    • 专利摘要:
    The present invention relates to a method for the production of a sol-gel based matrix. The metode comprises the steps of: a) providing a first alkoxysilane of the general formula R1-Si(OR2)3 and a second alkoxysilane of the general formula: b) preparing a first sol-gel component by polymerisation of the first alkoxysilane in the presence of an acid catalyst, c) preparing a second sol-gel component by polymerisation of the second alkoxysilane in the presence of an Lewis acid catalyst, d) Mixing the first sol-gel component and the second sol-gel component for the preparation of a sol-gel based matrix. The above method results in a sol-gel based matrix with high stability and high porosity. The sol-gel based material may be used for the production of a sensor.
    公开号:DK201370617A1
    申请号:DKP201370617
    申请日:2013-10-24
    公开日:2015-05-11
    发明作者:Thomas Just Sørensen；Martin Rosenberg；Bo W Laursen
    申请人:Københavns Uni；
    IPC主号:
    专利说明:

    Introduction
    The present invention relates to methods for the production of sol-gel based matrices as well as sol-gel based matrices obtainable by such methods. The sol gels of the present invention are useful for various purposes including use in sensors for measuring pH, radiation, oxygen concentration etc. due to their high stability and porosity.
    Background of the invention
    First generation optical sensors are currently being introduced in biotechnological production platforms. The sensors are composed of five different units, excluding the fiber optical connectors: i) light source, ii) substrate, iii) matrix, iv) indicator dye components, and v) detector.1'5
    Light sources and detectors are highly developed and are just a matter of cost. The substrate has to be chosen based on the platform in which the sensing will take place, typically a glass or a polymer support is used. The key parameter regarding the substrate is that the matrix material must be able to be at least partially immobilized in or on the substrate.
    The wish list for the matrix material is long: the matrix material should allow the analytes to pass through the film as unhindered as possible, it should encapsulate the sensor molecules, it should be transparent and have low auto-fluorescence, and it has to be stable in biological media for extended periods of time. The indicator dye components may be either a single ratiometric pH responsive dye, or two dyes with similar properties. The laughter is only possible if the physical stability of the matrix ensures that no dye is lost to the medium.
    The benchmark in materials for optical sensors has been set in sensors, where fluorescein has been used as the indicator dye component; 4 '8 despite the poor photostability of fluorescein.5 The critical parameters are the response time of the sensor, the leakage of the dye, the stability of the signal and the response to pH. While leakage of the highly water soluble fluorescein from prior art optical sensors has not been completely removed, 9 other more lipophilic dyes have been successfully encapsulated in sol-gel matrices.10, 11 However, even lipophilic dyes may be prone to leakage during long term use or in lipophlic / amphiphilic environments.
    Preparation of organically modified silicates (ORMOSILs) using alkyl and 3-glycidoxypropyl substituted trialkoxysilanes and various polymerization conditions have been reported previously in the scientific literature.1, 12, 13 Leakage has been controlled either using apolar additives11,14 or by attaching the dyes to bulky macromolecules.6, 7'15.16 It has been reported that Lewis acids can be a catalyst for polymerization of 3-glycidoxypropyltrialkoxysilanes, accelerating both the polyether and the polysiloxane formation.12,13,17 WO 2009/020259 discloses in example 2 A method in which 3-glycidoxypropyltrimethoxysilane (GPTMS), methyltriethoxysilane (MTES), ethanol (6.95 mM) and 35% HCl were mixed together and stirred at room temperature for three days to induce a condensation reaction. To the sol-gel solution thus prepared, 1 mM HPTS solution, which had been dissolved in ethanol, was added to give an HPTS mixture solution. The HPTS mixture solution was evenly coated onto the bottom surface of wells of a microtiter plate to prepare a fluorescent sensing membrane that can be used for carbon dioxide detection. The sol-gel solution containing HPTS was dried at room temperature for five days and further dried at 70 ° C for two days to improve mechanical strength and surface smoothness. WO 2009/020259 uses HCI as the initiator and the indicator moiety (HPTS) is non-covalently attached to a silane. WO 2004/077035 discloses a CO2 sensor comprising a pH indicator and a porous sol-gel matrix. The pH indicator may be hydroxypyrene trisulfonate (HPTS) and immobilized in the sol-gel. The sol-gel may be prepared from the monomeric ethyl triethoxysilane (ETEOS). In the specific method, two silanes are used (trimethylsilylpropane and triethoxysilane). However, none of the silanes suggested in the description contains an epoxy group. Furthermore, the indicator moiety is not covalently linked to a silane. WO 12/032342 discloses a sensor comprising a sol-gel layer incorporating a phosphorescent material, such as ruthenium oxide (RUO2). The sensor may be used to measure the O2 or H2S concentration. Details on the monomers used in the sol-gel are not disclosed. J. Mater. Chem. 2012, 22, 11720 shows a method in which two monomers (ETEOS and GPTMS) are used in the sol-gel. The monomers are reacted separately and methylimidazole is used to initiate the reaction of GPTMS. When the separately reacted monomers are mixed, the indicator moiety (HPTS) is added. Thus, a Lewis acid for initiating the reaction is not used and an indicator moiety (e.g. HPTS) is not covalently attached to a silane. Methods based on methylimidazole catalysis may be inferior, as tests performed by the present inventors have shown that methylimidazole reacts to form fluorescent compounds which are immobilized in the sol-gel.
    It is the object of the present invention to improve the porosity of sol-gel materials for optical sensing, while at the same time maintaining a high physical stability and a low auto-fluorescence. A high porosity results in a short response time, which makes it possible to react to a change faster.
    Summary of the invention
    The present invention relates to a method for the production of a sol-gel based matrix comprising the steps of: a) providing a first alkoxysilane of the general formula: R1-Si (OR2) 3 and a second alkoxysilane of the general formula:
    wherein R1 represents a straight or branched C1-C6 alkyl or C2-C6 alkenyl, a C3-C6 cycloalkyl, a C1-C6 aminoalkyl, a C1-C6 hydroxyalkyl, a C1-C6 cyanoalkyl, a phenyl, a group of the formula - Y- (XY) nH, Y is independently selected from straight or branched C1-C6 alkylene, X is a hetero atom or group selected from O, S, NH, and n is an integer of 1-5, or R1 represents a C 1 -C 6 alkyl substituted with a group Z, wherein Z is independently selected form the group comprising hydrogen, cyano, halogen, hydroxy, nitro, acyl, acylamino, acyloxy, C 1 -C 24 alkyl, C 1 -C 24 haloalkyl, C 1 -C 24 -alkenyl, C 1 -C 24 alkynyl, aryl, C 1 -C 24 alkoxy, C 1 -C 24 alkylsulfonyl, amino, aminocarbonyl, aminothiocarbonyl, aminocarbonylamino, aminothiocarbonylamino, aminocarbonyloxy, aminosulfonyl, aminosulfonyloxy, aminosulfonyl, aminosulfonyl, aminosulfonyl ester) amino, (carboxyl ester) oxy, sulfonyl, sulfonyloxy, thioacyl, thiol, thiocarbonyl, C 1 -C 24 alkylthio, heteroaryl, or a cycloalkyl; R2 independently represents a straight or branched C1-C6 alkyl; and R3 represents a linker selected from a group of the formula -R4- (X-R4) n- whereas R4 is independently selected from straight or branched C1-C6 alkylene, C1-C24 haloalkylene, X is a hetero atom or group selected among O, S, NH, and n is an integer of 0-12, b) preparing a first sol-gel component by polymerization of the first alkoxysilane in the presence of an acid catalyst, c) preparing a second sol-gel component by polymerization of the second alkoxysilane in the presence of a Lewis acid catalyst; (d) mixing the first sol-gel component and the second sol-gel component for the preparation of a sol-gel based matrix.
    It was discovered by the inventors that the use of a Lewis acid for the catalysis of the second sol-gel component did not result in the formation of fluorescent compounds or other by-products, as was the case for methylimidazole. Furthermore, the Lewis acid showed the added potential of being incorporated into the sol-gel, thus adding to the porosity.
    In another aspect of the present invention an additional alkoxysilane is added to step b) and / or c), said additional alkoxysilane being of the formula: R5-Si (OR2) 3 is R2 as defined above and R5 represents a group having covalently attached to an indicator or reference dye.
    While the present invention may work well in many applications with an indicator dye or reference dye non-covalently attached to the silane scaffold matrix, a more durable sol-gel based matrix may be obtained by attaching the indicator or reference dye covalently to the matrix. A more stable product may collect reliable data for prolonged time. The added physical stability may further broaden the application of the sensor incorporating the sol-gel based matrix to applications in which the indicator or reference dye may otherwise easily leak to the media.
    The dye indicator or the reference dye may be attached to the silane matrix in a variety of ways. In a certain embodiment R5 is of the general formula
    -R3-NH-C (= 0) -X-R3-F while R3 is as defined above and independently selected, and F represents an indicator or a reference dye.
    The reference dye and / or the indicator dye can be selected from a variety of possibilities well known to the person skilled in the art. According to a certain aspect of the present invention F is an indicator dye derived from 8-hydroxypyrene-1, 3,6-trisulfonic acid (HPTS), fluorescein, or rhodamine B.
    The type of reference dye is not particularly limited to a certain class of compounds. Thus, in an embodiment of the present invention F in the above formula, a reference dye is derived from triangulenium compounds, acridinium compounds, ruthenium doped sol-gel particles, ruthenium-based compounds with α-diimine ligands, porphorin with Pt or Pd as the central metal atom, Ru (bpy) 2 (dpp) CI2, Ru (bpy) 3CI2 / a lanthanide containing complex, polymeric metal containing structure, or other metal containing unit.
    According to the present invention, a Lewis acid is used in the polymerization of the second sol-gel component. Definitions of Lewis acids may vary from textbook to textbook. The IUPAC definition is "a molecular entity (and the corresponding chemical species) that is an electron-pair acceptor and therefore able to react with a Lewis base to form a Lewis adduct, by sharing the electron pair furnished by the Lewis base". Usually, the Lewis base is ΌΗ present in the media. In a certain embodiment of the present invention a Lewis acid is a triagonal planar species, such as BF3 or AICI3. Specific examples of Lewis acids according to the present invention include TiCU, AICI3, and BF3, or solvates or etherates thereof.
    The additional alkoxysilane may be added at any suitable point in time during the method. In a preferred aspect, the additional alkoxysilane is added to the first sol-gel component, the second sol-gel component or both during the preparation.
    When an indicator dye as well as a reference dye is present it is preferred that either the reference dye or the indicator dye is added to the first sol-gel component of step b) and the other dye is added to the second sol-gel component or step c).
    The first alkoxysilane may be selected in accordance with the formula indicated above. Specifically, the first alkoxysilane is selected from ethyltriethoxysilane (ETEOS), methyltriethoxysilane (MTEOS), propyltriethoxysilane (PrTEOS), n-octyltriethoxysilane (n-octyl TEOS), methyltrimethoxysilane (MTMOS), aminopropylene (MTMOS), aminopropyl trimethoxysilane (PhTMOS). In certain matrices a first silane with less bulky side groups may be preferred to ensure high response times. Examples of such preferred first alkoxysilanes are ETEOS, MTEOS, PrTEOS, and MTMOS.
    The second alkoxysilane may be selected in accordance with the formula indicated above. Specifically, second alkoxysilane is selected from 3-glycidoxypropyltrimethoxysilane (GPTMS).
    The method described herein produces a sol-gel based matrix. The sol-gel based matrix so produced is also part of the present invention.
    The relative amount of the individual components of the sol-gel based matrix may be adjusted in accordance with the need and desired properties of the final product. In a certain aspect the amount in mill from first alkoxysilane to second alkoxysilane is in the range of 10: 1 to 1:10. Suitably, the amount of the first alkoxysilane to second alkoxysilane is in the range of 5: 1 to 1: 5, such as 2: 1 to 1: 2, preferably around 1: 1.
    Brief description of the drawings
    FIG. 1 shows the general preparation steps for deposition of sensor material on a substrate,
    FIG. 2 shows the leakage over time of sensor spots.
    FIG. 3 shows the development over time for the ratiometric signal in four different buffer solutions,
    FIG. 4 shows the ratiometric responses; Fig. 4a shows TMAAcr-4 immobilized in the GPTMS-ETEOS matrix via lipophilic entrapment, and Figs. 4b shows TMAAcr-6 immobilized in the GPTMS-ETEOS matrix via covalent entrapment.
    FIG. 5 shows the emission spectra of the sensors in action; FIG. 5a shows the emission spectra of a GPTMS-ETEOS matrix with TMAAcr-4 and DMQA-1 lipophilic entrapped in the matrix, and Figs. Figure 5b shows the emission spectra of the GPTMS-ETEOS matrix with TMAAcr-6 covalently and DMQA-1 lipophilic entrapped in the GPTMS-ETEOS matrix.
    FIG. 6 shows the response times of the pH active dye DAOTA-2; FIG. 6a shows the response time in PhTEOS-GPTMS matrix, Fig. 6b shows the response time for ETEOS-GPTMS matrix, and Figs. 6c shows the response time for the PrTEOS-GPTMS matrix.
    FIG. 7 discloses the response time of the pH active dye DAOTA-2 in an ETEOS-GPTMS matrix, compared to a PVA and PEG-DA matrix.
    Detailed description of the invention
    The sol-gel based matrix is usually deposited on a substrate as part of a sensor. The substrate is generally selected to optimize the ability of the sol-gel to form an immobilized attachment to the substrate. Suitable substrates include glass, plastics, ceramics, and polymers. Suitable polymer substrates include polycarbonates, acrylics such as poly (methyl methacrylate), acrylonitrile-butadiene-styrene copolymer, polyvinyl chloride, polyethylene, polypropylene, polystyrene, polyurethanes, silicones, and vinylidene fluoride-hexafluoropropylene copolymer.
    The first sol-gel component is prepared by polymerization of the first alkoxysilane defined above in the presence of an acid catalyst. The acid catalyst may be any suitable acid, such as an inorganic or organic acid. Suitable inorganic acids include hydrochloric acid (HCl), nitric acid (HNO3), phosphoric acid (H3PO4), sulphuric acid (H2S04), hydrofluoric acid (HF), hydrobromic acid (HBr) and perchloric acid (HClO4). A preferred inorganic acid is hydrochloric acid. Suitable organic acids include lactic acid, acetic acid, formic acid, citric acid, oxalic acid, and malic acid. Furthermore, the acid catalyst may be any combination of the above compounds.
    To be suitable, the acid chosen must be able to hydrolyze the first alkoxysilane under the acidic conditions. The hydrolysis initiates the polymeric condensation reaction upon formation of a polymer silicon oxide network.
    The procedure for the preparation of the first sol-gel component generally includes that the first alkoxysilane is dissolved in an organic solvent, usually an alcohol like ethanol prior to the addition of the acid catalyst. The amounts in mole of acid are generally at the same level or lower than the molar amount of the first alkoxysilane. The mixture of first alkoxysilane, organic solvent and acid catalyst is left until the reaction is completed. The reaction time may be several days.
    The second sol-gel component is prepared by either dissolving the second alkoxysilane in a solvent before the addition of the Lewis acid catalyst or by mixing the alkoxysilane and the Lewis acid and then adding the solvent. The molar amount of Lewis acid catalyst is generally lower than the molar amount of the second alkoxysilane. In a preferred embodiment, the molar amount of Lewis acid to second alkoxysilane is 1: 2, such as 1: 3, preferably 1: 4. The solvent is usually an alcohol like ethanol but may be chosen among various solvents assumed by the skilled person to be inert under the conditions.
    The Lewis acid is believed to attack the epoxy ring of the second alkoxysilane whereby a secondary carbocation is formed. This intermediate carbocation can then react with another molecule in the polymerization process. The amount and type of second alkoxysilane should be chosen so as to be able to participate in the intended chemical reaction within a reasonable time. The formation of the second sol-gel component normally proceeds much faster than the formation of the first sol-gel component. A typical reaction time for the second sol-gel component is between 10 min and 3 hours. After the reaction, the second sol-gel component is typically allowed to rest for a few hours.
    After the two sol-gel components have been prepared separately, they are mixed. Typically, the molar amount of the first sol-gel component to the second sol-gel component is in the range of 5: 1 to 1: 5, such as 3: 1 to 1: 3, typically 2: 1 to 1: 2 , and suitably approximately 1: 1.
    If the sol-gel matrix is used for sensing, an indicator and / or reference dye may be incorporated into the matrix by a number of methods to obtain either a non-covalent or a covalent attachment. If a non-covalent attachment is used it is preferred to anchor the dye in some way to the matrix to avoid excessive leakage. A preferred anchoring method is the so-called lipophilic entrapment, according to which the dye core is provided with one or more lipophilic linkers. The lipophilic linkers will engage with the lipophilic environment of the network formed by the sol-gel components and thereby retard the leakage. In a preferred method, the dye core provided with one or more lipophilic linkers is added either to one or both of the sol-gel components or to the mixture of the first and second sol-gel components. To ensure sufficient maturation of the mixture it may be kept for 1 hour to 7 days before it is deposited on the substrate and cured. A covalent attachment of the dye is possible by linking the dye to one of the monomers before polymerization. In a preferred method, an additional alkoxysilane is prepared as a derivative of the first alkoxysilane by attaching the dye thereto. The additional alkoxysilane may be incorporated into either the first sol-gel component or the second sol-gel component. In a preferred aspect, the first or second alkoxysilane is allowed to polymerize for a short time, such as at least 15 minutes, before the further alkoxysilane is added to avoid end positioning.
    The mixture of the first sol-gel component and the second sol-gel component may be allowed to mature before deposition on a suitable substrate. The substrate is generally transparent at the wavelength used to monitor the emitted light. The amount of the mixture used for deposition varies depending on the purpose and geometry of the sensor. In a certain aspect, the amount is 100 pi or less, such as 50 μΙ or less, suitably 20 μΙ or less. The deposit may be referred to herein as a "spot".
    The addition of the mixture to the substrate may be allowed to deliberately solidify or the added amount of mixture may be spread on the substrate to form a film of substantially uniform thickness. After the deposit of the mixture on the substrate it is cured. The curing may be performed in a number of ways, including heating at elevated temperatures so as to form a solid film attached to the substrate. The temperature of the curing is suitably 70 ° C or above, such as 90 ° C or above, and suitably 100 ° C or above. Usually, the curing temperature does not exceed 150 ° C to avoid degradation of the materials, i.e. to maintain the porous three-dimensional polymer networks, which allow for fast diffusion of the analyte, such as a proton. The relatively unhindered diffusion of the analyte in the porous network is believed to be the reason for the observed fast response time.
    The research reported herein suggests that covalent attachment of the dye to the polymer network is preferred when long-term stability is important. Even when the dyes are provided with lipophilic linkers to retard the leakage from the film, the leakage is still too high for a product stable over a longer period of time to be obtained. For short-time use, such as non-reusable sensors, non-covalently attached dyes may be acceptable.
    Examples
    Methods and materials
    Compounds were used as received. Sol-gel monomers were purchased from Sigma-Aldrich. Sol-gel catalysts were purchased from Sigma-Aldrich and used as recieved. Solvents used were analytical or HPLC grade. An electronically controlled oven was used to cure the ORMOSIL thin films.
    Synthesis
    The synthesis of compounds l-BF4and 2-PFeare reported elsewhere.18
    General preparation of tetramethoxyamino-acridinium (TMAAcr): 2 (162 mg, 0.23 mmol) was dissolved in 15 ml of acetonitrile and n-octylamine (26 ml, 0.14 mmol) was added to the solution. The reaction mixture was heated to slight reflux temperature and stirred for 5 h. The reaction mixture was allowed to cool down when the color of the mixture had changed from blue to red-brown and MALDI-TOF analysis indicated a mass similar to that of the starting material was not present any more. The reaction mixture was washed with heptane (3 x 50 ml). The crude product was isolated by evaporation and recrystallized from ethanol, and the product was washed with ether and heptane several times. The product was isolated as a red-purple powder, which was metallic-green when filtered.
    General approach to activate TMAAcr for covalent attachment: TMAAcr (100 mg, 0.11 mmol) was dissolved in 20 ml of acetonitrile and then triethoxy (3-isocyanatopropyl) silane (1.1 ml, 0.45 mmol) was added dropwise using a syringe at room temperature. The mixture was stirred for 1 h when MALDI-TOF analysis indicated that 9 was not present. The reaction mixture was washed with heptane (3 x 50 ml) and then the acetonitrile phase was mixed with a 0.2 M KPF6 solution. The slurry was stirred for 20 min and then gently filtered. The precipitate was washed with water several times. The product was dissolved in dichloromethane through the filter and the non-dissolved solid in the filter was discarded. The product is collected by removal of the solvent yielding metallic-green flakes.
    General preparation of dimethoxyquinacridinium (DMQA): A primary amine (20 eq, 40 mmol) was added to a solution of DMB3C-BF419 in NMP (1.0 g, 2 mmol in 8 ml_). The solution was warmed to 140 ° C for 10-20 minutes (the degree of reaction is followed by MALDI-TOF mass spectroscopy). After cooling to RT, the reaction mixture was poured on to 0.2 M KPF4 (aq) (200 mL). The precipitate was collected, washed and dried. The crude can be recrystallized from methanol, reprecipitated from dichloromethane with ethyl acetate or reprecipitated from acetonitrile with ether depending on how lipophile the side chains are.
    General approach to activate DMQA for covalent attachment: DMAQ (70 mg, 0.143 mmol) was dissolved in 8 ml of anhydrous acetonitrile and then 3- (triethoxysilane) propyl isocyanate (cold, 100 µl, d = 0.999 g / ml, 0.404 mmol) was added. The flask was fitted with a stopper and stirred at room temperature for 4 h. After 4 h MALDI-TOF analysis indicated that the reaction mixture contained only starting material. Then excess of isocyanate (1 ml) was added together with approx. 1 ml or triethylamine. The mixture was heated to 65 ° C and stirred for 1.5 h. Then MALDI-TOF analysis indicated that the reaction mixture contained a compound with a mass of 649 m / z, which is the mass of the desired product and no mass corresponding to that. of the starting material was present. The reaction mixture was washed (still warm) with heptane (2 x 50 ml) and then dried over MgSO 4 for 10 min. The solvent was removed by evaporation at 50 ° C in vacuum and the crude product dissolved in a minimum of CH 2 Cl 2 and then diethyl ether (200 ml) was added and a green precipitate was allowed to form. The dark product was collected and dried in vacuum over KOH overnight.
    spectroscopy
    Emission spectroscopy was performed in front-face set-up for sensor spot samples and in a conventional L-shape set-up for measurements in solution. A Perkin-Elmer LS50B and a Horiba Fluorologist 3 were used interchangeably. Intensity based sensor measurements were only performed on the LS50B platform. Fluorescence lifetime based sensor measurements were performed only on the Fluorolog 3. Absorption spectroscopy was performed on a Perkin Elmer Lambda 1050, with integrating sphere (for sensor spots) and with a 3-detector module for solution samples.
    Sol-Gel preparation
    The procedure includes preparation of two separate gel components of the organic modified silanes: Ethyltriethoxysilane (ETEOS) or similar alkyl or aryl trialkoxy silane (XTEOS) and 3- (glycidoxy) propyltrimethoxysilane (GPTMS). All the different preparations and combinations are compiled in Table 1, and the detailed procedures are as follows.
    Table 1. The different compositions of sol-gels tested in this work; variations can be seen in the alkyl trialkoxy silane part, the Lewis acid, and the dye additives. The pKa of the resulting sensor is included._
    * Dye 6 pre-mixed with ETEOS component, zDye 6 pre-mixed with GPTMS component.
    ETEOS
    The ETEOS gel component is prepared from polymerization of the silicon network under acidic conditions. ETEOS is hydrolyzed under acidic conditions, which initiates a polymeric condensation reaction upon formation of a polymer silicon oxide network. The presented procedure is equivalent to the procedure reported by Wencel eta / .10.11
    Procedure for preparation of ETEOS gel component: 5 ml of ETEOS (0.02 mol) is dissolved in 8 ml of absolute ethanol (0.14 mol) upon stirring. Subsequently, 1.6 ml of 0.1 M HCl solution (0.16 mmol) was added dropwise. This mixture is then left on a stirring table for a minimum of 7 days to allow the polymerization process to proceed. GPTMS Gel Component.
    The GPTMS gel component is prepared from polymerization of the organic linker using a Lewis acid as initiator. In this procedure we use boron trifluoride diethyl etherate as the Lewis acid. The Lewis acid attacks the epoxy ring which allows for ring opening of the epoxy ring upon formation of a secondary carbocation. This intermediate carbocation can then react with another GPTMS molecule, initiating a polymerization reaction. Due to the acidic environment a polymerization of the silicon network equivalent to that described for the ETEOS component will proceed alongside.
    Procedure for preparation of GPTMS gel component: 6 ml of GPTMS (0.027 mol) is mixed with 11 ml of absolute ethanol (0.19 mol) upon stirring. Then 0.75 ml of cold boron trifluoride diethyl etherate (BF3 · 0 (CH2CH3) 2, 5.8 mmol) is added dropwise. The mixture is left with stirring for 30 min in a sealed container until the temperature of the mixture has dropped to room temperature. After 30 min 2 ml of MilliQ water (0.11 mol) is added to the solution. The resulting mixture was left with stirring for 4 h.
    When the two gel components have been prepared they are mixed in 1: 1 molar ratio and left for a minimum of 3 days to allow the networks to mix. This is referred to as the GPTMS-ETEOS mixture. GPTMS-ETEOS Mixture
    When the GPTMS and ETEOS components have been prepared they are mixed to obtain a 1: 1 molar ratio (1.1 ml GPTMS + 1 ml ETEOS) and the dyes are added in order to obtain a concentration of approx. 0.1 mM. The resulting mixture is then allowed to further mix for a minimum of 3 days.
    The GPTMS-ETEOS mixture with the dye entrapped can now be deposited onto a glass or plastic surface. When deposited it has to be cured at 110 degrees for 3-4 hours. The result is a porous and transparent matrix. XTEOS Variations A procedure analogous to that for the ETEOS Gel component described above used to make XTEOS gel components, with X = Pr and Ph.
    Preparation of XTEOS Gel Components X = Phenyl (Ph): Phenyltriethoxyilane (PhTEOS, 10 ml, M = 240.14 g / mol, d = 0.996 g / ml, 0.041 mol) and absolute ethanol (15 ml, d = 0.789 g / ml, 0.26 mol) was mixed and the freshly prepared 0.1 M HCl solution (2.8 ml, 0.28 mmol) was added. The solution was stirred for 15 min in the sealed vial, and then left on a vibration table for 20 days in the dark at room temperature. X = Propyl (Pr): Propyltriethoxyilane (PrTEOS, 10 ml, M = 206.13 g / mol, d = 0.892 g / ml, 0.043 mmol) and absolute ethanol (16 ml, d = 0.789 g / ml, 0.27 mol) was mixed and then freshly prepared 0.1 M HCl solution (3.2 ml, 0.32 mmol) was added. The solution was stirred for 15 min in the sealed vial, and then left on a vibration table for 20 days in the dark at room temperature.
    Lipophilic Entrapment
    In the lipophilic entrapment method, the dyes entrapped in the GPTMS-ETEOS network require that the dye has one or several lipophilic linker (s) attached to the dye to prevent leakage from the resulting matrix material.
    General Procedure for Lipophilic Entrapment of Dyes
    The ETEOS and GPTMS gel components are prepared and mixed as described above with the addition of the dye such that a final concentration of 0.1 mM is obtained. The resulting GPTMS-ETEOS dye mixture is then left on a stirring table for at least 3 days before deposition and cured at 110 ° C for 3-4 hours.
    Covalent Method:
    This procedure requires that the dye has been activated by linking to a trialkoxysilane group that can mix into the silicon network of either the ETEOS or GPTMS gels.
    General Procedure for Covalent Entrapment of Dyes into the GPTMS-ETEOS Matrix
    The ETEOS and GPTMS gel components are prepared and mixed as described above, with the exception that the silane functionalized dye is mixed into either the ETEOS or the GPTMS gel component after 1 hour after mixing the materials described to mix the ETEOS or the GPTMS gel components. The GPTMS and ETEOS components are left for polymerization reaction time described in the general procedure. The two components are then mixed in the described 1: 1 molar ratio and left at a stirring table for no less than 3 days. The dye should be added in an amount such that a final concentration of 0.1 mM of dye is obtained in the final GPTMS-ETEOS mixture. The resulting GPTMS-ETEOS dye mixture is then deposited and cured at 110 ° C for 3-4 hours.
    Fabrication of sensor spots
    The sensor spots were drop coated on a glass or polycarbonate substrate and then cured. The substrate material appears to be inconsequential as long as thin films can be prepared. For comparison sensor spots were prepared from direct incorporation of the dyes into PVA (from 10% w / w solutions in water) which were subsequently drop coated on glass. PEG-DA hydrogel with dye entrapped was prepared by mixing PEG-DA (Mn = 700) and ethanol in a 1: 1 v / v ratio and then the dye was added to obtain 1 mM. Then a catalytic amount of a solution of 2,2'-azobis (2-methylpropionitrile) in CH 2 Cl 2 (25 mg / ml) was added. The mixture was spread on a petri dish, the dish was equipped with a glass lid, and the mixture was baked in the oven at 110 ° C for 1 hour. A thin piece of the resulting hydrogel was immobilized on a clean glass slide using doublesided tape and the regular tape.
    Titrations
    To perform titrations rapidly a set-up employing an epi-fluorescence microscopy equipped with a halogen light source and an Ocean Optics spectrometer for detection. The sensor spot was attached to a homemade holder, which kept the spot in place in a large chamber filled with water, where pH was monitored externally with a pH meter. Alternatively, the sensor spot was affixed to the wall of a cuvette and the titration was performed in a Perkin Elmer LS50B, controlling the pH between measurements.
    Stability testing
    The photostability was followed by constant illumination of the sensor spot with wavelength selected light from a xenon lamp. The physical stability was tested by immersing the sensor spot in low or high pH aqueous solution, and monitoring the fluorescence from the solution.
    Response analysis
    The signal from the sensor is monitored after inducing a significant (more than 4 pH units) jump in pH. The time it takes to obtain a full (100%) and partial (90%) response, compared to the equilibrium signal is recorded.
    FIG. 1 shows the general preparation of sensor spots.
    Scheme 1: Above is shown the five components used to form the sol-gel sensor material in the present example.
    Results
    The tested sensors are prepared as illustrated in FIG. 1, on glass and polycarbonate substrates. The five components are mixed in a fashion that allows for the formation of a porous covalently linked 3D polymer network, which allows for fast diffusion of protons.
    Scheme 2 shows the structure of the pH-responsive and the reference dyes used in this study. The pKa values of the resulting sol-gel based sensors are compiled in Table 1. Cursory inspections of the structures, which are physically immobilized in the sol-gel show that a long alkyl chain is required to prevent leakage, while the molecules are covalently linked to the matrix can have either a long or a short linker.
    Scheme 2. Molecular structure of the pH responsive and the reference dyes.
    Stability
    Table 2. Leaking of 5 (6) -carboxyfluorescein (CF), DMQA-2, DAOTA-1, and 6-stearamido-fluorescein (AF18) from the ETEOS-GPTMS matrix given as fluorescence intensity measured from a PBS solution at pH 7 surrounding a glass slide coated with ETEOS-GPTMS-dye matrix using maximum sized slit widths at the emission and excitation sites of the spectrometer.
    Figure 2 shows leakage over time of sensor spots: non-bound 5 (6) -carboxyfluorescein (plus-signs), covalently bound DAOTA-1 (crosses), and covalently bound DMQA-2 (dots).
    Figure 2 shows the performance in leakage studies, against the performance of molecules without anchoring groups, and the data collected in Table 2. Leaking of the dyes entrapped or bound to the matrix was investigated by measuring the emission intensity of a PBS solution at pH 7.0 surrounding a non-bound dye (5 (6) -carboxy fluorescein, CF), covalently bound (DMQA-2 and DAOTA-1) using the largest possible slit widths on the excitation and emission sites of the spectrometer and an excitation wavelength of 450 nm, these data are shown in figure 2. While the physically bound dye and 6-stearamido-fluorescein (AF18) were also tested, we did not record the transient curve. All the leakage data is compiled in table 2. The results reveal that DAOTA-1 leaked to a small extend, which we, based on NMR data, can assign to a fraction of unlinked dye in the ETEOS-GPTMS matrix, this issue has previously been reported for fluorescein, which was only partially activated. The DMQA-2 compound could be based on NMR data to be 100% activated and consequently did not show any leakage. This shows that effective binding can indeed be obtained in the ETEOS-GPTMS matrix and leakage can be avoided completely by fully activating the dye for polymerization. The unbound CF showed extensive leakage and the data in Table 2 was obtained using half the slit widths as those used for DMQA-2 and DAOTA-1.
    To evaluate the photostability of the sensor we performed a 16-hour scan, see figure 3. No perceivable slope of the curves could be seen in this time interval, which proves that this system has a very high long-term stability under constant irradiation.
    Figure 3 shows the development of the ratiometric signal in four different buffer solutions at pH 3 during 16 h of irradiation at 525 nm of a DAOTA / DMQA based sensor.
    Sensor action
    The performance of the sensors is shown as titration curves in figure 4. The spectra behind the titration curves are shown in figure 5. It is clear that a pH-dependent sensor action is achieved for these two sensor systems. For the examples given in figures 4 and 5 the pKa values are ~ 5, the data for all prepared sensors are compiled in table 1, sensors with a pKa from 1.1 to 6.7 was made.
    Figure 4a shows the ratiometric pH response of TMAAcr-4 immobilized in GPTMS-ETEOS matrix via lipophilic entrapment. Figure 4b shows the pH response of TMAAcr-6 immobilized in the GPTMS-ETEOS matrix via covalent entrapment. The pKa values of TMAAcr-4 and TMAAcr-6 are determined to 4.9 (lipophilic entrapment) and 4.8 (covalent entrapment).
    Figure 5 shows spectra of the sensors in action. FIG. 5a shows the emission spectra of a GPTMS-ETEOS matrix with TMAAcr-4 and DMQA-1 lipophilic entrapped in the GPTMS-ETEOS matrix at different pH values between 3 (black) and 7.5 (red). FIG. 5b shows emission spectra of a GPTMS-ETEOS matrix with TMAAcr-6 covalently and DMQA-1 lipophilic entrapped in the GPTMS-ETEOS matrix at different pH values between 2 (black) and 7.5 (red). Excitation at 475 nm ± 25 nm.
    In order to evaluate the response time, the temporal evolution of the detected signal (intensity ratio) was monitored, when the sensor was monitoring a solution where the pH was changed drastically as well as moderately. Figure 6 shows the result, each panel shows the response of different matrices. It is clear that the response of the Lewis acid catalyzed sol-gel is much faster than the others tested. To highlight the differences an overlay is shown in figure 7. All the data are compiled in table 3. The alkyl trialkoxy-GPTMS matrices have by far the fastest response times, showing some hysteresis, with a response going from high pH to low pH of ~ 10 s and going from low pH to high pH of ~ 20s. Propyltrialkoxy silane derived matrices are faster responding than the ethyltrialkoxy silane derived matrices when the signal level of 90% is considered, while the full response occurs on a similar timescale for both matrices.
    Figure 6 shows the response time of pH-active dye DAOTA-2 in a PhTEOS-GPTMS (Fig. 6a), and ETEOS-GPTMS (Fig. 6b) and PrTEOS-GPTMS (Fig. 6c) matrices. High intensity: Low pH (<2). Low intensity: High pH (> 10).
    Figure 7 shows the response time of pH active dye DAOTA-2 in an ETEOS-GPTMS (red), PVA (blue) and PEG-DA (green) matrix. High intensity: Low pH (<2). Low intensity: High pH (> 10).
    Table 3. The response times (t90 and 10) given in seconds (s) of the ETEOS-GPTMS, PrTEOS-GPTMS, and PhTEOS-GPTMS matrices with the pH-active dye DAOTA-2 incorporated, and the response times of PVA film and PEG-DA hydrogel with the pH-active dye TMAAcr-4 incorporated. H-L refers to the response time going from high (H) pH (> 10) to a low (L) pH (<2) value, L-H has the opposite meaning. Numbers in parentheses refer to response times measured in the ETEOS-GPTMS matrix with the dyes DAOTA-1 and DMQA-2 covalently bound.
    Conclusion
    We have shown that our system has a shorter or comparable response time than previously reported and a high degree of photostability. Furthermore, with this sensor we have solved the leaking issue, using either covalent attachment or lipophilic entrapment of the active components. We have also shown that the activation of the active component is important in making leakage free film.
    References and footnotes 1. P. C. Jeronimo, A. N. Araujo and B. S. Μ. Μ. M. Conceicao, Talanta, 2007, 72,13-27. 2. S. M. Borisov and O. S. Wolfbeis, Chemical Review, 2008,108, 423-461. 3. C. McDonagh, C. S. Burke and B. D. MacCraith, Chemical Review, 2008, 108, 400-422. 4. O. S. Wolfbeis, Anal. Chem., 2008, 80, 4269-4283. 5. X. D. Wang and O. S. Wolfbeis, Anal Chem, 2013, 85, 487-508. 6. A. Lobnik, I. Oehme, I. Murkovic and OS Wolfbeis, analytics Chemica Acta, 1998, 367,159-165 · 7. MD Senarath-Yapa and SS Saavedra, Analytica chimica acta, 2001, 432, 89-94 · 8 M. Cajlakovic, A. Lobnikb and T. Werner, Analytica chimica acta, 2002, 455, 207-213. 9. S. R. Adams, A. T. Harootunian, Y. J. Buechler, S. S. Taylor, and R. Y. Tsien, Nature, 1991, 349, 694-697. 10. D. Wencel, B. D. MacCraith and C. McDonagh, Sensors and Actuators B: Chemical, 2009,139, 208-213. 11. D. Wencel, M. Barczak, P. Borowski and C. McDonagh, J. Mater. Chem., 2012, 2211720. 12. P. Innocenzi, G. Brusatin, M. Guglielmi and R. Bertani, Chem. Mater., 1999, 11, 1672-1679. 13. P. Innocenzi, G. Brusatin and F. Babonneau, Chem. Mater., 2000.12, 3726-3732. 14. D. Wencel, J. P. Moore, N. Stevenson and C. McDonagh, Anal Bioanal Chem, 2010, 398, 1899-1907. 15. T. M. Butler, B. D. MacCraith and C. McDonagh, Journal of Non-Crystalline Solids 1998 224 249-258. 16. P. J. SKRDLA, S. S. SAAVEDRA and N. R. ARMSTRONG, applied spectroscopy, 1999, 53, 785-791. 17. G. BRUSATIN, P. INNOCENZI and M. GUGLIELMI, Journal of Sol-Gel Science and Technology, 2003, 26, 303-306. 18. B. W. Laursen, F. C. Krebs, M. F. Nielsen, K. Bechgaard, J. B.
    Christensen and N. Harrit, J. Am. Chem. Soc., 1998, 120, 12255-12263. 19. J. C. Martin and R. G. Smith, J. Am. Chem. Soc., 1964, 86, 2252-2256.
    权利要求:
    Claims (10)
    [1] 1. A method for the production of a sol-gel based matrix comprising the steps of: a) providing a first alkoxysilane of the general formula: R1-Si(OR2)3 and a second alkoxysilane of the general formula:
    <img img-format="tif" img-content="drawing" file="DK201370617A1C00251.tif" id="icf0001" />
    wherein R1 represents a straight or branched Ci-C6 alkyl or C2-C6 alkenyl, a C3-C6 cycloalkyl, a Ci-C6 aminoalkyl, a Ci-C6 hydroxyalkyl, a Ci-C6 cyanoalkyl, a phenyl, a group of the formula -Y-(X-Y) nH, wherein Y independently is selected from straight or branched Ci-C6 alkylene, X is a hetero atom or group selected among O, S, NH, and n is an integer of 1-5, or R1 represents a Ci-C6 alkyl substituted with a group Z, wherein Z independently is selected form the group comprising hydrogen, cyano, halogen, hydroxy, nitro, acyl, acylamino, acyloxy, Ci-C24-alkyl, Ci-C24-haloalkyl, Ci-C24-alkenyl, Ci-C24-alkynyl, aryl, Ci-C24-alkoxy, Ci-C24-alkylsulfonyl, amino, aminocarbonyl, aminothiocarbonyl, aminocarbonylamino, aminothiocarbonylamino, aminocarbonyloxy, aminosulfonyl, aminosulfonyloxy, aminosulfonylamino, amidino, carboxyl, carboxyl ester, (carboxyl ester)amino, (carboxyl ester)oxy, sulfonyl, sulfonyloxy, thioacyl, thiol, thiocarbonyl, Ci-C24-alkylthio, heteroaryl, or a cycloalkyl; R2 independently represents a straight or branched Ci-C6 alkyl; and R3 represents a linker chosen from a group of the formula -R4-(X-R4)n- wherein R4 independently is selected from straight or branched Ci-C6 alkylene, Ci-C24-haloalkylene, X is a hetero atom or group selected among 0, S, NH, and n is an integer of 0-12, b) preparing a first sol-gel component by polymerisation of the first alkoxysilane in the presence of an acid catalyst, c) preparing a second sol-gel component by polymerisation of the second alkoxysilane in the presence of an Lewis acid catalyst, d) Mixing the first sol-gel component and the second sol-gel component for the preparation of a sol-gel based matrix.
    [2] 2. The method according to claim 1, wherein an additional alkoxysilane is added to step b) and/or c), said additional alkoxysilane being of the formula: R5-Si(OR2)3 wherein R2 is as defined above and R5 represents a group having covalently attached an indicator or reference dye.
    [3] 3. The method according to claim 2, wherein R5 is of the general formula -R3-NH-C(=0)-X-R3-F wherein R3 is as defined above and independently selected, and F represents an indicator or a reference dye.
    [4] 4. The method according to any of the preceding claims, wherein F is an indicator dye derived from 8-hydroxypyrene-l,3,6-trisulfonic acid (HPTS), fluorescein, or rhodamine B.
    [5] 5. The method according to any of the preceding claims, wherein F is a reference dye derived from triangulenium compounds, acridinium compounds, ruthenium doped sol-gel particles, ruthenium-based compounds with α-diimine ligands, porphorin with Pt or Pd as the central metal atom, Ru(bpy)2(dpp)CI2, Ru(bpy)3CI2/ a lanthanide containing complex, polymeric metal containing structure, or other metal containing unit.
    [6] 6. The method according to any of the preceding claims wherein the Lewis acid catalyst is selected among TiCI3, AICI3, and BF3, or solvates or etherates thereof.
    [7] 7. The method according to any of the preceding claims, wherein either the reference dye or the indicator dye is added to the first sol-gel component of step b) and the other dye is added to the second sol-gel component of step c).
    [8] 8. The method according to any of the preceding steps, wherein the first alkoxysilane is selected among ethyltriethoxysilane (ETEOS), methyltriethoxysilane (MTEOS), propyltriethoxysilane (PrTEOS), n-octyltriethoxysilane (n-octyl TEOS), methyltrimethoxysilane (MTMOS), aminopropyltrimethoxysilane (APTMOS), phenyltriethoxysilane (PhTEOS), and phenyl trimethoxysilane (PhTMOS).
    [9] 9. The method according to any of the preceding claims, wherein second alkoxysilane is selected among 3-glycidoxypropyltrimethoxysilane (GPTMS).
    [10] 10. Sol-gel based matrix obtainable by any of the preceding claims.
    类似技术:
    公开号 | 公开日 | 专利标题
    DK178111B1|2015-05-26|Sol-gel based matrix
    Klimant et al.1999|Fast response oxygen micro-optodes based on novel soluble ormosil glasses
    Tran-Thi et al.2011|Optical chemical sensors based on hybrid organic–inorganic sol–gel nanoreactors
    Dash et al.2008|Organically modified silica: Synthesis and applications due to its surface interaction with organic molecules
    Murtagh et al.1998|A Study of the Effects of Organic Modification and Processing Technique on the Luminescence Quenching Behavior of Sol− Gel Oxygen Sensors Based on a Ru | Complex
    Wang et al.2010|Optical oxygen sensors move towards colorimetric determination
    Mills et al.1997|Controlling the response characteristics of luminescent porphyrin plastic film sensors for oxygen
    Lu et al.2001|Luminescence quenching in polymer/filler nanocomposite films used in oxygen sensors
    Barczak et al.2016|Micro-and nanostructured sol-gel-based materials for optical chemical sensing |
    EP1889050A1|2008-02-20|Metal oxide membrane with a gas-selective compound
    Dmitriev et al.2018|Quenched-phosphorescence detection of molecular oxygen: applications in life sciences
    CN103257127B|2015-07-29|It is a kind of that to improve fluorescent indicator molecule dispersed and prepare the method for oxygen sensitive fluorescent screen in organic silica gel
    Hoang et al.2016|Sensitive naked-eye detection of gaseous ammonia based on dye-impregnated nanoporous polyacrylonitrile mats
    Frankær et al.2018|Biocompatible microporous organically modified silicate material with rapid internal diffusion of protons
    DeGraff et al.2005|Luminescence-based oxygen sensors
    US10656091B2|2020-05-19|Optical sensor for detecting a chemical species
    Roik et al.2018|Optically transparent silica film with pH-sensing properties: Influence of chemical immobilization and presence of β-cyclodextrin on protolytic properties of alizarin yellow
    Steyaert et al.2015|Nanofibre-based sensors for visual and optical monitoring
    Sousa et al.2021|Organic–inorganic hybrid sol–gel materials doped with a fluorescent triarylimidazole derivative
    Lee et al.2020|Intelligent environmental sensing: fabrication of switchable, reusable, and highly sensitive gas sensors with spiropyran-grafted anodic aluminum oxide templates
    WO2009118271A1|2009-10-01|Sol-gel- derived materials for optical fluorescent ph sensing
    Ismail et al.2011|Strength of interactions between immobilized dye molecules and sol–gel matrices
    Mohr2006|Polymers for optical sensors
    Hu2013|The development and characterization of fluorescent pH sensors based on silica and hydrogel support matrices
    Shi et al.2022|Polymerizable Oxygen Probe Derived from Platinum-Based Porphyrins for Oxygen Sensing and Pressure-Sensitive Paints
    同族专利:
    公开号 | 公开日
    US20190203049A1|2019-07-04|
    WO2015058778A1|2015-04-30|
    US20160251516A1|2016-09-01|
    US11236233B2|2022-02-01|
    EP3060607B1|2018-05-30|
    US10233328B2|2019-03-19|
    DK178111B1|2015-05-26|
    EP3060607A1|2016-08-31|
    引用文献:
    公开号 | 申请日 | 公开日 | 申请人 | 专利标题
    WO2003081223A2|2001-08-29|2003-10-02|Hrl Laboratories, Llc|Sensors with variable response behavior|
    US20100104476A1|2007-03-21|2010-04-29|Centre National De La Recherche Scientifique -Cnrs-|Fluorescent organic nanocrystals for producing biosensors|
    WO2009020259A1|2007-08-08|2009-02-12|Industry Foundation Of Chonnam National University|A multi-channel bioreactor with the immobillization of optical sensing membrane|
    WO2009118271A1|2008-03-25|2009-10-01|Dublin City University|Sol-gel- derived materials for optical fluorescent ph sensing|
    DE9103321U1|1991-03-19|1992-08-27|Thera Patent Gmbh & Co Kg Gesellschaft Fuer Industrielle Schutzrechte, 8031 Seefeld, De|
    JP3998786B2|1997-12-16|2007-10-31|触媒化成工業株式会社|Hard coat film forming coating liquid and hard coat film-coated substrate|
    WO2002059167A1|2001-01-25|2002-08-01|Sekisui Chemical Co., Ltd.|Polyvinyl acetal, polyvinyl acetal composition, ink, coating material, dispersant, heat-developable photosensitive material, ceramic green sheet, primer for plastic lens, recording agent for water-based ink, and adhesive for metal foil|
    EP1359198A1|2002-05-03|2003-11-05|SigmaKalon Group B.V.|Epoxy-modified polysiloxane resin based compositions useful for coatings|
    JP4041966B2|2002-06-18|2008-02-06|信越化学工業株式会社|Article with hard coat agent and hard coat film formed|
    JP2004175907A|2002-11-27|2004-06-24|Nippon Arc Co Ltd|Coating composition and coated plastic lens|
    WO2006106359A2|2005-04-06|2006-10-12|Dow Corning Corporation|Organosiloxane compositions|
    KR101282051B1|2010-12-21|2013-07-04|한국과학기술원|Fluorescent Dye-Siloxane Hybrid Resin|US10131802B2|2015-11-02|2018-11-20|Metashield Llc|Nanosilica based compositions, structures and apparatus incorporating same and related methods|
    US10519314B2|2015-11-16|2019-12-31|StoreDot Ltd.|Red-enhanced white LCD displays comprising sol-gel-based color conversion films|
    US10465110B2|2015-11-16|2019-11-05|StoreDot Ltd.|Rhodamine based salts|
    US10495917B2|2015-11-16|2019-12-03|StoreDot Ltd.|Protective layers produced by UV curing processes|
    US10472520B2|2015-11-16|2019-11-12|StoreDot Ltd.|Red enhancement in white LED displays using UV-cured color conversion films|
    US10533091B2|2015-11-16|2020-01-14|StoreDot Ltd.|Color conversion with solid matrix films|
    US10473979B2|2015-11-16|2019-11-12|StoreDot Ltd.|Color conversion films produced by UV curing processes|
    US10227492B2|2015-11-16|2019-03-12|StoreDot Ltd.|Modifications of the sol-gel films and production processes thereof|
    US9868859B2|2015-11-16|2018-01-16|StoreDot Ltd.|Color conversion in LCD displays|
    WO2017085707A1|2015-11-16|2017-05-26|StoreDot Ltd.|Rhodamine derivatives dyes and uses thereof|
    US10473968B2|2015-11-16|2019-11-12|StoreDot Ltd.|Protective layers produced by sol gel processes|
    US10059876B2|2015-11-16|2018-08-28|StoreDot Ltd.|Color conversion films with plasmon enhanced fluorescent dyes|
    US10100197B2|2016-08-31|2018-10-16|StoreDot Ltd.|Rhodamine derivatives dyes and uses thereof|
    KR101917425B1|2016-09-08|2018-11-09|동국대학교 산학협력단|Preparation method of flexible electrode, flexible electrode fabricated according to said method and flexible dye-sensitized solar cell comprising said electrode|
    DE102017200952A1|2017-01-20|2018-07-26|Fraunhofer-Gesellschaft zur Förderung der angewandten Forschung e.V.|Semiconductor device and method for manufacturing a semiconductor device|
    WO2020260684A1|2019-06-28|2020-12-30|Københavns Universitet|An optical sensor|
    法律状态:
    优先权:
    申请号 | 申请日 | 专利标题
    DK201370617|2013-10-24|
    DKPA201370617A|DK178111B1|2013-10-24|2013-10-24|Sol-gel based matrix|DKPA201370617A| DK178111B1|2013-10-24|2013-10-24|Sol-gel based matrix|
    US15/028,600| US10233328B2|2013-10-24|2014-10-24|Sol-gel based matrix|
    PCT/DK2014/050351| WO2015058778A1|2013-10-24|2014-10-24|Sol-gel based matrix|
    EP14792382.5A| EP3060607B1|2013-10-24|2014-10-24|Sol-gel based matrix|