    • 专利摘要:
    The present disclosure is an acryl film formed from a main dope solution including an acryl resin shown in the following formula 1 and CSR particles, and peel strength measured in peeling speed of 0.5mpm is 20gf/2inch or less, tear strength is 6gf or more, has excellent peel strength, thereby visual stain by thickness unevenness is improved, and having excellent tear strength and good brittleness. a and b are an integer and 1 or more.MMA-BMAwherein, MMA is methyl methacrylate unit and BMA is butyl methacrylate unit.
    公开号:EP3680281A1
    申请号:EP18851449.1
    申请日:2018-06-18
    公开日:2020-07-15
    发明作者:Young Soo Kim；Kyung Soo Kim；Ho Jun Lee；Hyun Woo Choi；Hyeok Mo KANG；Hyun Suk Chung；Bong Choon Kim；Jong Hyuk Eun
    申请人:Hyosung Chemical Corp；
    IPC主号:C08J5-00
    专利说明:
    [0001] The present disclosure relates to an acryl film which is easily capable of film forming and film carrying in solvent casting. Background Art
    [0002] Recently a liquid crystal display (LCD), which has low power consumption, operates in low voltage, and has light weight and thin film, is widely used in information display device such as cell phones, personal digital assistant computer monitors, televisions, etc. The information display device according to use is required reliability in harsh environment. For example, a liquid crystal display for car navigation system is required strict temperature and humidity conditions compared to a monitor for conventional television or personal computer as in car temperature and humidity can become very high. Also, in a liquid crystal display, a polarizer is used to make indication possible and as a liquid crystal display is required strict temperature and humidity conditions, a polarizer comprising it is required to have high durability.
    [0003] A polarizer conventionally has a laminated structure of transparent protective films to both sides or one side of a polaroid film comprising a polyvinyl alcohol-based resin having dichroism pigment absorbed and orientated. Moreover, conventionally in the protective film triacetyl cellulose(TAC) is widely used, and the protective film is adhered to a polaroid film through an adhesive comprising aqueous solution of a polyvinyl alcohol-based resin. However, a polarizer laminated protective films comprising triacetyl cellulose, due to high water vaper permeability of triacetyl cellulose, when used in high humidity and heat environment for a long time, polaroid performance can decline or peeling between a protective film and a polaroid film can occur. In order to solve the problem, an acrylic resin film having lower water vaper permeability compared to a triacetyl cellulose film was attempted to be used as a protective film of a polarizer.
    [0004] Existing acrylic protective films have been manufactured by melt casting method, but when manufactured in solvent casting method, there are advantages in environmentally friendly aspects such as thin film, mass-production, resin recycling. The solvent casting method dissolves solvent in an acryl film, presses to T-Die, dries solvent in a belt, and produces a film. Although adding optimized particles, increasing impulse strength, and securing slip property to carry a film are necessary but the process described above is possible. In addition, in this case the particles added should not be melt in solvent or be deformed.
    [0005] Korean Patent No. 1265007 discloses an adhesion type polarizer which doesn't occur light leakage of an image display unit in use environment change, an acrylic polymer comprising an adhesive layer contains an acrylate monomer unit having a way ring structure in desired amount, and the content is determined according to photoelastic factor X of a transparent protective film, and in case of phase difference of a transparent protective film is changed due to environment change such as heating, an adhesive layer is suggested to be adjust to generate phase difference change of an opposite code of a transparent protective film.
    [0006] Korean Patent No. 1114354 discloses a protective film for optical member having a photopolymerization acrylic polymer, an antistatic agent, and an adhesive layer comprising a polymerization initiator composition. In a photopolymerization acrylic polymer which introduced a light activator capable of cross-linked reaction by radical generated in an initiator and in a composition comprising a polymerization initiator in a desired ratio, additionally mixed an antistatic agent in proper amount, can omit aging process during hardening, and discloses a protective film capable of simplification of manufacturing process and antistatic property is excellent during peeling or using.
    [0007] Korean Patent Laid-Open No. 2015-0061591 discloses technology of producing a polarizer protective film, which has excellent adhesion between layers and inhomogeneous tolerance by wind, having a first functional layer formed using a compound comprising cyclic aliphatic hydrocarbon and an ethylene unsaturated double coupler and on top of it a second functional layer formed using a composition comprising urethane acrylate, and by using a fluoro aliphatic contained copolymer having a certain structure on a first functional layer.
    [0008] Japanese Patent Laid-Open No. 2014-240905 discloses technology to produce a polarizer having excellent adhesion, rework, flatness, and visibility, and film thickness and modulus of elasticity are in certain realm, a protective film A which has an acryl resin as the main component and a phase difference film B which has a cellulose derivative having a substituent with ether combination in a polarizer, a glucose frame as the main component are laminated in order, and both film A and B are connected through an ultraviolet hardening type adhesive.
    [0009] Meanwhile, when manufacturing an acrylic protective film in solvent casting method, after film peeling, thickness deviation in texture pattern is occurred, and when coating the surface, visual stain defect is caused, thereby improvement in regard of peel strength is in demand. Also, by improving tear strength, a film having better brittleness is in demand. Disclosure Technical Problem
    [0010] The present disclosure is provided to solve the above technical problems of the related art.
    [0011] The present disclosure is directed to providing an acryl film produced in solvent casting method having excellent peel strength and improving defect in visual stain by thickness unevenness and having excellent tear strength and good brittleness. Technical Solution
    [0012] The present disclosure provides an acryl film formed in solvent casting method from a main dope solution comprising an acryl resin shown in the following formula 1 and a core shell rubber (CSR) particle, wherein the acryl resin comprises, with respect to 100 parts by weight of the acryl resin, methyl methacrylate unit of 70 to 98 parts by weight and butyl methacrylate unit of 2 to 30 parts by weight,wherein peel strength measured in peeling speed of 0.5mpm is 20gf/2inch or less and tear strength is 6gf or more.
    [0013] Wherein, MMA is methyl methacrylate unit and BMA is butyl methacrylate unit.
    [0014] In addition, a core shell rubber according to the present disclosure has a core-shell structure, and a core is composed of 1 kind or 2 or more kinds selected in group comprising styrene butadiene rubber, polybutadiene (PBD), and acrylic ester, and a shell as a graft copolymer is composed of 1 kind or 2 or more kinds selected in group comprising MMA, styrene, and acrylic ester, and the diameter is 100nm to 300nm, and with respect to film solid of 100 parts by weight, comprising the core shell rubber of 1 to 30 parts by weight is preferable.
    [0015] Moreover, a molecular weight of the acryl resin of the present disclosure is preferably 50,000g/mol to 2,500,000g/mol.
    [0016] In addition, a solvent of solvent casting is preferably used mixing halogenation hydrocarbon and alcohol.
    [0017] Also, the present disclosure provides a method of manufacturing an acryl film comprising a step stretching the acryl film formed in solvent casting method from main dope solution comprising an acryl resin shown in the following formula 1 and a core shell rubber,wherein the acryl resin comprises, with respect to 100 parts by weight of the acryl resin, methyl methacrylate unit of 70 to 98 parts by weight and butyl methacrylate unit of 2 to 30 parts by weight,wherein the step comprises a step stretching the acryl film to a stretching ratio of 120% to 140%., at a stretching temperature of 100°C to 200°Cand at a stretching speed of 30% /min to 90%/min when weight ratio of residual solvent before stretching is 5% to 20%. Advantageous Effects
    [0018] The present disclosure provides an acryl film having excellent tear strength and good brittleness which peel strength is improved, thereby there is no defect in visual stain by thickness unevenness of a film. Brief Description of the Drawings
    [0019] FIG. 1 is a view showing a structure of a CSR particle according to an exemplary embodiment of the present disclosure. Detailed Description of the Preferred Embodiments
    [0020] Hereinafter, embodiments of the present disclosure will be described in detail. However, the description provided herein is for better understanding of the present disclosure, and the scope of the present disclosure is not limited thereto.
    [0021] The inventors of the present disclosure have conducted intensive research and various experiments to develop an acryl film excellent in peel strength of a film in solvent casting method and have found that, a molecular weight of an acryl resin in a range of 50,000 to 2,500,000g/mol, by using an acryl resin comprising certain components, obtaining an acryl film having excellent peel strength, and thus when peeling film thickness is in uniformity, and having excellent tear strength and good brittleness, thereby completing the present disclosure.
    [0022] In addition, an acryl film according to the present disclosure formed from main dope solution comprising an acryl resin shown in the following formula 1 and CSR particles, and peel strength measured in peeling speed of 0.5mpm is 20gf/2inch or less and tear strength is 6gf or more.
    [0023] Wherein, MMA is methyl methacrylate unit and BMA is butyl methacrylate unit.
    [0024] First, the description describes an acryl resin of the present disclosure. The acryl resin of the present disclosure is comprises a methyl methacrylate unit and a butyl methacrylate unit, and each of the monomer units is a copolymer resin including a repeating unit form.
    [0025] When considering optical property, transparency, activity, machinability, and productivity, with respect to the acryl resin of 100 parts by weight, it is preferably comprising methyl methacrylate unit of 70 to 98 parts by weight and butyl methacrylate unit of 2 to 30 parts by weight. When content of methyl methacrylate unit is in the range, excellent phase difference and optical property can be obtained. When the content of methyl methacrylate unit is less than 70 parts by weight, optical performance of a protective film declines, and when it is more than 98 parts by weight, uniformity of a protective film thickness decreases.
    [0026] In addition, with respect to 100 parts by weight of the acryl resin, a content of the butyl methacrylate unit is preferably 2 to 30 parts by weight. When the content of butyl methacrylate unit is in the range, preferable optical property can be obtained.
    [0027] In the present disclosure, by adding core-shell rubber particles (CSR) which don't melt and deformed in solvent to the acryl resin, impulse strength of a film is enhanced and film forming and film carrying are facilitated. A core shell rubber comprises a core which is composed of 1 kind or 2 or more kinds selected in group comprising styrene butadiene rubber, polybutadiene (PBD), and acrylic ester, and a shell as a graft copolymer is composed of 1 kind or 2 or more kinds selected in group comprising MMA, styrene, and acrylic ester,
    [0028] Also, a diameter of the core-shell rubber particle (CSR) is preferably 100 to 300nm. When a diameter of CSR is less than 100nm, effect of disclosure is not enough, and when it is more than 300nm, quality of a protective film degrades.
    [0029] Moreover, the core-shell rubber particle (CSR) is preferably 1 parts by weight or more and less than 30 parts by weight with respect to film solid of 100 parts by weight. When the content of the CSR particles of the present disclosure is in the range, a protective film excellent in both hardness and flexibility can be provided.
    [0030] In addition, a molecular weight of the acryl resin of the present disclosure is preferably 50,000 to 2,500,000 g/mol. When the molecular weight is less than 50,000 g/mol, productivity of a film decreases, and when the molecular weight is more than 2,500,000 g/mol, molding process is not easy. Also, a glass transition temperature (Tg) of the acryl resin of the present disclosure is preferably 120°C or more. When the glass transition temperature is less than the range, handling property decreases and which is not preferable.
    [0031] According to the acryl film of the present disclosure, a film thickness is preferably 10 to 60 µm. When the acryl film thickness is less than 10µm, phase difference characteristic can't be expressed enough, and when the acryl film thickness is more than 60µm, it is not proper to use in a polarizer of a thin film.
    [0032] Moreover, the acryl film of the present disclosure defined in the following equation 1 an in-plane retardation Ro and a thickness direction retardation Rth are in condition of 23°C and 55%RH and preferably 10nm or less. Ro = nx − ny ∗ d Rth = nx + ny / 2 − nz ∗ d
    [0033] In the equation 1, d is a film thickness (nm), nx is a maximum refractive index of the film in an in-plane horizontal direction, ny is a maximum refractive index of the film in an in-plane vertical direction of the film, and nz is a maximum refractive index of the film in a thickness direction. When a retardation of the in-plane and the thickness direction is more than 10nm, as an isotropic optical film, the performance is deteriorated.
    [0034] In the acryl film of the present disclosure, peel strength measured in peeling speed of 0.5mpm is preferably 20gf/2inch. Peel strength measured in the same method is more preferably 4gf/2inch to 17gf/2inch. When the peel strength is less than 4gf/2inch, defective occurrence rate in process is high, and when it is more than 17gf/2inch, uniformity in a film declines. Also, in the acryl film of the present disclosure, tear strength is preferably 6gf or more. When the tear strength is less than 6gf, brittleness of a film fails.
    [0035] Hereinafter, preferable manufacturing methods of the present disclosure are described in detail. Preparation of Acryl Resin
    [0036] In order to prepare an acryl film of the present disclosure, firstly a copolymer resin solution of a methyl methacrylate monomer and a butyl methacrylate monomer is prepared. In a copolymer of the monomers preparing method, a copolymer resin preparing method known in the art such as suspension polymerization, emulsified polymerization, bulk polymerization, or solution polymerization, etc. can be used. Preparation of Main Dope Solution including Acryl Resin and Nano Particles
    [0037] According to the present disclosure, a film is prepared by a solvent casting method (solution film forming method). In the solvent casting method, a film is formed by dissolving an acryl resin among casting solvent and obtaining main dope solution, casting the main dope solution on a supporter, and evaporating solvent, Also, the main dope solution preparation is based on mixing the acryl resin and supplementary additive in casting solvent.
    [0038] In case of preparing a film in solvent casting method, in order to prepare main dope solution, for solvent, organic solvent is preferable. For organic solvent, halogenated hydrocarbon is preferably used. For halogenation hydrocarbon, there is chlorinated hydrocarbon, methylene chloride, and chloroform, and among them methylene chloride is the most preferably used.
    [0039] In addition, other organic solvents other than halogenation hydrocarbon may be mixed and used. The organic solvents comprise ester, ketone, ether, alcohol, and hydrocarbon. For ester, methyl formate, ethyl formate, propyl formate, pentyl formate, methyl acylate, ethyl acylate, pentyl acylate, etc. can be used. For ketone, acetone, methyl ethyl ketone, diethyl ketone, diisobutyl ketone, cyclohexanone, methyl cyclohexanone, etc. can be used. For ether, diisopropyl ether, dimethoxy methane, dimethoxy ethane, 1, 4 - dioxane, 1, 3-dioxolan, tetrahydrofuran, anisol, phenetole, etc. can be used. For alcohol, methanol, ethanol, 1-propanol, 2-propanol, 1-butanol, 2-butanol, t-butanol, 1-pentanol, 2-pentanol, 2-methyl-2-buthanol, cyclohexanol, 2-fuloroethanol, 2, 2, 2 - trifluoroethanol, 2, 2, 3, 3 - tetrafluoro-1-propaanol, etc. can be used.
    [0040] More preferably methylene chloride is used as a main solvent and alcohol can be used as a minor solvent. Specifically, mixed solvent is preferably mixed in the mixture ratio of methylene chloride and alcohol of 80 : 20 to 95 : 5 weight ratio. Also, mixed solvent is more preferably mixed in the mixture ratio of methylene chloride and methanol of 85 : 15.
    [0041] In the acryl film preparing method, auxiliary additives may be more used. In the main dope solution, in each preparing process, according to use the auxiliary additives such as an ultraviolet light inhibitor, fine particles, an infrared light absorber, a release agent, etc. can be added. Specific types of such the additives are not limited if ordinarily used in the art, and the content is preferably used in the range not declining property of the film. Also, the time to add additive is determined according to types of additive. A process of lastly adding additive in dope preparation may be implemented.
    [0042] For additive of the present disclosure, core-shell rubber particles (CSR) in MMA material were used, and example of the structure is shown in FIG. 1.
    [0043] The main dope solution obtained by the method described above may be prepared in room temperature, in high temperature, or in low temperature dissolution method. Film Formation Process
    [0044] In solvent casting method of the present disclosure, main dope solution is poured from a nozzle of pressuring die on a metal supporter, leaving for a predetermined time, and a film in semi-drying state is formed. Then the film is peeled from the metal supporter, carried to a drying system, and removed the solvent by drying. Also, the film in drying state is performed a first axis stretching process or a second stretching process. By performing the stretching step, film uniformity and phase difference value of the protective film may increase.
    [0045] Specifically, the obtained main dope solution casts on a supporter through casting die and forms an acryl sheet. The support serves to evaporate the solvent present in the casting solution to form an acrylic film while transferring the sheet casting solution extruded from the die. The supporter or the surface is composed of metal, and thus it is preferable to bright finish the surface, and for the supporter, a steel belt such as a stainless steel belt, etc. is preferably used. Also, in regard of surface temperature of the metal supporter, if temperature is higher, evaporation of solvent existing in the casting undiluted solution is faster, but if the temperature is too high, there are problems such as foaming of casting undiluted solution or deteriorating flatness, and even though it is different according to solvent, 0 to 75°C is preferable and 5 to 45°C is more preferable. For the supporter, a metal supporter in plane conveyer belt form may be used.
    [0046] Moreover, the acryl sheet formed in the method described above goes through a stretching step in tender, and in pre-heating process, a glass transition temperature (Tg) of acryl flake is 100°C or more. The acryl film of the present disclosure goes through a stretchi ngstep in tender in the condition described above, left and right side ends of the film in which a surface of the film is damaged by a clip or a pin of tender are removed, and the film is prepared through a drying step.
    [0047] In case of using a tender stretching device, it is preferable to use a device capable of controlling the gripping length of the film from the left and right by the right and left gripping means of the tenter.
    [0048] In the case of using the tenter stretching device, the stretching operation may be conducted multi-stepwise and it is also preferred to perform biaxial stretching in the casting direction and in the width direction. Further, biaxial stretching may be conducted simultaneously or stepwise. In the case of "stepwise", it is feasible to perform stretching successively in different directions or it is also feasible that stretching in one direction is divided into multiple steps and stretching in a different direction is applied to any of the steps. Simultaneous biaxial-stretching includes stretching in one direction and relaxing tension in the other direction to be shrinked. A stretching ratio of simultaneous biaxial-stretching is preferably from 1.01 to 2.0 fold for both of the width direction and the longitudinal direction.
    [0049] A drying means generally blows hot air onto the both surfaces of the web, but a heating means by applying microweb in place of wind is also available. However, too rapid drying can easily damage flatness of a completed film.
    [0050] According to the present disclosure manufactured by the method described above, peel strength measured in peeling speed of 0.5mpm is 20gf/2inch or less, and tear strength is 6gf or more.
    [0051] Hereinafter, the present disclosure will be described in detail with reference to the following examples. However, the examples provided herein are for illustrating the present disclosure, and the scope of the present disclosure is not limited thereto. Example 1<Step 1> Acryl Resin Preparation
    [0052] A content of butyl methacrylate unit was 5 parts by weight, and an acryl shown in the following formula 1 was used.
    [0053] A main dope solution comprising methylene chloride of 65.18 parts by weight, methanol of 14.31 parts by weight, the acryl resin of 16.48 parts by weight, CSR (Kaneka Co. acryl type M-210 grade) of 3.69 parts by weight, Tinvuin 928 (BASF Co.) which is an ultraviolet absorber of 0.33 parts by weight, and Silica of 0.01 parts by weight was prepared. <Step 3> Film Forming Process
    [0054] Then, the main dope solution was cast on a steel belt using an applicator (width 2inch), until arrived to constant residual solvent, dried in room temperature, and a film was formed. Example 2 to 3
    [0055] An acryl film was manufactured in the same manner as in Example 1, except that an acryl resin of BMA content of an acryl resin is 10 weight% (Example 2) and 15 weight% (Example 3) was used. Comparative Example 1
    [0056] An acryl film was manufactured in the same manner as in Example 1, except that CSR was not added. Comparative Example 2
    [0057] An acryl film was manufactured in the same manner as in Example 1, except that an acryl resin shown in the following Formula 2 was used.
    [0058] An acryl film was manufactured in the same manner as in Comparative Example 2, except that the CSR was not added. 1. Peel Strength Evaluation
    [0059] For the films of the Example 1 to 3 and Comparative Example 1 to 3, samples of 50mm size was prepared, a peel strength was evaluated by forwarding a plate and by using AR-1000(Chemsultants International Inc.) equipment, the results are shown in Table 1. 2. Phase difference
    [0060] For the films of the Example 1 to 3 and Comparative Example 1 to 3, by using AxoScan (OPMF-1 Axometrics Co.) optical measurement equipment, in environmental conditions of 23°C and 55 %RH, in wavelength of 590nm, phase difference value Ro and Rth were measured, and the results are shown in Table 1. 3. Visual Stain Evaluation
    [0061] For the films of the Example 1 to 3 and Comparative Example 1 to 3, visual stain was evaluated with the naked eye. 4. Tear Strength Evaluation
    [0062] For the films of the Example 1 to 3 and Comparative Example 1 to 3, by using the following standard and equipment, tear strength was measured, and the results are shown in Table 1. Test Standard: Elmendorf method (KS M ISO 6383-2:2010) plastic film/ sheet tear resistance measuring method Manufacturer and model name: LabThink Co. SLY-SI model Table 1 Specimen Recipe (film solid criteria) Peel strength (gf/2inch) Phase difference Visual stain Brittleness Tear strength (gf) resin CSR (parts by weight) Plane direction (nm) Thickness direction (nm) Example1 MMA-BMA (content of BMA 5 parts by weight) 3.69 16 1 5 no 9.2 Example2 MMA-BMA (content of BMA 10 parts by weight) 3.69 12 2 7 no 9.1 Example3 MMA-BMA (content of BMA 15 parts by weight) 3.69 6 2 8 no 9.5 Comparative Example 1 MMA-BMA (content of BMA 5 parts by weight) 0 3 2 8 no 4.3 Comparative Example 2 General acryl 3.69 70 1 5 no 5.3 Comparative Example 3 General acryl 0 77 5 11 no 3.5
    [0063] As described in Table 1, when using the acryl resin and CSR particle suggested in the present disclosure, a high quality isotropic optical film having excellent peel strength, and thus there is no visual stain problem, and having excellent tear strength and good brittleness can be manufactured. If a CSR particle is not added, tear strength declines, and if a general acryl resin is used, peel strength is high so it is not good.
    权利要求:
    Claims (5)
    [0001] An acryl film formed in solvent casting method from a main dope solution comprising an acryl resin shown in the following formula 1 and a core shell rubber (CSR) particle,wherein the acryl resin comprises, with respect to 100 parts by weight of the acryl resin, methyl methacrylate unit of 70 to 98 parts by weight and butyl methacrylate unit of 2 to 30 parts by weight,wherein peel strength measured in peeling speed of 0.5mpm is 20gf/2inch or less and tear strength is 6gf or more. Formula 1
    [0002] The acryl film of claim 1, wherein the core shell rubber has a core-shell structure, and a core is composed of 1 kind or 2 or more kinds selected in group comprising styrene butadiene rubber, polybutadiene (PBD), and acrylic ester, and a shell as a graft copolymer is composed of 1 kind or 2 or more kinds selected in group comprising MMA, styrene, and acrylic ester, and the diameter is 100nm to 300nm, and per 100 weight of film solid, comprising 1 weight to 30 weight.
    [0003] The acryl film of claim 1, wherein a molecular weight of the acryl resin is 50,000g/mol to 2,500,000g/mol.
    [0004] The acryl film of claim 1, wherein a solvent of the solvent casting is used mixing halogenation hydrocarbon and alcohol.
    [0005] A method of manufacturing an acryl film comprising a step stretching the acryl film formed in solvent casting method from a main dope solution comprising an acryl resin shown in the following formula 1 and a core shell rubber,wherein the acryl resin comprises, with respect to 100 parts by weight of the acryl resin, methyl methacrylate unit of 70 to 98 parts by weight and butyl methacrylate unit of 2 to 30 parts by weight,wherein the step comprises a step stretching the acryl film to a stretching ratio of 120% to 140%., at a stretching temperature of 100°C to 200°C and at a stretching speed of 30% /min to 90%/min when weight ratio of residual solvent before stretching is 5% to 20%.a and b are an integer and 1 or more.MMA-BMAwherein, MMA is methyl methacrylate unit and BMA is butyl methacrylate unit.
    类似技术:
    公开号 | 公开日 | 专利标题
    US20170329050A1|2017-11-16|Optical laminate
    KR101547717B1|2015-09-07|Adhesive for polarizing plate, polarizing plate comprising the same and method for preparing thereof
    JP5324316B2|2013-10-23|Adhesive polarizing plate, image display device, and manufacturing method thereof
    TWI441733B|2014-06-21|Method for manufacturing multilayer laminated film
    JP4938632B2|2012-05-23|Liquid crystal panel and liquid crystal display device
    CN102272640B|2013-09-11|Optical film and liquid crystal display device comprising the same
    JP4928529B2|2012-05-09|Manufacturing method of polarizing plate, polarizing plate, optical film, and image display device
    TWI701466B|2020-08-11|Polarizng plate with protect film and laminated article containing the polarizing plate
    JP4587307B2|2010-11-24|Polyvinyl alcohol film, polarizing film, polarizing plate
    US9040129B2|2015-05-26|Protective film of polarizer, polarizer and method for producing it, and liquid crystal display device
    KR101407820B1|2014-06-17|Method for producing optical film, optical film, polarizing plate and display
    TWI411512B|2013-10-11|A method of manufacturing an optical film in which a concavo-convex structure is provided, an optical film, a gate grid polarizer, and a retardation film
    TWI398677B|2013-06-11|A polarizing element protective film, a polarizing plate, and an image display device
    US9864115B2|2018-01-09|Polarizing plate and method for manufacturing polarizing plate
    CN102754002B|2015-04-29|Methods for producing polarizing laminate film and polarizing plate
    EP2272901B1|2014-08-06|Optical film, and an electronic information device comprising the same
    TWI496672B|2015-08-21|Method for manufacturing polyvinyl alcohol film
    JP4751312B2|2011-08-17|Optical film, polarizing plate, and image display device
    CN103483987B|2018-05-11|Anchor layer is formed with coating fluid, band adhesive phase optical thin film and its manufacture method
    EP2233514B1|2013-01-02|Optical film and electronic information device employing the same
    KR101744381B1|2017-06-07|Polarizing plate protective film, polarizing plate, and liquid crystal display
    JP2008020891A|2008-01-31|Polarizing plate, image display device, and method of manufacturing polarizing plate
    EP2921902A1|2015-09-23|Liquid crystal panel and polarizer laminate used in said liquid crystal panel
    TWI449970B|2014-08-21|Composite polarizing plate and liquid crystal display device using the same
    JP2007316603A|2007-12-06|Composite polarizing plate and liquid crystal display device using the same
    同族专利:
    公开号 | 公开日
    US10934404B2|2021-03-02|
    JP2019535872A|2019-12-12|
    KR20190027012A|2019-03-14|
    EP3680281A4|2021-06-02|
    TW201912705A|2019-04-01|
    TWI669334B|2019-08-21|
    US20190292339A1|2019-09-26|
    WO2019045236A1|2019-03-07|
    CN109843993A|2019-06-04|
    引用文献:
    公开号 | 申请日 | 公开日 | 申请人 | 专利标题
    法律状态:
    2019-03-09| STAA| Information on the status of an ep patent application or granted ep patent|Free format text: STATUS: THE INTERNATIONAL PUBLICATION HAS BEEN MADE |
    2020-06-12| STAA| Information on the status of an ep patent application or granted ep patent|Free format text: STATUS: REQUEST FOR EXAMINATION WAS MADE |
    2020-06-12| PUAI| Public reference made under article 153(3) epc to a published international application that has entered the european phase|Free format text: ORIGINAL CODE: 0009012 |
    2020-07-15| AX| Request for extension of the european patent|Extension state: BA ME |
    2020-07-15| 17P| Request for examination filed|Effective date: 20190415 |
    2020-07-15| AK| Designated contracting states|Kind code of ref document: A1 Designated state(s): AL AT BE BG CH CY CZ DE DK EE ES FI FR GB GR HR HU IE IS IT LI LT LU LV MC MK MT NL NO PL PT RO RS SE SI SK SM TR |
    2020-12-09| DAV| Request for validation of the european patent (deleted)|
    2020-12-09| DAX| Request for extension of the european patent (deleted)|
    2021-01-27| RIN1| Information on inventor provided before grant (corrected)|Inventor name: KANG, HYEOK MO Inventor name: KIM, KYUNG SOO Inventor name: LEE, HO JUN Inventor name: CHOI, HYUN WOO Inventor name: EUN, JONG HYUK Inventor name: KIM, YOUNG SOO Inventor name: KIM, BONG CHOON Inventor name: CHUNG, HYUN SUK |
    2021-06-02| A4| Supplementary search report drawn up and despatched|Effective date: 20210506 |
    2021-06-02| RIC1| Information provided on ipc code assigned before grant|Ipc: B29C 41/28 20060101AFI20210429BHEP Ipc: B29C 55/12 20060101ALI20210429BHEP Ipc: C08J5/18 20060101ALI20210429BHEP Ipc: C08L 33/12 20060101ALI20210429BHEP Ipc: C08L 51/04 20060101ALI20210429BHEP Ipc: C08L 51/00 20060101ALI20210429BHEP Ipc: B29D7/01 20060101ALI20210429BHEP |
    优先权: