    Mixture for the manufacture of glass The invention relates to a mixture for the manufacture of glass fibers which comprises the following materials, according to the percentages by weight thus defined: soda ash 8 to 10% dolomite 2 to 8% borax pentahydrate 6 to 11% cullet 40 to 65% sand 15 to 30% limestone 2 to 6% nepheline 0 to 1.5%
    公开号:BE1021033B1
    申请号:E2009/0516
    申请日:2009-08-24
    公开日:2015-02-11
    发明作者:
    申请人:Knauf Insulation；
    IPC主号:
    专利说明:

    Mix for glass production
    The present invention relates to a mixture for the manufacture of glass, in particular a composition suitable for the manufacture of glass fibers, as well as to a process for the production of glass fibers.
    The glass fibers are known, among others, for their insulation qualities. For this particular application, the fibers are generally bonded with a synthetic resin and the finished product will have the form of rigid panels or soft mattresses to protect walls and ceilings, or the shape of shells to insulate the pipes.
    Compositions of raw material mixtures for the manufacture of glass fibers generally result from a compromise between the properties desired for these fibers and the constraints imposed by the industrial manufacturing processes. Generally, the molten glass is fed into a hollow body which rotates at high speed (centrifuge). This body has a peripheral wall perforated with many orifices through which the glass is sprayed under the action of the centrifugal force, so that so-called primary fibers are formed which are then stretched, for example by the action of flames or a gaseous stream .
    In one aspect, the present invention provides a blend for the manufacture of glass fibers according to claim 1, the dependent claims having preferred embodiments. The invention relates to a mixture for the production of glass fibers, comprising the following materials, according to the weight percentages thus defined: sodium carbonate 8 to 10% dolomite 2 to 8% borax pentahydrate 6 to 11%, preferably 8 to 10% by weight at 10% calcine 40 to 65%, preferably 40 to 50% sand 15 to 30%, preferably 20 to 30% limestone 2 to 6% nepheline 0 to 1.5%
    This composition has the advantage of being able to present several of the following interesting properties: the resulting fibers offer good insulating properties; the mixture melts at a temperature suitable for fiberizing in the centrifuges, reducing the risk of obstruction of the projection orifices of the centrifuges; the melted mixture homogenizes correctly in the oven, reducing the defects appearing during the fiberizing step; the cost of raw materials is advantageous; - the use of a large proportion of cullet (recycled glass) is beneficial for the environment.
    The cullet (also called cullet) used in the mixture according to the invention can come from two sources: flat glass and hollow glass (bottles). Preferably, the mixture according to the invention comprises between 0 and 30% by weight of flat glass cullet and between 10 and 50% by weight of hollow glass cullet.
    According to another aspect, the subject of the present invention is a method for manufacturing glass fibers according to claim 3. The invention relates to a process for manufacturing glass fibers from a mixture of raw materials, comprising the steps following: - loading of raw materials into the melting zone of an oven, the mixture of raw materials comprising the following materials, according to the weight percentages thus defined: sodium carbonate 8 to 10% dolomite 2 to 8% borax pentahydrate 6 at 11% calcine 40 to 65% sand 15 to 30% limestone 2 to 6% nepheline 0 to 1.5% - heating the mixture to a temperature above the liquidus temperature of the resulting glass, to form a molten glass capable of forming fibers ; - Fiberization of molten glass, that is to say, transformation of molten glass into fibers, for example by means of centrifuges.
    Two particular embodiments of the invention will now be described, as examples.
    Here are two examples (Ex.1 and Ex.2) of mixture composition according to the invention. The contents of different ingredients are given in percentages by weight.
    These mixtures made it possible to manufacture glass fibers according to the centrifugation process previously described. After sizing with an organic binder, they formed insulating glass wool.
    权利要求:
    Claims (4)
    [1]
    1. Mixture for the manufacture of glass fibers, characterized in that it comprises the following materials, according to the weight percentages thus defined: sodium carbonate 8 to 10% dolomite 2 to 8% borax pentahydrate 6 to 11% cullet 40 at 65% sand 15 to 30% limestone 2 to 6% nepheline 0 to 1.5%
    [2]
    2. Mixture according to claim 1, characterized in that it comprises: sodium carbonate 8 to 10% dolomite 2 to 8% borax pentahydrate 8 to 10% cullet 40 to 50% sand 20 to 30% limestone 2 to 6% nepheline 0 to 1.5%
    [3]
    3. Mixture according to claim 1 or claim 2, characterized in that it comprises between 0 and 30% weight of flat glass cullet and between 10 and 50% by weight of hollow glass cullet.
    [4]
    4. A method of manufacturing glass fibers from a mixture of raw materials, characterized in that it comprises the following steps: - loading of raw materials into the melting zone of an oven, the mixture of raw materials including the following materials, according to the weight percentages thus defined: sodium carbonate 8 to 10% dolomite 2 to 8% borax pentahydrate 6 to 11% caldn 40 to 65% sand 15 to 30% limestone 2 to 6% nepheline 0 to 1.5 - heating the mixture to a temperature above the liquidus temperature of the resulting glass, to form a molten glass capable of forming fibers; - Fiberization of molten glass by centrifugation.
    类似技术:
    公开号 | 公开日 | 专利标题
    EP0915811B1|2004-07-14|Method and device for waste recycling in a mineral fibre manufacturing plant
    CN1260258C|2006-06-21|Process for producing epoxidized diene polymer
    JP2009509909A|2009-03-12|Composition and production method of continuous basalt fiber
    RU2013133836A|2015-01-27|PRELIMINARY PROCESSING OF RAW MATERIALS FOR PRODUCING BASALT FIBERS
    CN104261669B|2017-04-19|Method for preparing continuous basalt fiber with industry waste solid as raw material
    CN102531402A|2012-07-04|Method for producing alkali-free glass fiber by albite serving as fluxible clarifying agent
    BE1021033B1|2015-02-11|MIXTURE FOR THE MANUFACTURE OF GLASS.
    FR2467183A1|1981-04-17|CERAMIC FIBERS AND WOOLS OBTAINED FROM FLY ASH
    KR20170026704A|2017-03-09|Mineral fiber and manufacturing method thereof
    JP4670149B2|2011-04-13|A method for producing rock wool made from granulated products of municipal waste incineration ash
    CN107893330A|2018-04-10|A kind of preparation method of plasma grafting processing complex fiber material
    CA2942733A1|2015-10-15|Composite comprising a mineral wool comprising a sugar
    CN106750702A|2017-05-31|A kind of preparation method of flame retardant plastics film
    CN108359160A|2018-08-03|A kind of preparation method of stretch-proof nanosized SiO_2-high density polyethylene |-lignocellulose fiber composite plastic
    CN103910927A|2014-07-09|High-molecular composition used for plastic building template and its preparation method
    CN102603197B|2013-11-27|Method for producing alkali-free glass fiber by taking industrial slag as raw material
    RU2234473C1|2004-08-20|Charge for production of mineral wool
    CN104530575A|2015-04-22|Glass fiber reinforced polypropylene
    CN109054399A|2018-12-21|A kind of heat-resisting melting silicone rubber and preparation method thereof
    CN104341752A|2015-02-11|Heatproof biodegradable plastic and its preparation method
    TW201329007A|2013-07-16|Process for melting and refining silica-based glass
    WO2012131241A1|2012-10-04|Powder material including activating glass for cement products
    CN108026374A|2018-05-11|Mixture containing plastics and organic fiber
    RU2306302C1|2007-09-20|Method for building article finishing
    BE1025982B1|2019-09-04|NON-CARRIER CONCRETE TYPE CONSTRUCTION MATERIAL COMPRISING LIME-LINKED LINEN ANAS AND A SLEEVE ACCELERATOR
    同族专利:
    公开号 | 公开日
    BE1017687A6|2009-03-03|
    引用文献:
    公开号 | 申请日 | 公开日 | 申请人 | 专利标题
    US2414068A|1943-12-14|1947-01-07|American Rock Wool Corp|Method for utilizing borate tailings|
    GB950843A|1959-07-23|1964-02-26|Owens Corning Fiberglass Corp|Glass batch compositions and method of producing fibres therefrom|
    JP2007217280A|2007-04-27|2007-08-30|Nippon Sheet Glass Co Ltd|Manufacturing method of glass staple fiber using cullet as raw material|
    WO2014128714A1|2013-02-19|2014-08-28|Council Of Scientific & Industrial Research|Energy efficient soda lime silicate glass compositions using borax pentahydrate|
    法律状态:
    优先权:
    申请号 | 申请日 | 专利标题
    BE2008/0468|2008-08-25|
    BE2008/0468A|BE1017687A6|2008-08-25|2008-08-25|Mixture, useful for the preparation of glass fibers, comprises materials comprising sodium carbonate, dolomite, borax pentahydrate, cullet, sand, limestone and nepheline|
    [返回顶部]