    • 专利摘要:
    A casting of a white cast iron alloy and a method of producing the casting are disclosed. A white cast alloy is 5 also disclosed. The casting has a solution treated microstructure that comprises a ferrous matrix of retained austenite and chromium carbides dispersed in the matrix, with the carbides comprising 15 to 60% volume fraction of the alloy. The matrix composition comprises: manganese: 8 10 to 20 wt%; carbon:0.8 to 1.5 wt%; chromium: 5 to 15 wt%; and iron: balance (including incidental impurities). 4237433_1 (GHKatters) P81372.AU.2 9/04/13 ffilv% HIM Awl', IR, Figure 1 10 W, V 1XI, Ell w EW IN M m OR 10, np IS g IMIR -, X allows, ON IM WERW a m 0 mom IN SIMMS\ -111111 - , M X ........... ffi m MILIL. "I ill Mll W, 'S.,:M ME A '1 'M IN "'I SO INNER 0, xm Rll g * ONOWN R IM 'M Rl Wl 'MKlXx MOR M MKIN EM IlRl!lPVMAWl MM M W,K z :,. MINE IMISIMMIMIN NN INN M I MMEN Mm , xn M IX I 'M SO nm Figure 2
    公开号:AU2013203224A1
    申请号:U2013203224
    申请日:2013-04-09
    公开日:2013-05-02
    发明作者:Kevin Dolman
    申请人:Weir Minerals Australia Ltd；
    IPC主号:C22C37-06
    专利说明:
    - 1 METAL ALLOYS FOR HIGH IMPACT APPLICATIONS Field of the invention 5 This invention relates to metal alloys for high impact applications and particularly, although by no means exclusively, to alloys of iron having high toughness, and castings of these alloys. 10 Background High chromium white cast iron, such as disclosed in US Patent 1,245,552, is used extensively in the mining and mineral processing industry for the manufacture of 15 equipment that is subject to severe abrasion and erosion wear, for example slurry pumps and pipelines, mill liners, crushers, transfer chutes and ground-engaging tools. The high chromium white cast iron disclosed in the US patent comprises 25-30 wt% Cr, 1.5-3 wt% C, up to 3 wt% Si, and 20 balance Fe and trace amounts of Mn, S, P, and Cu. The microstructures of high chromium white cast iron contain extremely hard (around 1500 HV - according to Australian Standard 1817, part 1) chromium carbides 25 (Fe,Cr) 7
    C
    3 in a ferrous matrix with a hardness of about 700 HV. These carbides provide effective protection against the abrasive or erosive action of silica sand (around 1150 HV) which is the most abundant medium encountered in ores fed to mining and mineral processing plants. 30 In general terms, high chromium white cast iron offers greater wear resistance than steels which have been hardened by quench-and-temper methods, and also provides moderate corrosion resistance compared to stainless 35 steels. However, white cast iron has a low fracture toughness (<30 MPa.lm), making it unsuitable for use in high impact situations such as in crushing machinery. 4237433_1 (GHKatters) P81372.AU.2 9/04/13 - 2 Fracture toughness is a function of (a) the carbide content, and its particle size, shape, and distribution throughout the matrix, and (b) the nature of the ferrous 5 matrix, i.e. whether it comprises austenite, martensite, ferrite, pearlite or a combination of two or more of these phases. Furthermore, high chromium white cast iron has low thermal 10 shock resistance and cannot cope with very sudden changes of temperature. Previous attempts by the inventor to produce a tougher white cast iron by adding quantities of other elements 15 such as manganese to high chromium white cast iron were unsuccessful. Specifically, the various alloying elements in white cast iron, namely chromium, carbon, manganese, silicon, nickel and iron, can partition differently during solidification, resulting in a wide range of potential 20 chemical compositions in the ferrous matrix. For example, it is possible to obtain a white cast iron with a ferrous matrix containing more than 1.3 wt% carbon, but this can result in the presence of embrittling proeutectoid carbides in the microstructure. It is also possible to 25 obtain a white cast iron with a ferrous matrix containing less than 0.8 wt% carbon, but this can result in an unstable austenitic ferrous matrix with a low work hardening capacity. Furthermore, it is possible to obtain a white cast iron with a ferrous matrix containing a low 30 chromium content, which can result in poor corrosion resistance. This disclosure is concerned particularly, although by no means exclusively, with the provision of a high chromium 35 white cast iron which has an improved combination of toughness and hardness. It is desirable that the high chromium white cast iron be suitable for high impact 4237433_1 (GHKatters) P81372.AU.2 9/04/13 - 3 abrasive wear applications, such as used in crushing machinery or slurry pumps. Summary of the Disclosure 5 Through experimental work carried out by the applicant, it has been unexpectedly discovered that an inverse relationship exists between the chromium and carbon concentrations of the ferrous matrix formed during 10 solidification of a range of high chromium cast irons. Quantification of this inverse relationship between chromium and carbon in the ferrous matrix has made it possible for the applicant to provide bulk chemical compositions of selected high chromium cast irons 15 containing manganese that result in microstructures containing phases with the required chemistries to yield white cast irons with toughness, work hardening capacity, wear resistance and corrosion resistance to be suitable for use in high impact abrasive wear applications. 20 The experimental work carried out by the applicant revealed that chromium has a significant impact on the carbon content in the ferrous matrix where previously there was no understanding of this effect. It was thought 25 previously that chromium largely formed carbides of the form M 7
    C
    3 carbides (where "M" comprises Cr, Fe, and Mn), i.e. carbides having a high ratio of chromium to carbon. The experimental work, however, identified that considerable chromium is retained in solid solution and 30 that there exists an inverse relationship between chromium content in the ferrous matrix and the amount of carbon that is retained in the ferrous matrix of high chromium white cast irons, whereby as the bulk chromium concentration of a high chromium white cast iron increases 35 the chromium in the matrix of the alloy increases and the carbon in the matrix decreases. 4237433_1 (GHKatters) P81372.AU.2 9/04/13 - 4 The experimental work carried out by the applicant has shown that, during solidification of high chromium cast irons, chromium and carbon partition preferentially to the 5 primary and eutectic M 7
    C
    3 carbides leaving a residual amount of chromium and carbon in the ferrous matrix. In addition, the applicant has shown that when 12 wt% manganese is added to high chromium cast iron, the manganese, to a first approximation, is evenly distributed 10 between the M 7
    C
    3 carbides and the ferrous matrix - that is, both the carbides and the ferrous matrix contain a nominal 12 wt% manganese. The applicant therefore believes that it is possible to 15 obtain a predetermined amount of chromium and carbon in the ferrous matrix of high chromium cast irons containing 8-20 wt% manganese, by having regard to the following findings of the applicant for the partitioning of chromium and carbon in these alloys during the solidification 20 process. Finding No. 1 - When about 12 wt% manganese is added to high chromium cast irons the manganese does not partition preferentially to any particular phase and is 25 approximately evenly distributed between the carbides and ferrous matrix. Finding No. 2 - The residual carbon content of the ferrous matrix is inversely proportional to the residual 30 chromium content of the ferrous matrix. For example, experimental work carried out by the applicant found that when a high chromium cast iron, with a bulk chemical composition of Fe-20Cr-3.OC solidifies, the residual chemical composition of the ferrous matrix is 35 approximately Fe-12Cr-1.1C, compared to an example where, when a bulk chemical composition of Fe-lOCr-3.OC solidifies, the residual chemical composition of the 4237433_1 (GHKatters) P81372.AU.2 9/04/13 - 5 ferrous matrix is approximately Fe-6Cr-1.6C, and compared to an example where, when a bulk chemical composition of Fe-30Cr-3.OC solidifies, the residual chemical composition of the ferrous matrix is approximately Fe-18Cr-0.8C. 5 The applicant has further found that the chemistry of the ferrous matrix of a bulk alloy Fe-20Cr-12Mn-3.OC is Fe 12Cr-12Mn-1.1C after solidification (that is a 12 wt% Mn and 1.1 wt% C ferrous matrix containing 12 wt% Cr in solid 10 solution). Accordingly, there is provided a casting of a white cast iron alloy having the following ferrous matrix chemistry in a solution treated condition; 15 manganese: 8 to 20 wt% carbon: 0.8 to 1.5 wt%; chromium: 5 to 15 wt%; and iron: balance (including incidental impurities); and 20 having a microstructure comprising: (a) retained austenite as the matrix; and 25 (b) carbides dispersed in the matrix, the carbides comprising 5 to 60% volume fraction of the casting. The term "solution treated condition" is understood herein 30 to mean heating the alloy to a temperature and holding the alloy at the temperature for a time to dissolve the carbides and quickly cooling the alloy to room temperature to retain the microstructure. 35 The chromium concentration and/or the carbon concentration in the bulk chemistry of the white cast iron alloy may be selected having regard to an inverse relationship between 4237433_1 (GHKatters) P81372.AU.2 9/04/13 - 6 chromium concentration and carbon concentration in the matrix to control the matrix concentration of one or both of the chromium and the carbon to be within the above described ranges so that the casting has required 5 properties, such as toughness and/or hardness and/or wear resistance and/or work hardening capacity and/or corrosion resistance. For example, the chromium concentration in the bulk 10 chemistry of the white cast iron alloy may be selected having regard to the inverse relationship between chromium concentration and carbon concentration in the matrix to control the matrix concentration of carbon to be greater than 0.8 wt% and less than 1.5 wt%, typically less than 15 1.2 wt%, typically more than 1 wt% in the solution treated condition. In this example, the manganese concentration in the bulk chemistry may be 10-16, typically 10-14 wt%, and more typically 12 wt%. 20 The concentrations of chromium, carbon and manganese in the bulk chemistry of the white cast iron alloy may be selected so that the casting has the following mechanical properties in the solution treated form of the casting: e Tensile strength: at least 650, typically at least 25 750 MPa. e Yield strength: at least 500, typically at least 600 MPa. e Fracture toughness: at least 50, typically at least 60 MPalm. 30 e Elongation: at least 1.2% e Hardness: at least 350, typically at least 400 Brinell. e Plastically deformability under compressive load: at least 10% 35 e High work hardening capacity: up to at least 550 Brinell in service. 4237433_1 (GHKatters) P81372.AU.2 9/04/13 The carbides may be 5 to 60% volume fraction of the casting, typically 10 to 40% volume fraction of the casting, and more typically 15-30% volume fraction of the casting. The microstructure may comprise 10 to 20 volume% 5 carbides dispersed in the retained austenite matrix. The carbides may be chromium-iron-manganese carbides. The carbide phase of the above casting after solution 10 treatment may be primary chromium-iron-manganese carbides and/or eutectic chromium-iron-manganese carbides and the retained austenite matrix may be primary austenite dendrites and/or eutectic austenite. 15 The carbides may also be niobium carbide and/or a chemical mixture of niobium carbide and titanium carbide. Metal alloys containing these carbides are described in the patent specification entitled "Hard Metal Material" lodged on 1 February 2011 with an International application in 20 the name of the applicant and the entire patent specification of this application is incorporated herein by cross-reference. The patent specification mentioned in the preceding 25 paragraph describes that the terms "a chemical mixture of niobium carbide and titanium carbide" and "niobium/titanium carbides" are understood to be synonyms. In addition, the patent specification describes that the term "chemical mixture" is understood in this context to 30 mean that the niobium carbides and the titanium carbides are not present as separate particles in the mixture but are present as particles of niobium/titanium carbides. For carbide volume fractions below 5%, the carbides do not 35 make a significant contribution to the wear resistance of the alloy. However, for carbide volume fractions greater than 60%, there is insufficient ferrous matrix to hold the 4237433_1 (GHKatters) P81372.AU.2 9/04/13 - 8 carbides together. As a result, the fracture toughness of the alloy may be unsuitable for crushing machinery. The matrix may be substantially free of ferrite. 5 The term "substantially free of ferrite" indicates that the intention is to provide a matrix that comprises retained austenite without any ferrite but at the same time recognises that in any given situation in practice 10 there may be a small amount of ferrite. The white cast iron alloy of the casting may have a bulk composition comprising: chromium: 10 to 40 wt%; 15 carbon: 2 to 6 wt%; manganese: 8 to 20 wt%; silicon: 0 to 1.5 wt%; and balance of iron and incidental impurities. 20 The white cast iron alloy may comprise 0.5 to 1.0 wt% silicon. The white cast iron alloy may comprise 2 to 4 wt% carbon. 25 The white cast iron alloy of the casting may have a bulk composition comprising: chromium: 7 to 36 wt%; carbon: 3 to 8.5 wt%; manganese: 5 to 18 wt%; 30 silicon: 0 to 1.5 wt%; titanium: 2 to 13 wt%; and balance of iron and incidental impurities. The white cast iron alloy of the casting may have a bulk 35 composition comprising: chromium: 7 to 36 wt%; carbon: 3 to 8.5 wt%; 4237433_1 (GHKatters) P81372.AU.2 9/04/13 - 9 manganese: 5 to 18 wt%; silicon: 0 to 1.5 wt%; niobium: 8 to 33 wt%; and balance of iron and incidental impurities. 5 The white cast iron alloy of the casting may have a bulk composition comprising: chromium: 7 to 36 wt%; carbon: 3 to 8.5 wt%; 10 manganese: 5 to 18 wt%; silicon: 0 to 1.5 wt%; niobium and titanium: 5 to 25 wt%; and balance of iron and incidental impurities. 15 The white cast iron alloy of the casting may have a bulk composition comprising chromium, carbon, manganese, silicon, any one or more of the transition metals titanium, zirconium, hafnium, vanadium, niobium, tantalum, chromium, molybdenum and tungsten; and balance of iron and 20 incidental impurities, with the amount of the transition metal or metals selected so that carbides of these metal or metals in the casting comprise up to 20 volume % of the casting. 25 The casting may be equipment that is subject to severe abrasion and erosion wear, such as slurry pumps and pipelines, mill liners, crushers, transfer chutes and ground-engaging tools. 30 There is also provided equipment that is subject to severe abrasion and erosion wear, such as slurry pumps and pipelines, mill liners, crushers, transfer chutes and ground-engaging tools that includes the casting. 35 The equipment may be crushing machinery or slurry pumps. There is also provided a white cast iron alloy comprising 4237433_1 (GHIatters) P81372.AU.2 9/04/13 - 10 the following bulk chemistry: chromium: 10 to 40 wt%; carbon: 2 to 6 wt%; 5 manganese: 8 to 20 wt%; silicon: 0 to 1.5 wt%; and balance of iron and incidental impurities. The white cast iron alloy may comprise 12 to 14 wt% 10 manganese. The white cast iron alloy may comprise 0.5 to 1.0 wt% silicon. 15 The white cast iron alloy may comprise 2 to 4 wt% carbon. There is also provided a white cast iron alloy comprising the following bulk chemistry: chromium: 7 to 36 wt%; 20 carbon: 3 to 8.5 wt%; manganese: 5 to 18 wt%; silicon: 0 to 1.5 wt%; titanium: 2 to 13 wt%; and balance of iron and incidental impurities. 25 There is also provided a white cast iron alloy comprising the following bulk chemistry: chromium: 7 to 36 wt%; carbon: 3 to 8.5 wt%; 30 manganese: 5 to 18 wt%; silicon: 0 to 1.5 wt%; niobium: 8 to 33 wt%; and balance of iron and incidental impurities. 35 There is also provided a white cast iron alloy comprising the following bulk chemistry: chromium: 7 to 36 wt%; 4237433_1 (GHKatters) P81372.AU.2 9/04/13 - 11 carbon: 3 to 8.5 wt%; manganese: 5 to 18 wt%; silicon: 0 to 1.5 wt%; niobium and titanium: 5 to 25 wt%; and 5 balance of iron and incidental impurities. There is also provided a white cast iron alloy comprising a bulk chemistry comprising chromium, carbon, manganese, silicon, any one or more of the transition metals 10 titanium, zirconium, hafnium, vanadium, niobium, tantalum, chromium, molybdenum and tungsten; and balance of iron and incidental impurities, with the amount of the transition metal or metals selected so that carbides of these metal or metals in a solid form of the alloy comprise up to 20 15 volume % of the solid form. There is also provided a method of producing a casting of the above-described white cast iron alloy, the method comprising the steps of: 20 (a) forming a melt of the above-described white cast iron alloy; (b) pouring the melt into a mould to form the 25 casting; and (c) allowing the casting to cool substantially to room temperature. 30 Step (a) of the method may comprise adding (a) niobium or (b) niobium and titanium to the melt in a form that produces particles of niobium carbide and/or particles of a chemical mixture of niobium carbide and titanium carbide in a microstructure of the casting. The method may 35 include additional method steps as described in the above mentioned specification entitled "Hard Metal Material" lodged on 1 February 2011 with the above-mentioned 4237433_1 (GHKatters) P81372.AU.2 9/04/13 - 12 International application in the name of the applicant. As is indicated above, the entire patent specification of this application is incorporated herein by cross reference. 5 The method may further comprise heat treating the casting after step (c) by: (d) heating the casting to a solution treatment 10 temperature; and (e) quenching the casting. Step (e) may comprise quenching the casting in water. 15 Step (e) may comprise quenching the casting substantially to room temperature. The resulting microstructure may be a matrix of retained 20 austenite and carbides dispersed in the matrix, the carbides comprising 5 to 60% volume fraction of the casting The resulting ferrous matrix may be austenitic to the 25 extent that it is substantially free of ferrite. The resulting ferrous matrix may be wholly austenitic due to the rapid cooling process. The solution treatment temperature may be in a range of 30 900'C to 1200'C, typically 1000'C to 1200'C. The casting may be retained at the solution treatment temperature for at least one hour, but may be retained at the said solution treatment temperature for at least two 35 hours, to ensure dissolution of all secondary carbides and attainment of chemical homogenization. 4237433_1 (GHKatters) P81372.AU.2 9/04/13 - 13 Brief description of the drawings The white cast iron alloy and casting will now be described further by way of example only, and with 5 reference to the accompanying drawings, in which: Figure 1 is a micrograph of the microstructure of an as cast iron alloy in accordance with an embodiment of the inventions. 10 Figure 2 is a micrograph of the microstructure of the as cast iron alloy in Figure 1 after heat treatment. Detailed description 15 Although a range of white cast iron alloy compositions are with the scope of the present invention, the following description is directed to one cast iron alloy in particular as an example. 20 It is noted that the applicant has carried out extensive experimental work in relation to the white cast iron alloy of the present invention that has established the upper and lower limits of the ranges of the elements and the 25 volume fractions of the carbides in the following as-cast microstructure of the present invention comprising: (a) a ferrous matrix comprising retained austenite, the matrix having a composition of: 30 manganese: 8 to 20 wt% carbon: 0.8 to 1.5 wt%; chromium: 5 to 15 wt%; and iron: balance (including incidental 35 impurities); and (b) chromium carbides comprising 5 to 60% volume 4237433_1 (GHIatters) P81372.AU.2 9/04/13 - 14 fraction. The example white cast iron alloy had the following bulk composition: 5 chromium: 20 wt%; carbon: 3 wt%; manganese: 12 wt%; silicon: 0.5 wt%; and 10 a balance of iron and incidental impurities. A melt of this white cast iron alloy was prepared and cast into samples for metallurgical test work, including hardness testing, toughness testing and metallography. 15 The test work was performed on as-cast samples that were allowed to cool in moulds to room temperature. Test work was also carried out on the as-cast samples that were then subjected to a solution heat treatment involving reheating 20 the as-cast samples to a temperature of 1200'C for a period of 2 hours followed by a water quench. A summary of the hardness and toughness test results is set out in Table 1 below. 25 Table 1 - Summary of Test Results Alloy form Hardness Hardness (HB Fracture Ferrite (HV50) - converted) Toughness meter (MPam ) reading As cast 413 393 49.85 0% Solution treated at 446 424 56.35 0% 1200 Celsius 4237433_1 (GHatters) P81372.AU.2 9/04/13 - 15 The microstructure of the white cast iron alloy in the as cast form (Figure 1) shows large austenite dendrites in a matrix of eutectic austenite. By contrast, the solution heat treated form of the iron alloy (Figure 2) shows 5 austenite dendrites generally well dispersed in a retained austenite matrix. The ferrite meter readings for the as cast and solution heat treated samples (that is, magnetism readings), show that the samples were non-magnetic. This, therefore, indicates that the castings did not include 10 ferrite or martensite or pearlite in the ferrous matrix. Compositional analysis of the retained austenite matrix is revealed a chromium content in the matrix solid solution of about 12 wt% and a carbon content in the matrix of 15 about 1.1 wt%. The retained austenite matrix therefore can be regarded as a manganese steel with relatively high chromium content in solid solution for improved hardness and improved corrosion resistance, which are not features of conventional austenitic manganese steel. 20 Additionally, the volume percentage of chromium carbides contributed to hardness and overall wear resistance. Although the hardness results in Table 1 are below typical hardness measurements of wear resistant cast iron alloys, 25 it was found that hardness of the iron alloy increased after work hardening treatments to a level that is comparable to hardness of known wear resistant cast iron alloys. 30 Further samples of the same white cast iron alloy were cast and then subjected to heat treatment at 1200'C for a period of 2 hours. The samples had a microstructure comprising primary 35 austenite dendrites plus eutectic carbides and eutectic austenite. 4237433_1 (GHKatters) P81372.AU.2 9/04/13 - 16 Microanalysis of the samples revealed the following: e Both the elements chromium and carbon partition heavily to the carbide phase which was identified as 5 (Fe, Cr, Mn) 7
    C
    3 by Electron Back Scattered Diffraction. e To a first approximation, the element manganese is evenly distributed between the carbides and austenite phases. 10 e 11.3% by volume of the microstructure consisted of primary austenite dendrites. e 22.3% by volume of the microstructure consisted of 15 eutectic carbides. e 66.4% by volume of the microstructure consisted of eutectic austenite. 20 e The carbon content of the austenite phase was 0.98 wt%. e The manganese content of the austenite phases was 11.8 wt% and 11.6 wt%. 25 e The ferrous matrix of the alloy consisted of 11.3% by volume primary austenite dendrites and 66.4% by volume eutectic austenite. 30 e The chemistry of the ferrous matrix was Fe - 12Cr 12Mn - 1.OC - 0.4Si, which is essentially a basic manganese steel containing 12% chromium in solid solution. 35 Fracture toughness testing was carried out on two samples according to the procedure described in "Double Torsion Technique as a Universal Fracture Toughness Method", 4237433_1 (GHKatters) P81372.AU.2 9/04/13 - 17 Outwater, J.O. et al., Fracture Toughness and Slow-Stable Cracking, ASTM STP 559, American Society for Testing and Materials, 1974, pp 127- 138. 5 The applicant found that the presence of manganese in the alloy allowed the ferrous matrix to become surface work hardened by the action of compressive loading during service to provide a material with moderate wear resistance and excellent toughness, attributable to the 10 presence of a metastable austenitic structure formed by water quenching of the casting from a temperature of about 1200'C to room temperature. The wholly austenitic structure could be retained during cooling to room temperature due to the presence of both a high manganese 15 content and a specific carbon content. Because of the synergistic combination of the presence of the manganese, a casting that was made out of a white cast iron alloy of the invention offers significantly improved 20 fracture toughness compared to regular high chromium white cast iron, in combination with the advantages of white cast iron of (a) high abrasion and erosion wear resistance, (b) relatively high yield strength, and (c) moderate corrosion resistance in acidic environments. 25 The white cast iron alloy of the above-mentioned example had an average fracture toughness of 56.3 MPalm. This result compares favourably with toughness values of 25-30 MPa.lm. for high chromium white cast irons. It is 30 anticipated that this fracture toughness makes the alloys suitable for use in high impact applications, such as pumps, including gravel pumps and slurry pumps. The alloys are also suitable for machinery for crushing rock, minerals or ore, such as primary crushers. 35 One advantage of the white cast iron alloy of the present invention is that hot working of the as formed alloy 4237433_1 (GHKatters) P81372.AU.2 9/04/13 - 18 breaks up the carbide into discrete carbides, thereby improving the ductility of the alloy. Reference to any prior art in the specification is not, 5 and should not be taken as, an acknowledgment or any form of suggestion that this prior art forms part of the common general knowledge in Australia or any other country. Many modifications may be made to the preferred embodiment 10 of the present invention as described above without departing from the spirit and scope of the present invention. It will be understood that the term "comprises" or its 15 grammatical variants as used in this specification and claims is equivalent to the term "includes" and is not to be taken as excluding the presence of other features or elements. 20 4237433_1 (GHKatters) P81372.AU.2 9/04/13
    权利要求:
    Claims (26)
    [1] 1. A casting of a white cast iron alloy having a solution treated microstructure comprising: (a) a ferrous matrix comprising retained austenite, the matrix having a composition of: manganese: 8 to 20 wt% 10 carbon: 0.8 to 1.5 wt%; chromium: 5 to 15 wt%; and iron: balance (including incidental impurities); and 15 (b) chromium carbides dispersed in the matrix, the carbides comprising 15 to 60% volume fraction of the alloy.
    [2] 2. The casting defined in claim I wherein the 20 chromium concentration and/or the carbon concentration in a bulk chemistry of the white cast iron alloy is selected having regard to an inverse relationship between chromium concentration and carbon concentration in the matrix to control the matrix concentration of one or both of the 25 chromium and the carbon to be within the ranges in the matrix defined in claim 1 so that the casting has required properties, such as toughness and/or hardness and/or wear resistance and/or work hardening capacity and/or corrosion resistance. 30
    [3] 3. The casting defined in claim I or claim 2 wherein the matrix concentration of carbon is greater than 0.8 wt% and less than 1.5 wt%. 35
    [4] 4. The casting defined in any one of the preceding claims wherein the matrix concentration of carbon is less than 1.2 wt%. -237 3 1 (0HMUatters) 81372. A .2 9/04/13 - 20 5. The casting defined in any one of the preceding claims wherein the matrix concentration of carbon is more than 1 wt%.
    [5] 5
    [6] 6. The casting defined in any one of the preceding claims wherein the carbides comprise 5 to 60% volume fraction of the casting. 10
    [7] 7. The casting defined in any one of the preceding claims wherein the carbides comprise 10 to 40% volume fraction of the casting.
    [8] 8. The casting defined in any one of the preceding 15 claims wherein the microstructure comprises 15 to 30 volume% carbides dispersed in the retained austenite matrix.
    [9] 9. The casting defined in any one of the preceding 20 claims wherein the carbides comprise chromium-iron manganese carbides.
    [10] 10. The casting defined in any one of the preceding claims wherein after solution treatment the ferrous matrix 25 comprises primary austenite dendrites and/or eutectic austenite and the carbide phase comprise primary chromium iron-manganese carbides and/or eutectic chromium-iron manganese carbides. 30
    [11] 11. The casting defined in any one of the preceding claims wherein the carbides comprise niobium carbide and/or a chemical mixture of niobium carbide and titanium carbide. 35
    [12] 12. The casting defined in any one of the preceding claims wherein the matrix is substantially free of ferrite. -233 1 (0H1Matters) 81372. A.2 9/04/13 - 21
    [13] 13. The casting defined in any one of the preceding claims comprising the following bulk composition: chromium: 10 to 40 wt%; 5 carbon: 2 to 6 wt%; manganese: 8 to 20 wt%; silicon: 0 to 1.5 wt%; and balance of iron and incidental impurities. 10
    [14] 14. The casting defined in claim 13 wherein the bulk composition comprises 0.5 to 1.0 wt% silicon.
    [15] 15. The casting defined in claim 13 or claim 14 wherein the bulk composition comprises 2 to 4 wt% carbon. 15
    [16] 16. The casting defined in any one of the claims 1 to 12 comprising the following bulk composition: chromium: 7 to 36 wt%; carbon: 3 to 8.5 wt%; 20 manganese: 5 to 18 wt%; silicon: 0 to 1.5 wt%; titanium: 2 to 13 wt%; and balance of iron and incidental impurities. 25
    [17] 17. The casting defined in any one of the claims I to 12 comprising the following bulk composition: chromium: 7 to 36 wt%; carbon: 3 to 8.5 wt%; manganese: 5 to 18 wt%; 30 silicon: 0 to 1.5 wt%; niobium: 8 to 33 wt%; and balance of iron and incidental impurities.
    [18] 18. The casting defined in any one of the claims I to 35 12 comprising the following bulk composition: chromium: 7 to 36 wt%; carbon: 3 to 8.5 wt%; -237 3 1 (0HMUatters) 81372. A .2 9/04/13 - 22 manganese: 5 to 18 wt%; silicon: 0 to 1.5 wt%; niobium and titanium: 5 to 25 wt%; and balance of iron and incidental impurities. 5
    [19] 19. Equipment that is subject to severe abrasion and erosion wear, such as slurry pumps and pipelines, mill liners, crushers, transfer chutes and ground-engaging tools that includes the casting defined in any one of the 10 preceding claims.
    [20] 20. A white cast iron alloy comprising the following bulk chemistry: chromium: 7 to 36 wt%; 15 carbon: 3 to 8.5 wt%; manganese: 5 to 18 wt%; silicon: 0 to 1.5 wt%; titanium: 2 to 13 wt%; and balance of iron and incidental impurities. 20
    [21] 21. A white cast iron alloy comprising the following bulk chemistry: chromium: 7 to 36 wt%; carbon: 3 to 8.5 wt%; 25 manganese: 5 to 18 wt%; silicon: 0 to 1.5 wt%; niobium: 8 to 33 wt%; and balance of iron and incidental impurities. 30
    [22] 22. A white cast iron alloy comprising the following bulk chemistry: chromium: 7 to 36 wt%; carbon: 3 to 8.5 wt%; manganese: 5 to 18 wt%; 35 silicon: 0 to 1.5 wt%; niobium and titanium: 5 to 25 wt%; and balance of iron and incidental impurities. -233 1 (0H1Matters) 81372. A.2 9/04/13 - 23
    [23] 23. A method of producing the casting defined in any one of claims I to 18 comprising the steps of: 5 (a) forming a melt of the white cast iron alloy defined in any one of claims 20 to 22; (b) pouring the melt into a mould to form the casting; and 10 (c) allowing the casting to cool substantially to room temperature.
    [24] 24. The method defined in claim 23 further comprises 15 heat treating the casting after step (c) by: (d) heating the casting to a solution treatment temperature; and 20 (e) quenching the casting.
    [25] 25. The method defined in claim 24 wherein the solution treatment temperature is in a range of 900*C to 12000C. 25
    [26] 26. The method defined in claim 24 or claim 25 wherein the casting is retained at the solution treatment temperature for at least one hour. 30 -237 3 1 (0HMUatters) 81372. A .2 9/04/13
    类似技术:
    公开号 | 公开日 | 专利标题
    US9976204B2|2018-05-22|Metal alloys for high impact applications
    KR102128026B1|2020-06-29|Ultrahigh-strength, high toughness, wear-resistant steel plate and manufacturing method thereof
    KR102218051B1|2021-02-22|High-hardness, high-toughness, wear-resistant steel plate and manufacturing method thereof
    KR102206319B1|2021-01-22|Austenitic abrasion-resistant steel sheet
    BR112015011069B1|2021-03-23|MARTENSITIC CAST STEEL AND ITS PRODUCTION METHOD
    Limooei et al.2012|Optimization of properties and structure with addition of titanium in hadfield steels
    Hosseini et al.2011|Optimization of heat treatment to obtain desired mechanical properties of high carbon Hadfield steels
    Javaheri et al.2018|Computational design of a novel medium-carbon, low-alloy steel microalloyed with niobium
    Moghaddam et al.2013|Impact–abrasion wear characteristics of in-situ VC-reinforced austenitic steel matrix composite
    KR20200105925A|2020-09-09|Austenitic wear-resistant steel plate
    Mahlami et al.2014|An Overview on high manganese steel casting
    Gürol et al.2020|Effect of carbon and manganese content on the microstructure and mechanical properties of high manganese austenitic steel
    CN111566230A|2020-08-21|Tough and corrosion-resistant white cast iron
    El-Fawkhry et al.2014|Eliminating heat treatment of Hadfield steel in stress abrasion wear applications
    Bedolla-Jacuinde2016|Niobium in Cast Irons
    AU2013203224B2|2015-02-05|Metal alloys for high impact applications
    Maldonado-Ruiz et al.2014|Effect of V-Ti on the microstructure and abrasive wear behavior of 6CrC cast steel mill balls
    Olawale et al.2018|Failure analysis of a crusher jaw
    US3262776A|1966-07-26|Medium carbon vanadium steel
    RU2753397C1|2021-08-16|Casting of high-strength wear-resistant steel and methods for heat treatment of castings of high-strength wear-resistant steel
    Sebeck et al.2018|High Mn, High Al Steels for Thick Plate Armor Applications
    KR102342651B1|2021-12-24|Erosion and corrosion resistance white cast iron
    RUANGCHAI et al.2021|Effects of annealing treatment on microstructure and hardness in the 28 wt% Cr cast iron with Mo/W addition
    Sahoo2012|A study on the effect of austempering temperature, time and copper addition on the mechanical properties of austempered ductile iron
    Olawale et al.2011|A study of premature failure of crusher jaws
    同族专利:
    公开号 | 公开日
    AU2013203224B2|2015-02-05|
    引用文献:
    公开号 | 申请日 | 公开日 | 申请人 | 专利标题
    GB340382A|1929-11-20|1931-01-01|Edgar Allen & Company Ltd|Improvements in alloy steels|
    法律状态:
    2015-06-04| FGA| Letters patent sealed or granted (standard patent)|
    优先权:
    申请号 | 申请日 | 专利标题
    AU2010900377||2010-02-01||
    AU2010904415||2010-10-01||
    AU2011208952A|AU2011208952A1|2010-02-01|2011-02-01|Metal alloys for high impact applications|
    AU2013203224A|AU2013203224B2|2010-02-01|2013-04-09|Metal alloys for high impact applications|AU2013203224A| AU2013203224B2|2010-02-01|2013-04-09|Metal alloys for high impact applications|