substituted with at least one selected from a methyl group, an ethyl group, a propyl group, a vinyl group, -F, -CI, - Br, -I, a cyano group, a hydroxy group, and a nitro group.
    [0003] The lithium secondary battery of claim 1, wherein,in Formula 2, a1 is 1 or 2.
    [0004] The lithium secondary battery of claim 1, wherein,in Formula 2,
    i) a1 is 1, and L1 is an ethylene group; or
    ii) a1 is 2, and L1 is a methylene group.
    [0005] The lithium secondary battery of one of the preceding claims, wherein,in Formula 2, R1 to R4 are each independently selected from:a C1-C30 alkyl group; a vinyl group; and a C1-C30 alkyl group substituted with at least one selected from a methyl group, an ethyl group, a propyl group, a butyl group, -F, -CI, -Br, -I, a cyano group, a hydroxyl group, and a nitro group.
    [0006] The lithium secondary battery of claim 1, wherein,in Formula 2 above, R1 to R4 are each independently a C1-C30 alkyl group.
    [0007] The lithium secondary battery of claim 1, wherein,in Formula 2 above, R1 to R4 are each independently a methyl group.
    [0008] The lithium secondary battery of claim 1, wherein,the compound of Formula 2 is Compound 1 below:
    [0009] The lithium secondary battery of one of the preceding claims, whereina weight content of the compound represented by Formula 2 above is 0.05 wt% or more and less than 5 wt% based on a total weight of the electrolyte.
    [0010] The lithium secondary battery of claim 1, wherein,a weight content of the compound represented by Formula 2 above is 0.1 wt% to 4 wt% based on a total weight of the electrolyte.
    [0011] The lithium secondary battery of claim 1, wherein,in Formula 1 above, M is at least one element selected from Al, Mn, and Co.
    [0012] The lithium secondary battery of claim 1, wherein,the cathode active material is represented by Formula 3 or Formula 4:         Formula 3     Lix'Niy'Co1-y'-z'Alz'O2          Formula 4     Lix'Niy'CO1-y'-z'Mnz'O2 wherein in Formulae 3 and 4, 0.9≤x'≤1.2, 0.6≤y'≤0.98, 0<z'≤0.2, and 0<1-y'-z'≤0.2 are satisfied.
    类似技术:
    公开号 | 公开日 | 专利标题
    KR101905246B1|2018-10-05|Manufacturing method of lithium secondary battery
    KR102184372B1|2020-11-30|Composite cathode active material, preparation method thereof, and cathode and lithium battery containing the same
    US8546024B2|2013-10-01|Non-aqueous electrolyte lithium secondary battery
    EP2840640B1|2017-02-22|Lithium secondary battery
    EP2541663B1|2017-01-18|Nonaqueous electrolyte and lithium secondary battery using the same
    US5352548A|1994-10-04|Secondary battery
    JP5467189B2|2014-04-09|Non-aqueous electrolyte and electrochemical cell including the same
    CN107431197B|2020-08-21|Non-aqueous electrolyte and lithium secondary battery comprising same
    EP2109177B1|2017-06-28|Non-aqueous electrolyte and non-aqueous electrolyte secondary battery using the same
    US10320032B2|2019-06-11|Organic electrolytic solution and lithium battery using the same
    US8999575B2|2015-04-07|Positive electrode and lithium battery including the same
    KR101202863B1|2012-11-19|Negative electrode for battery and lithium ion battery using the same
    US9118062B2|2015-08-25|Anode and method of manufacturing the same, and battery and method of manufacturing the same
    US8999579B2|2015-04-07|Surface treated anode active material and method of making the same, anode including the same, and lithium battery including the same
    JP6380376B2|2018-08-29|Non-aqueous electrolyte secondary battery
    CN101496200B|2011-11-09|Cathode active material and lithium secondary battery containing them
    KR101212203B1|2012-12-13|Electrolyte for rechargeable lithium battery, and rechargeable lithium battery including the same
    JP6784927B2|2020-11-18|Electrolyte for non-aqueous electrolyte batteries, and non-aqueous electrolyte batteries using this
    US7851093B2|2010-12-14|Nonaqueous electrolyte for secondary battery and secondary battery including the same
    US9088036B2|2015-07-21|Rechargeable lithium battery
    JP6019058B2|2016-11-02|Nonaqueous electrolyte for lithium secondary battery and lithium secondary battery provided with the same
    EP2168199B1|2015-03-25|Non-aqueous electrolyte and electrochemical device comprising the same
    KR101223628B1|2013-01-17|Rechargeable lithium battery
    EP2827433A1|2015-01-21|Secondary battery electrolyte and secondary battery using same
    KR101754800B1|2017-07-06|Cathode, preparation method thereof, and lithium battery containing the same
    同族专利:
    公开号 | 公开日
    KR20200101043A|2020-08-27|
    CN111584934A|2020-08-25|
    US20200266490A1|2020-08-20|
    引用文献:
    公开号 | 申请日 | 公开日 | 申请人 | 专利标题
    法律状态:
    2020-07-24| PUAI| Public reference made under article 153(3) epc to a published international application that has entered the european phase|Free format text: ORIGINAL CODE: 0009012 |
    2020-07-24| STAA| Information on the status of an ep patent application or granted ep patent|Free format text: STATUS: REQUEST FOR EXAMINATION WAS MADE |
    2020-08-26| 17P| Request for examination filed|Effective date: 20200217 |
    2020-08-26| AK| Designated contracting states|Kind code of ref document: A1 Designated state(s): AL AT BE BG CH CY CZ DE DK EE ES FI FR GB GR HR HU IE IS IT LI LT LU LV MC MK MT NL NO PL PT RO RS SE SI SK SM TR |
    2020-08-26| AX| Request for extension of the european patent|Extension state: BA ME |