    • 专利摘要:
    A peening method which can sufficiently improve fatigue properties of a lap fillet welded joint having a thin steel sheet as a base sheet, in which a knocking pin has, on its tip, a curvature radius in a vertical cross section in a direction orthogonal to a welding direction of 0.05 mm to 0.50 mm and equal to or less than a curvature radius of a weld toe, the knocking pin is continuously knocked as a series of knocking toward a direction inclined relative to the welding direction, the series of knocking is repeatedly performed in the welding direction, at that time, a knocking mark group made of a plurality of knocking marks formed by the series of knocking is superimposed on at least a part of an adjacent knocking mark group while an end part in the direction orthogonal to the welding direction of the knocking mark group is separated from an end part in the direction orthogonal to the welding direction of the adjacent knocking mark group.
    公开号:EP3689531A1
    申请号:EP18862689.9
    申请日:2018-08-03
    公开日:2020-08-05
    发明作者:Naoki Yamaguchi；Tsuyoshi Shiozaki
    申请人:JFE Steel Corp；
    IPC主号:B23K31-00
    专利说明:
    [0001] This disclosure relates to a method of peening a lap fillet welded joint having a thin steel sheet as a base sheet and welded structures. In particular, this disclosure has an object of improving the fatigue properties of a lap fillet welded joint. BACKGROUND
    [0002] Generally, many suspension parts of automobiles are formed by joining various parts by lap fillet welded joints. Further, since the suspension parts of automobiles are subject to repeated loads during use, it is known that fatigue fracture easily occurs in the joint parts.
    [0003] Most of fracture modes of fatigue fracture occurring in a lap fillet welded joint is one caused by a crack developed in a direction parallel to a welding direction. This fracture mode is caused by stress in a direction orthogonal to the welding direction. Therefore, the fatigue properties of a lap fillet welded joint are of great significance for suspension parts of automobiles.
    [0004] Conventional techniques of improving the fatigue properties of a welded joint include a peening method, as illustrated in FIG. 1, comprising knocking a weld toe 4 using a knocking pin 5 to thereby deform the shape of the weld toe 4 and relax stress concentration caused by repeated bending, while applying compressive residual stress by plastic deformation.
    [0005] In FIG. 1, reference signs 1 and 2 each indicate a thin steel sheet, reference sign 3 indicates a weld metal, and reference sign 6 indicates a knocking pin tip.
    [0006] As such a peening method, for example, JP 3002229 B (PTL 1) proposes a "method of improving fatigue strength of a weld joint in a welded steel structure by hammer knocking an excess weld toe of the weld joint using a hammer knocking device, in which, knocking is repeated two or three times using a hammer chip with a tip radius of 1.0 mm to 2.8 mm under conditions of a knocking pressure of 3 kg/cm2 to 5 kg/cm2 and a hammer knocking angle of 30 degrees to 50 degrees, thereby applying to the surface of the excess weld toe a compressive residual stress equivalent to the yielding point of a base sheet".
    [0007] JP 2014-008507 A (PTL 2) proposes a "method comprising applying knocking power to a base end of a knocking pin by an air-driven part and peening a weld portion with a tip of the knocking pin, in which the curvature radius of the knocking pin tip is adjusted to 1.5 mm to 3.0 mm, and a knocking mark having a curvature radius of 1.5 mm to 3.0 mm and a depth of 0.5 mm or less in a cross section perpendicular to a welding direction is formed at least in a weld toe".
    [0008] However, in the techniques of PTL 1 and PTL 2, knocking is performed by merely moving a knocking pin (hammer) along a weld toe toward a welding direction, and thus, a fold mark 7 at the weld toe is formed by plastic flow as illustrated in FIG. 2 and a fatigue fracture occurs originating from the fold mark 7 at the weld toe, and as a result, the fatigue properties are not sufficiently improved.
    [0009] In FIG. 2, reference sign 8 indicates a fold mark at a knocking mark edge.
    [0010] JP 4837428 B (PTL 3) proposes a "method of subjecting a weld toe to ultrasonic impact processing, comprising imparting ultrasonic vibration to a pin provided at a tip part and imparting ultrasonic impact to a weld toe using the pin, in which the curvature radius of the tip part of the pin is 1.0 mm or more and 2.0 mm or less, and a recessed shape with a curvature radius of 1.5 mm or more and less than 2.5 mm is formed in a cross section perpendicular to a welding direction of the weld toe".
    [0011] Further, JP 2013-071140 A (PTL 4) proposes a "welded joint having excellent fatigue resistance comprising a weld toe subjected to peening, in which, the radius ρ (mm) and the flank angle θ (°) of the weld toe before the peening and the curvature radius r (mm) of a tip part of a vibration terminal used in the peening satisfy the following formulas (1) and (2) and a fold mark is not formed at the weld toe after the peening by plastic processing during peening ρ / θ ≥ r / 100
    [0012] In addition, JP 4392337 B (PTL 5) proposes a "processing method using a ultrasonic impact device for subjecting a material surface to ultrasonic impact processing to improve residual stress, the ultrasonic impact device having a plurality of pins for giving ultrasonic impact to the material surface, the pins being arranged in a line, the method comprising subjecting the material surface to ultrasonic impact processing by scanning the pins in a direction inclined relative to the arrangement direction of the pins, in which an angle formed by the arrangement direction of the pins and the scanning direction of the pins is an angle at which an edge generated by swelling on the material surface as a result of impacting a single pin is overlapped with an edge generated by swelling on the material surface as a result of impacting an adjacent pin, the plurality of pins are scanned on the material surface in a direction orthogonal to the direction in which attempts are made to improve the residual stress to thereby form a plurality of processed bands by ultrasonic impact processing, and the processed bands have three or more edges at least in a direction orthogonal to the processed bands". CITATION LISTPatent Literatures
    [0013] PTL 1: JP 3002229 B PTL 2: JP 2014-008507 A PTL 3: JP 4837428 B PTL 4: JP 2013-071140 A PTL 5: JP 4392337 BNon-Patent Literatures
    [0014] NPL 1: Improvement of Fatigue Properties by FPB Treatment, Journal of the Japan Society for Precision Engineering, Vol. 72, No. 9 (2006), pp. 1071-1074 NPL 2: Effect of External Geometry of Reinforcement on the Fatigue Strength of a Welded Joint, Journal of the Japan Welding Society, Vol. 40 (1971), No. 8, pp. 723-735 SUMMARY(Technical Problem)
    [0015] However, when the method of PTL 3 is applied to a lap fillet welded joint having, as a base sheet, a steel sheet with a small thickness, in particular, a thin steel sheet having a thickness of 3.5 mm or less, a fold mark at a weld toe is formed and thus fatigue properties cannot be sufficiently improved.
    [0016] Further, in the method of PTL 4, the curvature radius of a tip of a vibration terminal (knocking pin) and the radius and the flank angle of a weld toe before peening are adjusted based on the predetermined relational expression. Based on the relational expression, for example, when the curvature radius of the weld toe before peening is 0.3 mm, the flank angle of the weld toe needs to be 15° or less. Further, the flank angle of the weld toe is typically about 60°, and thus the method of PTL 4 cannot be applied to most welded joints in actual construction.
    [0017] Moreover, when the curvature radius of a tip of a knocking pin is increased as in PTL 3 and PTL 4, a higher driving force is required to apply pressure necessary for producing plastic deformation, and thus, when a base sheet is a high-strength steel sheet, an expensive and large device such as air-driven type and ultrasonic type needs to be used. On the other hand, when the stiffness of a base sheet is low, the base sheet would be deformed.
    [0018] In addition, the method of PTL 5 can neither sufficiently suppress crack development caused by stress in a direction orthogonal to a welding direction, nor produce a sufficient effect of improving fatigue properties of a lap fillet welded joint.
    [0019] Although NPL 1 proposes a surface modification treatment method (fine-particle bombardment processing method (FPB treatment method)) comprising subjecting the material to plastic deformation by bombarding fine particles with a diameter of 50 µm to 100 µm to a material to be treated, the method requires a large device and a splattering preventing device for the fine particles, and it is difficult in the method to apply local processing to a complicated structure such as a weld toe of a fillet welded joint.
    [0020] It could thus be helpful to provide a peening method which can sufficiently improve fatigue properties of a lap fillet welded joint having a thin steel sheet as a base sheet by this disclosure.
    [0021] It could also be helpful to provide a welded structure obtained by the peening method. (Solution to Problem)
    [0022] It has been conventionally believed that when a weld toe has a curvature radius of 1.0 mm or less, stress concentration cannot be sufficiently relaxed and thus, to sufficiently obtain an effect of relieving stress concentration, it is necessary to increase, to some degree, the curvature radius in a vertical cross section in a direction orthogonal to a welding direction of a tip of a knocking pin (hereinafter, also referred to as "curvature radius of a knocking pin tip").
    [0023] The inventors made intensive studies to solve the above problems and discovered the following.(1) At a weld toe, stress remains due to cooling after the welding and fine asperities (hereinafter, also referred to as "weld ripples") 9 having a diameter of 0.05 mm or less as illustrated in FIG. 3 occur, and the stress and fine asperities are factors that deteriorate the fatigue properties, in particular, in a welded joint having a high-strength steel sheet having a tensile strength of 780 MPa or more as a base sheet. (2) In this regard, when peening is performed to apply compressive stress to a weld toe through plastic deformation and make weld ripples collapsed to be flattened, stress concentration is relaxed even with a reduced curvature radius of a knocking pin tip. (3) In particular, when the curvature radius of a knocking pin tip is made smaller than that of a weld toe, it is possible to effectively prevent the occurrence of the fold mark 7 at the weld toe illustrated in FIG. 2.
    [0024] However, it was not possible to obtain a sufficient fatigue property improving effect by merely making the curvature radius of a knocking pin tip smaller than that of a weld toe.
    [0025] The inventors thus made further studies and discovered the following. (4) The fold mark 8 at a knocking mark edge illustrated in FIG. 2 may provide the origin of fatigue fracture. In particular, as illustrated in FIG. 4, when a lap fillet welded joint is continuously knocked along a weld toe in a welding direction, fold marks 8 at knocking mark edges are continuously connected in a direction orthogonal to a stress loading direction, that is, the welding direction, and as a result, the stress intensity factor is increased to promote development of a crack, deteriorating fatigue properties (in FIG. 4, reference sign 10 indicates a knocking mark and reference sign 11 indicates a weld bead). (5) To prevent the deterioration of fatigue properties, it is effective to prevent fold marks 8 at knocking mark edges from being continuously connected in the welding direction. (6) Specifically, the following process (a) or (b) is effective. (a) A knocking pin is continuously knocked as a series of knocking toward a direction inclined relative to a welding direction across a weld toe and the series of knocking is repeatedly performed in the welding direction. At that time, knocking mark groups 12, each being made of a plurality of knocking marks 10 as illustrated in FIG. 5, are formed by superimposing a knocking mark group made of a plurality of knocking marks formed by the series of knocking on at least a part of an adjacent knocking mark group while separating an end part of the knocking mark group in a direction orthogonal to the welding direction from an end part of the adjacent knocking mark group in a direction orthogonal to the welding direction. (b) A knocking pin is knocked while the knocking pin is oscillated with a fixed width to a direction orthogonal to a welding direction across a weld toe and moved in the welding direction to thereby form a knocking region 13 having a plurality of knocking marks 10 as illustrated in FIG. 6. In the knocking region 13, end parts of knocking marks 10 that are located in an end part along a width direction of the knocking region 13 and superimposed on each other are separated from each other in the direction orthogonal to the welding direction, or, end parts of knocking marks 10 that are located at the widthwise edge of the knocking region 13 are connected to one another in the welding direction at three knock points or less. (7) The fatigue properties of a lap fillet welded joint having a thin steel sheet as a base sheet can be significantly improved by any of the processes (a) and (b) stated above without deformation such as curl of the base sheet.
    [0026] Further, the inventors made intensive studies and found that when the knocking pin 5 having a tip with a relatively small radius as in this disclosure is used, the contact area between the weld toe 4 as a knocked part and a knocking pin tip 6 is decreased, and as a result, the knocking load of the knocking pin 5 may be small for ensuring proper knocking pressure.
    [0027] On the other hand, however, the inventors discovered that as illustrated in FIG. 8, when a knocking tool 17 having the knocking pin 5 on its tip is fixed with a knocking tool holder 18 and pressed against the weld toe 4, if the pressing load surpasses the knocking load of the knocking pin 5, the knocking pin tip 6 and the weld toe 4 are brought into close contact with each other, and the knocking effect cannot be obtained.
    [0028] Then, the inventors made intensive studies to solve the problem, and as a result, found that when the knocking tool 17 is fixed with the knocking tool holder 18, the knocking tool 17 is clamped with a viscoelastic material 20 as illustrated in FIG. 9 to thereby cause inconsistence between the vibration of the knocking tool holder 18 and that of the knocking pin 5, and then the weld toe 4 and the knocking pin tip 6 are not brought into close contact with each other even if the pressing load is high, and a sufficient knocking effect can be obtained.
    [0029] This disclosure is based on the aforementioned discoveries and further studies.
    [0030] Specifically, we provide the following. 1. A method of peening a lap fillet welded joint, comprising knocking a weld toe of the lap fillet welded joint using a knocking pin attached to a tip of a knocking tool, whereinthe knocking pin has, on its tip, a curvature radius in a vertical cross section in a direction orthogonal to a welding direction of 0.05 mm to 0.50 mm and equal to or less than a curvature radius of the weld toe,the knocking pin is continuously knocked as a series of knocking toward a direction inclined relative to the welding direction across the weld toe,the series of knocking is repeatedly performed in the welding direction,at that time, a knocking mark group made of a plurality of knocking marks formed by the series of knocking is superimposed on at least a part of an adjacent knocking mark group while an end part in the direction orthogonal to the welding direction of the knocking mark group is separated from an end part in the direction orthogonal to the welding direction of the adjacent knocking mark group. 2. The method of peening a lap fillet welded joint according to 1., wherein the series of knocking is performed at an inclination angle relative to the welding direction of 30° to 45°. 3. The peening method according to 1. or 2., wherein the knocking tool is clamped with a viscoelastic material on a holder of the knocking tool. 4. A welded structure having a lap fillet welded joint,comprising a plurality of knocking mark groups in which a plurality knocking marks run at an angle relative to a welding direction across a weld toe of the lap fillet welded joint, whereinthe knocking marks have a curvature radius in a cross section perpendicular to the weld line direction of 0.05 mm to 0.50 mm, andeach knocking mark group is superimposed on at least a part of an adjacent knocking mark group while an end part in a direction orthogonal to a welding direction of the knocking mark group is separated from an end part in the direction orthogonal to the welding direction of the adjacent knocking mark group. 5. The welded structure according to 4., wherein each knocking mark group has the knocking marks running at a slanting angle of 30° to 45° with respect to the welding direction. 6. The welded structure according to 4. or 5., wherein the lap fillet welded joint has a base sheet with a tensile strength of 780 MPa or more. 7. A method of peening a lap fillet welded joint, comprising knocking a weld toe of the lap fillet welded joint using a knocking pin attached to a tip of a knocking tool, whereinthe knocking pin has, on its tip, a curvature radius in a vertical cross section in a direction orthogonal to a welding direction of 0.05 mm to 0.50 mm and equal to or less than a curvature radius of the weld toe,the knocking pin is knocked while the knocking pin is oscillated in the direction orthogonal to the welding direction across the weld toe and moved in the welding direction,the knocking pin has an oscillation width around the weld toe at least twice a width of a knocking mark per knock point, and in a knocking region determined according to the oscillation width of the knocking pin, end parts of knocking marks located in an end part along a width direction of the knocking region and superimposed on each other are separated from each other in the direction orthogonal to the welding direction, or, end parts of knocking marks located in an end part along the width direction of the knocking region are contacted with each other at three knock points or less in the direction orthogonal to the welding direction. 8. The peening method according to 7., wherein the knocking tool is clamped with a viscoelastic material on a holder of the knocking tool. 9. A welded structure having a lap fillet welded joint,comprising a knocking region having a plurality of knocking marks running across a weld toe of the lap fillet welded joint, whereinin the knocking region,the knocking marks have a total length on the weld toe of 50 % or more of the whole length of the weld toe, andthe knocking region has a width at least twice a width of a knocking mark per knock point,and further, in the knocking region, end parts knocking marks located in an end part along a width direction of the knocking region and superimposed on each other are separated from each other in a direction orthogonal to a welding direction, or, end parts of knocking marks located in an end part along the width direction of the knocking region are contacted with each other at three knock points or less in the direction orthogonal to the welding direction. 10. The welded structure according to 9., wherein the lap fillet welded joint has a base sheet with a tensile strength of 780 MPa or more. (Advantageous Effect)
    [0031] According to this disclosure, it is possible to significantly improve fatigue properties of a lap fillet welded joint having a thin steel sheet as a base material.
    [0032] Further, since a smaller tool can be used as compared with air-driven type and ultrasonic type tools, peening is available at a position where peening could not be performed due to posture and weight constraints imposed by a large tool, and workability and productivity are also improved. Moreover, as to a welded structure having low stiffness which could not be subjected to peening due to the possibility of deformation, fatigue properties can be significantly improved without deformation such as curl of a base sheet. In addition, pre-treatment using a grinder or the like proposed in claim 2 of PTL 4 is not required, which fact also improves workability and productivity.
    [0033] Further, when the welded structure of this disclosure is applied to, for example, automotive parts, high-strength steel sheets are applicable to automotive parts requiring excellent fatigue properties, and through this point it becomes possible to improve the fuel consumption of automobiles. BRIEF DESCRIPTION OF THE DRAWINGS
    [0034] In the accompanying drawings:FIG.1 is a schematic diagram illustrating one typical example of peening; FIG. 2 is a schematic diagram illustrating one example of a fold mark formed during peening; FIG. 3 is a micro-image illustrating one example of a weld toe of a lap fillet welded joint; FIG. 4 is a schematic diagram illustrating a knocking mark formed by a conventional peening method and a stress loading direction of a representative fatigue fracture mode; FIG. 5 is a schematic diagram illustrating a knocking mark (knocking mark group) formed by a peening method according to one of the disclosed embodiments and a stress loading direction of a representative fatigue fracture mode; FIG. 6 is a schematic diagram illustrating a knocking mark (knocking region) formed by a peening method according to another embodiment and a stress loading direction of a representative fatigue fracture mode; FIG. 7 is a diagram illustrating a shape of a test piece; FIG. 8 is a schematic diagram illustrating a holding manner of a knocking tool in a knocking tool holder; and FIG. 9 is a sectional view taken along line A-A of FIG. 8. DETAILED DESCRIPTION
    [0035] The present disclosure is described in detail below based on embodiments. [First embodiment]
    [0036] A method of peening a lap fillet welded joint according to a first embodiment, comprises knocking a weld toe 4 of the lap fillet welded joint using a knocking pin 5 attached to a tip of a knocking tool, wherein the knocking pin 5 has, on its tip, a curvature radius in a vertical cross section in a direction orthogonal to a welding direction of 0.05 mm to 0.50 mm and equal to or less than a curvature radius of the weld toe 4, the knocking pin 5 is continuously knocked as a series of knocking toward a direction inclined relative to the welding direction across the weld toe 4, the series of knocking is repeatedly performed in the welding direction, and at that time, a knocking mark group 12 made of a plurality of knocking marks 10 formed by the series of knocking is superimposed on at least a part of an adjacent knocking mark group 12 while an end part in a direction orthogonal to the welding direction of the knocking mark group 12 is separated from an end part of the adjacent knocking mark group 12 in a direction orthogonal to the welding direction.
    [0037] The method of peening a lap fillet welded joint according to the first embodiment is described below.
    [0038] A curvature radius of the knocking pin tip 6 being 0.05 mm to 0.50 mm and equal to or less than a curvature radius of the weld toe 4
    [0039] As stated above, when weld ripples 9 formed on the weld toe 4 during welding are collapsed to be flattened, stress concentration is relaxed even if the curvature radius of the knocking pin tip 6 is decreased, and a fold mark 7 at the weld toe can be effectively prevented from occurring. Therefore, the curvature radius of the knocking pin tip 6 is set to 0.50 mm or less and equal to or less than the curvature radius of the weld toe 4 of the welded joint before peening. Further, from the viewpoint of effectively collapsing the weld ripples 9, the curvature radius of the knocking pin tip 6 needs to be set to 0.05 mm or more.
    [0040] For example, in the case of a lap fillet welded joint having a thin steel sheet with a thickness of 3.6 mm or less as a base sheet, the curvature radius of the weld toe 4 is typically about 0.50 mm to 1.0 mm, and thus the knocking pin tip 6 having a curvature radius of 0.05 mm to 0.50 mm is used.
    [0041] Further, in the method of peening a lap fillet welded joint according to the first embodiment, it is important that the knocking pin 5 is continuously knocked as a series of knocking toward a direction inclined relative to the welding direction across the weld toe 4, the series of knocking is repeatedly performed in the welding direction, and at that time, a knocking mark group 12 made of a plurality of knocking marks 10 formed by the series of knocking is superimposed on at least a part of an adjacent knocking mark group 12 while an end part in a direction orthogonal to the welding direction of the knocking mark group 12 is separated from an end part of the adjacent knocking mark group 12 in a direction orthogonal to the welding direction.
    [0042] As used herein, the knocking mark group 12 refers to a series of knocking marks 10 running at a predetermined inclination angle relative to the welding direction as illustrated in FIG. 5.
    [0043] Further, the end part of the knocking mark group 12 in a direction orthogonal to the welding direction refers to a region ranging from the end of the knocking mark group 12 in a direction orthogonal to the welding direction to 1 % of the width of the knocking mark group 12.
    [0044] Specifically, as stated above, a fold mark 8 at a knocking mark edge illustrated in FIG. 2 may provide the origin of fatigue fracture. In particular, as illustrated in FIG. 4, when the lap fillet welded joint is continuously knocked along the weld toe 4 in the welding direction, fold marks 8 at knocking mark edges are continuously connected in a direction orthogonal to a stress loading direction, that is, the welding direction, and as a result, the stress intensity factor is increased to promote development of a crack, deteriorating fatigue properties. To prevent the deterioration of fatigue properties, it is effective to prevent fold marks 8 at knocking mark edges from being continuously connected in the welding direction.
    [0045] Therefore, in the method of peening the first embodiment, the knocking pin 5 is continuously knocked as a series of knocking toward a direction inclined relative to the welding direction across the weld toe 4 (in other words, knocking is performed so that the knocking marks 10 are superimposed with each other and have a center line inclined relative to the welding direction) and the series of knocking is repeatedly performed in the welding direction. At that time, knocking mark groups 12 made of a plurality of knocking marks 10 as illustrated in FIG. 5 are formed by superimposing a knocking mark group 12 made of a plurality of knocking marks 10 formed by the series of knocking on at least a part of an adjacent knocking mark group 12 while separating an end part of the knocking mark group 12 in a direction orthogonal to the welding direction from an end part of the adjacent knocking mark group 12 in a direction orthogonal to the welding direction.
    [0046] When the series of knocking is performed, it is preferable to set an inclination angle relative to the welding direction θ (hereinafter, also referred to as "scanning angle") to 30° to 45°.
    [0047] When the scanning angle is set to 30° or more, since the fold mark 8 at the knocking mark edge can be particularly advantageously prevented from being continuously connected in the welding direction, the effect of improving fatigue properties is increased. On the other hand, a scanning angle of more than 45° leads to deterioration in workability.
    [0048] Further, no limitation is placed on the scanning distance of the series of knocking in a direction orthogonal to the welding direction (hereinafter, also referred to as "scanning width") as long as the knocking mark group 12 is formed across the weld toe 4, yet the scanning width is preferably set to 1.0 mm or more. The upper limit of the scanning width is not particularly limited, yet it is preferably set to about 3.0 mm from the viewpoint of work efficiency.
    [0049] Further, the series of knocking is preferably applied to a region up to at least about 0.5 mm on each of the weld metal side and the base sheet side around the weld toe 4 in a direction orthogonal to the welding direction, and particularly preferably applied around the weld toe 4.
    [0050] Further, the distance between the centers of knocking mark groups 12 adjacent to each other on the weld toe 4 is preferably 0.70 to 0.99 times the length of a knocking mark 10 formed per knock in the welding direction. Therefore, a knocking mark group 12 made of a plurality of knocking marks 10 formed by the series of knocking can be superimposed more advantageously on at least a part of an adjacent knocking mark group 12 while an end part of the knocking mark group 12 in a direction orthogonal to the welding direction can be separated from an end part of the adjacent knocking mark group 12 in a direction orthogonal to the welding direction.
    [0051] Further, other than the above peening conditions are not particularly limited, yet it is sufficient to follow the conventional methods. For example, in the series of knocking, the knocking frequency may be 50 Hz to 300 Hz and the scanning rate may be 3 mm/s to 30 mm/s. Moreover, the knocking angle of the knocking pin 5 (an angle formed on a plane perpendicular to the welding direction by the centerline of the knocking pin 5 and a straight line perpendicular to the base sheet (thin steel sheet) surface of the weld toe 4 of the lap fillet welded joint) may be preferably 30° to 60°.
    [0052] As stated above, by knocking the weld toe 4 of the lap fillet welded joint, a welded structure having the lap fillet welded joint according to the first embodiment as illustrated in FIG. 5 can be obtained, the welded structure comprising a plurality of knocking mark groups 12 in which a plurality of knocking marks 10 run at an angle relative to the welding direction across the weld toe 4 of the lap fillet welded joint, wherein the knocking marks 10 have a curvature radius in a cross section perpendicular to the weld line direction of 0.05 mm to 0.50 mm, and each knocking mark group 12 is superimposed on at least a part of an adjacent knocking mark group 12 while an end part in a direction orthogonal to a welding direction the knocking mark group 12 is separated from an end part of the adjacent knocking mark group 12 in the direction orthogonal to the welding direction.
    [0053] Note that θ, which denotes the inclination angle relative to the welding direction of the knocking mark group 12 (i.e., the angle formed by the running direction of the knocking marks 10 of the knocking mark group 12 and the welding direction), is the same as the scanning angle, and L1, which denotes the width of the knocking mark group 12 (width in a direction orthogonal to the welding direction), is the same as the scanning width. θ is preferably in a range of 30° to 45° and L1 is preferably in a range of 1.0 mm to 3.0 mm. [Second embodiment]
    [0054] The method of peening a lap fillet welded joint according to a second embodiment, comprising knocking a weld toe 4 of the lap fillet welded joint using a knocking pin 5 attached to a tip of a knocking tool, wherein the knocking pin 5 has, on its tip, a curvature radius in a vertical cross section in a direction orthogonal to a welding direction of 0.05 mm to 0.50 mm and equal to or less than a curvature radius of the weld toe 4, the knocking pin 5 is knocked while the knocking pin 5 is oscillated in a direction orthogonal to the welding direction across the weld toe 4 and moved in the welding direction, the knocking pin 5 has an oscillation width around the weld toe at least twice a width of the knocking mark 10 per knock point, and in a knocking region 13 defined according to the oscillation width of the knocking pin 5, end parts of knocking marks 10 located in an end part along a width direction of the knocking region 13 and superimposed on each other are separated from each other in a direction orthogonal to the welding direction, or, end parts of knocking marks 10 located in an end part along the width direction of the knocking region 13 are contacted with each other at three knock points or less in the direction orthogonal to the welding direction.
    [0055] The method of peening a lap fillet welded joint according to the second embodiment is described below.
    [0056] A curvature radius of a knocking pin tip 6 being 0.05 mm to 0.50 mm and equal to or less than a curvature radius of a weld toe 4
    [0057] As stated above, when weld ripples 9 formed at the weld toe 4 during welding are collapsed to be flattened, stress concentration is relaxed even if the curvature radius of the knocking pin tip 6 is decreased and a fold mark 7 at the weld toe can be effectively prevented from occurring. Therefore, the curvature radius of the knocking pin tip 6 is set to 0.50 mm or less and equal to or less than the curvature radius of the weld toe 4 of the welded joint before peening. Further, from the viewpoint of effectively collapsing the weld ripples 9, the curvature radius of the knocking pin tip 6 needs to be set to 0.05 mm or more.
    [0058] For example, in the case of a lap fillet welded joint having a thin steel sheet with a thickness of 3.6 mm or less as a base sheet, the curvature radius of the weld toe 4 is typically about 0.50 mm to 1.0 mm, and thus the knocking pin tip 6 having a curvature radius of 0.05 mm to 0.50 mm is used.
    [0059] Further, in the method of peening a lap fillet welded joint according to the second embodiment, the knocking pin 5 is knocked while the knocking pin 5 is oscillated in a direction orthogonal to the welding direction across the weld toe 4 and moved in the welding direction. At that time, the oscillation width of the knocking pin 5 is set to be at least twice the width of the knocking mark 10 per knock point, that is, the width (in a direction orthogonal to the welding direction) of one knocking mark.
    [0060] Specifically, as stated above, the fold mark 8 at the knocking mark edge illustrated in FIG. 2 may provide the origin of fatigue fracture. In particular, as illustrated in FIG. 4, when the lap fillet welded joint is continuously knocked along the weld toe 4, the fold mark 8 at the knocking mark edge are continuously connected in a direction orthogonal to a stress loading direction, that is, the welding direction, and as a result, the stress intensity factor is increased to promote development of a crack, deteriorating fatigue properties.
    [0061] Therefore, in the method of peening a lap fillet welded joint according to the second embodiment, the knocking pin 5 is knocked while the knocking pin 5 is oscillated in a direction orthogonal to the welding direction across the weld toe 4 (in other words, the knocking pin 5 is oscillated so that the knocking pin 5 crosses the weld toe 4 at least a predetermined number of times and the knocking marks 10 formed by the knocking are superimposed on one another) and moved in the welding direction. At that time, as illustrated in FIG. 6, by setting the oscillation width of the knocking pin 5 (in a direction orthogonal to the welding direction) to be at least twice, and preferably 2.5 times or more of a width of one knocking mark 10, L0, the knocking region 13 having a plurality of knocking marks 10 is formed and end parts in a direction orthogonal to the welding direction of knocking marks 10 located in an end part along a width direction of the knocking region 13 and superimposed on each other are separated from each other, or, end parts in a direction orthogonal to the welding direction of knocking marks 10 located in an end part along the width direction of the knocking region 13 are contacted with each other at three knock points or less.
    [0062] As used herein, the end part in a direction orthogonal to the welding direction of the knocking mark 10 refers to a region ranging from the end in a direction orthogonal to the welding direction of the knocking mark 10 on an end part along a width direction of the knocking region 13 to 1 % of the width of the knocking mark 10.
    [0063] Therefore, it becomes possible to prevent the fold mark 8 at the knocking mark edge from continuously running in the welding direction to improve fatigue properties.
    [0064] The upper limit of the oscillation width is not particularly limited, but it is preferably set to 3.0 mm from the viewpoint of work efficiency.
    [0065] Further, the oscillation range preferably includes a region at least including the weld toe 4 in the center and extending by about 0.5 mm to both the weld metal side and the base sheet side in a direction orthogonal to the welding direction, and particularly preferably includes the weld toe 4 in the center.
    [0066] Moreover, preferably, the knocking frequency is set to 50 Hz to 300 Hz, the oscillation frequency is set to 1 Hz to 20 Hz, and the scanning rate is set to 0.1 mm/s to 20 mm/s.
    [0067] Other than the above peening conditions are not particularly limited, yet it is sufficient to follow the conventional methods.
    [0068] As stated above, by knocking a weld toe 4 of a lap fillet welded joint, a welded structure having the lap fillet welded joint according to the second embodiment can be obtained, the welded structure comprising a knocking region 13 having a plurality of knocking marks 10 running across the weld toe 4 of the lap fillet welded joint, wherein in the knocking region 13, the knocking marks 10 have a total length on the weld toe 4 of 50 % or more of the whole length of the weld toe 4, and the knocking region 13 has a width at least twice a width of a knocking mark 10 per knock point, and further, in the knocking region 13, end parts of knocking marks 10 located in an end part along a width direction of the knocking region 13 and superimposed on each other are separated from each other in a direction orthogonal to the welding direction, or, end parts of knocking marks 10 located in an end part along the width direction of the knocking region 13 are contacted with each other at three knock points or less in the direction orthogonal to the welding direction.
    [0069] The knocking region 13 is defined as a region having a maximum width (maximum width in a direction orthogonal to the welding direction), L2, the region including a plurality of contiguous (or mutually superimposed) knocking marks 10 as illustrated in FIG. 6.
    [0070] However, from the viewpoint of sufficiently obtaining a stress relieving effect by peening, it is necessary to make the total length on the weld toe 4 of the knocking marks 10 in the knocking region 13 50 % or more of the whole length of the weld toe 4. The total length on the weld toe 4 of the knocking marks 10 is preferably 70 % or more and more preferably 90 % or more of the whole length of the weld toe 4. Alternatively, it may be 100 %.
    [0071] Adjusting the knocking frequency, oscillation frequency, and scanning rate in the welding direction to the above ranges makes it possible that in the knocking region, as illustrated in FIG. 6, the knocking marks 10 have a total length on the weld toe 4 of 50 % or more of the whole length of the weld toe 4 and in the knocking region 13, end parts of knocking marks 10 located in an end part along a width direction of the knocking region 13 and superimposed on each other are separated from each other in a direction orthogonal to the welding direction, or, end parts of knocking marks 10 located in an end part along the width direction of the knocking region 13 are contacted with each other at three knock points or less in the direction orthogonal to the welding direction.
    [0072] Further, in particular, adjusting the knocking frequency to 50 Hz to 150 Hz, oscillation frequency to 1 Hz to 10 Hz, and scanning rate in the welding direction to 0.1 mm/s to 5 mm/s makes it possible that in the knocking region, the knocking marks have a total length on the weld toe of 90 % or more of the whole length of the weld toe.
    [0073] Moreover, from the viewpoint of improving fatigue properties, it is preferable that the straight line connecting the centers of knocking marks 10 superimposed on each other is not parallel to the welding direction. Therefore, it is preferable that the knocking frequency fi is inconsistent with the oscillation frequency f2, specifically, f1/f2 is a non-integer.
    [0074] The width of the knocking region 13, L2 is typically almost the same as the oscillation width. Therefore, the knocking region 13 has a width at least twice a width of one knocking mark. The knocking region 13 preferably has a width of 2.5 times or more of a width of one knocking mark. The width of the knocking region 13, L2 is preferably 3.0 mm or less, and more preferably 1.0 mm or less.
    [0075] While the first and second embodiments have been described above, it is particularly preferable to apply the peening according to these embodiments to a lap fillet welded joint having a thin steel sheet with a thickness of 1.0 mm to 3.6 mm (more preferably, 2.0 mm to 3.0 mm) and a tensile strength of 780 MPa or more as a base sheet.
    [0076] Further, the knocking pin 5 has any tip shape if the curvature radius of the tip is equal to or less than the curvature radius of the weld toe 4. For example, the knocking pin 5 may have a tip with a semicylindrical, hemispherical, semielliptical, or approximately semicylindrical shape.
    [0077] Moreover, when the peening is performed according to the embodiments stated above, not only an air-driven device and ultrasonic device but also an electric device can be also used, and thus, it is very advantageous in terms of workability.
    [0078] In addition, the welding method is not particularly limited, and the peening method can be applied to any welded joint obtained by, for example, arc welding and laser welding.
    [0079] Further, although the holding method of the knocking tool 17 is not particularly specified, when the knocking tool 17 is pressed against the weld toe 4 using the knocking tool holder 18 as illustrated in FIG. 8, it is desirable from the reason stated above to clamp the knocking tool 17 with the viscoelastic material 20 as illustrated in FIG. 9. In FIG. 9, reference sign 19 indicates a bolt.
    [0080] The material property of the viscoelastic material 20 is not particularly limited if it has viscosity which makes the vibration of the knocking tool holder 18 inconsistent with that of the knocking pin 5. However, a polymer substance such as rubber and gel is preferable. EXAMPLES(Example 1)
    [0081] An example according to the first embodiment will be described.
    [0082] Steel sheets with a size of 300 mm × 70 mm (thickness: 2.9 mm) were cut out of various steel materials. Two steel sheets thus cut out were fixed with a jig and subjected to lap fillet arc welding under the conditions listed in Table 1 to produce various lap fillet arc welded joints. Next, a weld toe 4 of each produced lap fillet arc welded joint was subjected to peening using an electric or air-driven (air pressure of 0.5 MPa) device under the conditions listed in Tables 2 and 4 to 6 to form knocking marks 10 on the lap fillet arc welded joint as illustrated in FIG. 5.
    [0083] The peening was performed until a slag of the surface of the weld toe 4 was fractured and the internal metallic luster was exposed. Further, the knocking pin 5 was continuously knocked as a series of knocking toward a direction inclined relative to the welding direction across the weld toe 4, the series of knocking was repeatedly performed in the welding direction, and at that time, a knocking mark group 12 made of a plurality of knocking marks 10 formed by the series of knocking was superimposed on at least a part of an adjacent knocking mark group 12 while an end part of the knocking mark group 12 in a direction orthogonal to the welding direction was separated from an end part of the adjacent knocking mark group 12 in a direction orthogonal to the welding direction. Further, the used knocking pin 5 had a tip with a hemispherical shape. The scanning rate in the series of knocking was 10 mm/s.
    [0084] The curvature radius of the weld toe 4 as listed in Tables 4 to 6 was determined by averaging the measurement results at five locations for each welded joint according to NPL 2.
    [0085] Test pieces having a shape illustrated in FIG. 7 were collected from the lap fillet arc welded joints after the peening so that a weld bead 11 became the center part of the test piece. Using the test pieces, plane bending fatigue test was conducted in accordance with JIS Z 2275 under the conditions listed in Table 3 to evaluate fatigue properties based on the following criterion.
    [0086] Passed (Particularly Excellent): Fatigue life was beyond three million times (if the test piece was not fractured at a stress repeating count of three million, fatigue life was judged as beyond three million times).
    [0087] Passed (Excellent): Fatigue life was two million times or more and three million times or less.
    [0088] Failed: Fatigue life was less than two million times.
    [0089] The evaluation results are also listed in Tables 4 to 6. Table 1 Shielding gas Current (A) Voltage (V) Welding rate (cm/min) 80 vol.% Ar-20 vol.% CO2 230 23 80 Table 2 Device Knocking pin diameter (mm) Knocking frequency (Hz) Electric type 3 100 Air-driven type 3 20 Table 3 Nominal stress range (MPa) Stress ratio Frequency (Hz) Counts when test ends 500 0 10 3 million times Table 4 No. Tensile streangth of steel sheet (base sheet) (MPa) Peening conditions Shape of weld toe after peening Fatigue life (times) Remarks Curvature radius of knocking pin (mm) Curvature radius of weld toe before peening (mm) Device Scanning angle (°) Scanning width (mm) Curvature radius of knocking mark (mm) Inclination angle relative to welding direction of knocking mark group θ (°) Width of knocking mark group L1 (mm) Presence/ absence of fold mark in weld toe 1 980 0.04 0.50 electric type 30 1.0 0.04 30 1.0 absent 1.5 mill. Comparative Example 2 980 0.05 0.50 electric type 30 1.0 0.05 30 1.0 absent 2.5 mill. Example 3 980 0.10 0.50 electric type 30 1.0 0.10 30 1.0 absent beyond 3 mill. Example 4 980 0.40 0.50 air-driven type 30 1.0 0.40 30 1.0 absent beyond 3 mill. Example 5 980 0.50 0.50 air-driven type 30 1.0 0.50 30 1.0 absent 2.5 mill. Example 6 980 0.51 0.50 air-driven type 30 1.0 0.51 30 1.0 present 0.31 mill. Comparative Example Table 5 No. Tensile streangth of steel sheet (base sheet) (MPa) Peening conditions Shape of weld toe after peening Fatigue life (times) Remarks Curvature radius of knocking pin (mm) Curvature radius of weld toe before peening (mm) Device Scanning angle (°) Scanning width (mm) Curvature radius of knocking mark (mm) Inclination angle relative to welding direction of knocking mark group θ (°) Width of knocking mark group L1 (mm) Presence/ absence of fold mark in weld toe 7 980 0.10 0.50 electric type 0 1.0 0.10 0 1.0 absent 1 mill. Comparative Example 8 980 0.10 0.50 electric type 20 1.0 0.10 20 1.0 absent 2.5 mill. Example 9 980 0.10 0.50 electric type 30 1.0 0.10 30 1.0 absent beyond 3 mill. Example 10 980 0.10 0.50 electric type 45 1.0 0.10 45 1.0 absent beyond 3 mill. Example 11 980 0.10 0.50 electric type 50 1.0 0.10 50 1.0 absent 2.5 mill. Example Table 6 No. Tensile streangth of steel sheet (base sheet) (MPa) Peening conditions Shape of weld toe after peening Fatigue life (times) Remarks Curvature radius of knocking pin (mm) Curvature radius of weld toe before peening (mm) Device Scanning angle (°) Scanning width (mm) Curvature radius of knocking mark (mm) Inclination angle relative to welding direction of knocking mark group θ (°) Width of knocking mark group L1 (mm) Presence/ absence of fold mark in weld toe 12 980 0.10 0.50 electric type 30 1.0 0.10 30 1.0 absent beyond 3 mill. Example 13 780 0.10 0.50 electric type 30 1.0 0.10 30 1.0 absent beyond 3 mill. Example 14 690 0.10 0.50 electric type 30 1.0 0.10 30 1.0 absent 2.6 mill. Example 15 590 0.10 0.50 electric type 30 1.0 0.10 30 1.0 absent 2.3 mill. Example 16 440 0.10 0.50 electric type 30 1.0 0.10 30 1.0 absent 2 mill. Example
    [0090] As listed in Tables 4 to 6, our examples had excellent fatigue life.
    [0091] Further, as listed in Table 5, when an inclination angle relative to the welding direction is controlled to be 30° to 45°, excellent fatigue life was obtained.
    [0092] Moreover, as listed in Table 6, when a steel sheet having a tensile strength of 780 MPa or more was used as a base sheet, fatigue properties could be advantageously improved. (Example 2)
    [0093] An example according to the second embodiment stated above will be described.
    [0094] Steel sheets with a size of 300 mm × 70 mm (thickness: 2.9 mm) were cut out of various steel materials. Two steel sheets thus cut out were fixed with a jig and subjected to lap fillet arc welding under the conditions listed in Table 1 to produce various lap fillet art welded joints. Next, a weld toe 4 of each produced lap fillet arc welded joint was subjected to peening using an electric or air-driven (air pressure of 0.5 MPa) device under the conditions listed in Tables 2 and 7 to 9 while the knocking pin 5 was oscillated in a direction orthogonal to the welding direction around the weld toe 4. The peening was performed until a slag of the surface of the weld toe 4 was fractured and the internal metallic luster was exposed. Further, the used knocking pin 5 had a tip with a hemispherical shape.
    [0095] The curvature radiuses of the weld toes 4 listed in Tables 7 to 9 were determined by averaging the measurement results at five locations for each welded joint according to NPL 2.
    [0096] In any example in which the knocking pin 5 was oscillated, in a knocking region 13 determined according to the oscillation width of the knocking pin 5, knocking marks 10 located in an end part along a width direction of the knocking region 13 and superimposed on each other had end parts separated from each other in a direction orthogonal to the welding direction, or, knocking marks 10 located in an end part along the width direction of the knocking region 13 had end parts contacting with each other at three knock points or less in the direction orthogonal to the welding direction.
    [0097] Test pieces having a shape illustrated in FIG. 7 were collected from the lap fillet arc welded joints after the peening so that a weld bead 11 became the center part of the test piece. Using the test pieces, plane bending fatigue test was conducted in accordance with JIS Z 2275 under the conditions listed in Table 3 to evaluate fatigue properties based on the following criterion.
    [0098] Passed (Particularly Excellent): Fatigue life was beyond three million times (if the test piece was not fractured at a stress repeating count of three million, fatigue life was judged as beyond three million times).
    [0099] Passed (Excellent): Fatigue life was two million times or more and three million times or less.
    [0100] Failed: Fatigue life was less than two million times.
    [0101] The evaluation results are also listed in Tables 7 to 9. Table 7 No. Tensile streangth of steel sheet (base sheet) (MPa) Peening conditions Shape of weld toe after peening Fatigue life (times) Remarks Curvature radius of knocking pin (mm) Curvature radius of weld toe before peening (mm) Device Oscillation width (mm) Oscillation frequency (Hz) Scanning rate (mm/s) Curvature radius of knocking mark (mm) Width of one knocking mark L0 (mm) Width of knocking region L2 (mm) Ratio of total length of knocking marks on weld toe to whole length of weld toe (%) Presence/ absence of fold mark in weld toe 101 980 0.04 0.50 electric type 0.6 7 1 0.04 0.2 0.6 90 absent 1.5 mill. Comparative Example 102 980 0.05 0.50 electric type 0.6 7 1 0.05 0.2 0.6 90 absent 2.5 mill. Example 103 980 0.10 0.50 electric type 0.6 7 1 0.10 0.2 0.6 90 absent beyond 3 mill. Example 104 980 0.40 0.50 air-driven type 0.6 7 1 0.40 0.2 0.6 70 absent beyond 3 mill. Example 105 980 0.50 0.50 air-driven type 0.6 7 1 0.50 0.2 0.6 70 absent 2.5 mill. Example 106 980 0.51 0.50 air-driven type 0.6 7 1 0.51 0.2 0.6 70 present 0.31 mill. Comparative Example Table 8 No. Tensile streangth of steel sheet (base sheet) (MPa) Peening conditions Shape of weld toe after peening Fatigue life (times) Remarks Curvature radius of knocking pin (mm) Curvature radius of weld toe before peening (mm) Device Oscillation width (mm) Oscillation frequency (Hz) Scanning rate (mm/s) Curvature radius of knocking mark (mm) Width of one knocking mark L0 (mm) Width of knocking region L2 (mm) Ratio of total length of knocking marks on weld toe to whole length of weld toe (%) Presence/ absence of fold mark in weld toe 107 980 0.10 0.50 electric type 0.6 7 7 0.10 0.2 0.6 70 absent beyond 3 mill. Example 108 980 0.10 0.50 electric type 0.5 7 7 0.10 0.2 0.5 70 absent beyond 3 mill. Example 109 980 0.10 0.50 electric type 0.4 7 7 0.10 0.2 0.4 70 absent 2 mill. Example 110 980 0.10 0.50 electric type 0.6 4 4 0.10 0.2 0.6 90 absent 2 mill. Example 111 980 0.10 0.50 electric type no oscillation 0.10 0.2 0.2 100 absent 1 mill. Comparative Example Table 9 No. Tensile streangth of steel sheet (base sheet) (MPa) Peening conditions Shape of weld toe after peening Fatigue life (times) Remarks Curvature radius of knocking pin (mm) Curvature radius of weld toe before peening (mm) Device Oscillation width (mm) Oscillation frequency (Hz) Scanning rate (mm/s) Curvature radius of knocking mark (mm) Width of one knocking mark L0 (mm) Width of knocking region L2 (mm) Ratio of total length of knocking marks on weld toe to whole length of weld toe (%) Presence/ absence of fold mark in weld toe 112 980 0.10 0.50 electric type 0.6 7 7 0.10 0.2 0.6 70 absent beyond 3 mill. Example 113 780 0.10 0.50 electric type 0.6 7 7 0.10 0.2 0.6 70 absent beyond 3 mill. Example 114 690 0.10 0.50 electric type 0.6 7 7 0.10 0.2 0.6 70 absent 2.6 mill. Example 115 590 0.10 0.50 electric type 0.6 7 7 0.10 0.2 0.6 70 absent 2.3 mill. Example 116 440 0.10 0.50 electric type 0.6 7 7 0.10 0.2 0.6 70 absent 2 mill Example
    [0102] As listed in Tables 7 to 9, our examples had excellent fatigue life.
    [0103] Further, as listed in Table 8, when the oscillation width of the knocking pin 5 was 2.5 times or more of the width of one knocking mark, particularly excellent fatigue life was obtained.
    [0104] Moreover, as listed in Table 9, when a steel sheet having a tensile strength of 780 MPa or more was used as a base sheet, fatigue properties could be advantageously improved. (Example 3)
    [0105] To demonstrate an effect when a knocking tool was clamped with a viscoelastic material in fixing the knocking tool with a holding jig, the peening was performed with the method according to the first embodiment while the knocking tool was held in such a way as illustrated in FIGS. 8 and 9. The method is described below.
    [0106] Steel sheets (thickness of 2.9 mm) were subjected to lap fillet arc welding under the conditions listed in Table 1 to produce various lap fillet arc welded joints. Next, a weld toe 4 of each produced lap fillet arc welded joint was subjected to peening using an air-driven (air pressure of 0.5 MPa) device under the conditions listed in Tables 2 and 11 to form knocking marks 5 on the lap fillet arc welded joint as illustrated in FIG.5.
    [0107] A knocking tool 17 was clamped with a viscoelastic material 20 as illustrated in FIGS. 8 and 9 by inserting the viscoelastic material 20 between the knocking tool 17 which had a mechanism of oscillating a knocking pin 5 and a knocking tool holder 18, and fastening a bolt 19. In the example, a gel sheet made of silicon was used as the viscoelastic material 20.
    [0108] The peening was performed until a slag of the surface of the weld toe 4 was fractured and the internal metallic luster was exposed. Further, the knocking pin 5 was continuously knocked as a series of knocking toward a direction inclined relative to a welding direction across the weld toe 4, and the series of knocking was repeatedly performed in the welding direction. At that time, a knocking mark group 12 made of a plurality of knocking marks 10 formed by the series of knocking was superimposed on at least a part of an adjacent knocking mark group 12 while an end part of the knocking mark group 12 in a direction orthogonal to the welding direction was separated from an end part of the adjacent knocking mark group 12 in a direction orthogonal to the welding direction. Further, the used knocking pin 5 had a tip with a hemispherical shape. The scanning rate in the series of knocking was 5 mm/s.
    [0109] The curvature radiuses of the weld toes 4 listed in Table 11 were determined by averaging the measurement results at five locations for each welded joint according to NPL 3.
    [0110] Test pieces having a shape illustrated in FIG. 7 were collected from the lap fillet arc welded joints after the peening so that a weld bead 11 became the center part of the test piece. Using the test pieces, plane bending fatigue test was conducted in accordance with JIS Z 2275 under the conditions listed in Table 10 to evaluate fatigue properties based on the following criterion.
    [0111] Passed (Particularly Excellent): Fatigue life was beyond three million times (if the test piece was not fractured at a stress repeating count of three million, fatigue life was judged as beyond three million times).
    [0112] Passed (Excellent): Fatigue life was two million times or more and three million times or less.
    [0113] Failed: Fatigue life was less than two million times.
    [0114] The evaluation results are also listed in Table 11. Table 10 Nominal stress range (MPa) Stress ratio Frequency (Hz) Counts when test ends 600 0 10 3 mill. Table 11 No. Tensile streangth of base sheet (MPa) Peening conditions Shape of weld toe after peening Fatigue life (times) Remarks Curvature radius of knocking pin ρp (mm) Curvature radius of weld toe before peening ρa (mm) Knocking angle β (°) Scanning angle (°) Scanning width (mm) Presence/ absence of viscoelastic material of holder Curvature radius of knocking mark (mm) Inclination angle relative to welding direction of knocking mark group θ (°) Width of knocking mark group L1 (mm) 2 980 0.5 1.8 0 30 5 absent 1.5 30 5 2.1 mill. Example 114 980 0.5 1.8 0 30 5 present 1.5 30 5 beyond 3 mill. Example
    [0115] As listed in Table 11, particularly excellent fatigue life was obtained when the knocking tool was clamped with the viscoelastic material. (Example 4)
    [0116] As with Example 3, to demonstrate an effect when a knocking tool was clamped with a viscoelastic material in fixing the knocking tool with a holding jig, the peening was performed with the method according to the second embodiment while the knocking tool was held in such a way as illustrated in FIGS. 8 and 9. The method is described below.
    [0117] Steel sheets (thickness of 2.9 mm) were subjected to lap fillet arc welding under the conditions listed in Table 1 to produce various lap fillet arc welded joints. Next, a weld toe 4 of each produced lap fillet arc welded joint was subjected to peening using an air-driven (air pressure of 0.5 MPa) device under the conditions listed in Tables 2 and 12 while a knocking pin 5 was oscillated in a direction orthogonal to the welding direction around the weld toe 4.
    [0118] The peening was performed until a slag of the surface of the weld toe 4 was fractured and the internal metallic luster was exposed. Further, the used knocking pin 5 had a tip with a hemispherical shape.
    [0119] A knocking tool 17 was clamped with a viscoelastic material 20 as illustrated in FIGS. 8 and 9 by inserting the viscoelastic material 20 between the knocking tool 17 which has a mechanism of oscillating the knocking pin 5 and a knocking tool holder 18, and fastening a bolt 19. In the example, a gel sheet made of silicon was used as the viscoelastic material 20.
    [0120] The curvature radius of the weld toe 4 listed in Table 12 were determined by averaging the measurement results at five locations for each welded joint according to NPL 3.
    [0121] In any example in which the knocking pin 5 was oscillated, in a knocking region 13 determined according to the oscillation width of the knocking pin 5, knocking marks 10 located in an end part along a width direction of the knocking region 13 and superimposed on each other had end parts separated from each other in a direction orthogonal to the welding direction, or, knocking marks 10 located in an end part along the width direction of the knocking region 13 have end parts contacting with each other at three knock points or less in the direction orthogonal to the welding direction.
    [0122] Test pieces having a shape illustrated in FIG. 7 were collected from the lap fillet arc welded joints after the peening so that a weld bead 11 became the center part of the test piece. Using the test pieces, plane bending fatigue test was conducted in accordance with JIS Z 2275 under the conditions listed in Table 10 to evaluate fatigue properties based on the following criterion.
    [0123] Passed (Particularly Excellent): Fatigue life was beyond three million times (if the test piece was not fractured at a stress repeating count of three million, fatigue life was judged as beyond three million times).
    [0124] Passed (Excellent): Fatigue life was two million times or more and three million times or less.
    [0125] Failed: Fatigue life was less than two million times.
    [0126] The evaluation results are also listed in Table 12. Table 12 No. Tensile streangth of base sheet (MPa) Peening conditions Shape of weld toe after peening Fatigue life (times) Remarks Curvature radius of knocking pin ρp (mm) Curvature radius of weld toe before peening ρa (mm) Knocking angle β (°) Oscillation width (mm) Oscillation frequency (Hz) Scanning rate (mm/s) Presence/ absence of viscoelastic material of holder Curvature radius of knocking mark (mm) Width of one knocking mark L0 (mm) Width of knocking mark group L2 (mm) Ratio of total length of knocking marks on weld toe to whole length of weld toe (%) 102 980 0.5 1.8 0 3 7 3 absent 1.5 1 3 90 2.1 mill. Example 115 980 0.5 1.8 0 3 7 3 present 1.5 1.5 3 100 beyond 3 mill. Example
    [0127] As listed in Table 12, particularly excellent fatigue life was obtained when the knocking tool was clamped with the viscoelastic material. REFERENCE SIGNS LIST
    [0128] 1:Thin steel sheet (base sheet)2:Thin steel sheet (base sheet)3:Weld metal4:Weld toe5:Knocking pin6:Knocking pin tip7:Fold mark of a weld toe8:Fold mark at a knocking mark edge9:Weld ripple10:Knocking mark11:Weld bead12:Knocking mark group13:Knocking region17:Knocking tool18:Knocking tool holder19:Bolt20:Viscoelastic material
    权利要求:
    Claims (10)
    [0001] A method of peening a lap fillet welded joint, comprising knocking a weld toe of the lap fillet welded joint using a knocking pin attached to a tip of a knocking tool, whereinthe knocking pin has, on its tip, a curvature radius in a vertical cross section in a direction orthogonal to a welding direction of 0.05 mm to 0.50 mm and equal to or less than a curvature radius of the weld toe,the knocking pin is continuously knocked as a series of knocking toward a direction inclined relative to the welding direction across the weld toe,the series of knocking is repeatedly performed in the welding direction,at that time, a knocking mark group made of a plurality of knocking marks formed by the series of knocking is superimposed on at least a part of an adjacent knocking mark group, while an end part in the direction orthogonal to the welding direction of the knocking mark group is separated from an end part in the direction orthogonal to the welding direction of the adjacent knocking mark group.
    [0002] The method of peening a lap fillet welded joint according to claim 1, wherein the series of knocking is performed at an inclination angle relative to the welding direction of 30° to 45°.
    [0003] The peening method according to claim 1 or 2, wherein the knocking tool is clamped with a viscoelastic material on a holder of the knocking tool.
    [0004] A welded structure having a lap fillet welded joint, comprising a plurality of knocking mark groups in which a plurality knocking marks run at an angle relative to a welding direction across a weld toe of the lap fillet welded joint, whereinthe knocking marks have a curvature radius in a cross section perpendicular to the weld line direction of 0.05 mm to 0.50 mm, andeach knocking mark group is superimposed on at least a part of an adjacent knocking mark group while an end part in a direction orthogonal to a welding direction of the knocking mark group is separated from an end part in the direction orthogonal to the welding direction of the adjacent knocking mark group.
    [0005] The welded structure according to claim 4, wherein each knocking mark group has the knocking marks running at a slanting angle of 30° to 45° with respect to the welding direction.
    [0006] The welded structure according to claim 4 or 5, wherein the lap fillet welded joint has a base sheet with a tensile strength of 780 MPa or more.
    [0007] A method of peening a lap fillet welded joint, comprising knocking a weld toe of the lap fillet welded joint using a knocking pin attached to a tip of a knocking tool, whereinthe knocking pin has, on its tip, a curvature radius in a vertical cross section in a direction orthogonal to a welding direction of 0.05 mm to 0.50 mm and equal to or less than a curvature radius of the weld toe,the knocking pin is knocked while the knocking pin is oscillated in the direction orthogonal to the welding direction across the weld toe and moved in the welding direction,the knocking pin has an oscillation width around the weld toe at least twice a width of a knocking mark per knock point, and in a knocking region determined according to the oscillation width of the knocking pin, end parts of knocking marks located in an end part along a width direction of the knocking region and superimposed on each other are separated from each other in the direction orthogonal to the welding direction, or, end parts of knocking marks located in an end part along the width direction of the knocking region are contacted with each other at three knock points or less in the direction orthogonal to the welding direction.
    [0008] The peening method according to claim 7, wherein the knocking tool is clamped with a viscoelastic material on a holder of the knocking tool.
    [0009] A welded structure having a lap fillet welded joint, comprising a knocking region having a plurality of knocking marks running across a weld toe of the lap fillet welded joint, whereinin the knocking region,the knocking marks have a total length on the weld toe of 50 % or more of the whole length of the weld toe, andthe knocking region has a width at least twice a width of a knocking mark per knock point,and further, in the knocking region, end parts of knocking marks located in an end part along a width direction of the knocking region and superimposed on each other are separated from each other in a direction orthogonal to a welding direction, or, end parts of knocking marks located in an end part along the width direction of the knocking region are contacted with each other at three knock points or less in the direction orthogonal to the welding direction.
    [0010] The welded structure according to claim 9, wherein the lap fillet welded joint has a base sheet with a tensile strength of 780 MPa or more.
    类似技术:
    公开号 | 公开日 | 专利标题
    KR101737712B1|2017-05-18|Lap welded member, automobile component, method for welding lapped part, and method for manufacturing lap welded member
    CN101254583B|2013-06-19|Method and apparatus for increasing fatigue notch capability of airfoils
    JP5258154B2|2013-08-07|Method for forming an aluminum alloy article and method for improving the ductility of an aluminum alloy article
    EP2769797B1|2017-03-22|Resistance spot welding method for high-tensile steel plates, and resistance spot welding joint
    JP3456995B2|2003-10-14|Hard rolling method for parts
    EP1559796B1|2017-04-19|Method of increasing toughness of heat-affected part of steel product welded joint
    JP2007521964A|2007-08-09|Method of joining two or more shaped parts or metal plates by mechanical joining and pressure welding at one or more connection points
    EP2644293A1|2013-10-02|Method for manufacturing l-shaped product
    JP3710435B2|2005-10-26|Band saw, band saw processing apparatus and band saw manufacturing method
    CA2909397C|2017-07-25|Spot welding method
    JP2004009113A|2004-01-15|Joint structure of main body and lid
    EP1459846B1|2012-11-14|Leaf spring for vehicle and method of manufacturing the leaf spring
    EP1674187A1|2006-06-28|Weld structure having excellent brittle crack propagation resistance and method of welding the weld structure
    JP4719297B2|2011-07-06|Welded joint with excellent fatigue resistance and method for producing the same
    JP2008229720A|2008-10-02|Spot-welded joint of high-strength steel sheets excellent in tensile strength, automotive component having the same joint, and spot-welding method of high-strength steel sheets
    CN104531979A|2015-04-22|Technology for refining metal surface crystal grains by electric pulse and ultrasonic coupling
    US20020017173A1|2002-02-14|Method and apparatus for trimming aluminum sheet
    JP5042648B2|2012-10-03|Laser welding method for structure made of steel plate
    EP3103578B1|2020-12-09|Method for manufacturing welded structure
    EP2055853A1|2009-05-06|Tool for joining reinforcing bars
    CN108025401B|2020-08-04|Arc fillet weld and method for manufacturing same
    Jolu et al.2010|Effect of joint line remnant on fatigue lifetime of friction stir welded Al–Cu–Li alloy
    EP2298465B1|2018-09-26|Press-forming method of tubular part having cross-section of irregular shape
    CN1791696A|2006-06-21|Steel bar for steering rack, method for producing the same, and steering rack using the same
    JP2005148053A|2005-06-09|Method for estimating limit breaking load of spot welded part
    同族专利:
    公开号 | 公开日
    KR102243326B1|2021-04-21|
    JPWO2019064930A1|2019-11-14|
    JP6504326B1|2019-04-24|
    EP3689531A4|2020-11-18|
    CN111132793A|2020-05-08|
    US20200269358A1|2020-08-27|
    WO2019064930A1|2019-04-04|
    KR20200055074A|2020-05-20|
    引用文献:
    公开号 | 申请日 | 公开日 | 申请人 | 专利标题
    法律状态:
    2019-04-06| STAA| Information on the status of an ep patent application or granted ep patent|Free format text: STATUS: THE INTERNATIONAL PUBLICATION HAS BEEN MADE |
    2020-07-03| PUAI| Public reference made under article 153(3) epc to a published international application that has entered the european phase|Free format text: ORIGINAL CODE: 0009012 |
    2020-07-03| STAA| Information on the status of an ep patent application or granted ep patent|Free format text: STATUS: REQUEST FOR EXAMINATION WAS MADE |
    2020-08-05| AX| Request for extension of the european patent|Extension state: BA ME |
    2020-08-05| 17P| Request for examination filed|Effective date: 20200416 |
    2020-08-05| AK| Designated contracting states|Kind code of ref document: A1 Designated state(s): AL AT BE BG CH CY CZ DE DK EE ES FI FR GB GR HR HU IE IS IT LI LT LU LV MC MK MT NL NO PL PT RO RS SE SI SK SM TR |
    2020-11-18| A4| Supplementary search report drawn up and despatched|Effective date: 20201015 |
    2020-11-18| RIC1| Information provided on ipc code assigned before grant|Ipc: B23K 31/00 20060101AFI20201009BHEP Ipc: B23K9/23 20060101ALI20201009BHEP Ipc: C21D 10/00 20060101ALI20201009BHEP Ipc: C21D9/50 20060101ALI20201009BHEP Ipc: B23K9/00 20060101ALI20201009BHEP Ipc: C21D7/06 20060101ALI20201009BHEP |
    2021-01-06| DAV| Request for validation of the european patent (deleted)|
    2021-01-06| DAX| Request for extension of the european patent (deleted)|
    优先权:
    申请号 | 申请日 | 专利标题
    [返回顶部]