    • 专利摘要:
    The invention discloses a continuous hot rolled coil for a high collapse-resistant SEW petroleum casing and a manufacturing method thereof, and belongs to the technical field of hot continuous rolling production. Provided is a continuous hot rolled coil for a high collapse-resistant SEW petroleum casing with low alloy element cost and excellent initial welding property, and a manufacturing method thereof. The production cost of the hot continuous rolled coil is lowered by reducing expensive alloy elements such as Mo and V therein, and strictly controlling the content components of chemical elements such as Cr, Mn and Ti. According to the manufacturing method, a continuous cast slab is used as an initial billet and subjected to rough rolling by refined grains for 5-7 passes under the temperature-controlled heating condition to form an intermediate billet, and then the intermediate billet is subjected to fine turning for at least 4 passes, then finally cooled and coiled to complete the production and processing of the continuous hot rolled coils, and achieve the purpose of controlling the initial yield strength and the initial tensile strength.
    公开号:EP3683326A1
    申请号:EP18854330.0
    申请日:2018-06-20
    公开日:2020-07-22
    发明作者:Kaihua ZHANG；Xiaoyu YE；Xuegang XIONG；Yi Wang
    申请人:Pangang Group Panzhihua Iron and Steel Research Institute Co Ltd；
    IPC主号:C21D9-00
    专利说明:
    [0001] The invention relates to a continuous hot rolled coil, in particular to a continuous hot rolled coil for a high collapse-resistant SEW petroleum casing, and belongs to the technical field of continuous hot rolling production. The invention also relates to a manufacturing method of the continuous hot rolled coil thereof. Background of the Invention
    [0002] The petroleum casing is not only an important pipeline material in the oil and natural gas exploitation process but also an essential construction material in drilling for oil and gas. Especially in recent years, deep and ultra-deep drilling leads to stringent requirements for the performance of petroleum casing; that is, the strength grade of high collapse-resistant SEW petroleum casing is getting higher and higher with the increasing demand. In the past, seamless pipes are mainly used as high fight casings, which severely affecting the quality and benefit of oil drilling and exploitation due to many disadvantages like large wall thickness deviation, uneven performance, low chance resistance, perforation cracking and fast casing damage.
    [0003] In recent years, a variety of high collapse-resistant SEW petroleum casings have been studied and produced. For example, the patent application document (patent number: 201110427453.9 ) discloses a high collapse-resistant SEW petroleum casing and a manufacturing method thereof, comprising the following chemical compositions: 0.25%-0.33% of C, 0.19%-0.28% of Si, 1.10%-1.30% of Mn, P (≤0.020%) and S (≤0.008%). However, the patent only relates to the manufacturing process of petroleum casings rather than the coils for petroleum casings; moreover, for the final steel pipes, the yield strength is 720-760 MPa and the tensile strength is more than 820 MPa, indicating a low yield strength. For another example, the patent application document (patent number: 200910018524.2 ) discloses a steel for N80, P110 and L80 SEW SEW petroleum casings and a manufacturing method of the steel and the petroleum casings thereof, comprising the following chemical compositions: 0.10%-0.28% of C, 0.12%-0.25% of Si, 1.10%-1.60% of Mn, 0.03-0.14% of P, 0.002-0.03% of S, 0.20%-0.70% of Cr, 0.07%-0.17% of Nb, 0.05%- 0.15% of V, and 0.10-0.22% of Ti. In this patent, a great amount of expensive Nb and V are added and inevitably increase the alloy cost. Here is another example. The patent application document (patent number: 201310468738.6 ) discloses a P110 SEW petroleum casing and a manufacturing method thereof, comprising the following chemical compositions: 0.24%-0.28% of C, 0.15%-0.30% of Si, 1.25%-1.50% of Mn, P (≤0.020%), S (≤0.008%), 0.05%-0.08% of V and 0.010-0.30% of Ti. In this patent, as V is added, the strength of the petroleum casing is enhanced through V precipitation; however, the alloy cost is still relatively high. At the same time, the yield strength of the hot rolled coil of the invention is more than 570 MPa , making it difficult for subsequent pipe welding, which requires the yield strength of 780 MPa -850 MPa and the tensile strength of 880-970 MPa .
    [0004] For this reason, it is a high priority to develop a high collapse-resistant SEW petroleum casing with excellent performance, which will be of far-reaching significance for saving the oil production cost and improving the oil production level. One of the most urgent problems to be solved by those skilled in the art is to produce continuous hot rolled coils for high collapse-resistant SEW petroleum casings by using a low-cost process route to reduce the strength of hot rolled coils and to facilitate subsequent pipe welding process and ensure the quenching and tempering treatment strength of welded pipes. Summary of the Invention
    [0005] The technical problem to be solved by the invention is to provide a continuous hot rolled coil for a high collapse-resistant SEW petroleum casing with low alloy element cost and excellent initial welding property. Further, the invention provides a manufacturing method of the continuous hot rolled coil thereof.
    [0006] A technical scheme for solving the technical problem of the invention is: a continuous hot rolled coil for a high collapse-resistant SEW petroleum casing, and the continuous hot rolled coil is a continuous cast and rolled coil comprising the following chemical components in parts by weight: 0.22-0.32% of C, 0.10-0.30% of Si, 1.10-1.40% of Mn, 0.30-0.60% of Cr, P (≤0.020%), S (≤0.010%), 0.008-0.019% of Ti, Fe and inevitable impurities.
    [0007] For the continuous cast and rolled coil, the initial yield strength is 340-360 MPa and the initial tensile strength is 620-640 MPa . For the quenched and tempered continuous cast and rolled coil, the initial yield strength is 840 MPa -910 MPa and the initial tensile strength is 940-1030 MPa .
    [0008] Further, the chemical compositions consist of 0.24-0.30% of C, 0.10-0.30% of Si, 1.20-1.40% of Mn, 0.40-0.50% of Cr, P (≤0.018%), S (≤0.005%), 0.010-0.017% of Ti, Fe and inevitable impurities.
    [0009] In the manufacturing method of the continuous hot rolled coil, a continuous cast slab is used as an initial billet and subjected to rough rolling by refined grains for 5-7 passes under the temperature-controlled heating condition to form an intermediate billet, and the intermediate billet is subjected to finish rolling for at least 4 passes, then finally cooled and coiled to complete the production and processing; wherein the deformation of the billet must be not less than 18% in each pass where the billet is subjected to rough milling by refined grains, the intermediate billet subjected to rough rolling by refined grains is 3.8-4.2 times thicker than the finished continuous hot rolled coil, and the cooling method before coiling and after finish rolling is air cooling.
    [0010] Further, the heating temperature is kept at 1180-1220 °C during each pass of rough rolling by refined grains. Preferably, the initial thickness of the continuous cast slab is 200-250 mm.
    [0011] Further, each pass of finish rolling is completed at once by a finishing mill unit.
    [0012] Further, the inlet temperature is kept at 970-1020 °C during finish rolling and the final rolling temperature is 850-900 °C.
    [0013] Further, the slab subjected to rough rolling by refined grains is fed into a hot coil box for coiling the head and tail thereof alternately, and then is uncoiled for temperature control and finish rolling in a finish rolling area.
    [0014] The beneficial effects of the invention are as follows: the application realizes the reduction of expensive alloy elements like Mo and V, and the strict control of the content of expensive chemical elements like Cr, Ti and Si and the rolling production process; namely, a continuous cast slab is used as an initial billet and is subjected to rough rolling by refined grains for 5-7 passes under the temperature-controlled heating condition to form an intermediate billet, and the intermediate billet is subjected to finish rolling for at least 4 passes, then finally cooled and coiled to complete the production and processing of the continuous hot rolled coil. Especially, the deformation of the billet must be not less than 18% in each pass where the billet is subjected to rough milling by refined grains, the intermediate billet subjected to rough rolling by refined grains is 3.8-4.2 times thicker than the finished continuous hot rolled coil, and the cooling method before coiling and after finish rolling is air cooling. In this way, the purpose of reducing the production cost is achieved, and the mechanical properties of the material can be ensured due to the existence of Cr which can improve the strength of the material and its collapse resistance. Then, supplemented by the rolling parameters of the process steps thereof, the purpose of improving the welding and mechanical property of the continuous hot rolled coil provided by the application can be achieved, Namely, for the continuous hot rolled coil, the initial yield strength is 340-360 MPa and the initial tensile strength is 620-640 MPa , which ensures both the excellent welding property of the continuous hot rolled coil and the finished product. For the quenched and tempered continuous hot rolled coil, the initial yield strength is 840 MPa -910 MPa and the initial tensile strength is 940-1030 MPa . Brief Description of the Drawings
    [0015] Fig. 1 is a metallographic structure of some banded structures formed by air cooling of a continuous hot rolled coil for a high collapse-resistant SEW petroleum casing of the invention. Detailed Description of the Preferred Embodiment
    [0016] In order to solve the technical problem in the prior art, the invention provides a continuous hot rolled coil for a high collapse-resistant SEW petroleum casing with low alloy element cost and excellent initial welding property. Further, the invention provides a manufacturing method of the continuous hot rolled coil thereof. The continuous hot rolled coil consists of the following chemical components in parts by weight: 0.22-0.32% of C, 0.10-0.30% of Si, 1.10-1.40% of Mn, 0.30-0.60% of Cr, P (≤0.020%), S (≤0.010%), 0.008-0.019% of Ti, Fe and inevitable impurities. For the continuous cast and rolled coil, the initial yield strength is 340-360 MPa and the initial tensile strength is 620-640 MPa . For the quenched and tempered continuous cast and rolled coil, the initial yield strength is 840 MPa -910 MPa and the initial tensile strength is 940-1030 MPa. Further, a continuous cast slab is used as an initial billet and subjected to rough rolling by refined grains for 5-7 passes under the temperature-controlled heating condition to form an intermediate billet, and the intermediate billet is subjected to fine rolling for at least 4 passes, then finally cooled and coiled to complete the production and processing of the continuous hot rolled coils; wherein the deformation of the billet must be not less than 18% in each pass where the billet is subjected to rough milling by refined grains, the intermediate billet subjected to rough rolling by refined grains is 3.8-4.2 times thicker than the finished continuous hot rolled coil, and the cooling method before coiling and after finish rolling is air cooling. The application can realize the reduction of expensive alloy elements like V and Mo, and the strict control of the content of expensive alloy elements like Cr, Ti and Si and the rolling production process; namely, a continuous cast slab is used as an initial billet and subjected to rough rolling by refined grains for 5-7 passes under the temperature-controlled heating condition to form an intermediate billet, and then the intermediate billet is subjected to finish rolling for at least 4 passes, then finally cooled and coiled to complete the production and processing of the continuous hot rolled coil. Especially, the deformation of the billet must be not less than 18% in each pass where the billet is subjected to rough milling by refined grains, the intermediate billet subjected to rough rolling by refined grains is 3.8-4.2 times thicker than the finished continuous hot rolled coil, and the cooling method before coiling and after finish rolling is air cooling. In this way, the purpose of reducing the production cost is achieved, and the mechanical properties of the material can be ensured due to the existence of Cr which can improve the strength of the material and its collapse resistance. Then, supplemented by the rolling parameters of the process steps thereof, the purpose of improving the welding and mechanical property of the continuous hot rolled coil provided by the application can be achieved, excellent welding property of the continuous hot rolled coil and the finished product can be ensured. Namely, for the continuous hot rolled coil, the initial yield strength is 340-360 MPa and the initial tensile strength is 620-640 MPa , which ensures both the excellent welding property of the continuous hot rolled coil and the finished product. For the quenched and tempered continuous hot rolled coil, the initial yield strength is 840 MPa-910 MPa and the initial tensile strength is 940-1030 MPa . Fig. 1 is a metallographic structure of some banded structures formed by air cooling of a continuous hot rolled coil for a high collapse-resistant SEW petroleum casing of the invention, with the aim of controlling the strength of the continuous hot rolled coil before subsequent heat treatment.
    [0017] In the above embodiments, in order to maximize the welding and mechanical property of the continuous hot rolled coil described in this application, the application provides a continuous hot rolled coil with more stringent chemical compositions, i.e. the chemical compositions consist of 0.24-0.30% of C, 0.10-0.30% of Si, 1.20-1.40% of Mn, 0.40-0.50% of Cr, P (≤0.018%), S (≤0.005%), 0.010-0.017% of Ti, Fe and inevitable impurities. Further, the invention adjusts the corresponding procedures in the rolling production process; that is, the heating temperature is kept at 1180-1220 °C during each pass of rough rolling by refined grains, the initial thickness of the continuous cast slab is 200-250 mm, each pass of finish rolling is completed at once by a finishing mill unit, the inlet temperature is kept at 970-1020 °C during finish rolling and the final rolling temperature is 850-900 °C, and the slab subjected to rough rolling by refined grains is fed into a hot coil box for coiling the head and tail thereof alternately, then is uncoiled for temperature control and finish rolling in a finish rolling area. The application adjusts and improves the performance of the finished steel plate by controlling the compositions and making full use of trace alloy elements; namely, making full use of the alloy elements such as C, Si, Mn, Cr and Mo rather than adjusting the performance of the finished steel plate by controlling the impurity content, wherein the role of various trace alloy elements in the finished steel plate is as follows: C is a carbide former capable of improving the strength. However, high C content is easy to form banded structure. This patent makes the best matching in controlled rolling and cooling process, effectively inhibiting the formation of banded structure. Si is a solid soluble in ferrite, and can improve the yield strength of steel. High Si content will deteriorate the processing and toughness, and the scale on the surface is "red rust", which is not easy to descale. Mn is an austenite former, which can improve the hardenability of steel, and play a solid solution strengthening role in steel. In addition, Mn can improve the strength of steel, easily form structure segregation in case of too high Mn content, and affect the impact and drop hammer performance. Cr is an element that strongly improves hardenability and is a strong precipitate former. During subsequent heat treatment, the heat treatment process window can be expanded to form precipitates, thus obviously improving the strength of steel products. Mo is able to improve the stability of austenite and the subsequent heat treatment control process (enlarge heat treatment process window). The strength of steel is improved through precipitation with V and Ti. Moreover, Mo has obvious refining effect on precipitated phase, which can inhibit the maturation and growth of precipitated phase and keep the proportion of precipitated phase below 10 nm at above 70%. Example
    [0018] The production technical process of the invention is as follows: molten iron desulphurization → converter smelting and combined blowing → deoxidization and alloying → LF electric heating → RH vacuum treatment → calcium-wire feeding → continuous casting → slab heating → high pressure water descaling → rough milling →coiling by hot coil box → finish rolling → laminar cooling → coiling → packaging and warehousing.
    [0019] The continuous hot rolled coil for high collapse-resistant SEW petroleum casing is smelted in a conventional converter and is continuously casted to obtain finished steel, with the chemical compositions comprising 0.22-0.32% of C, 0.10-0.30% of Si, 1.10-1.40% of Mn, 0.30-0.60% of Cr, P (≤0.020%), S (≤0.010%), 0.008-0.019% of Ti, Fe and inevitable impurities.
    [0020] The slab obtained from continuous casting is heated to 1180-1220 °C for heat preservation and rough rolling. Depending on the thickness of finished product, the slab with a thickness of 200-250 mm is subjected to rough rolling for 5 or 7 passes, with the deformation not less than 18 %. The thickness of the intermediate billet varies according to the finished product, but the intermediate billet must be more than four times thicker than the finished product.
    [0021] The billet subjected to rough rolling is then coiled in a hot coil box, which can be, for example, a coreless transfer hot coil box. The head-to-tail exchange of the intermediate billet is realized in the hot coil box to ensure the uniform temperature of the whole billet length, and remove the secondary oxide scale to ensure a smooth slab surface.
    [0022] The intermediate billet is shifted and uncoiled after being coiled by a hot coil box, entered a finish rolling area for finish rolling with the finish rolling entry temperature of 970-1020 °C and the final rolling temperature of 850-900 °C; and air cooling is adopted after finish rolling.
    [0023] The following are five embodiments of the invention. Table 1 shows the chemical compositions of the five embodiments of the invention, Table 2 shows the control values of the hot rolling process, and Table 3 shows the mechanical properties of coils. Table 1 Chemical compositions in example Example C Si Mn Cr P S Ti 1 0.29 0.2 1.30 0.43 0.012 0.002 0.016 2 0.27 0.19 1.27 0.44 0.012 0.003 0.016 3 0.29 0.22 1.31 0.45 0.013 0.002 0.014 4 0.28 0.22 1.32 0.46 0.011 0.002 0.013 5 0.28 0.21 1.34 0.44 0.012 0.002 0.014 Table 2 Control value of hot rolling process in examples Examples Tapping temperature/°C Thickness of intermediate billet/mm Initial rolling temperature/°C Finish rolling temperature/°C 1 1212 44 1005 882 2 1208 44 1002 885 3 1210 44 997 865 4 1205 44 992 872 5 1210 44 1000 883 Table 3 Mechanical properties of steel coil in examples Examples Yield strength (ReL) MPa Tensile strength (Rm) MPa Elongation (A) % Cold bend B=35, α=180°, d=a 1 345 637 37.0 Acceptable 2 344 623 37.5 Acceptable 3 348 634 38.5 Acceptable 4 351 636 36.0 Acceptable 5 363 639 37.0 Acceptable
    权利要求:
    Claims (8)
    [0001] A continuous hot rolled coil for a high collapse-resistant SEW petroleum casing, characterized in that the continuous hot rolled coil consists of the following chemical components in parts by weight: 0.22-0.32% of C, 0.10-0.30% of Si, 1.10-1.40% of Mn, 0.30-0.60% of Cr, P (≤0.020%), S (≤0.010%), 0.008-0.019% of Ti, Fe and inevitable impurities; for the continuous hot rolled coil thereof , the initial yield strength is 340-360 MPa and the initial tensile strength is 620-640 MPa ; for the quenched and tempered continuous hot rolled coil, the yield strength is 840 MPa -910 MPa and the tensile strength is 940-1030 MPa .
    [0002] The Continuous Hot Rolled Coil for a High Collapse-Resistant SEW Petroleum Casing according to claim 1, characterized in that the chemical compositions are 0.24-0.30% ofC, 0.10-0.30% of Si, 1.20-1.40% of Mn, 0.40-0.50% of Cr, P (≤0.018%), S (≤0.005%), 0.010-0.017% of Ti, Fe and inevitable impurities.
    [0003] A manufacturing method for a continuous hot rolled coil according to claim 1 or 2, characterized in that the manufacturing method, a continuous cast slab is used as an initial billet and subjected to rough rolling by refined grains for 5-7 passes under the temperature-controlled heating condition to form an intermediate billet, and the intermediate billet is subjected to fine rolling for at least 4 passes, then finally cooled and coiled to complete the production and processing of the continuous hot rolled coils; wherein the deformation of the billet must be not less than 18% in each pass where the billet is subjected to rough milling by refined grains, the intermediate billet subjected to rough rolling by refined grains is 3.8-4.2 times thicker than the finished continuous hot rolled coil, and the cooling method before coiling and after finish rolling is air cooling.
    [0004] The manufacturing method according to claim 3, characterized in that the heating temperature is kept at 1180-1220 °C during each pass of rough rolling of refined grains.
    [0005] The manufacturing method according to claim 3, characterized in that the initial thickness of the continuous cast slab is 200-250 mm.
    [0006] The manufacturing method according to claim 3, characterized in that each pass of finish rolling is completed at once by a finishing mill unit.
    [0007] The manufacturing method according to claim 6, characterized in that the inlet temperature is kept at 970-1020 °C during finish rolling and the final rolling temperature is 850-900 °C.
    [0008] The manufacturing method according to claim 3, characterized in that the slab subjected to rough rolling by refined grains enters a hot coil box for coiling the head and tail thereof alternately, and then is uncoiled for temperature control and finish rolling in a finish rolling area.
    类似技术:
    公开号 | 公开日 | 专利标题
    US10577671B2|2020-03-03|High-hardness hot-rolled steel product, and a method of manufacturing the same
    US9863015B2|2018-01-09|Manufacturing method for strip casting 550 MPa-grade high strength atmospheric corrosion-resistant steel strip
    EP2824198B1|2019-09-18|Method for producing seamless steel pipe having high-strength and excellent sulfide stress cracking resistance
    WO2016082669A1|2016-06-02|Low-alloy high-strength high-tenacity steel panel and method for manufacturing same
    CN107502821A|2017-12-22|The economical X 70 pipeline steel plate and its manufacture method used under a kind of special think gauge ultra-low temperature surroundings
    EP1918397B1|2016-07-20|Seamless steel pipe for pipe line and method for producing same
    RU2588755C2|2016-07-10|Steel strip with low ratio of yield strength to ultimate strength and high impact strength and method for production thereof
    CA2752741C|2013-07-30|Method for manufacturing seamless pipes
    US9790566B2|2017-10-17|Manufacturing method for strip casting 700 MPa-grade high strength atmospheric corrosion-resistant steel
    CN109280847B|2020-05-29|High-carbon alloy chain tool steel and manufacturing method thereof
    EP1846584B1|2017-05-24|Austenitic steel having high strength and formability method of producing said steel and use thereof
    JP4500688B2|2010-07-14|Steel product manufacturing method
    EP2949774B1|2018-08-08|780 mpa class cold rolled dual-phase strip steel and manufacturing method thereof
    CN108467993B|2020-02-18|Ultra-wide high-toughness hot-rolled thick plate for low-temperature pipeline and production method thereof
    US6846371B2|2005-01-25|Method for making high-strength high-toughness martensitic stainless steel seamless pipe
    CN104805375B|2017-03-01|A kind of ultra thick gauge high tenacity X80 pipeline steel and its manufacture method
    JP2013129879A|2013-07-04|High-strength seamless steel tube for oil well with superior sulfide stress cracking resistance, and method for producing the same
    CN1273635C|2006-09-06|Manufacturing method of cold forming high intensity steel for welded structure
    CN101985722B|2012-07-25|Pipeline steel plate with low yield ratio, fine grains and high strength and production method thereof
    CN104419878B|2017-03-29|Superhigh intensity cold rolling dual phase steel with weatherability and its manufacture method
    CN1318631C|2007-05-30|Method for producing high strength high toughness X80 pipeline steel and its hot-rolled plate
    CN101768698B|2011-06-22|Low cost yield strength 700MPA level non-tempering processing high strength steel plate and manufacturing method thereof
    US8366843B2|2013-02-05|Method of manufacturing a martensitic stainless steel pipe
    CN103866204B|2016-02-17|The large sstrain X80 dual phase sheet steel that the large soft reduction process of a kind of low temperature is produced
    CN101845599B|2012-05-30|Weathering steel and manufacturing method thereof
    同族专利:
    公开号 | 公开日
    CN107502822B|2019-06-14|
    CN107502822A|2017-12-22|
    EP3683326A4|2021-06-02|
    WO2019047587A1|2019-03-14|
    US20200399728A1|2020-12-24|
    引用文献:
    公开号 | 申请日 | 公开日 | 申请人 | 专利标题
    法律状态:
    2019-03-16| STAA| Information on the status of an ep patent application or granted ep patent|Free format text: STATUS: THE INTERNATIONAL PUBLICATION HAS BEEN MADE |
    2020-06-19| STAA| Information on the status of an ep patent application or granted ep patent|Free format text: STATUS: REQUEST FOR EXAMINATION WAS MADE |
    2020-06-19| PUAI| Public reference made under article 153(3) epc to a published international application that has entered the european phase|Free format text: ORIGINAL CODE: 0009012 |
    2020-07-22| 17P| Request for examination filed|Effective date: 20191115 |
    2020-07-22| AK| Designated contracting states|Kind code of ref document: A1 Designated state(s): AL AT BE BG CH CY CZ DE DK EE ES FI FR GB GR HR HU IE IS IT LI LT LU LV MC MK MT NL NO PL PT RO RS SE SI SK SM TR |
    2020-07-22| AX| Request for extension of the european patent|Extension state: BA ME |
    2020-12-16| DAV| Request for validation of the european patent (deleted)|
    2020-12-16| DAX| Request for extension of the european patent (deleted)|
    2021-06-02| A4| Supplementary search report drawn up and despatched|Effective date: 20210504 |
    2021-06-02| RIC1| Information provided on ipc code assigned before grant|Ipc: C22C 38/28 20060101AFI20210428BHEP Ipc: C21D1/18 20060101ALI20210428BHEP Ipc: C21D8/10 20060101ALI20210428BHEP Ipc: C21D8/02 20060101ALI20210428BHEP Ipc: C21D9/46 20060101ALI20210428BHEP Ipc: C22C 38/02 20060101ALI20210428BHEP Ipc: C22C 38/04 20060101ALI20210428BHEP Ipc: C21D9/08 20060101ALN20210428BHEP |
    优先权:
    申请号 | 申请日 | 专利标题
    [返回顶部]