    • 专利摘要:
    A container (1) for foodstuff is disclosed, comprising a tray (2) formed from a sheet of material comprising one or more layers, wherein the material of each of the layers comprises at least 85 % of amorphous polyethylene terephthalate (APET), said tray comprising a bottom part (4), one or more side walls (5) and a peripheral sealing rim (6) at its top, said sealing rim having a substantially flat upward facing sealing surface (7), wherein, at least in the top layer of the formed tray, the material is modified so that the APET therein has an increased softness at relevant sealing temperatures, and wherein the surface energy of the top layer is reduced by means of one or more surface energy changing agents. The container may further comprise a lidding film (3), which is bonded to the tray by means of a gas-proof seal. Furthermore, a method of producing such a tray is disclosed.
    公开号:DK201670703A1
    申请号:DKP201670703
    申请日:2016-09-14
    公开日:2017-08-07
    发明作者:Ram Søren Sarusie；Carsten Linding Borregaard Lauridsen
    申请人:R Faerch Plast As；
    IPC主号:
    专利说明:

    Sealed container for foodstuffs The present invention relates to a sealed container for foodstuffs.
    Background of the invention
    In the food industry, it is well known to pack different kinds of foodstuff into sealed containers made from plastic materials. Such containers may typically consist of some form of tray, which is sealed with a lid or a lidding film to protect the foodstuff inside the tray.
    Often, the tray and the lid or lidding film are made from amorphous polyethylene terephthalate (APET). This material is preferred due to its characteristics, which make it very suitable for storage of foodstuffs, for instance a high transparency and a significantly higher impermeability to oxygen than other plastic materials traditionally used for making trays, such as polystyrene (PS) or polypropylene (PP).
    Depending on the type of foodstuffs to be packed and stored in the containers, there are different requirements to be met by the seal. In general, the seal must be able to withstand cooling, storage and transportation without the lid or lidding film loosening from the tray. For some kinds of foodstuff such as fresh meat, the seal must also be gas-proof in order to keep a modified atmosphere inside the container for a specifi ed number of days, in which the foodstuff must be able to be stored before use.
    If the sealing media in the tray as well as in the lid or lidding film is APET, such a seal can be obtained by heating the lid or lidding film and the sealing rim of the tray, to whi ch the lid or li dding film is to be seal ed, to a temperature of around 180 °C and pressing the two parts tightly together for a short period of time. This heat sealing procedure does not involve actual melting of the APET, but the material becomes soft and secondary chemical bonds occur between the sealing media of the tray and the sealing media of the lid or lidding film.
    In the APET industry, it is common to employ some kind of surface modification due to the inherent adhesion between two APET surfaces. The surface modification reduces the coefficient of friction (CoF) on the outer layers of an APET tray in order to obtain proper de-nesting. Surface modification for de-nesting is done either by adding internal or external slip agents, which in both cases act on the surfaces.
    External slip agents are typically pøl ydimethylsiloxane (PDMS) or other functionalised siloxanes. These are commonly referred to as “silicones”. As a result of their physico-chemical nature, further to reducing CoF, these will also lower the surface energy of the APET surface.
    Internal slip agents for APET are typically fatty' amides, e.g. erucamide (cis-13-docosenoarnide), behenami.de (docosanamide), oleamide (9-octadecenoamide) or other compounds which, like the fatty amides, tend to migrate to the surface, resulting in a reduction of CoF. The driving force for these compounds to migrate towards the surface is their higher hydrophobicity compared to APET. Thus, the migration of these compounds to the surface, in addition to lowering the CoF, will also result in a lowering of the surface energy.
    To summarize, all slip agents, internal as well as external, intended for APET not only lower the Co F, but also lower the surface energy of the APET surface. Hence, these compounds will hereinafter be collectively referred to as “surface energy changing agents”.
    It is known in the food packaging industry that it is beneficial for the sealing performance to use highly modified PET as sealing top layer. PET modification is done by modifying the backbone of the polyethylene terephthalate polymer through the incorporation of a comonomer, such as isophthalic acid (IPA), cycloh.exanedimeth.anol (CHDM) or diethyleneglycol (DEG). These modifications make the materials softer at relevant sealing temperatures, which facilitates the bonding between the lid or lidding film and the sealing surface of the tray.
    By “highly modifi ed PET” is meant a PET, in which the degree of modification is substantially higher than in standard PET grades intended for bottles and trays, e.g. in the case of IP A modification, substantially higher than 1.6-1.8 mole %, which is considered an industry standard. A well-known problem connected to heat sealing involving APET sealing media is that if the sealing rim of the fray is contaminated with even rather small amounts of food substances, for instance meat juice when packing fresh meat, the seal will not be gas-proof. This means that the seal cannot keep the modified atmosphere inside the container for the specifi ed amount of time, which results in accelerated decay of the foodstuff stored in the container.
    The most used solutions to these problems involve the use of multi-layer plastic sheets or film for producing the tray and the lid or lidding film. Besides APET, these mul ti-layer sh eets or film comprise a sealing layer of another type of plastic material, which is more meltable than APET, such as PP or (most typical) PE, which is laminated, extrusion coated or co-extruded onto the APET layer. If the other material is PE, the trays are known as APET-PE trays.
    The use of such multi-layer materials with a sealing layer of another plastic material solves the above-specified problems because, unlike APET, these materials do actually melt during the heat sealing process at a temperature, which is low er than the one needed for heat sealing APET. This means that heat sealing of these other plastic materials results in stronger and tighter seals than heat sealing of ΑΡΕΙ". In fact, if they are made properly, these seals will be made gas-proof even if the sealing rim should be contaminated as described above.
    From a sealing point of view, the above-described kind of solutions is ideal. However, it has some production-related drawbacks. When the trays are thermoformed, 30-50 % of the plastic sheet, from which they are formed, do not become a part of a tray but end up as so-called skeletal waste. In order to reduce the waste from the production, this skeletal waste is traditionally reused in extrusion of new sheets. This is no problem, if the sheet is made from pure or highly modified APET. In the case of multi-layer sheets, how'ever, the APET will be contaminated with the material from the sealing layer, typically PE.
    This contamination of the reused APET material causes serious production problems in the extrusion and thermoforming processes relating to opacity, sagging and brittleness of the resulting trays and lids or lidding film. Thus, the use of PE or another material as a sealing layer along with the APET layer in a multi-layer sheet either results in a decreased quality of the produced containers or in an increased amount of waste, which add costs to the production. These drawbacks also inhibi t post-consumer recycling of multi-material (APET-PE) trays, the PE material contaminating the recycling material stream. A highly modified PET may also be used as sealing layer. However, this material is rather expensive and requires, when used in applications sensitive to contamination, higher pressure and temperature during the sealing process than the other mentioned materials. Thus, the use of a highly modified PET as sealing layer reduces the prod uction rate and increases the costs of the sealing equipment. Furthermore, even with the required process parameters, highly modified PET is still sensitive to contamination and sealing rim warpage.
    Having clean surfaces is advantageous for obtaining good heat sealing between APET surfaces because contaminan ts, like meat juice, reduce the sealing performance. in fact, even the use of slip agents (internal or external) reduces the sealing performance. Consequently, silicones are not used in applications with high heat sealing requirements.
    With internal (migrating) slip agents, however, it is possible to precisely add a quantity, which is evenly distributed and at the same time sufficiently high to give the desired slip performance and not unnecessarily high anywhere on the surface, which would have a detrimental effect on the sealing performance.
    Brief description of the invention
    It is an object of the present invention to provide containers that overcome the above-mentioned problems without sacrificing the advantages related to the use of APEX as the basis material of trays as well as lidding films.
    The present invention relates to a container for foodstuff, said container comprising a tray formed from a sheet of material comprising one or more layers, wherein the material of each of the layers of the formed tray comprises at least 85 % of amorphous polyethylene terephthalate (APEX), said tray comprising a bottom part, one or more side walls and a peripheral sealing rim at its top, said sealing rim having a substantially flat upward facing sealing surface, wherein, at least in the top layer of the formed tray, i.e. the layer forming the sealing surface, the material is modified in such a way that the APET therein has an increased softness at relevant sealing temperatures, typically between 120 °C and 200 °C, and wherein the surface is modified by means of one or more surface energy changing agents, for instance in the form of intern al and/or external slip agents, so that the surface energy of the top layer is reduced.
    The combination of a relatively high level of backbone modification of the top layer material and a reduction of the surface energy of the top layer makes it possible to obtain gas-proof seals with trays made of an APET without any sealing layers of PE or the like, even if the sealing rim is contaminated with meat juice or the like as described above.
    This is counter-intuitive and surprising, because the use of externally applied surface energy changing agents, such as for instance silicones, or abnormally high contents of internal slip agents, which results in a reduction of the surface energy, is well-known to have a detrimental influence on the seal ing properties if the polyester material within the top layer is not or only slightly modified, which is usually the case for PET intended for bottle or tray production. In addition, even with a highly modified PET as the top layer material, but without a reduction of the surface energy, the sealing properties are not sufficient to satisfy the high demands of the fresh meat market. Only when the highly modified PET and the reduction of surface energy are combined, a solution is obtained, which can comply with the high demands of this market when it comes to performance and economic considerations.
    It should be noticed that by the expression “amorphous polyethylene terephthalate” is meant polyethylene terephthalate, which is essentially amorphous in the sense that proper steps have been taken in order to minimise the rate of the crystallisation that, to some degree, will always take place in the material. Such steps include the selection of a proper type of PET (in relation to the contents of comonomers in the material) and minimising of the peri od of tim e, in which the material has a temperature, at which there is a significant rate of crystallisation.
    In an embodiment of the invention, the modification of the material of at least the top layer is obtained by modifying the backbone of the polyethylene terephthalate polymer therein through the incorporation of a comonomer, such as isophthalic acid (IPA), cyclohexanedimethanol (CHDM) or diethyleneglycol (DEG).
    In an embodiment of the invention, the modified APET material, at least in the top layer, comprises more than 4 mole %, preferably more than 6 mole %, most preferably more than 8 mole %, of monomers other than ethyl ene glycol or terephthalic acid residues.
    The modification of the APET material may be obtained by using individual PET polymers, each with a mix of different backbone modifications, by blending a number of different PET polymers, each being modified with a given backbone modification, or by any combination thereof.
    The application of such modifications of the APET material to the specified levels has proved to be optimal for obtaining the desired positive effect on the sealing properties when combined with the reduction of the surface energy of the top layer. These levels of modification are significantly higher than the modification levels typically used for meeting other objectives, such as keeping the crystallisation rate low for facilitating the production of transparent trays.
    In an embodiment of the invention, a surface energy changing agent is applied at least onto the sealing surface along the full circumference of the tray.
    In an embodimen t of the invention, the externally applied surface energy changing agent is a siloxane type of polymer, such as a silicone in the form of polydimethylsiloxane (PDMS) or a functionalised siloxane.
    The application of an external surface energy changing agent, such as a silicone, has proven to result in significantly improved sealing properties when combined with the above-described modification of the material of the top layer, which is surprising because application of silicones and the like is known to normally be detrimental to the heat sealing properties.
    In an embodiment of the invention, a surface energy changing agent, for instance in the form of a fatty amide slip masterbatch, is incorporated in the formulation during extrusion of the sheet.
    Similar effects as with externally applied surface energy changing agents can be obtained by reducing the surface energy through the incorporation of a surface energy changing agent within the material.
    In an embodiment of the invention , the external and/or internal application of surface energy changing agent(s) cause(s) the surface energy of the top layer to be reduced by at least 20 %, preferably by at least 30 %, most preferably by at least 40 %.
    The above-described levels of reduction of the surface energy have proved to be sufficient for obtaining the desired positive effect on the heat sealing properties.
    In an embodiment of the invention, the material of each of the layers of the formed tray has an intrinsic viscosity between 0.6 dl/'g and 1.1 dl/g, preferably between 0.7 dl/g and 0.9 dl/g, most preferably between 0.7 dl/g and 0.8 dl/g.
    The unit “dl/g” uses for quantifying the intrinsic viscosity is an abbreviation of the expression “decilitres per gram”, otherwise known as inverse concentration.
    The use of PET with intrinsic viscosities within these ranges has proved to be advantageous in that it gives a good balance between processability and product properties, such as transparency and impact properties.
    In an embodiment of the invention , the thickness of material of the tray is between 200 pm and 1200 pm.
    If the thickness of material of the tray is chosen within this range, the requirements regarding stiffness, barrier properties and impact resistance are all fulfilled.
    In an embodiment of the inventi on, the contain er further comprises a lidding film, which is bonded to the tray by a gas-proof seal formed along the sealing rim.
    In an embodiment of the invention, the lidding film is soft and flexible, having a thickness of material between 10 μηι and 200 μτη, preferably between 15 μτη and 150 μηι.
    For economic and manufacturing reasons, it can be advantageous to use lidding films which are soft and flexible.
    If the thickness of material of the soft and flexible lidding film is chosen within this range, the requirements regarding strength and barrier properties are all fulfilled.
    In an embodiment of the inventi on, the li dding film comprises at least on e layer of polyethylene terephthalate.
    The use of PET in the lidding film is advantageous due to the material characteristics, which make it very suitable for storage of foodstuffs, such as a high transparency and a high impermeability to oxygen as already mentioned above.
    The at least one PET' layer may, for instance, consist of bi-axially oriented PET (BO-PET), a PET sealing layer and/or other functional layers relating to barrier properties, puncture resistance, etc. in an aspect of the invention, it relates to a method of producing a container for foodstuff, said method comprising the steps of: extruding a sheet of material comprising one or more layers, wherein the material of each of the layers comprises at least 85 % of amorphous polyethylene terephthalate (APET) and at least the material of a top layer of the sheet is modified in such a way that the APET therein has an increased softness at relevant sealing temperatures, typically between 1.20 °C and 200 °C, and wherein the surface is modified by means of one or more surface energy changing agents, for instance in the form of internal and/or external slip agents, so that the surface energy of the top layer is reduced; and forming, for instance by thermoforming, a tray made from the extruded sheet of material, said tray comprising a bottom part, one or more side walls and a peripheral sealing rim at its top, said sealing rim having a substantially flat upward facing sealing surface formed by the top layer of the sheet of material.
    This method results in a tray with the advantages described above.
    Thermoforming is known to be a cost-efficient, fast and reliable way of forming different kinds of pails from plastic materials as the ones used for the present invention.
    In an embodiment of the invention, the modification of the material of at least the top layer is obtained by modifying the backbone of the polyethyl ene terephthalate polymer therein through the incorporation of a comonomer, such as isophthalic acid (IPA), cyclohexanedimethanol (CHDM) or diethyleneglycol (DEG).
    In an embodiment of the invention, the reduction of the surface energy is obtained at least partly by applying a surface energy changing agent, for instance in the form of a siloxane type of polymer, such as a silicone, at least onto the sealing surface of the formed tray along the full circumference of the tray, for instance by means of roll coating or immersion in a bath containing the surface energy changing agent.
    Roll coating and dip coating are well-known and reliable methods for applying materials to a given surface.
    In an embodiment of the invention, the reduction of the surface energy is obtained at least partly through the incorporation of a surface energy changing agent, for instance in the form of a fatty amide slip masterbatch, in the formulation during the extrusion of the sheet.
    In an embodiment of the invention, the method further comprises a step of bonding a lidding film to the sealing surface of the tray by means of a process that involves the use of heat and pressure.
    Bonding a lidding film to the sealing surface by means of a process using heat and pressure enables for obtaining a gas-proof seal between the tray and the lidding film, even if the sealing rim is contaminated with meat j uice or the like.
    Figures A few exemplary embodiments of the invention are described more in detail in the following with reference to the figures of which
    Fig. 1 shows an exploded view of a container according to an embodiment of the in vention,
    Fig.2a showrs a cross-sectional view' of a container according to an embodiment of the invention,
    Fig. 2b shows an enlarged detail of Fig. 2a,
    Fig. 3 a show s a top view of a container according to an embodiment of the invention,
    Fig. 3b shows a side view' of the same con tainer as shown in Fig. 3 a, and
    Fig. 4 i llustrates schematically an apparatus for making trays of containers according to an embodiment of the invention.
    Detailed description of the invention
    The present invention relates to a container 1 for foodstuffs comprising a tray 2 and potentially also a lidding film 3 and to a method for producing such a container 1.
    The tray 2 is made of APET, which can be transparent (natural) or coloured (either opaque or transparent). Thus, it is a full polyester tray 2 with sealing properties matching the ones of the APET-PE solutions currently dominating the market.
    Typically, the tray 2 is thermo formed from a sheet of material. This sheet may comprise one or more layers, typical ly three l ayers, wherein th e backbone of the APET within the material of at least the top layer is highly modified through the incorporation of a comonomer, such as isophthalic acid (IPA), cyclohexanedimethanol (CHDM ) or diethyleneglycol (DEG).
    The resulting modification of the APET material may be obtained by using individual PET polymers, each with a mix of different backbone modifications, by blending a number of different PET polymers, each being modified with a given backbone modification, or by any combination thereof.
    This modification of the top layer material results in an increase of the softness of the APET at relevant sealing temperatures. In typical embodiments of the invention, the carboxylic acid component of the APET is modifi ed to comprise a certain amount of isophthalic acid residues and/or the hydroxyl component of the APET is modified to comprise a certain amount of cyclohexanedimethanol and/or diethyleneglycol residues.
    In order to obtain the desired sealing properties, the above-described modification of the top layer material must be combined with a reduction of the surface energy on the surface of the highly modified APET top layer of the tray 2. The reduction of the surface energy has proved to increase the sealing performance significantly when combined with highly modified APET. Two fundamentally different ways of changing the surface energy are by applying an external surface energy changing agent on top of the top layer and/or by adding a surface energy changing agent intern ally in the formulation d uring extrusion of the sheet,
    Especially, this reduction of the surface energy is crucial on the sealing rim 6 of the tray 2, but it is not necessarily limited to this area. This can be accomplished by either externally applying a silicone (or more correctly a siloxane type of polymer) on th e top layer of the sheet or the tray 2, for instance using a roll as illustrated in Fig. 4 and described below, or by adding abnormally high amounts of internal slip agents through a masterbatch in the formulation for the extruded sheet as compared to the amounts necessary for obtaining the desired slip property'. A well-known method to change the surface energy is to apply a si licone onto the surface of the top layer material. Within the packaging industry, this is normally done in order to reduce the coefficient of friction of the surface for de-nesting purposes. Typically, the externally applied silicone would be po 1 ydi methyl si lox ane (PDMS) or a functionalized siloxane.
    External application of a silicone via for instance a silicone bath is generally avoided on APET trays used for heat seal purposes due to the reduction of the sealing performance of the APET rel ated thereto. It is a well-known and general knowledge that external employment of a silicone on A PET trays results in reduced sealing properties thereof. A lowering of the surface energy on the surface of a polyester can also be achieved internally by incorporating an internal slip masterbatch in the formulation during the extrusion of the sheet. This method is commonly used to reduce the coefficient of friction of the surface for de-nesting purposes. However, just like external application of a silicone, the incorporation of a slip masterbatch changes the surface energy of the polyester by introducing molecules of lower polarity than PET at the interface with the air.
    It is believed that the reduced surface energy of the polyester top layer is beneficial by rendering the surface more hydrophobic and, thus, increasing the contact angle of water-like droplets including fresh meat juice. As a derived effect of this, it may also red uce the amount of meat j uice contaminant deposited on the sealing surface due to the more hydrophobic nature of the surface.
    The top layer may also comprise some additional material(s) making the sheet easier to unwind and the stacked trays easier to separate from each other.
    For manufacturing purposes, the molecular length of the PET defined by the so-called intrinsic viscosity is ideally between 0.7 dl/g and 0.8 dl/g. An intrinsic viscosity between 0.7 dl/g and 0.9 dl/g is acceptable, whereas PET materials having intrinsic viscosities below 0.6 dl/g or above 1.1 dl/g are not relevant for this purpose.
    Fig. illustrates an exploded view of a container 1 according to an embodiment of the invention, in which an externally applied surface energy changing agent 8 is used. The illustrated container 1 consists of two main parts, namely a tray 2 and a lidding film 3.
    The tray 2 comprises a bottom part 4, a number of side walls 5 and a peripheral sealing rim 6 at its top. The sealing rim 6 has an upward facing and flat sealing surface 7, onto which is applied a surface energy changing agent 8 extending along the frill circumference of the tray 2.
    In the shown embodiment, the tray 2 has four straight side walls 5 connected to each other by rounded comers. How ever, the tray 2 may be of any shape, such as for instance circular (with one single, curved side wall) or triangular (with three straight side wails).
    In the illustrated embodiment, the surface energy changing agent 8 is placed at least on the sealing surface 7 of the sealing rim 6, typically by roll coating, so that none of the surface energy changing agent 8 will end up on the skeletal waste from the thermoforming or inside the tray 2 after sealing of the container 1.
    As mentioned above, other embodiments of the invention may include external application of a surface energy changing agent 8 by other means onto the sheet of material, from which the container 1 is formed, such as for instance a silicone bath prior to the thermoforming of the container 1, as well as internal application of a surface energy changing agent, for instance through the incorporation of a suitable masterbatch in the formulation during extrusion of the sheet.
    The shelf life of foodstuff packed in a container 1 according to the invention is similar to the shelf life obtained when using APET-PE trays. Due to the sealing properties achieved by the combination of highly modified top layer material and reduced surface energy as defined by the present invention, the seal of the container 1 is as secure as the ones of APET-PE trays. Furthermore, the sealing can be made at temperatures, which cause no warping of the APET material of the tray 2. Thus, the bonded area is as gas-proof for the modified atmosphere, e.g. nitrogen, oxygen and/or carbon dioxide, surrounding the foodstuff as in any APET-PE seal.
    Test have shown, that containers 1 according to the invention have a weld strength less than 0.6 bar (absolute pressure) measured in a vacuum tank, which is a common way of testing the seal strength of containers used in the food packaging industry. This means that the seal can withstand an internal overpressure of at least 0.4 bar and normally 0.5-0.7 bar (overpressure) in the sealed tray 2.
    Fig. 2a shows a cross-sectional view of the same container 1 as shown in Fig. 1, and Fig. 2b shows an enlarged detail thereof, illustrating the position of the externally applied surface energy changing agent 8 between the lidding film 3 and the sealing rim 6 of the tray 2, when the container 1 is sealed.
    Figs. 3a and 3b show' a top view and a side view, respectively, of the container 1 w'ith the lidding film 3 heat sealed to the sealing rim 6 of the tray 2.
    Fig. 4 illustrates schematically an apparatus for making trays 2 of containers 1 according to an embodiment of the invention.
    In general, a ro ll coating machine works by transferring a layer of coating from the surface of a roll to the surface of a part. The transfer roll system illustrated schematically in Fig. 4 utilizes three rolls, namely a pickup roll 14, a transfer roll 15 and a coating roll 16, to transfer the surface energy changing agent 8 from a tank 13 or reservoir containing the surface energy' changing agent in a liquid form to the sealing surface of the tray 2.
    The pickup roll 14 picks up the surface energy changing agent 8 from the tank 13 and transfers it to the transfer roll 15, from which it is passed on to the coating roll 16 and, finally, to the sealing surface of the tray 2.
    Transfer roll systems are capable of depositing a thinner layer of coating than two roll systems (without the transfer roll 15). This is due to the fact that a film split occurs at every roll interface, i.e. at the interface between two rolls 14-16 and between the coating roll 16 and the tray 2, so that on each surface, onto which the surface energy changing agent 8 is deposited, the thickness of the layer will be thinner than on the surface of the preceding roll in the roll train.
    It shoul d be noted that the figures show the layer of the surface energy changing agent 8 much thicker than is the reality in practice. In fact, this layer is very thin in practice.
    List of reference numbers 1. Container 2. Tray 3. Lidding film 4. Bottom part 5. Sidewall 6. Sealing rim 7. Sealing surface 8. Externally applied surface energy changing agent 9. Thermo forming apparatus 10. Thermo forming tool 11. Conveyor 12. Conveyor roll 13. Tank 14. Pickup roll 15. Transfer roll 16. Coating roll
    权利要求:
    Claims (17)
    [1] 1, A container (1) for foodstuff, said container comprising a tray (2) formed from a sheet of material compri sing one or more layers, wherein the material of each of the layers of the formed tray comprises at least 85 % of amorphous polyethylene terephthalate (APET), said tray comprising a bottom part (4), one or more side walls (5) and a peripheral sealing rim (6) at its top, said sealing rim having a substantially flat upward facing sealing surface (7), wh erein, at least in the top layer of the formed tray , i.e. the layer forming the sealing surface, the material is modified in such a way that the APET therein has an increased softness at relevant sealing temperatures, typically between 120 °C and 200 °C, and wherein the surface is modified by means of one or more surface energy-changing agents, for instance in the form of internal and/or external slip agents, so that the surface energy of the top layer is red uced.
    [2] 2. The con tainer accordin g to claim 1, wherein the modificat ion of the materi al of at least the top layer is obtained by modifying the backbone of the polyethylene terephthalate polymer therein through the incorporation of a comonomer, such as isophthalic acid (IPA), cyclohexaneditnethanol (CHDM) or diethyleneglycol (DEG).
    [3] 3. The container according to claim 1 or 2, wherein the modified APET material, at least in the top layer, comprises more than 4 mole %, preferably more than 6 mole %, most preferably more than 8 mole %, of monomers other than ethylene glycol or terephthalic acid residues.
    [4] 4. The container according to any of the preceding claims, wherein a surface energy changing agent (8) is applied at least onto the sealing surface along the full circumference of the tray.
    [5] 5. The container according to claim 4, wherein the externally applied surface energy changing agent is a siloxane type of polymer, such as a silicone in the form of polydimethylsiloxane (PDMS) or a functionalised siloxane.
    [6] 6. The container according to any of the preceding claims, wherein a surface energy changing agent, for instance in the form of a fatty amide slip masterbatch, is incorporated in the formulation during extrusion of the sheet.
    [7] 7. The container according to any of the preceding claims, wherein the external and/or internal application of surface energy changing agent(s) causc(s) the surface energy of the top layer to be reduced by at least 20 %, preferably by at least 30 %, most preferably by at least 40 %.
    [8] 8. The container according any of the preceding claims, wherein the material of each of the layers of the formed tray has an intrinsic viscosity between 0.6 dl/g and 1.1 dl/g, preferably between 0.7 dl/g and 0.9 dl/g, most preferably between 0.7 dl/g and 0.8 dl/g.
    [9] 9. The container according to any of the preceding claims, wherein the thickness of material of the tray is between 200 pm and 1200 pm.
    [10] 10. The container according to any of the preceding claims further comprising a lidding film (3), which is bonded to the tray by a gas-proof seal formed along the sealing rim.
    [11] 11. The container according to claim 10, wherein the lidding film is soft and flexible, having a thickness of material between 10 pm and 200 pm, preferably between 15 pm and 150 pm.
    [12] 12. The container according to claim 10 or 11, w'herein the lidding film comprises at least one layer of polyethylene terephthalate.
    [13] 13. A method of producing a container (1) for foodstuff, said method comprising the steps of: extruding a sheet of material comprising one or more layers, wherein the material of each of the layers comprises at least 85 % of amorphous polyethylene terephthalate (APET) and, at least the material of a top layer of the sheet is modified in such a way that the APET therein has an increased softness at relevant sealing temperatures, typically between 120 °C and 200 °C, and wherein the surface is modified by means of one or more surface energy changing agents, for instance in the form of internal and/or external slip agents, so that the surface energy of the top layer is reduced; and forming, for instance by thermoforming, a tray (2) made from the extruded sheet of material, said tray comprising a bottom part (4), one or more side walls (5) and a peripheral sealing rim (6) at its top, said sealing rim having a substantially flat upwurd facing sealing surface (7) formed by the top layer of the sheet of material.
    [14] 14. The method according to claim 13, wherein the modification of the material of at least the top layer is obtained by modifying the backbone of the polyethylene terephthalate polymer therein through the incorporation of a comonomer, such as isophthalic acid (IPA), cyclohcxanedimethanol (CHDM) or diethyieneglycol (DEG).
    [15] 15. The method according to claim 13 or 14, wherein the reduction of the surface energy is obtained at least partly by applying a surface energy changing agent (8), for instance in the form of a siloxane type of polymer, such as a silicone, at least onto the sealing surface of the formed tray along the full circumference of the tray, for instance by means of roll coating or immersion in a bath containing the surface energy changing agent.
    [16] 16. The method according to any of claims 13-15, wherein the reduction of the surface energy is obtained at least partly by incorporating a surface energy changing agent, for instance in the form of a fatty amide slip masterbatch, in the formulation during the extrusion of the sheet.
    [17] 17. The method according to any of claims 13-16, further comprising a step of bonding a liddin g film (3) to the sealing surface of the tray by means of a process that involves the use of heat and pressure.
    类似技术:
    公开号 | 公开日 | 专利标题
    JP6211117B2|2017-10-11|Dual openable food packaging with thermoformed polyester film lid
    US3865302A|1975-02-11|Container for cooking food therein
    JP5833534B2|2015-12-16|Heat-sealable composite polyester film
    JP5030356B2|2012-09-19|Heat-shrinkable heat-sealable polymer film for packaging
    KR101563026B1|2015-10-23|Peelable composite thermoplastic sealants in packaging films
    EP2643238B1|2016-05-25|Sealed container for foodstuffs
    CN1308137C|2007-04-04|Package lid, method for manufacturing the same and package sealed with the lid
    JP2005515100A|2005-05-26|Heat-sealable and shrinkable multilayer polymer film
    EP3184453B1|2022-03-09|Sealable container, sealed container and processes for making thereof
    KR20040027933A|2004-04-01|Heat-Shrinkable Laminate Useful for Packaging
    US9248947B2|2016-02-02|Film for thermal adhesion to a rigid biopolymer structure
    EP3296227B1|2019-10-02|Container for foodstuffs
    JP4733452B2|2011-07-27|Package
    US11084259B2|2021-08-10|Coextruded multilayer film
    WO2020068053A1|2020-04-02|Liners for bulk containers
    DK2447056T3|2015-10-19|Packaging is easy to open
    CN106457796A|2017-02-22|Packaging comprising fresh food product
    同族专利:
    公开号 | 公开日
    DK179002B1|2017-08-07|
    DK3296227T3|2019-12-16|
    EP3296227B1|2019-10-02|
    EP3296227A1|2018-03-21|
    引用文献:
    公开号 | 申请日 | 公开日 | 申请人 | 专利标题
    US5039001A|1990-06-18|1991-08-13|Kraft General Foods, Inc.|Microwavable package and process|
    EP1398278A1|2002-09-11|2004-03-17|Northern Foods PLC|Food container with easy open seal|
    US20040213967A1|2003-04-22|2004-10-28|Herbert Peiffer|Coextruded, heatsealable and peelable polyester film, process for its production and its use|
    US20050150891A1|2003-12-16|2005-07-14|Amcor Flexibles Europe|Packaging having a perforable lid|
    EP2643238B1|2010-11-25|2016-05-25|R. Faerch Plast A/S|Sealed container for foodstuffs|
    EP2535185A1|2011-06-16|2012-12-19|Point Plastic S.r.l.|Multilayer film made of recyclable plastic material, container comprising said film and related package|
    WO2013015867A1|2011-07-27|2013-01-31|E. I. Du Pont De Nemours And Company|Multilayer films for reclosable packaging|
    WO2013075713A1|2011-11-22|2013-05-30|Danapak Flexibles A/S|A sheet, a method of making and using a sheet as a lid for packages.|
    US9561886B2|2011-09-21|2017-02-07|Toray Plastics , Inc.|Barrier lidding structure based on polypropylene film|
    CN104619603B|2012-09-07|2017-08-15|凸版印刷株式会社|Cover material and packing container|DE102018215422A1|2018-09-11|2020-03-12|Mitsubishi Polyester Film Gmbh|Heat-sealable polyester film for the production of menu trays, processes for their production and their use|
    法律状态:
    优先权:
    申请号 | 申请日 | 专利标题
    DKPA201670703A|DK179002B1|2016-09-14|2016-09-14|Food container|DKPA201670703A| DK179002B1|2016-09-14|2016-09-14|Food container|
    EP17186881.3A| EP3296227B1|2016-09-14|2017-08-18|Container for foodstuffs|